CN105440968A - Glittering antistatic AB glue membrane and preparation method thereof - Google Patents
Glittering antistatic AB glue membrane and preparation method thereof Download PDFInfo
- Publication number
- CN105440968A CN105440968A CN201510969746.8A CN201510969746A CN105440968A CN 105440968 A CN105440968 A CN 105440968A CN 201510969746 A CN201510969746 A CN 201510969746A CN 105440968 A CN105440968 A CN 105440968A
- Authority
- CN
- China
- Prior art keywords
- antistatic
- layer
- coating
- release film
- glued membrane
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the technical field of AB glue membranes, and concretely relates to a glittering antistatic AB glue membrane and a preparation method thereof. The glittering antistatic AB glue membrane comprises a release-film layer, a high-viscosity glittering coating, a base-material layer, an anti-static viscose-glue layer and a peelable-film layer, the upper surface and the lower surface of the high-viscosity glittering coating are respectively bonded with the lower surface of the release-film layer and the upper surface of the base-material layer, and the upper surface and the lower surface of the antistatic viscose-glue layer are respectively bonded with the lower surface of the base-material layer and the upper surface of the peelable-film layer. The glittering antistatic AB glue membrane possesses glittering effect, is not influenced in light transmittance, guarantees picture authenticity and enhances user experience. The glittering antistatic AB glue membrane also possesses antistatic effect and overcomes electrostatic effect in daily life.
Description
Technical field
The present invention relates to AB glued membrane technical field, be specifically related to a kind of sudden strain of a muscle and bore antistatic AB glued membrane and preparation method thereof.
Background technology
Along with the development of toughened glass safeguard film for cellular phone, increasing traditional protection film replace by toughened glass protective membrane.Wherein the core technology of toughened glass protective membrane is AB double faced adhesive tape.
But the AB double faced adhesive tape function singleness of existing toughened glass protective membrane, can not meet the daily demand of client.
Summary of the invention
In order to overcome the shortcoming and defect existed in prior art, the object of the present invention is to provide a kind of sudden strain of a muscle to bore antistatic AB glued membrane, this sudden strain of a muscle is bored antistatic AB glued membrane and is had sudden strain of a muscle brill effect, and does not affect light penetration, ensure that the true of picture, strengthens Consumer's Experience; There is antistatic effect simultaneously, overcome the electrostatic influence in daily life.
Another object of the present invention is to provide a kind of and dodge the preparation method boring antistatic AB glued membrane, this preparation method's technique is simple, convenient operation and control, steady quality, and production efficiency is high, and production cost is low, is applicable to large-scale industrial production.
Object of the present invention is achieved through the following technical solutions: a kind of sudden strain of a muscle bores antistatic AB glued membrane, comprise release film layer, high sticky sudden strain of a muscle is bored coating, substrate layer, antistatic adhesive-layer and peel off rete, upper surface, the lower surface of high sticky sudden strain of a muscle brill coating are fitted with the lower surface of release film and the upper surface of substrate layer respectively, and upper surface, the lower surface of antistatic adhesive-layer are fitted with the lower surface of substrate layer and the upper surface of stripping film respectively.
Sudden strain of a muscle of the present invention is bored antistatic AB glued membrane and is had sudden strain of a muscle brill effect, and does not affect light penetration, ensure that the true of picture, strengthens Consumer's Experience; There is antistatic effect simultaneously, overcome the electrostatic influence in daily life.
Preferably, described release film layer is any one in PET release film, PE release film, OPP release film, BOPET release film and BOPP release film.The present invention is by adopting above-mentioned release film, and it is release and protected effect is good.
Described substrate layer is PET film.The present invention, by adopting PET film as substrate layer, makes AB glued membrane have good light transmission and light diffusing.
Described antistatic adhesive-layer is antistatic pressure sensitive glue-line.The present invention is by adopting antistatic pressure sensitive glue-line as antistatic adhesive-layer, and it is antistatic and bonding effect is good.
Described stripping rete is PET stripping film.The present invention is by adopting PET stripping film, and its peeling effect is good, is convenient to being separated of stripping film and substrate layer.
Preferably, the thickness of described release film layer is 25-75 μm.The present invention passes through by the gauge control of release film at 25-75 μm, and it is release and protected effect is good.Particularly, the thickness of described release film layer can be 25 μm, 40 μm, 50 μm, 60 μm or 75 μm.More preferred, the thickness of described release film layer is 50 μm.
Described height glues and dodges the thickness boring coating is 10-200 μm.The present invention bores the gauge control of coating at 10-200 μm by height being glued sudden strain of a muscle, and it is effective that it dodges brill.Particularly, described height glues and dodges the thickness boring coating can be 10 μm, 50 μm, 100 μm, 150 μm or 200 μm.Preferably, described height glues and dodges the thickness boring coating is 100 μm.
The thickness of described substrate layer is 50-200 μm.The present invention passes through by the gauge control of substrate layer at 50-200 μm, and its translucent effect is good.Particularly, the thickness of described substrate layer can be 50 μm, 100 μm, 120 μm, 150 μm or 200 μm.Preferably, the thickness of described substrate layer is 120 μm.
The thickness of described antistatic adhesive-layer is 20-200 μm.The present invention passes through by the gauge control of antistatic adhesive-layer at 20-200 μm, and it is antistatic and bonding effect is good.Particularly, the thickness of described antistatic adhesive-layer can be 20 μm, 50 μm, 100 μm, 50 μm or 200 μm.Preferably, the thickness of described antistatic adhesive-layer is 100 μm.
The thickness of described stripping rete is 25-75 μm.The present invention passes through by the gauge control of stripping film at 25-75 μm, and its peeling effect is good.Particularly, the thickness of described stripping rete can be 25 μm, 40 μm, 50 μm, 60 μm or 75 μm.Preferably, the thickness of described stripping rete is 50 μm.
Preferably, the raw material of described antistatic adhesive-layer is the pressure sensitive adhesive being added with static inhibitor, and the addition of static inhibitor is the 0.1%-5% of pressure sensitive adhesive weight.Pressure sensitive adhesive of the present invention by adding static inhibitor, and controls the 0.1%-5% that its addition is pressure sensitive adhesive weight, and obtained antistatic adhesive-layer antistatic effect is good, and light transmission is good.
Preferably, described static inhibitor is that Korea S one believes that the model of chemical production is the static inhibitor of AT0-505.By adopting Korea S one, the present invention believes that the model of chemical production is the static inhibitor of AT0-505, its antistatic effect is good.
Described pressure sensitive adhesive is liquid add-on type reaction silica gel or liquid acrylic glue.The present invention is by adopting liquid add-on type reaction silica gel or liquid acrylic glue as pressure sensitive adhesive, and its bonding effect is good.
Preferably, the mixture that the raw material that described height glues sudden strain of a muscle brill coating is made up of with weight ratio 100:0.01-1 thermohardening type acrylic resin hardening liquid and pearlescence.The present invention glues by adopting thermohardening type acrylic resin hardening liquid and pearlescence the raw material dodging and bore coating as height, and to control its weight ratio be 1:0.01-1, obtained height is sticky to be dodged and bores coating and have to dodge and bore effect, and does not affect light penetration, ensure that the true of picture, strengthen Consumer's Experience.
Described thermohardening type acrylic resin hardening liquid is 3126 hardening liquids that hundred million chemical industry company limiteds are moistened in Fanyu.3126 hardening liquids of the present invention by adopting Fanyu to moisten hundred million chemical industry company limiteds, its thermofixation is effective, and curing speed soon, bore coating and have sudden strain of a muscle brill effect, and do not affect light penetration, ensure that the true of picture, strengthen Consumer's Experience by the sticky sudden strain of a muscle of the height obtained.
Dodge the preparation method boring antistatic AB glued membrane, comprise the steps:
(1) thermohardening type acrylic resin and the pearlescence ratio by weight 100:0.01-1 is mixed, obtain mixed hardening liquid;
(2) get a PET film as substrate layer, the mixed hardening liquid that step (1) is obtained is coated in PET film, through baking oven for heating solidification, forms high sticky sudden strain of a muscle and bores coating; Glue at height the upper surface dodging brill coating and fit one deck release film as release film layer;
(3) in the another side pressure-sensitive adhesive coating of PET film, through baking oven for heating solidification, tack coat is formed; Fit one deck stripping film as stripping rete at the lower surface of tack coat, and obtained sudden strain of a muscle bores antistatic AB glued membrane.
Preparation method's technique of the present invention is simple, convenient operation and control, steady quality, and production efficiency is high, and production cost is low, is applicable to large-scale industrial production.
Preferably, described step (1) is specially: thermohardening type acrylic resin hardening liquid and the pearlescence ratio by weight 100:0.01-1 mixed, adopt physical agitation machine, adopt ultrasonic disperse instrument aid dispersion simultaneously, filter with 15 μm of filter cores after stirring 40-80min, obtain mixed hardening liquid.
Preferably, in described step (2), coating method adopts comma formula scraper for coating, and oven temperature is 100-200 DEG C, and baking time is 1-3min.
Preferably, in described step (3), oven temperature is 130-200 DEG C, and baking time is 1-3min.
Beneficial effect of the present invention is: sudden strain of a muscle of the present invention is bored antistatic AB glued membrane and had sudden strain of a muscle brill effect, and does not affect light penetration, ensure that the true of picture, strengthens Consumer's Experience; There is antistatic effect simultaneously, overcome the electrostatic influence in daily life.
Preparation method's technique of the present invention is simple, convenient operation and control, steady quality, and production efficiency is high, and production cost is low, is applicable to large-scale industrial production.
Accompanying drawing explanation
Fig. 1 is part sectioned view of the present invention.
Reference numeral is: 1-release film layer, 2-high sticky sudden strain of a muscle bore coating, 3-substrate layer, 4-antistatic adhesive-layer, 5-stripping rete.
Embodiment
For the ease of the understanding of those skilled in the art, below in conjunction with embodiment and accompanying drawing 1, the present invention is further illustrated, and the content that embodiment is mentioned not is limitation of the invention.
Embodiment 1
See Fig. 1, a kind of sudden strain of a muscle bores antistatic AB glued membrane, comprise release film layer 1, high sticky sudden strain of a muscle is bored coating 2, substrate layer 3, antistatic adhesive-layer 4 and peel off rete 5, upper surface, the lower surface of high sticky sudden strain of a muscle brill coating 2 are fitted with the lower surface of release film and the upper surface of substrate layer 3 respectively, and upper surface, the lower surface of antistatic adhesive-layer 4 are fitted with the lower surface of substrate layer 3 and the upper surface of stripping film respectively.
Described release film layer 1 is PET release film; Described substrate layer 3 is PET film; Described antistatic adhesive-layer 4 is antistatic pressure sensitive glue-line; Described stripping rete 5 is PET stripping film.
The thickness of described release film layer 1 is 25 μm; Described height glues and dodges the thickness boring coating 2 is 10 μm; The thickness of described substrate layer 3 is 50 μm; The thickness of described antistatic adhesive-layer 4 is 20 μm; The thickness of described stripping rete 5 is 25 μm.
The raw material of described antistatic adhesive-layer 4 is the pressure sensitive adhesive being added with static inhibitor, and the addition of static inhibitor is 0.1% of pressure sensitive adhesive weight.
Described static inhibitor is that Korea S one believes that the model of chemical production is the static inhibitor of AT0-505; Described pressure sensitive adhesive is liquid add-on type reaction silica gel.
The mixture that the raw material that described height glues sudden strain of a muscle brill coating 2 is made up of with weight ratio 100:0.01 thermohardening type acrylic resin hardening liquid and pearlescence; Described thermohardening type acrylic resin hardening liquid is 3126 hardening liquids that hundred million chemical industry company limiteds are moistened in Fanyu.
Dodge the preparation method boring antistatic AB glued membrane, comprise the steps:
(1) thermohardening type acrylic resin and the pearlescence ratio by weight 100:0.01 is mixed, obtain mixed hardening liquid;
(2) get a PET film as substrate layer 3, the mixed hardening liquid that step (1) is obtained is coated in PET film, through baking oven for heating solidification, forms high sticky sudden strain of a muscle and bores coating 2; Glue at height the upper surface dodging brill coating 2 and fit one deck release film as release film layer 1;
(3) in the another side pressure-sensitive adhesive coating of PET film, through baking oven for heating solidification, tack coat is formed; Fit one deck stripping film as stripping rete 5 at the lower surface of tack coat, and obtained sudden strain of a muscle bores antistatic AB glued membrane.
Described step (1) is specially: thermohardening type acrylic resin hardening liquid and the pearlescence ratio by weight 100:0.01 mixed, adopt physical agitation machine, adopt ultrasonic disperse instrument aid dispersion simultaneously, filter with 15 μm of filter cores after stirring 40min, obtain mixed hardening liquid.
In described step (2), coating method adopts comma formula scraper for coating, and oven temperature is 100 DEG C, and baking time is 3min.
In described step (3), oven temperature is 130 DEG C, and baking time is 3min.
Embodiment 2
The difference of the present embodiment and above-described embodiment 1 is:
Described release film layer 1 is PE release film.
The thickness of described release film layer 1 is 40 μm; Described height glues and dodges the thickness boring coating 2 is 50 μm; The thickness of described substrate layer 3 is 80 μm; The thickness of described antistatic adhesive-layer 4 is 50 μm; The thickness of described stripping rete 5 is 40 μm.
The raw material of described antistatic adhesive-layer 4 is the pressure sensitive adhesive being added with static inhibitor, and the addition of static inhibitor is 1% of pressure sensitive adhesive weight.
Described pressure sensitive adhesive is liquid acrylic glue.
The mixture that the raw material that described height glues sudden strain of a muscle brill coating 2 is made up of with weight ratio 100:0.1 thermohardening type acrylic resin hardening liquid and pearlescence.
Described step (1) is specially: thermohardening type acrylic resin hardening liquid and the pearlescence ratio by weight 100:0.1 mixed, adopt physical agitation machine, adopt ultrasonic disperse instrument aid dispersion simultaneously, filter with 15 μm of filter cores after stirring 50min, obtain mixed hardening liquid.
In described step (2), coating method adopts comma formula scraper for coating, and oven temperature is 120 DEG C, and baking time is 2.5min.
In described step (3), oven temperature is 150 DEG C, and baking time is 2.5min.
Embodiment 3
The difference of the present embodiment and above-described embodiment 1 is:
Described release film layer 1 is OPP release film.
The thickness of described release film layer 1 is 50 μm; Described height glues and dodges the thickness boring coating 2 is 100 μm; The thickness of described substrate layer 3 is 120 μm; The thickness of described antistatic adhesive-layer 4 is 100 μm; The thickness of described stripping rete 5 is 50 μm.
The raw material of described antistatic adhesive-layer 4 is the pressure sensitive adhesive being added with static inhibitor, and the addition of static inhibitor is 2% of pressure sensitive adhesive weight.
Described pressure sensitive adhesive is liquid add-on type reaction silica gel.
The mixture that the raw material that described height glues sudden strain of a muscle brill coating 2 is made up of with weight ratio 100:0.5 thermohardening type acrylic resin hardening liquid and pearlescence.
Described step (1) is specially: thermohardening type acrylic resin hardening liquid and the pearlescence ratio by weight 100:0.5 mixed, adopt physical agitation machine, adopt ultrasonic disperse instrument aid dispersion simultaneously, filter with 15 μm of filter cores after stirring 60min, obtain mixed hardening liquid.
In described step (2), coating method adopts comma formula scraper for coating, and oven temperature is 150 DEG C, and baking time is 2min.
In described step (3), oven temperature is 170 DEG C, and baking time is 2min.
Embodiment 4
The difference of the present embodiment and above-described embodiment 1 is:
Described release film layer 1 is BOPET release film.
The thickness of described release film layer 1 is 60 μm; Described height glues and dodges the thickness boring coating 2 is 150 μm; The thickness of described substrate layer 3 is 160 μm; The thickness of described antistatic adhesive-layer 4 is 150 μm; The thickness of described stripping rete 5 is 0 μm.
The raw material of described antistatic adhesive-layer 4 is the pressure sensitive adhesive being added with static inhibitor, and the addition of static inhibitor is 4% of pressure sensitive adhesive weight.
Described pressure sensitive adhesive is liquid acrylic glue.
The mixture that the raw material that described height glues sudden strain of a muscle brill coating 2 is made up of with weight ratio 100:0.8 thermohardening type acrylic resin hardening liquid and pearlescence.
Described step (1) is specially: thermohardening type acrylic resin hardening liquid and the pearlescence ratio by weight 100:0.8 mixed, adopt physical agitation machine, adopt ultrasonic disperse instrument aid dispersion simultaneously, filter with 15 μm of filter cores after stirring 70min, obtain mixed hardening liquid.
In described step (2), coating method adopts comma formula scraper for coating, and oven temperature is 180 DEG C, and baking time is 1.5min.
In described step (3), oven temperature is 180 DEG C, and baking time is 1.5min.
Embodiment 5
The difference of the present embodiment and above-described embodiment 1 is:
Described release film layer 1 is BOPP release film.
The thickness of described release film layer 1 is 75 μm; Described height glues and dodges the thickness boring coating 2 is 200 μm; The thickness of described substrate layer 3 is 200 μm; The thickness of described antistatic adhesive-layer 4 is 200 μm; The thickness of described stripping rete 5 is 75 μm.
The raw material of described antistatic adhesive-layer 4 is the pressure sensitive adhesive being added with static inhibitor, and the addition of static inhibitor is 5% of pressure sensitive adhesive weight.
Described pressure sensitive adhesive is liquid add-on type reaction silica gel or liquid acrylic glue.
The mixture that the raw material that described height glues sudden strain of a muscle brill coating 2 is made up of with weight ratio 100:1 thermohardening type acrylic resin hardening liquid and pearlescence.
Described step (1) is specially: thermohardening type acrylic resin hardening liquid and the pearlescence ratio by weight 100:1 mixed, adopt physical agitation machine, adopt ultrasonic disperse instrument aid dispersion simultaneously, filter with 15 μm of filter cores after stirring 80min, obtain mixed hardening liquid.
In described step (2), coating method adopts comma formula scraper for coating, and oven temperature is 200 DEG C, and baking time is 1min.
In described step (3), oven temperature is 200 DEG C, and baking time is 1min.
Above-described embodiment is the present invention's preferably implementation, and in addition, the present invention can also realize by alternate manner, and any apparent replacement is all within protection scope of the present invention without departing from the inventive concept of the premise.
Claims (10)
1. one kind is dodged the antistatic AB glued membrane of brill, it is characterized in that: comprise release film layer, high sticky sudden strain of a muscle is bored coating, substrate layer, antistatic adhesive-layer and peel off rete, upper surface, the lower surface of high sticky sudden strain of a muscle brill coating are fitted with the lower surface of release film and the upper surface of substrate layer respectively, and upper surface, the lower surface of antistatic adhesive-layer are fitted with the lower surface of substrate layer and the upper surface of stripping film respectively.
2. one according to claim 1 is dodged and is bored antistatic AB glued membrane, it is characterized in that: described release film layer is any one in PET release film, PE release film, OPP release film, BOPET release film and BOPP release film; Described substrate layer is PET film; Described antistatic adhesive-layer is antistatic pressure sensitive glue-line; Described stripping rete is PET stripping film.
3. one according to claim 1 is dodged and is bored antistatic AB glued membrane, it is characterized in that: the thickness of described release film layer is 25-75 μm; Described height glues and dodges the thickness boring coating is 10-200 μm; The thickness of described substrate layer is 50-200 μm; The thickness of described antistatic adhesive-layer is 20-200 μm; The thickness of described stripping rete is 25-75 μm.
4. one according to claim 1 is dodged and is bored antistatic AB glued membrane, it is characterized in that: the raw material of described antistatic adhesive-layer is the pressure sensitive adhesive being added with static inhibitor, and the addition of static inhibitor is the 0.1%-5% of pressure sensitive adhesive weight.
5. one according to claim 4 is dodged and is bored antistatic AB glued membrane, it is characterized in that: described static inhibitor is that Korea S one believes that the model of chemical production is the static inhibitor of AT0-505; Described pressure sensitive adhesive is liquid add-on type reaction silica gel or liquid acrylic glue.
6. the one according to any one of claim 1-5 is dodged and is bored antistatic AB glued membrane, it is characterized in that: the mixture that the raw material that described height glues sudden strain of a muscle brill coating is made up of with weight ratio 100:0.01-1 thermohardening type acrylic resin hardening liquid and pearlescence; Described thermohardening type acrylic resin hardening liquid is 3126 hardening liquids that hundred million chemical industry company limiteds are moistened in Fanyu.
7. a kind ofly dodge the preparation method boring antistatic AB glued membrane as claimed in claim 6, it is characterized in that: comprise the steps:
(1) thermohardening type acrylic resin and the pearlescence ratio by weight 100:0.01-1 is mixed, obtain mixed hardening liquid;
(2) get a PET film as substrate layer, the mixed hardening liquid that step (1) is obtained is coated in PET film, through baking oven for heating solidification, forms high sticky sudden strain of a muscle and bores coating; Glue at height the upper surface dodging brill coating and fit one deck release film as release film layer;
(3) in the another side pressure-sensitive adhesive coating of PET film, through baking oven for heating solidification, tack coat is formed; Fit one deck stripping film as stripping rete at the lower surface of tack coat, and obtained sudden strain of a muscle bores antistatic AB glued membrane.
8. according to claim 6ly a kind ofly dodge the preparation method boring antistatic AB glued membrane, it is characterized in that: described step (1) is specially: thermohardening type acrylic resin hardening liquid and the pearlescence ratio by weight 100:0.01-1 is mixed, adopt physical agitation machine, adopt ultrasonic disperse instrument aid dispersion simultaneously, filter with 15 μm of filter cores after stirring 40-80min, obtain mixed hardening liquid.
9. according to claim 6ly a kind ofly dodge the preparation method boring antistatic AB glued membrane, it is characterized in that: in described step (2), coating method adopts comma formula scraper for coating, and oven temperature is 100-200 DEG C, and baking time is 1-3min.
10. according to claim 6ly a kind ofly dodge the preparation method boring antistatic AB glued membrane, it is characterized in that: in described step (3), oven temperature is 130-200 DEG C, and baking time is 1-3min.