CN105400987A - 一种铜合金材料 - Google Patents

一种铜合金材料 Download PDF

Info

Publication number
CN105400987A
CN105400987A CN201510759162.8A CN201510759162A CN105400987A CN 105400987 A CN105400987 A CN 105400987A CN 201510759162 A CN201510759162 A CN 201510759162A CN 105400987 A CN105400987 A CN 105400987A
Authority
CN
China
Prior art keywords
alloy material
copper alloy
copper
weight percent
iron
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510759162.8A
Other languages
English (en)
Inventor
王建飞
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Taicang Jiegong Precision Metal Material Co Ltd
Original Assignee
Taicang Jiegong Precision Metal Material Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Taicang Jiegong Precision Metal Material Co Ltd filed Critical Taicang Jiegong Precision Metal Material Co Ltd
Priority to CN201510759162.8A priority Critical patent/CN105400987A/zh
Publication of CN105400987A publication Critical patent/CN105400987A/zh
Pending legal-status Critical Current

Abstract

本发明提出了一种铜合金材料，包括以下重量百分比含量的原材料组成：锌5%~15%；钴0.5%~3%；铝0.2%~1.5%；锰1%~4.5%；铁0.15%~1%；锑0.05%~0.8%；硒0.01%~0.35%；钛0.1%~1.5%；余量为铜以及少量杂质。本发明所提出的铜合金材料与现有技术相比，显著提高了材料的强度以及耐腐性能，同时，提高了材料的屈服强度和抗拉强度，而且，延展性，稳定性高。

Description

一种铜合金材料
技术领域
本发明涉及金属材料技术领域，具体涉及一种铜合金材料。
背景技术
铜合金被广泛应用于汽车部件、家电部件、电气、电子、光学部件、配管构件、水暖金属件或者各种阀门等。且由于近年来全球变暖，强烈要求制品或者构件的小型、轻量化和薄壁化，在比重比铁大的铜合金中，需要通过高强度化来应对上述要求。尤其在气象机械、气象光学仪器领域，对仪器的重量有着较高的要求，以及对仪器的精密程度要求较高，就需要使用高强度的且轻质的合金材料，很多气象观测站，由于地域、交通的限制，不能够满足较重仪器的搬运和安装，仪器更换也存在很大的难度，这就需要在仪器的配备上有着较高的要求，仪器的精密度，以及仪器的使用寿命要求高。对于仪器制作时使用的材料，尤其是传感器，以及数据采集芯片使用的铜合金的要求很高，传统的简单的铜合金材料基本无法满足要求。传统的铜合金不仅在质量重、感应的灵敏度差以及能够被使用的次数少，不能满足气象领域的仪器使用要求。
而且，常用的铜合金材料的强度较低、不耐磨、不耐腐蚀、延展性不好、不易加工，质量稳定性很差。
因此，针对上述问题，本发明提出了一种新的技术方案。
发明内容
本发明的目的是提供一种高强度，耐磨性好，耐腐蚀性强的铜合金材料。
本发明是通过以下技术方案来实现的：
一种铜合金材料，包括以下重量百分比含量的原材料组成：
锌5%~15%；
钴0.5%~3%；
铝0.2%~1.5%；
锰1%~4.5%；
铁0.15%~1%；
锑0.05%~0.8%；
硒0.01%~0.35%；
钛0.1%~1.5%；
余量为铜以及少量杂质。
进一步地，还包括重量百分比为0.035%~0.12%的镧。
进一步地，还包括重量百分比为0.015%~0.025%铋。
本发明的有益效果是：本发明所提出的铜合金材料与现有技术相比，显著提高了材料的强度以及耐腐性能，同时，提高了材料的屈服强度和抗拉强度，而且，延展性，稳定性高。
具体实施方式
下面结合实施例对本发明做进一步地说明。
实施例1
一种铜合金材料，包括以下重量百分比含量的原材料组成：
锌5%；
钴0.5%；
铝0.2%；
锰1%；
铁0.15%；
锑0.05%；
硒0.01%；
钛0.1%；
镧0.035%；
铋0.015%；
余量为铜以及少量杂质。
实施例2
一种铜合金材料，包括以下重量百分比含量的原材料组成：
锌10%；
钴1.25%；
铝0.45%；
锰2%；
铁0.4%；
锑0.25%；
硒0.08%；
钛0.65%；
镧0.06%；
铋0.02%；
余量为铜以及少量杂质。
实施例3
一种铜合金材料，包括以下重量百分比含量的原材料组成：
锌15%；
钴3%；
铝1.5%；
锰4.5%；
铁1%；
锑0.8%；
硒0.35%；
钛1.5%；
镧0.12%；
铋0.025%；
余量为铜以及少量杂质。
本发明所提出的铜合金材料与现有技术相比，显著提高了材料的强度以及耐腐性能，同时，提高了材料的屈服强度和抗拉强度，而且，延展性，稳定性高。
以上所述，仅是本发明的实施例而已，并非是对本发明作任何其他形式的限制，而依据本发明所提出的实施例所作的任何修改或等同变化，仍属于本发明所要求保护的范围。

Claims (3)

1.一种铜合金材料，其特征在于：包括以下重量百分比含量的原材料组成：
锌5%~15%；
钴0.5%~3%；
铝0.2%~1.5%；
锰1%~4.5%；
铁0.15%~1%；
锑0.05%~0.8%；
硒0.01%~0.35%；
钛0.1%~1.5%；
余量为铜以及少量杂质。
2.根据权利要求1所述一种铜合金材料，其特征在于：还包括重量百分比为0.035%~0.12%的镧。
3.根据权利要求1所述一种铜合金材料，其特征在于：还包括重量百分比为0.015%~0.025%铋。
CN201510759162.8A 2015-11-10 2015-11-10 一种铜合金材料 Pending CN105400987A (zh)