CN105440902A - 一种疏水增强型泵阀防腐用粉末涂料 - Google Patents
一种疏水增强型泵阀防腐用粉末涂料 Download PDFInfo
- Publication number
- CN105440902A CN105440902A CN201510865510.XA CN201510865510A CN105440902A CN 105440902 A CN105440902 A CN 105440902A CN 201510865510 A CN201510865510 A CN 201510865510A CN 105440902 A CN105440902 A CN 105440902A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder coating
- nano
- minute
- hydrophobicity
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明公开了一种疏水增强型泵阀防腐用粉末涂料,由下列重量份的原料制成:羟基聚酯树脂52-54、氟碳树脂7-8、异氰尿酸三缩水甘油酯4-5、纳米三氧化二铝13-15、全氟辛基三乙氧基硅烷0.8-0.9、浓度为75wt%的乙醇溶液25-30、硅烷偶联剂kh5600.5-0.6、碳酸钙14-16、硬脂酸2.5-3.5、纳米硅溶胶6-7、聚乙烯吡咯烷酮2-3、二月桂酸二丁锡1-1.2、聚二甲基硅氧烷0.9-1.1、水适量。本发明制成的粉末涂料流平性好、涂层光滑、防腐性能强,经过静电喷涂在泵阀材料的表面,具有耐擦拭、不脱落、使用寿命长的效果。
Description
技术领域
本发明涉及涂料技术领域,尤其涉及一种疏水增强型泵阀防腐用粉末涂料。
背景技术
近年来,粉末涂料的应用已超越了涂料工业中的水性涂料和高固体涂料等,成为工业界使用较多的涂料品种之一。粉末涂装工艺解决了传统油漆涂装工艺所存在的易燃、易爆和污染环境等问题,而且其涂层具备优越的性能,原料可回收再用,涂装工艺简单。可广泛应用于泵、阀门壳体涂装上。由于泵阀是铸件或锻件,因此其表面粗糙,目前现有技术针对阀门表面处理的功能性粉末涂料技术还存在一定缺陷,致使涂层出现缩孔、针眼和严重桔皮状等缺陷,进而导致泵阀在食品、生物、制药、化工、航天和电子等特殊领域应用受到限制。而且大部分泵阀都会用在高含水、高含砂、强腐蚀的介质环境等因素影响,加重了泵阀的腐蚀,更易在泵阀上结垢,从而造成泵阀使用寿命短,检验周期短、工作量大的问题,给使用带来不便,一般的表面强化工艺主要有金属镀层、陶瓷涂层、其他一些涂层,虽然在一定程度上减缓了磨损,提高了耐腐蚀性,但是都存在着不足之处:金属镀层容易分层导致脱落;陶瓷抗冲击性能差,容易发生碎裂现象;一些聚合物涂层力学和热性能差等。因而研究开发具有耐候、防水防腐等功能的粉末涂料,具有技术促进与产业提高的意义。
发明内容
本发明目的就是为了弥补已有技术的缺陷,提供一种疏水增强型泵阀防腐用粉末涂料。
本发明是通过以下技术方案实现的:
一种疏水增强型泵阀防腐用粉末涂料,由下列重量份的原料制成:羟基聚酯树脂52-54、氟碳树脂7-8、异氰尿酸三缩水甘油酯4-5、纳米三氧化二铝13-15、全氟辛基三乙氧基硅烷0.8-0.9、浓度为75wt%的乙醇溶液25-30、硅烷偶联剂kh5600.5-0.6、碳酸钙14-16、硬脂酸2.5-3.5、纳米硅溶胶6-7、聚乙烯吡咯烷酮2-3、二月桂酸二丁锡1-1.2、聚二甲基硅氧烷0.9-1.1、水适量。
所述一种疏水增强型泵阀防腐用粉末涂料,由以下具体步骤制备而成:
(1)将纳米三氧化二铝放入浓度为75wt%的乙醇溶液中,搅拌分散均匀,然后加入全氟辛基三乙氧基硅烷,加热回流2-2.5小时,冷却后加入硅烷偶联剂kh560,继续搅拌反应2-3小时,最后减压蒸馏,脱去体系中的溶剂,在真空干燥箱中以80-85℃的温度干燥60-80分钟,得到活性纳米三氧化二铝;
(2)将碳酸钙与硬脂酸混合,放入球磨机中,加热至50-60℃球磨40-50分钟,取出后放入烘箱中干燥,然后放入粉碎机中,过400目筛待用;将聚乙烯吡咯烷酮加入3-4倍量的水中,加热至完全溶解,冷却后与纳米硅溶胶混合,加入上述400目粉末,以500转/分的速度分散20-30分钟得到混合浆料,然后将混合浆料喷雾干燥,得到改性填料;
(3)将羟基聚酯树脂、氟碳树脂、异氰尿酸三缩水甘油酯放入高速搅拌机中以1000转/分的速度搅拌20-30分钟后加入活性纳米三氧化二铝以及改性填料,继续搅拌10-15分钟后出料,将混合料送入双螺杆熔融挤出机,继续加入其余剩余成分,熔融挤出,压片,经粉碎过180目筛得到微细粉即得。
本发明的优点是:本发明添加少量的氟碳树脂替代部分羟基聚酯树脂,在粉末涂料固化的过程中,氟碳树脂中的氟碳链段发生了表面富集,所以少量的氟就可以明显提高涂层的疏水疏油性,同时可以提高涂层的耐热水、耐酸碱性能以及柔韧性;配合添加经过特殊工艺处理制得的活性纳米三氧化二铝,很容易与F-C键形成化学键接,使涂层结构更牢固,而且涂层表面对水的接触角急剧增大,进一步提高了涂层的疏水性,制成的粉末涂料有远比一般粉末涂料优异的抗腐蚀、耐酸碱、耐候性、憎水憎油性等。
本发明将碳酸钙通过一系列的工艺进行改性后制成填料添加到粉末涂料的制备中,不仅具备良好的疏水性,同时能够提高涂层的耐冲击性;本发明制成的粉末涂料流平性好、涂层光滑、防腐性能强,经过静电喷涂在泵阀材料的表面,具有耐擦拭、不脱落、使用寿命长的效果。
具体实施方式
一种疏水增强型泵阀防腐用粉末涂料,由下列重量份(公斤)的原料制成:羟基聚酯树脂52、氟碳树脂7、异氰尿酸三缩水甘油酯4、纳米三氧化二铝13、全氟辛基三乙氧基硅烷0.8、浓度为75wt%的乙醇溶液25、硅烷偶联剂kh5600.5、碳酸钙14、硬脂酸2.5、纳米硅溶胶6、聚乙烯吡咯烷酮2、二月桂酸二丁锡1、聚二甲基硅氧烷0.9、水适量。
所述一种疏水增强型泵阀防腐用粉末涂料,由以下具体步骤制备而成:
(1)将纳米三氧化二铝放入浓度为75wt%的乙醇溶液中,搅拌分散均匀,然后加入全氟辛基三乙氧基硅烷,加热回流2小时,冷却后加入硅烷偶联剂kh560,继续搅拌反应2小时,最后减压蒸馏,脱去体系中的溶剂,在真空干燥箱中以80℃的温度干燥60分钟,得到活性纳米三氧化二铝;
(2)将碳酸钙与硬脂酸混合,放入球磨机中,加热至60℃球磨40分钟,取出后放入烘箱中干燥,然后放入粉碎机中,过400目筛待用;将聚乙烯吡咯烷酮加入3倍量的水中,加热至完全溶解,冷却后与纳米硅溶胶混合,加入上述400目粉末,以500转/分的速度分散20分钟得到混合浆料,然后将混合浆料喷雾干燥,得到改性填料;
(3)将羟基聚酯树脂、氟碳树脂、异氰尿酸三缩水甘油酯放入高速搅拌机中以1000转/分的速度搅拌20分钟后加入活性纳米三氧化二铝以及改性填料,继续搅拌10分钟后出料,将混合料送入双螺杆熔融挤出机,继续加入其余剩余成分,熔融挤出,压片,经粉碎过180目筛得到微细粉即得。
将本发明粉末涂料采用静电喷涂施工方法作用于泵、阀门等器件表面上,经过180℃的充分固化,自然冷却至室温,放置24小时后,测定涂层性能:漆膜外观平整光滑,表面色调一致,无颗粒、针孔、气泡、皱纹;附着力达到1级,耐中性盐雾性2000小时无异常,抗冲击强度大于60cm。
Claims (2)
1.一种疏水增强型泵阀防腐用粉末涂料,其特征在于,由下列重量份的原料制成:羟基聚酯树脂52-54、氟碳树脂7-8、异氰尿酸三缩水甘油酯4-5、纳米三氧化二铝13-15、全氟辛基三乙氧基硅烷0.8-0.9、浓度为75wt%的乙醇溶液25-30、硅烷偶联剂kh5600.5-0.6、碳酸钙14-16、硬脂酸2.5-3.5、纳米硅溶胶6-7、聚乙烯吡咯烷酮2-3、二月桂酸二丁锡1-1.2、聚二甲基硅氧烷0.9-1.1、水适量。
2.根据权利要求1所述一种疏水增强型泵阀防腐用粉末涂料,其特征在于,由以下具体步骤制备而成:
(1)将纳米三氧化二铝放入浓度为75wt%的乙醇溶液中,搅拌分散均匀,然后加入全氟辛基三乙氧基硅烷,加热回流2-2.5小时,冷却后加入硅烷偶联剂kh560,继续搅拌反应2-3小时,最后减压蒸馏,脱去体系中的溶剂,在真空干燥箱中以80-85℃的温度干燥60-80分钟,得到活性纳米三氧化二铝;
(2)将碳酸钙与硬脂酸混合,放入球磨机中,加热至50-60℃球磨40-50分钟,取出后放入烘箱中干燥,然后放入粉碎机中,过400目筛待用;将聚乙烯吡咯烷酮加入3-4倍量的水中,加热至完全溶解,冷却后与纳米硅溶胶混合,加入上述400目粉末,以500转/分的速度分散20-30分钟得到混合浆料,然后将混合浆料喷雾干燥,得到改性填料;
(3)将羟基聚酯树脂、氟碳树脂、异氰尿酸三缩水甘油酯放入高速搅拌机中以1000转/分的速度搅拌20-30分钟后加入活性纳米三氧化二铝以及改性填料,继续搅拌10-15分钟后出料,将混合料送入双螺杆熔融挤出机,继续加入其余剩余成分,熔融挤出,压片,经粉碎过180目筛得到微细粉即得。