CN105418993A - Tread rubber of radial tire - Google Patents
Tread rubber of radial tire Download PDFInfo
- Publication number
- CN105418993A CN105418993A CN201510947843.7A CN201510947843A CN105418993A CN 105418993 A CN105418993 A CN 105418993A CN 201510947843 A CN201510947843 A CN 201510947843A CN 105418993 A CN105418993 A CN 105418993A
- Authority
- CN
- China
- Prior art keywords
- rubber
- carbon black
- meridian tyre
- resistance
- tyre according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to tread rubber of a radial tire. The tread rubber disclosed by the invention is prepared by mixing natural rubber, butadiene styrene rubber and cis-1,4-polyisoprene rubber; due to the matching of other auxiliary materials, the tread rubber not only has good properties of cutting resistance, prickling resistance, crack extension resistance and tear and chipping resistance, but also has the characteristics of lower dynamic heat generation and better heat resistance; the tread rubber can be used for a long time and is not easy to age, and a prepared tire is good in abrasion resistance and aging resistance.
Description
Technical field
The invention belongs to tread rubber technical field, be specifically related to a kind of meridian tyre.
Background technology
Radial is widely used in engineering transportation equipment now, and in use, because working conditions is relatively harsh, not cut resistant when using such as have sharp-pointed ore pavement conditions under more bad pavement conditions under, easily collapses and use up block; The existing tread rubber that can adapt to more bad pavement conditions, when using under fair speed condition, dynamic heat build up is high, easy delamination, bulge.Existingly can adapt to that more bad pavement conditions can use again under fair speed condition, under the natural condition such as daylight long-term to place easily aging.
Though TBR tire tread formula lays particular emphasis on the compound physical performance need solving certain aspect in prior art.But fail the relation of the every physical and mechanical properties of overall equilbrium tread mix.
Summary of the invention
In order to solve above-mentioned technical problem, the invention provides a kind of meridian tyre.The natural rubber that tread rubber of the present invention adopts, styrene-butadiene rubber(SBR), suitable 1,4-polyisoprene rubber mixes, coordinate other auxiliary materials not only to have good cut resistant, resistance to puncture, the expansion of cracking resistance mouth and anti tear and fall block performance, but also have that dynamic heat build up is lower, the good feature of resistance toheat, and can life-time service, not easily aging, tire wear, the resistance to deterioration of preparation are good.
A kind of meridian tyre of the present invention is realized by following technical scheme:
Described tread rubber comprises the component of following portions by weight:
Natural rubber 70-90 styrene-butadiene rubber(SBR) 10-50
Along Isosorbide-5-Nitrae-polyisoprene rubber 10-50 silane coupling agent Si-691-4
Stearic acid 1-4 sulphur 2-4
Carbon black 10-50 white carbon black 7-15
Plasticizer A 1-4 resol resin 1-4
Zinc oxide 1-8 anti-aging agent 1-10
Anti-recovery agent WK-9011-4 altax 0.5-2
Accelerant CZ 0.5-3 aromatic hydrocarbon oil 10-40.
Described natural rubber is 1# smoke sheet rubber or 3# smoke sheet rubber.
Described carbon black is N220 and N234.
Carbon black N220 and N234 mixes according to the ratio of weight ratio 1:1,
Described described anti-aging agent is Microcrystalline Wax and anti-aging agent RD.
Microcrystalline Wax and anti-aging agent RD mix according to the ratio of weight ratio 1:1.
Described described white carbon black is the precipitated silica of particle diameter 20-100nm.
Described a kind of meridian tyre, is grouped into by following one-tenth by weight:
Natural rubber 50 styrene-butadiene rubber(SBR) 40
Along Isosorbide-5-Nitrae-polyisoprene rubber 10 silane coupling agent Si-692
Stearic acid 2 sulphur 2.5
Carbon black 45 white carbon black 10
Plasticizer A 2 resol resin 2
Zinc oxide 4 anti-aging agent 3
Anti-recovery agent WK-9012 altax 1.2
Accelerant CZ 1 aromatic hydrocarbon oil 12.
Beneficial effect of the present invention is, the natural rubber that tread rubber of the present invention adopts, styrene-butadiene rubber(SBR), suitable 1,4-polyisoprene rubber mixes, coordinate other auxiliary materials not only to have good cut resistant, resistance to puncture, the expansion of cracking resistance mouth and anti tear and fall block performance, but also have that dynamic heat build up is lower, the good feature of resistance toheat, and can life-time service, not easily aging, tire wear, the resistance to deterioration of preparation are good.
Embodiment
Below in conjunction with specific embodiment, the present invention is further described, so that those skilled in the art more understands the present invention, but does not therefore limit the present invention.
Embodiment 1
A kind of meridian tyre is grouped into by following one-tenth by weight:
Natural rubber 50 styrene-butadiene rubber(SBR) 40
Along Isosorbide-5-Nitrae-polyisoprene rubber 10 silane coupling agent Si-692
Stearic acid 2 sulphur 2.5
Carbon black 45 white carbon black 10
Plasticizer A 2 resol resin 2
Zinc oxide 4 anti-aging agent 3
Anti-recovery agent WK-9012 altax 1.2
Accelerant CZ 1 aromatic hydrocarbon oil 12.
Described natural rubber is 1# smoke sheet rubber or 3# smoke sheet rubber.
Described carbon black is that N220 and N234 mixes according to the ratio of weight ratio 1:1,
Described described anti-aging agent is that Microcrystalline Wax and anti-aging agent RD mix according to the ratio of weight ratio 1:1.
Described described white carbon black is the precipitated silica of particle diameter 20-100nm.
After testing, 80 weeks abrasion performance (the Pico)/cm of the tread rubber sizing material in the present embodiment
3for 0.00010-0.0020;
300% stress at definite elongation reaches 33.5Mpa; Hardness is 75 Shao Er; Tensile strength at yield is 25.3MPa; Tensile yield is 580%; Compression heat generation is 35 DEG C; Cut resistant decrement is less than 1.4g.
Claims (8)
1. a meridian tyre, is characterized in that, described tread rubber comprises the component of following portions by weight:
Natural rubber 70-90 styrene-butadiene rubber(SBR) 10-50
Along Isosorbide-5-Nitrae-polyisoprene rubber 10-50 silane coupling agent Si-691-4
Stearic acid 1-4 sulphur 2-4
Carbon black 10-50 white carbon black 7-15
Plasticizer A 1-4 resol resin 1-4
Zinc oxide 1-8 anti-aging agent 1-10
Anti-recovery agent WK-9011-4 altax 0.5-2
Accelerant CZ 0.5-3 aromatic hydrocarbon oil 10-40.
2. a kind of meridian tyre according to claim 1, is characterized in that, described natural rubber is 1# smoke sheet rubber or 3# smoke sheet rubber.
3. a kind of meridian tyre according to claim 2, is characterized in that, described carbon black is N220 and N234.
4. a kind of meridian tyre according to claim 3, is characterized in that, carbon black N220 and N234 mixes according to the ratio of weight ratio 1:1.
5. a kind of meridian tyre according to claim 4, is characterized in that, described described anti-aging agent is Microcrystalline Wax and anti-aging agent RD.
6. a kind of meridian tyre according to claim 5, is characterized in that, Microcrystalline Wax and anti-aging agent RD mix according to the ratio of weight ratio 1:1.
7. a kind of meridian tyre according to claim 6, is characterized in that, described described white carbon black is the precipitated silica of particle diameter 20-100nm.
8. a kind of meridian tyre according to claim 7, is characterized in that, is grouped into by following one-tenth by weight:
Natural rubber 50 styrene-butadiene rubber(SBR) 40
Along Isosorbide-5-Nitrae-polyisoprene rubber 10 silane coupling agent Si-692
Stearic acid 2 sulphur 2.5
Carbon black 45 white carbon black 10
Plasticizer A 2 resol resin 2
Zinc oxide 4 anti-aging agent 3
Anti-recovery agent WK-9012 altax 1.2
Accelerant CZ 1 aromatic hydrocarbon oil 12.