CN105401029A - 一种耐热铸造合金 - Google Patents
一种耐热铸造合金 Download PDFInfo
- Publication number
- CN105401029A CN105401029A CN201510928408.XA CN201510928408A CN105401029A CN 105401029 A CN105401029 A CN 105401029A CN 201510928408 A CN201510928408 A CN 201510928408A CN 105401029 A CN105401029 A CN 105401029A
- Authority
- CN
- China
- Prior art keywords
- aluminum
- copper alloy
- alloy
- heat
- copper
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种耐热铸造合金,所述耐热铸造合金为铝铜合金,所述合金包括的合金元素及质量配比为:铝71%-78%、铜14%-18%、钪2%-8%、铬1%-5%、锆0.8%-2.4%、镍0.1%-0.4%、镁0.05%-0.08%、锰0.02%-0.05%;所述铝铜合金熔炼过程包括:熔炼、搅拌、精炼细化处理。通过上述方式,本发明合金具有优异的高温强度、以及良好的尺寸稳定性,能够满足汽车发动机等耐高温铸件的需求。
Description
技术领域
本发明涉及铸造合金领域,特别是涉及一种耐热铸造合金。
背景技术
铸造铝合金在实现轻量化、降低能源消耗、减少环境污染等方面具有显著作用,因而在汽车发动机领域得到广泛使用。
随着汽车工业的迅速发展,传统的铸造铝合金材料高温强度、耐热疲劳能力等已临近极限状态,不能满足汽车发动机的发展需求。
发明内容
本发明主要解决的技术问题是:针对现有技术的不足,提供一种耐热铸造合金,具有优异的高温强度、以及良好的尺寸稳定性,能够满足汽车发动机等耐高温铸件的需求。
为解决上述技术问题,本发明采用的一个技术方案是:提供一种耐热铸造合金,所述耐热铸造合金为铝铜合金,所述铝铜合金包括的合金元素有:铝、铜、钪、铬、锆、镍、镁、锰,所述各合金元素所占的质量百分比为:铝71%-78%、铜14%-18%、钪2%-8%、铬1%-5%、锆0.8%-2.4%、镍0.1%-0.4%、镁0.05%-0.08%、锰0.02%-0.05%;
所述铝铜合金熔炼过程包括如下步骤:
a、首先将铝铜合金放入熔炼炉内,经高温熔炼成铝铜合金溶液;
b、然后将熔炼炉内的铝铜合金溶液放入保温炉内,在保温炉的***施加转动磁强,在磁强转动过程中产生感应涡流对所述铝铜合金溶液进行搅拌;
c、最后进行除气、精炼、变质、静置等精炼细化处理。
在本发明一个较佳实施例中,所述铝铜合金的高温熔炼温度为550-600℃。
在本发明一个较佳实施例中,所述铝铜合金的抗拉强度为650-700MPa,伸长率为10%,硬度为220HBW。
本发明的有益效果是:本发明通过添加合理配方量的合金元素,并结合合理的熔炼工艺,使得到的铝铜合金溶液具有优异的高温强度、以及良好的尺寸稳定性,能够满足汽车发动机等耐高温铸件的需求。
具体实施方式
下面对本发明的较佳实施例进行详细阐述,以使本发明的优点和特征能更易于被本领域技术人员理解,从而对本发明的保护范围做出更为清楚明确的界定。
本发明实施例包括:
实施例一:
一种耐热铸造合金,所述耐热铸造合金为铝铜合金,所述铝铜合金包括的合金元素有:铝、铜、钪、铬、锆、镍、镁、锰,所述各合金元素所占的质量百分比为:铝71%、铜15%、钪7%、铬4%、锆2.4%、镍0.4%、镁0.05%、锰0.05%;所述铝铜合金的抗拉强度为650MPa,伸长率为10%,硬度为220HBW。
所述铝铜合金熔炼过程包括如下步骤:
a、首先将铝铜合金放入熔炼炉内,经550℃高温熔炼成铝铜合金溶液;
b、然后将熔炼炉内的铝铜合金溶液放入保温炉内,在保温炉的***施加转动磁强,在磁强转动过程中产生感应涡流对所述铝铜合金溶液进行搅拌;
c、最后进行除气、精炼、变质、静置等精炼细化处理。
实施例二:
一种耐热铸造合金,所述耐热铸造合金为铝铜合金,所述铝铜合金包括的合金元素有:铝、铜、钪、铬、锆、镍、镁、锰,所述各合金元素所占的质量百分比为:铝72%、铜18%、钪8%、铬1%、锆0.7%、镍0.2%、镁0.08%、锰0.02%;所述铝铜合金的抗拉强度为680MPa,伸长率为10%,硬度为220HBW。
所述铝铜合金熔炼过程包括如下步骤:
a、首先将铝铜合金放入熔炼炉内,经580℃高温熔炼成铝铜合金溶液;
b、然后将熔炼炉内的铝铜合金溶液放入保温炉内,在保温炉的***施加转动磁强,在磁强转动过程中产生感应涡流对所述铝铜合金溶液进行搅拌;
c、最后进行除气、精炼、变质、静置等精炼细化处理。
实施例三:
一种耐热铸造合金,所述耐热铸造合金为铝铜合金,所述铝铜合金包括的合金元素有:铝、铜、钪、铬、锆、镍、镁、锰,所述各合金元素所占的质量百分比为:铝78%、铜14%、钪2%、铬5%、锆0.8%、镍0.1%、镁0.08%、锰0.02%;所述铝铜合金的抗拉强度为700MPa,伸长率为10%,硬度为220HBW。
所述铝铜合金熔炼过程包括如下步骤:
a、首先将铝铜合金放入熔炼炉内,经600℃高温熔炼成铝铜合金溶液;
b、然后将熔炼炉内的铝铜合金溶液放入保温炉内,在保温炉的***施加转动磁强,在磁强转动过程中产生感应涡流对所述铝铜合金溶液进行搅拌;
c、最后进行除气、精炼、变质、静置等精炼细化处理。
本发明揭示了一种耐热铸造合金,通过添加合理配方量的合金元素,并结合合理的熔炼工艺,使得到的铝铜合金溶液具有优异的高温强度、以及良好的尺寸稳定性,能够满足汽车发动机等耐高温铸件的需求。
以上所述仅为本发明的实施例,并非因此限制本发明的专利范围,凡是利用本发明说明书内容所作的等效结构或等效流程变换,或直接或间接运用在其他相关的技术领域,均同理包括在本发明的专利保护范围内。
Claims (3)
1.一种耐热铸造合金,其特征在于,所述耐热铸造合金为铝铜合金,所述铝铜合金包括的合金元素有:铝、铜、钪、铬、锆、镍、镁、锰,所述各合金元素所占的质量百分比为:铝71%-78%、铜14%-18%、钪2%-8%、铬1%-5%、锆0.8%-2.4%、镍0.1%-0.4%、镁0.05%-0.08%、锰0.02%-0.05%;
所述铝铜合金熔炼过程包括如下步骤:
a、首先将铝铜合金放入熔炼炉内,经高温熔炼成铝铜合金溶液;
b、然后将熔炼炉内的铝铜合金溶液放入保温炉内,在保温炉的***施加转动磁强,在磁强转动过程中产生感应涡流对所述铝铜合金溶液进行搅拌;
c、最后进行除气、精炼、变质、静置等精炼细化处理。
2.根据权利要求1所述的耐热铸造合金,其特征在于,所述铝铜合金的高温熔炼温度为550-600℃。
3.根据权利要求1所述的耐热铸造合金,其特征在于,所述铝铜合金的抗拉强度为650-700MPa,伸长率为10%,硬度为220HBW。