CN105462297B - A kind of automatically cleaning water aluminum-silver slurry and preparation method thereof - Google Patents

A kind of automatically cleaning water aluminum-silver slurry and preparation method thereof Download PDF

Info

Publication number
CN105462297B
CN105462297B CN201510976658.0A CN201510976658A CN105462297B CN 105462297 B CN105462297 B CN 105462297B CN 201510976658 A CN201510976658 A CN 201510976658A CN 105462297 B CN105462297 B CN 105462297B
Authority
CN
China
Prior art keywords
aluminum
silver slurry
automatically cleaning
weight
aluminum paste
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201510976658.0A
Other languages
Chinese (zh)
Other versions
CN105462297A (en
Inventor
周治国
王丹利
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanghai Normal University
Original Assignee
Shanghai Normal University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shanghai Normal University filed Critical Shanghai Normal University
Priority to CN201510976658.0A priority Critical patent/CN105462297B/en
Publication of CN105462297A publication Critical patent/CN105462297A/en
Application granted granted Critical
Publication of CN105462297B publication Critical patent/CN105462297B/en
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The present invention relates to a kind of automatically cleaning water aluminum-silver slurry and preparation method thereof, the water aluminum-silver slurry is oiliness aluminum paste Surface coating TiO2Film, pass through TiO2Automatically cleaning and water solubility are realized in the photocatalysis of film, the preparation method of the water aluminum-silver slurry, first with the commercially available oiliness aluminum paste of organic solvent washing, remove the organic matter of excess surface；Secondly, oiliness aluminum paste is pre-processed using titanate coupling agent, oiliness aluminum paste surface is formed covalent key connection；Then butyl titanate is added dropwise, the titanium dioxide of tetrabutyl titanate hydrolysis is formed film on aluminum paste surface, is finally prepared into water aluminum-silver slurry.Compared with prior art, the water aluminum-silver slurry that prepared by the present invention does not influence the metallic luster of aluminium flake, has good photocatalytic self-cleaning performance.

Description

A kind of automatically cleaning water aluminum-silver slurry and preparation method thereof
Technical field
The present invention relates to technical field of coatings, and in particular to a kind of TiO with self-cleaning function2Coating type water aluminium silver Slurry and preparation method thereof.
Background technology
Aluminum paste is a kind of indispensable metallic pigments in production and living, is a kind of by special thin snowflake shape or silver dollar shape piece The pulpous state aluminium pigment that alumina particles are handled through special process.Aluminum paste has good adhesive force, covering power and albedo, simultaneously There is the effect and suspension characteristic of uniqueness, and one kind for becoming most study, being most widely used Metallic pigments.
Along with the proposition of friendly environment society, coating also develop by gradual hydrotropismization and automatically cleaning direction.Traditional oils Property aluminum paste is not easily dispersed in water paint, without adapting to water paint due to substantial amounts of solvent naphtha be present；Simultaneously because Aluminium is a kind of amphoteric metal, oxidizable in meta-acid or the water paint of meta-alkali to lose metallic luster and produce hydrogen, closed Space in can produce " rise and listen ", for production bring certain potential safety hazard.Therefore, it is necessary to the aluminium silver applied to water paint Slurry is modified processing, to ensure the stability of water aluminum-silver slurry.
Automatic cleaning coating can make surface contaminant or dust granule automatic under the effect of the external force such as gravity, rainwater, wind-force Come off or removed by photocatalytic degradation, there are water saving, energy-saving and environmental protection.TiO2Coating is that one kind is based on inorganic light The automatic cleaning coating of semi-conducting material is catalyzed, its automatically cleaning principle includes two aspects：1、TiO2Produced under ultraviolet light irradiation Raw electron-hole pair, can be with adsorbing in TiO2The H of material surface2O and O2Generation redox reaction and generate hydrogen-oxygen freedom Base, hydroxyl free radical have very high activity, can be with decomposing organic pollutant, so as to realize self-cleaning surface；2、TiO2In light Super parents surface can be changed into according under, makes pollutant and TiO2Intimate surface contact, photocatalysis Decomposition efficiency is improved, while also had Pollutant is washed away beneficial to rainwater, realizes self-cleaning surface.So TiO2Material is shown well under practical service environment Automatically cleaning characteristic, thus in automatic cleaning coating field there is the actual use bigger than super-hydrophobic coat to be worth.
The surface modifying method of aluminum paste is a lot, and classification is also different.It can substantially be divided into：Coating modification method, deposition table Face is modified method, mechanochemical reaction, local reaction method, sol-gal process and microcapsule method etc..Coating modification method is typically in aluminium Powder surface covers a stratification compound film, and its unique transparency will not damage the luster performance of aluminium powder, thus more be ground Study carefully, but the compound hydrophily deficiency that prior art cladding is used, easy dry linting, and automatically cleaning can not be accomplished.
The content of the invention
It is an object of the present invention to overcome the above-mentioned drawbacks of the prior art and provide a kind of simple to operate, production Cost is low, does not influence the original gloss of aluminium flake, and covering power is high, the excellent automatically cleaning water aluminum-silver slurry of photocatalysis performance and its preparation side Method.
The purpose of the present invention can be achieved through the following technical solutions：A kind of automatically cleaning water aluminum-silver slurry, it is oiliness aluminium Silver paste Surface coating TiO2Film, pass through TiO2Automatically cleaning and water solubility are realized in the photocatalysis of film.The aluminum paste not shadow The original gloss of aluminium flake is rung, belongs to water soluble paint, and there is good photocatalytic self-cleaning function, belongs to Environmentally friendly coatings.
A kind of preparation method of automatically cleaning water aluminum-silver slurry described above, using sol-gal process, uses organic solvent first Commercially available oiliness aluminum paste is washed, removes the organic matter of excess surface；Secondly, oiliness aluminum paste is entered using titanate coupling agent Row pretreatment, makes oiliness aluminum paste surface form covalent key connection；Then butyl titanate is added dropwise, makes tetrabutyl titanate hydrolysis Titanium dioxide forms film on aluminum paste surface, is finally prepared into water aluminum-silver slurry.It specifically includes following steps：
(1) parts by weight of oiliness aluminum paste 1 are mixed with the parts by weight of acetone 1.5~3.5, removes having for oiliness aluminum paste surface Machine thing, obtain aluminum paste solid；
(2) titanate coupling agent is mixed with organic solvent, obtains mixed solution A, by butyl titanate and organic solvent Mixing, obtains mixed solution B；
(3) by the aluminum paste solid obtained by step (1) and the parts by weight of organic solvent 5~10, mixed solution A, the weight of water 0.1 Part is mixed, isolated solid mixture after 60~80 DEG C of reactions；
(4) solid mixture obtained by step (3) is mixed with the parts by weight of organic solvent 5~10, the parts by weight of water 0.1, adjusted PH to 7~8, under the conditions of 60~80 DEG C, is added dropwise mixed solution B, and ageing, which separates, after reaction produces automatically cleaning water aluminum-silver slurry.
The mass ratio of the medium oil aluminum paste of step (1) and acetone is 1：(1.5~3.5).
Step (2), step (3), the organic solvent described in step (4) are alcohols solvent, including ethanol or isopropanol.
Titanate coupling agent described in step (2) includes Di(dioctylpyrophosphato) ethylene titanate and three ethanol Chelate solution, (dioctylphyrophosphoric acid acyloxy) titanate esters of isopropyl three or double (the two octyloxy pyrophosphoric acid ester groups) ethylenes of amine One kind in titanate esters.
The mass concentration of step (2) described mixed solution A is 10%；
The mass concentration of the mixed solution B is 25%-75%.
The mass ratio of aluminum paste solid and titanate coupling agent in described step (3) is 1:(0.08-0.2)；It is described The step of (4) in solid mixture and butyl titanate mass ratio be 1：(0.25-0.5).
The conditioning agent for being used to adjust pH in step (4) is triethylamine or ammoniacal liquor.
Mixed solution B time for adding is 1~5h in step (4).
Digestion time is 3~6h in step (4).
In order to characterize the performance of the automatically cleaning water aluminum-silver slurry of the present invention, field emission scanning electron microscope is utilized (FESEM) and EDS power spectrums carry out surface topography sign and elementary analysis to the coating sample of preparation.
Compared with prior art, beneficial effects of the present invention are embodied in following several respects：
(1) prepare simply, production cost is low.
(2) water aluminum-silver slurry Surface coating of the invention has one layer of fine and close TiO2Film, the original gold of aluminium flake is not influenceed Belong to gloss, and due to TiO2The presence of film so that aluminum paste of the invention has good photocatalytic self-cleaning performance, is applicable In various water-based stoving paints, water-based ink and aqueous architectural material etc..
Brief description of the drawings
Fig. 1 is the surface microscopic FESEM shape appearance figures (2 μm of ratios) of the commercially available aluminum paste of present invention acetone treatment；
Fig. 2 is the TiO that present invention gained has self-cleaning function2The surface microscopic FESEM shapes of coating type water aluminum-silver slurry Looks figure (10 μm of ratios)；
Fig. 3 is the TiO that present invention gained has self-cleaning function2The surface microscopic FESEM shapes of coating type water aluminum-silver slurry Looks figure (2 μm of ratios)；
Fig. 4 is the TiO that present invention gained has self-cleaning function2The surface microscopic EDS power spectrums of coating type water aluminum-silver slurry Figure.
Embodiment
Embodiments of the invention are elaborated below, the present embodiment is carried out lower premised on technical solution of the present invention Implement, give detailed embodiment and specific operating process, but protection scope of the present invention is not limited to following implementation Example.
Embodiment 1
A kind of automatically cleaning water aluminum-silver slurry, it is aluminum paste Surface coating TiO2Film, pass through TiO2The photocatalysis of film Realize automatically cleaning and water solubility.
Above-mentioned automatically cleaning aluminum paste is prepared using sol-gal process, specifically includes following steps：
(1) the commercially available parts by weight of oiliness aluminum paste 1 are mixed with the parts by weight of acetone 1.6, isolated aluminium after certain time Silver paste solid is stand-by；
(2) titanate coupling agent Di(dioctylpyrophosphato) ethylene titanate is mixed with isopropanol, obtains titanium The mixed solution A of acid esters coupling agent Di(dioctylpyrophosphato) ethylene titanate volume fraction 10%；By the fourth of metatitanic acid four Ester mixes with isopropanol, obtains the mixed solution B of butyl titanate volume fraction 25%；
(3) aluminum paste solid obtained by step (1) and the isopropanol of 9 parts by weight are taken, the mixed solution A of 1 parts by weight, and The water of 0.1 parts by weight is mixed, and is reacted under conditions of 80 DEG C.Solid mixture separated after a period of time stand-by；
(4) solid mixture obtained by step (3) is mixed with the isopropanol of 9 parts by weight and the water of 0.1 parts by weight, uses ammonia Water adjusts pH to 7, and the mixed solution B of 1 parts by weight is added dropwise under conditions of 60 DEG C, wherein, mixed solution B divides 2.5h uniformly to drip Add, 4h is aged after being added dropwise to complete, then separate solid with solvent, gained solid is automatically cleaning aluminum paste.
Following performance test is carried out to the above-mentioned automatically cleaning water aluminum-silver slurry being prepared：
(1) its surface topography is observed using field emission scanning electron microscope, is to be made in the present embodiment as Figure 1-3 Automatically cleaning aluminum paste surface FESEM photos, as seen from the figure aluminum paste Surface coating have one layer of fine and close film.
(2) its surface mass, such as Fig. 4 are analyzed using field emission scanning electron microscope energy dispersive spectrometer (EDS) measure It is shown, it is the EDS energy spectrum diagrams of obtained automatically cleaning aluminum paste in the present embodiment, surface coated one layer of aluminum paste as seen from the figure Fine and close film is TiO2。
Embodiment 2
A kind of automatically cleaning aluminum paste preparation method, is comprised the following steps that：
(1) 1 parts by weight oiliness aluminum paste is mixed with the acetone of 2.6 parts by weight, after certain time by solid mixture with Solvent separates；
(2) titanate coupling agent Di(dioctylpyrophosphato) ethylene titanate is mixed with isopropanol, obtains titanium The mixed solution A of acid esters coupling agent Di(dioctylpyrophosphato) ethylene titanate mass fraction 10%；By the fourth of metatitanic acid four Ester mixes with isopropanol, obtains the mixed solution B of butyl titanate mass fraction 25%；
(3) aluminum paste and the isopropanol of 8 parts by weight crossed acetone treatment, the mixed solution A and 0.1 weight of 1 parts by weight The water mixing of part is measured, reacts, separates solid mixture after a period of time stand-by under conditions of 60 DEG C；
(4) solid mixture obtained by step (3) is mixed with the isopropanol of 9 parts by weight and the water of 0.1 parts by weight, uses ammonia Water adjusts pH to 7, and the mixed solution B of 1 parts by weight is added dropwise under conditions of 60 DEG C, wherein, mixed solution B divides 2h uniformly to drip Add, 3h is aged after being added dropwise to complete, then separate solid with solvent, gained solid is automatically cleaning aluminum paste.
Examined through field emission scanning electron microscope and field emission scanning electron microscope energy dispersive spectrometer, find aluminium silver Starch the fine and close TiO of Surface coating2Film.
Embodiment 3
A kind of automatically cleaning aluminum paste preparation method, is comprised the following steps that：
(1) 1 parts by weight oiliness aluminum paste is mixed with the acetone of 1.5 parts by weight, after certain time by solid mixture with Solvent separates；
(2) titanate coupling agent isopropyl three (dioctylphyrophosphoric acid acyloxy) titanate esters are mixed with isopropanol, obtained The mixed solution A of titanate coupling agent isopropyl three (dioctylphyrophosphoric acid acyloxy) titanate esters mass fraction 10%；By metatitanic acid Four butyl esters mix with isopropanol, obtain the mixed solution B of butyl titanate mass fraction 25%；
(3) aluminum paste and the isopropanol of 9 parts by weight crossed acetone treatment, the mixed solution A and 0.1 weight of 1 parts by weight The water mixing of part is measured, reacts, separates solid mixture after a period of time stand-by under conditions of 60 DEG C；；
(4) solid mixture obtained by step (3) is mixed with the isopropanol of 9 parts by weight and the water of 0.1 parts by weight, uses ammonia Water adjusts pH to 7, and the mixed solution B of 1 parts by weight is added dropwise under conditions of 60 DEG C, wherein, mixed solution B divides 2h uniformly to drip Add, 4h is aged after being added dropwise to complete, then separate solid with solvent, gained solid is automatically cleaning aluminum paste.
Examined through field emission scanning electron microscope and field emission scanning electron microscope energy dispersive spectrometer, find aluminium silver Starch the fine and close TiO of Surface coating2Film.
Embodiment 4
A kind of automatically cleaning aluminum paste preparation method, is comprised the following steps that：
(1) 1 parts by weight oiliness aluminum paste is mixed with the acetone of 3 parts by weight, after certain time by solid mixture with it is molten Agent separates；
(2) titanate coupling agent Di(dioctylpyrophosphato) ethylene titanate is mixed with isopropanol, obtains titanium The mixed solution A of acid esters coupling agent Di(dioctylpyrophosphato) ethylene titanate mass fraction 10%；By the fourth of metatitanic acid four Ester mixes with isopropanol, obtains the mixed solution B of butyl titanate mass fraction 25%；
(3) aluminum paste and the isopropanol of 9 parts by weight crossed acetone treatment, the mixed solution A and 0.1 weight of 1 parts by weight The water mixing of part is measured, separates solid mixture with solvent after 60 DEG C of reactions；
(4) solid mixture obtained by step (3) is mixed with the isopropanol of 9 parts by weight and the water of 0.1 parts by weight, uses ammonia Water adjusts pH to 7, and the mixed solution B of 0.5 parts by weight is added dropwise under conditions of 60 DEG C, wherein, mixed solution B divides 2.5h uniform It is added dropwise, 4h is aged after being added dropwise to complete, then separates solid with solvent, gained solid is automatically cleaning aluminum paste.
Examined through field emission scanning electron microscope and field emission scanning electron microscope energy dispersive spectrometer, find aluminium silver Starch the fine and close TiO of Surface coating2Film.
Embodiment 5
A kind of automatically cleaning aluminum paste preparation method, is comprised the following steps that：
(1) the commercially available oiliness aluminum paste of 1 parts by weight is mixed with 3 pbw acetones, isolated aluminium silver after certain time It is stand-by to starch solid；
(2) titanate coupling agent Di(dioctylpyrophosphato) ethylene titanate is mixed with isopropanol, obtains titanium Acid esters coupling agent Di(dioctylpyrophosphato) ethylene titanate mass fraction is 10% mixed solution A；By metatitanic acid four Butyl ester mixes with isopropanol, obtains the mixed solution B that butyl titanate mass fraction is 25%；
(3) by the aluminum paste solid obtained by step (1) and the isopropanol of 5 parts by weight, 2 parts by weight mixed solution A and The water of 0.1 parts by weight is mixed, and is reacted under conditions of 80 DEG C, obtains solid mixture, wherein aluminum paste solid is with mixing The addition of solution A is to make gained solid mixture and the mass ratio of titanate coupling agent be 1:0.08, will be solid after a period of time The separation of body mixture is stand-by；
(4) solid mixture obtained by step (3) is mixed with the isopropanol of 5 parts by weight and the water of 0.1 parts by weight, uses ammonia Water adjusts pH to 8, and mixed solution B is added dropwise under conditions of 80 DEG C, and mixed solution B addition is to make the solid mixture Mass ratio with butyl titanate is 1：0.5, wherein, mixed solution B divides 1h to be uniformly added dropwise, and 6h is aged after being added dropwise to complete, then Solid is separated with solvent, gained solid is automatically cleaning aluminum paste.
Examined through field emission scanning electron microscope and field emission scanning electron microscope energy dispersive spectrometer, find aluminium silver Starch the fine and close TiO of Surface coating2Film.
Embodiment 6
A kind of automatically cleaning aluminum paste preparation method, is comprised the following steps that：
(1) the commercially available oiliness aluminum paste of 1 parts by weight is mixed with 3.5 pbw acetones, isolated aluminium after certain time Silver paste solid is stand-by；
(2) titanate coupling agent Di(dioctylpyrophosphato) ethylene titanate is mixed with isopropanol, obtains titanium Acid esters coupling agent Di(dioctylpyrophosphato) ethylene titanate mass fraction is 10% mixed solution A；By metatitanic acid four Butyl ester mixes with isopropanol, obtains the mixed solution B that butyl titanate mass fraction is 75%；
(3) by the aluminum paste solid and isopropanol of 10 parts by weight obtained by step (1), mixed solution A and 0.1 parts by weight Water mixed, reacted under conditions of 60 DEG C, obtain solid mixture, wherein aluminum paste solid and mixed solution A adds Dosage is to make gained solid mixture and the mass ratio of titanate coupling agent be 1:0.2.By solid mixture point after a period of time From stand-by；
(4) solid mixture obtained by step (3) is mixed with the isopropanol of 10 parts by weight and the water of 0.1 parts by weight, used Ammoniacal liquor adjusts pH to 7.5, and mixed solution B is added dropwise under conditions of 60 DEG C, and mixed solution B addition is to mix the solid The mass ratio of compound and butyl titanate is 1：0.25, wherein, mixed solution B divides 1h to be uniformly added dropwise, and 5h is aged after being added dropwise to complete, Then solid is separated with solvent, gained solid is automatically cleaning aluminum paste.
Examined through field emission scanning electron microscope and field emission scanning electron microscope energy dispersive spectrometer, find aluminium silver Starch the fine and close TiO of Surface coating2Film.

Claims (7)

1. a kind of automatically cleaning water aluminum-silver slurry, it is characterised in that the water aluminum-silver slurry is aluminum paste Surface coating TiO2Film, lead to Cross TiO2Automatically cleaning and water solubility are realized in the photocatalysis of film；
Described automatically cleaning water aluminum-silver slurry is made using sol-gal process, specifically includes following steps：
(1) parts by weight of oiliness aluminum paste 1 are mixed with the parts by weight of acetone 1.5~3.5, removes the organic of oiliness aluminum paste surface Thing, obtain aluminum paste solid；
(2) titanate coupling agent is mixed with organic solvent, obtains mixed solution A, butyl titanate is mixed with organic solvent, Obtain mixed solution B；
(3) the aluminum paste solid obtained by step (1) and the parts by weight of organic solvent 5~10, mixed solution A, the parts by weight of water 0.1 are entered Row mixing, isolated solid mixture after 60~80 DEG C of reactions；
(4) solid mixture obtained by step (3) is mixed with the parts by weight of organic solvent 5~10, the parts by weight of water 0.1, adjusts pH to 7 Under the conditions of~8,60~80 DEG C, mixed solution B is added dropwise, ageing, which separates, after reaction produces automatically cleaning water aluminum-silver slurry；
The mass ratio of aluminum paste solid and titanate coupling agent in described step (3) is 1:(0.08-0.2)；Described step Suddenly the mass ratio of the solid mixture in (4) and butyl titanate is 1：(0.25-0.5).
2. a kind of automatically cleaning water aluminum-silver slurry according to claim 1, it is characterised in that step (2), step (3), step (4) organic solvent described in is ethanol or isopropanol.
A kind of 3. automatically cleaning water aluminum-silver slurry according to claim 1, it is characterised in that the titanate esters described in step (2) Coupling agent includes chelate solution, the isopropyl three (two of Di(dioctylpyrophosphato) ethylene titanate and triethanolamine Octyl group pyrophosphoric acid acyloxy) one kind in titanate esters or Di(dioctylpyrophosphato) ethylene titanate.
A kind of 4. automatically cleaning water aluminum-silver slurry according to claim 1, it is characterised in that step (2) described mixed solution A Mass concentration be 10%；
The mass concentration of the mixed solution B is 25%-75%.
5. a kind of automatically cleaning water aluminum-silver slurry according to claim 1, it is characterised in that be used to adjust pH in step (4) Conditioning agent be triethylamine or ammoniacal liquor.
A kind of 6. automatically cleaning water aluminum-silver slurry according to claim 1, it is characterised in that mixed solution B in step (4) Time for adding is 1~5h.
7. a kind of automatically cleaning water aluminum-silver slurry according to claim 1, it is characterised in that digestion time is 3 in step (4) ~6h.
CN201510976658.0A 2015-12-23 2015-12-23 A kind of automatically cleaning water aluminum-silver slurry and preparation method thereof Expired - Fee Related CN105462297B (en)