CN105441022A - Method for preparing calcium hydroxide adhesive - Google Patents
Method for preparing calcium hydroxide adhesive Download PDFInfo
- Publication number
- CN105441022A CN105441022A CN201510994808.0A CN201510994808A CN105441022A CN 105441022 A CN105441022 A CN 105441022A CN 201510994808 A CN201510994808 A CN 201510994808A CN 105441022 A CN105441022 A CN 105441022A
- Authority
- CN
- China
- Prior art keywords
- calcium hydroxide
- sizing agent
- preparation
- reaction
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a method for preparing a calcium hydroxide adhesive. The method comprises the following steps: (1) pretreating vegetable protein; (2) thickening with ethanol; and (3) preparing the adhesive. According to the method, the prepared calcium hydroxide adhesive is environment-friendly and has the water resistance and adhesive performance meeting the market requirement by means of reasonable material selection and scientific proportion designing; and the preparation process is simple and is harmless to the environment.
Description
Technical field
The present invention relates to sizing agent preparing technical field, particularly relate to a kind of preparation method of calcium hydroxide sizing agent.
Background technology
Along with the raising of people's living standard, the demands such as various furniture and adornment get more and more.Can use sizing agent in a large number in the product processing such as furniture and adornment, and sizing agent common mostly on the market is adhesive made of synthetic resin.Can free formaldehyde be distributed in such sizing agent use procedure, human body is worked the mischief.Along with the enhancing of people's environmental consciousness, need a kind of sizing agent that can be used for green, environmental protection people badly.
Inorganic adhesive bonding strength is high, water-tolerant, but its fragility is large, plane docking, overlap joint, impact, stripping strength is all lower.Natural polymer sizing agent, nontoxic, safety, but water tolerance and gumminess poor, cause it in disfavor in actual application.The invention discloses a kind of method that natural polymer and calcium hydroxide compound prepare novel adhesive.
Summary of the invention
The technical problem that the present invention mainly solves is to provide a kind of preparation method of calcium hydroxide sizing agent, can solve existing sizing agent and there is Form aldehyde release, the problems such as contaminate environment more.
For solving the problems of the technologies described above, the technical scheme that the present invention adopts is: the preparation method providing a kind of calcium hydroxide sizing agent, comprises the steps:
(1) vegetable-protein pre-treatment: taking 250 ~ 400 parts of granularities is 80 object starch and soyflours, puts into the mixed solution of clorox and hydrogen peroxide, 50 DEG C of constant temperature, 1000 revs/min, reaction 3 ~ 5h; Take 20 ~ 30 parts of polyvinyl alcohol and above-mentioned solution put into by 30 ~ 50 parts of acrylamides, reaction 2 ~ 4h;
(2) ethanol increases glutinous: mixed solution obtained in step (1) is cooled to 40 ~ 50 DEG C, slowly adds ethanolic soln under certain condition, reaction 3 ~ 4h;
(3) tackiness agent allotment: the solution naturally cooling obtained by step (2), adds 50 ~ 60 parts of calcium hydroxides, with 1000 revs/min of stirring velocitys, under 50 DEG C ~ 70 DEG C temperature condition, stir 1 ~ 2h, naturally cool to room temperature, place 2 ~ 3h, be described calcium hydroxide sizing agent.
In a preferred embodiment of the present invention, in described step (1), described starch and soyflour mixing quality ratio are 1 ~ 3:2 ~ 5.
In a preferred embodiment of the present invention, in described step (1), described clorox and hydrogen peroxide mixed volume ratio are 2 ~ 3:5 ~ 7.
In a preferred embodiment of the present invention, in described step (2), described reaction conditions is stir 30min with the stirring velocity of 800r/min, is then rapidly heated to 70 ~ 80 DEG C, isothermal reaction 2h; It is 3 ~ 5ml/min that ethanolic soln adds speed.
The invention has the beneficial effects as follows: the preparation method of a kind of calcium hydroxide sizing agent of the present invention, by the proportion design of material choose reasonable and science, make prepared calcium hydroxide sizing agent green, environmental protection, water tolerance and gumminess are all met the need of market, and preparation technology is simple, to environment without harm.
Embodiment
Below preferred embodiment of the present invention is described in detail, can be easier to make advantages and features of the invention be readily appreciated by one skilled in the art, thus more explicit defining is made to protection scope of the present invention.
The embodiment of the present invention comprises:
Embodiment 1
(1) vegetable-protein pre-treatment: to take 400 parts of granularities be 80 objects take mass ratio as starch and the soy powder blend of 3:5 mixing, and putting into is clorox and the hydrogen peroxide mixed solution of 3:7 mixing by volume, and 50 DEG C of constant temperature, react 5h by 1000 revs/min; Take 30 parts of polyvinyl alcohol and above-mentioned solution put into by 50 parts of acrylamides, reaction 4h;
(2) ethanol increases glutinous: mixed solution obtained in step (1) is cooled to 50 DEG C, stirs 30min, be then rapidly heated to 80 DEG C, isothermal reaction 2h with the stirring velocity of 800r/min; Slowly ethanolic soln is added, reaction 4h with 5ml/min speed;
(3) tackiness agent allotment: the solution naturally cooling obtained by step (2), adds 60 parts of calcium hydroxides, with 1000 revs/min of stirring velocitys, under 70 DEG C of temperature condition, stirs 2h, naturally cools to room temperature, place 3h, be described calcium hydroxide sizing agent.
Embodiment 2
(1) vegetable-protein pre-treatment: to take 250 parts of granularities be 80 objects take mass ratio as starch and the soy powder blend of 1:2 mixing, and putting into is clorox and the hydrogen peroxide mixed solution of 2:5 mixing by volume, and 50 DEG C of constant temperature, react 3h by 1000 revs/min; Take 20 parts of polyvinyl alcohol and above-mentioned solution put into by 30 parts of acrylamides, reaction 2h;
(2) ethanol increases glutinous: mixed solution obtained in step (1) is cooled to 40 DEG C, stirs 30min, be then rapidly heated to 70 DEG C, isothermal reaction 2h with the stirring velocity of 800r/min; Slowly ethanolic soln is added, reaction 3h with 3ml/min speed;
(3) tackiness agent allotment: the solution naturally cooling obtained by step (2), adds 50 parts of calcium hydroxides, with 1000 revs/min of stirring velocitys, under 50 DEG C of temperature condition, stirs 1h, naturally cools to room temperature, place 2h, be described calcium hydroxide sizing agent.
Calcium hydroxide sizing agent bond strength prepared by aforesaid method is 1.25 ~ 1.63Mpa, and viscosity is 800 ~ 1000mPaS (20 DEG C), and 40 ~ 58S set time (100 DEG C), free formaldehyde is released to zero.
The foregoing is only embodiments of the invention; not thereby the scope of the claims of the present invention is limited; every utilize description of the present invention to do equivalent structure or equivalent flow process conversion; or be directly or indirectly used in other relevant technical fields, be all in like manner included in scope of patent protection of the present invention.
Claims (5)
1. a preparation method for calcium hydroxide sizing agent, is characterized in that, comprises the steps:
(1) vegetable-protein pre-treatment: taking 250 ~ 400 parts of granularities is 80 object starch and soyflours, puts into the mixed solution of clorox and hydrogen peroxide, 50 DEG C of constant temperature, 1000 revs/min, reaction 3 ~ 5h; Take 20 ~ 30 parts of polyvinyl alcohol and above-mentioned solution put into by 30 ~ 50 parts of acrylamides, reaction 2 ~ 4h;
(2) ethanol increases glutinous: mixed solution obtained in step (1) is cooled to 40 ~ 50 DEG C, slowly adds ethanolic soln under certain condition, reaction 3 ~ 4h;
(3) tackiness agent allotment: the solution naturally cooling obtained by step (2), adds 50 ~ 60 parts of calcium hydroxides, with the stirring velocity of 1000 revs/min, under 50 DEG C ~ 70 DEG C temperature condition, stir 1 ~ 2h, naturally cool to room temperature, place 2 ~ 3h, be described calcium hydroxide sizing agent.
2. the preparation method of a kind of calcium hydroxide sizing agent according to claim 1, is characterized in that, in described step (1), described starch and soyflour mixing quality ratio are 1 ~ 3:2 ~ 5.
3. the preparation method of a kind of calcium hydroxide sizing agent according to claim 1, is characterized in that, in described step (1), described clorox and hydrogen peroxide mixed volume ratio are 2 ~ 3:5 ~ 7.
4. the preparation method of a kind of calcium hydroxide sizing agent according to claim 1, is characterized in that, in described step (2), described reaction conditions is stir 30min with the stirring velocity of 800r/min, is then rapidly heated to 70 ~ 80 DEG C, isothermal reaction 2h; It is 3 ~ 5ml/min that ethanolic soln adds speed.
5. according to the preparation method of a kind of calcium hydroxide sizing agent one of Claims 1-4 Suo Shu, it is characterized in that, described calcium hydroxide sizing agent bond strength is 1.25 ~ 1.63Mpa, and 20 DEG C of viscosity are 800 ~ 1000mPaS, 100 DEG C set time 40 ~ 58S, free formaldehyde is released to zero.