CN105441048B - A kind of water-soluble comb polymer pressure break temporarily blocks up diversion agent and its prepares application method - Google Patents
A kind of water-soluble comb polymer pressure break temporarily blocks up diversion agent and its prepares application method Download PDFInfo
- Publication number
- CN105441048B CN105441048B CN201510866016.5A CN201510866016A CN105441048B CN 105441048 B CN105441048 B CN 105441048B CN 201510866016 A CN201510866016 A CN 201510866016A CN 105441048 B CN105441048 B CN 105441048B
- Authority
- CN
- China
- Prior art keywords
- agent
- water
- pressure break
- temporarily
- comb polymer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention provides a kind of water-soluble comb polymer pressure breaks temporarily to block up diversion agent, and including following components, the mass percent shared by each component and each component is:Gelling agent 0.2~2.0%;Fluid loss additive 0.1~2%;Toughener 1~10%;Clay stabilizer 1~4%;High-temperature stabilizer 0.05~0.2%;Capsule breaker 0.01~0.1%;Remaining component is water, and the gelling agent is water-soluble comb polymer, physical crosslinking structure can be self-assembly of by comb-type structure, the trade name of the gelling agent is one hundred Chinese toon high temperature gel, is produced by one hundred Chinese toon Petroleum Technology Co., Ltd of Chengdu.The present invention additionally provides the method for preparation and use that above-mentioned water-soluble comb polymer pressure break temporarily blocks up diversion agent simultaneously.Water solubility pressure break provided by the invention temporarily block up diversion agent without Hou Ning, it is small to formation damage, while also have can automatic identification crack, the characteristics of sealing ratiod is high.
Description
Technical field
The present invention relates to it is a kind of can be applied to oil, gas well hydraulic fracturing the temporary stall of water-soluble comb polymer pressure break to
Agent and the preparation and application of the temporary stifled diversion agent, belong to oil-gas reservoir yield-increasing technology field.
Background technology
With continually developing for China's petroleum resources, reservoir geology condition becomes increasingly complex, and exploits difficulty also increasingly
Greatly.In recent years, it for strong anisotropism, hypotonic, ultra-permeable reservior, to further improve transformation efficiency, realizes uniformly transformation, carries
Temporarily stifled steering technique is gone out.It is to add in temporarily stifled diversion agent in real time in hydraulic fracturing process, temporarily blocks up established man-made fracture,
Forcing crack, high pressure presses off new crack, fracturing transformation effect is improved to increase communication probability in other direction crack initiation extensions.
In this technology, good temporarily stifled material is the key that realize effectively temporary stifled pressure break.
At present, the temporarily stifled diversion agent as pressing crack construction can be divided mainly into water-soluble temporarily stifled diversion agent, oil-soluble both at home and abroad
Temporarily stifled diversion agent, temporarily stifled three kinds of diversion agent of degrading certainly.Water-soluble temporarily stifled diversion agent is broadly divided into two major class:Cross-linking system and Fei Jiao
Conjuncted system.Be crosslinked class diverting agent mainly using high molecular polymer, by chemical crosslinking formed gel reach the temporary stall in crack to
Required structural strength realizes de-plugging after construction by oxidizing broken glue.Zhou Fayuan et al. has studied a kind of pressure break
Diverting agent ZFJ realizes temporary block up by the way that water-soluble polymer secondary cross-linking is formed gel.Patent 201010134590.9 describes
A kind of water solubility diverting agent, it is raw material using guanidine glue and alundum (Al2O3) etc., is crosslinked under formation conditions, forms pressure-bearing and reaches
The rubber plug of 30MPa, so as to fulfill closure.Non-crosslinked class diverting agent is generally using materials such as gelatine, water-absorbing resins.Patent
91101010.6th, CN 102093864 A, CN 102020984 A and patent CN200410009408.1 disclose describe it is several
Kind of diverting agent, these diverting agents are made of materials such as gelatine, guanidine glue, and the aquation pressure that makes breakthroughs reaches 8MPa under formation conditions
Plugged zone.South monarch et al. is relied to use a kind of noncrosslinking water uptake expansion material, and as diverting agent, breakthrough pressure gradient reaches
47.1MPa/m.This two classes water solubility pressure break temporarily blocks up diversion agent all there are certain deficiency, is mainly manifested in:
1) pressing crack construction cannot be carried out immediately after adding in diverting agent, need certain Hou Ning times;
2) non-crosslinked class, which temporarily blocks up the products such as gelatine, the guanidine glue that diversion agent uses, all has higher water insoluble matter content, right
Formation damage is big;Class diverting agent is crosslinked although water insoluble matter content is few in the high molecular polymer used, cross-linking process will produce
Raw a large amount of water-insolubles, can also cause serious injury stratum.
Due to these two aspects, the popularization and application that water-soluble pressure break temporarily blocks up diversion agent is caused to be restricted.
Invention content
The present invention provides a kind of novel water-soluble comb polymer pressure breaks temporarily to block up diversion agent, which temporarily blocks up
Diversion agent without Hou Ning, it is small to formation damage, while also have can automatic identification crack, the characteristics of sealing ratiod is high.
Technical solution is used by realizing above-mentioned purpose of the present invention:
A kind of water-soluble comb polymer pressure break temporarily blocks up diversion agent, including following components, shared by each component and each component
Mass percent be:Gelling agent 0.2~2.0%;Fluid loss additive 0.1~2%;Toughener 1~10%;Clay stabilizer 1~
4%;High-temperature stabilizer 0.05~0.2%;Capsule breaker 0.01~0.1%;Remaining component is water, and the gelling agent is water
Dissolubility comb-shaped polymer can be self-assembly of physical crosslinking structure by comb-type structure, and the trade name of the gelling agent is one hundred
Chinese toon high temperature gel, product designation BCG-5 are produced, industrial goods, the following institute of structural formula by one hundred Chinese toon Petroleum Technology Co., Ltd of Chengdu
Show:
The fluid loss additive is dewatering nano silica.
The one kind of the toughener for the poly- acetic ester fiber of hydrophilic modifying, in vinal, fibre length 5mm~
Between 50mm.
The clay stabilizer is potassium chloride.
The high-temperature stabilizer is one or both of sodium thiosulfate, methanol.
The capsule breaker content is ammonium persulfate.
The present invention additionally provides the method for preparation and use that above-mentioned water-soluble comb polymer pressure break temporarily blocks up diversion agent simultaneously,
Include the following steps:
(1), under cycle or blender stirring condition, in clear water by above-mentioned mass percent be slowly added to gelling agent,
Fluid loss additive, toughener, clay stabilizer and high-temperature stabilizer, fully cycle or stirring, treat that gelling agent is completely dissolved, obtain
Temporarily stifled diversion agent;
(2), connect bypass line in fracture well head, after hydraulic fracturing seam suspend pressure break pump truck, by temporary stall to
Agent is pumped into shaft bottom by cementing truck from bypass line, and adding in capsule by above-mentioned mass percent while pumping temporarily stifled diversion agent breaks
Jelly;It will temporarily block up after diversion agent has replaced without Hou Ning, and continue main pressing crack construction, and realize that pressure break will turn in seam;Also it will can temporarily block up
Diversion agent is pumped into the mulling slot of fracturing blender truck, and temporary stifled diversion agent is pumped into shaft bottom by fracturing unit truck.
By the use of a kind of water-soluble comb polymer with special construction as gelling agent in the present invention, in aqueous solution,
The gelling agent does not need to be chemically crosslinked, and is self-assembly of physical crosslinking structure by comb-type structure, is temporarily blocked up so as to reach crack
Structural strength needed for turning to.Since this physical crosslinking structure is reversible, thus with very strong thixotropy.It was pumping
Cheng Zhong, under Strong shear effect, self-assembled structures destroy, and viscosity is low, good fluidity, easily enters crack deep.It is split when entering
After seam, flow velocity reduces, and shear action weakens, and self-assembled structures restore again, realizes and effectively blocks.Due to this spy of solution
Property makes it have automatic identification crack, the characteristics of fracture sealing ratiod is high.The physical crosslinking knot being self-assembly of of comb-type structure
Structure is rigidly strong, thus the performance characteristics also with good temperature resistance, salt resistance.Its own is free of water-insoluble, is handed over without chemistry
Connection, will not generate water-insoluble, thus the injury that will not result in blockage to stratum.The gelling agent solution thixotropy is good, viscoplasticity
By force, it is easily adhered to crack and rock surface is realized and blocked.
Fluid loss additive described herein is dewatering nano silica.Dewatering nano material can not only change rock table
The wetability in face, moreover it is possible to and gellant molecules chain bridge joint, false filter cake is formed, significantly reduces leak-off.Due to nano silicon dioxide
Grain is sufficiently small, and the particle into formation pore throat can will not damage stratum with drain outflow is returned again.In addition, the toughening
Agent is the poly- acetic ester fiber of hydrophilic modifying, one kind in vinal, and fibre length is between 5mm~50mm.The toughening
Agent mainly using fiber reinforced principle, improves the breakthrough pressure of temporarily blocking layer.
Based on above-mentioned condition, the application compared with prior art, has effect following prominent:
(1) the water-soluble comb polymer pressure break is temporarily blocked up diversion agent and is pumped into behind shaft bottom without Hou Ning, can continue main pressure break
The construction time is shortened in construction.
(2) system is self-assembly of physical crosslinking structure by comb-type structure, reaches the temporary stall in crack to required
Structural strength, solve the disadvantages that conventional water-soluble pressure break diverting agent water insoluble matter content height, it is big to formation damage.
(3) the characteristics of system makes it have automatic identification crack due to strong thixotropy, and sealing ratiod is high.
Specific embodiment
Below in conjunction with specific embodiment, the present invention is described in detail, the embodiment be to the present invention furtherly
It is bright rather than limit the scope of the invention.
Gelling agent described in following embodiment is water-soluble comb polymer, can be self-assembly of object by comb-type structure
Manage cross-linked structure, the trade name of the gelling agent is one hundred Chinese toon high temperature gel, product designation BCG-5, by one hundred Chinese toon petroleum science and technology of Chengdu
Co., Ltd produces, industrial goods.The fluid loss additive is dewatering nano silica.The toughener is hydrophilic modifying poly-vinegar acid
One kind in ester fiber, vinal, fibre length is between 5mm~50mm.The clay stabilizer is potassium chloride.Institute
High-temperature stabilizer is stated as one or both of sodium thiosulfate, methanol.The capsule breaker content is ammonium persulfate.
Embodiment 1
The method of preparation and use that the water-soluble comb polymer pressure break provided in the present embodiment temporarily blocks up diversion agent is as follows:
Under cycle or blender stirring condition, be slowly added to by mass percentage in clear water 0.8% gelling agent,
0.5% fluid loss additive, 3% toughener, 1% clay stabilizer, 0.1% high-temperature stabilizer, fully cycle or stirring, wait to be gelled
Agent is completely dissolved, and obtains temporarily blocking up diversion agent.
Bypass line is connected in fracture well head before construction, suspends pressure break pump truck after hydraulic fracturing seam, by temporary stall
Shaft bottom is pumped into from bypass line by 700 type cementing trucks to agent, pumps the quality percentage by 0.04% while temporarily blocking up diversion agent
Than adding in capsule breaker.It will temporarily block up after diversion agent has replaced without Hou Ning, and continue main pressing crack construction, and realize that pressure break will turn in seam
To.
Embodiment 2
The method of preparation and use that the water-soluble comb polymer pressure break provided in the present embodiment temporarily blocks up diversion agent is as follows:
Under cycle or blender stirring condition, be slowly added to by mass percentage in clear water 1.2% gelling agent,
1% fluid loss additive, 5% toughener, 2% clay stabilizer, 0.1% high-temperature stabilizer, fully cycle or stirring, treat gelling agent
It is completely dissolved, obtains temporarily blocking up diversion agent.
Discharge capacity is reduced after hydraulic fracturing seam, temporary stifled diversion agent is pumped into instead of fracturing fluid in the mulling slot of fracturing blender truck,
Temporary stifled diversion agent is pumped by shaft bottom by fracturing unit truck, glue is added in by 0.08% mass percent while pumping temporarily stifled diversion agent
Capsule gel breaker.It will temporarily block up after diversion agent has replaced without Hou Ning, and continue main pressing crack construction, and realize that pressure break will turn in seam.
It should be understood that for those of ordinary skills, can be improved or converted according to the above description,
And all these modifications and variations should all belong to the protection domain of appended claims of the present invention.
Claims (5)
1. a kind of water-soluble comb polymer pressure break temporarily blocks up diversion agent, it is characterised in that including following components, each component and each
Mass percent shared by component is:Gelling agent 0.2~2.0%;Fluid loss additive 0.1~2%;Toughener 1~10%;Clay is steady
Determine agent 1~4%;High-temperature stabilizer 0.05~0.2%;Capsule breaker 0.01~0.1%;Remaining component be water, the glue
Solidifying agent is water-soluble comb polymer, and physical crosslinking structure, the commodity of the gelling agent can be self-assembly of by comb-type structure
Entitled one hundred Chinese toon high temperature gel, product designation BCG-5 are produced, industrial goods, structure by one hundred Chinese toon Petroleum Technology Co., Ltd of Chengdu
Formula is as follows:
The fluid loss additive is dewatering nano silica;The toughener is the poly- acetic ester fiber of hydrophilic modifying, polyvinyl alcohol
One kind in fiber, fibre length is between 5mm~50mm.
2. water-soluble comb polymer pressure break according to claim 1 temporarily blocks up diversion agent, it is characterised in that:The clay is steady
Agent is determined for potassium chloride.
3. water-soluble comb polymer pressure break according to claim 1 temporarily blocks up diversion agent, it is characterised in that:The high temperature is steady
Agent is determined for one or both of sodium thiosulfate, methanol.
4. water-soluble comb polymer pressure break according to claim 1 temporarily blocks up diversion agent, it is characterised in that:The capsule is broken
Jelly content is ammonium persulfate.
5. water-soluble comb polymer pressure break described in claim 1 temporarily blocks up the method for preparation and use of diversion agent, feature exists
In including the following steps:
(1), under cycle or blender stirring condition, gelling agent is slowly added to by above-mentioned mass percent, drop is filtered in clear water
Agent, toughener, clay stabilizer and high-temperature stabilizer, fully cycle or stirring are lost, treats that gelling agent is completely dissolved, is temporarily blocked up
Diversion agent;
(2), bypass line is connected in fracture well head, suspends pressure break pump truck after hydraulic fracturing seam, will temporarily block up diversion agent and lead to
It crosses cementing truck and is pumped into shaft bottom from bypass line, adding in capsule by above-mentioned mass percent while pumping temporarily stifled diversion agent breaks glue
Agent;It will temporarily block up after diversion agent has replaced without Hou Ning, and continue main pressing crack construction, and realize that pressure break will turn in seam;It also can be by temporary stall
It is pumped into the mulling slot of fracturing blender truck to agent, temporary stifled diversion agent is pumped by shaft bottom by fracturing unit truck.