CN105397874A - Method for manufacturing antiskid bamboo-wood composite boards - Google Patents
Method for manufacturing antiskid bamboo-wood composite boards Download PDFInfo
- Publication number
- CN105397874A CN105397874A CN201510801322.0A CN201510801322A CN105397874A CN 105397874 A CN105397874 A CN 105397874A CN 201510801322 A CN201510801322 A CN 201510801322A CN 105397874 A CN105397874 A CN 105397874A
- Authority
- CN
- China
- Prior art keywords
- bamboo
- wood composite
- composite board
- parts
- manufacture method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a method for manufacturing antiskid bamboo-wood composite boards, and relates to the technical field of composite materials. The antiskid bamboo-wood composite boards are mainly made of bamboos and plates. The method comprises the following steps of (1) material sorting, (2) drying, (3) grinding, (4) afterdrying, (5) recombination of blank pieces, (6) life preserving, and (7) antiskid paint coating. According to the method, due to the organic combination of bamboos and wood, material drawing is prevented from being too simplex in mode, the bottle neck problem of existing raw materials is effectively solved, the inherent fiber structure of the raw materials is basically not destroyed, and the amount of adopted glue between the materials is reduced; in addition, the surfaces of the bamboo-wood composite boards are coated with antiskid paint so that a good antiskid effect can be achieved, and the indoor security is improved.
Description
Technical field
The present invention relates to technical field of composite materials, be specifically related to a kind of manufacture method of anti-sliding bamboo wood composite board.
Background technology
Along with the fast-developing timber supply and demand contradiction of China's economy, particularly large through level, high-quality timber resources scarcity.The raw materials for production of current wood-base fibre and particle panel material and other Wood products are based on fast-growing industrial cut stock, and fast-growing industrial cut stock material is loose, density is low, intensity is low.And bamboo wood fast growth, fertility are strong, the cycle is short, output is high, aboundresources, and bamboo wood has stronger longitudinal toughness, higher hardness, bending strength, therefore wood substituted by bamboo is the important measures alleviating timber supply and demand contradiction, is also a kind of alternative raw material of high-quality.Have a lot to the method that bamboo wood is processed merely, the patent No. be 99117809.2 Chinese invention patent disclose a kind of method of recombining bamboo material into reinforced shapes, mao bamboon is split into bamboo silk by it, and impregnation is die-filling after drying, then through high pressure compacting and curing molding.The method improves the utilization rate to bamboo wood, the good stability of section bar, but there is following defect: 1) raw material generally is full bamboo, and draw materials too single, raw material supply is more nervous; 2) a large amount of waste materials can be produced when mao bamboon is cooked well-thought-out plan silk, comprise dust, particle, part and fracture of wire, reduce the utilization rate of raw material; 3) fiber elongation method process bamboo wood, makes the fibre structure of bamboo wood receive and destroys largely, will use the glue of more amount in regrouping process, and cost is high and increase the density (proportion) of section bar.In addition, it is exactly not anti-skidding that timber floor and bamboo flooring also exist a very large potential safety hazard, and especially have the family of child, the urine everywhere of child more easily allows people slip.
Summary of the invention
(1) technical problem solved
For the deficiencies in the prior art, the invention provides a kind of manufacture method of anti-sliding bamboo wood composite board.The present invention makes the utilization rate of material higher, draws materials more extensive, utilizes the feature of bamboo wood quality to avoid destroying when suppressing the fibre structure of material; In addition, good anti-skidding effect can be played at bamboo-wood plyboard surface coating antislip paint.
(2) technical scheme
For realizing above object, the present invention is achieved by the following technical programs:
A manufacture method for anti-sliding bamboo wood composite board, comprises the following steps:
(1) select materials: bamboo wood can select the leftover pieces after mao bamboon, assorted bamboo, small-bore bamboo or bamboo processing, and timber can select willow, willow or the timber leftover pieces after processing;
(2) dry: above-mentioned raw materials being dried to moisture content is 9% ~ 11%;
(3) roll: the bamboo wood after step (2) is gone green grass or young crops, timber peeling, through cal rolling well-thought-out plan matter and wooden blank;
(4) again dry: it is 7% ~ 12% that the bamboo matter after step (3) and wooden blank are dried to moisture content;
(5) compound of blank: bamboo matter blank, wooden blank are carried out to applying glue, hot pressing, cooled to obtain bamboo-wood composite board;
(6) health: by bamboo-wood composite board health 3 ~ 7 days;
(7) antislip paint is coated with: at bamboo-wood plyboard surface coating antislip paint.
Preferably, described step (2) is: first raw material is placed on natural seasoning place, when gas is done to moisture content 35%, send into dry kiln and carry out force drying, the humidity controlled in dry kiln is 70% ~ 90%, and the time is 5 ~ 6 days, the temperature controlling first day is 50 DEG C ~ 60 DEG C, and the programming rate of 10 DEG C of keeping heating up every day, until temperature reaches 100 DEG C, make moisture content be reduced to 9% ~ 11%.
Preferably, described step (4) is: the bamboo matter after cal rolling and wooden blank put into conditioning room, and control temperature is 30 DEG C ~ 45 DEG C, and humidity is 70% ~ 90%, makes moisture content be adjusted to 7% ~ 12%.
Preferably, the adhesive that the Process of Applying Glue of described step (5) adopts is waterproof glue, and this waterproof glue selects modified phenolic or soluble polyurethane.
Preferably, the hot pressing of described step (5) is:
1. heat pre-pressing stage: by heating plate and material surface contact, maintenance pressure is 1mpa ~ 1.5mpa, and temperature is 90 DEG C ~ 100 DEG C, and the time is 2min ~ 3min;
2. packing stage: intensified pressure, make pressure be 3mpa ~ 5mpa, temperature is increased to 120 DEG C ~ 140 DEG C, and the time is 5min ~ 10min;
3. shape the stage: reduce pressure, make pressure be 1.5mpa ~ 2mpa, temperature is 80 DEG C ~ 100 DEG C, and the time is 2min ~ 6min.
Preferably, the constituent of the antislip paint of described step (7) is: linear alkyl arylsulfonates 35 parts, 15 parts, phenolic resins, alkylphenol-polyethenoxy alcohol sulfuric ester sodium salt 60 parts, 1 part, sodium chloride, rosin 3 parts, ethanol 3 parts, sodium metasilicate 2 parts, titanium dioxide 2 parts.
Preferably, described bamboo-wood composite board is composited by three layers, and upper and lower superficial layer is bamboo matter base layer, and sandwich layer is wooden base layer.
(3) beneficial effect
The invention provides a kind of manufacture method of anti-sliding bamboo wood composite board, there is following beneficial effect:
1, raw-material sustainability: although bamboo growth cycle short, become a useful person fast, but the share comparing timber resources shared is less, if excessively developed, probably cause bamboo wood to degenerate, this just requires plannedly to make good use of limited bamboo timber resource and timber resources; The three-decker of bamboo-wood plyboard, two superficial layers adopt bamboo matter base layer, and sandwich layer adopts wooden base layer, and this is beneficial to and realizes raw-material sustainable development;
2, scientific and reasonable for structure: the high bamboo wood of intensity is large, hardness is as surfacing, with fast growing wood as core material, effectively enhance the Self-regulation ability of system internal stress change, overcome single bamboo clappers to a great extent and the problem such as solid wood board size is unstable, yielding, substantially the intrinsic fibre structure of raw material is not destroyed, make the cemented surface of storeroom little, glue consumption is few;
3, safety coefficient improves: can play good anti-skidding effect at bamboo-wood plyboard surface coating antislip paint, and this antislip paint is without harmful components, green is safety again.
Detailed description of the invention
For making the object of the embodiment of the present invention, technical scheme and advantage clearly, below in conjunction with the embodiment of the present invention, the technical scheme in the embodiment of the present invention is clearly and completely described, obviously, described embodiment is the present invention's part embodiment, instead of whole embodiments.Based on the embodiment in the present invention, those of ordinary skill in the art, not making the every other embodiment obtained under creative work prerequisite, belong to the scope of protection of the invention.
Embodiment 1:
A manufacture method for anti-sliding bamboo wood composite board, comprises the following steps:
(1) select materials: bamboo wood can select the leftover pieces after mao bamboon, assorted bamboo, small-bore bamboo or bamboo processing, and timber can select willow, willow or the timber leftover pieces after processing;
(2) dry: first raw material to be placed on natural seasoning place, when gas is done to moisture content 35%, send into dry kiln and carry out force drying, the humidity controlled in dry kiln is 80%, time is 5 ~ 6 days, and controlling the temperature of first day is 50 DEG C ~ 60 DEG C, and the programming rate of 10 DEG C of keeping heating up every day, until temperature reaches 100 DEG C, moisture content is made to be reduced to 10%;
(3) roll: the bamboo wood after step (2) is gone green grass or young crops, timber peeling, through cal rolling well-thought-out plan matter and wooden blank;
(4) again dry: the bamboo matter after cal rolling and wooden blank put into conditioning room, and control temperature is 30 DEG C ~ 45 DEG C, and humidity is 80%, makes moisture content be adjusted to 10%;
(5) compound of blank: first modified phenolic applying glue is carried out to bamboo matter blank, wooden blank, carry out hot-pressing processing subsequently: 1. heat pre-pressing stage: by heating plate and material surface contact, maintenance pressure is 1mpa ~ 1.5mpa, and temperature is 90 DEG C ~ 100 DEG C, and the time is 2min ~ 3min; 2. packing stage: intensified pressure, make pressure be 3mpa ~ 5mpa, temperature is increased to 120 DEG C ~ 140 DEG C, and the time is 5min ~ 10min; 3. shape the stage: reduce pressure, make pressure be 1.5mpa ~ 2mpa, temperature is 80 DEG C ~ 100 DEG C, and the time is 2min ~ 6min; Finally cool to obtain bamboo-wood composite board, bamboo-wood composite board is composited by three layers, and upper and lower superficial layer is bamboo matter base layer, and sandwich layer is wooden base layer;
(6) health: by bamboo-wood composite board health 5 days;
(7) antislip paint is coated with: at bamboo-wood plyboard surface coating antislip paint, the constituent of antislip paint is: linear alkyl arylsulfonates 35 parts, 15 parts, phenolic resins, alkylphenol-polyethenoxy alcohol sulfuric ester sodium salt 60 parts, 1 part, sodium chloride, rosin 3 parts, ethanol 3 parts, sodium metasilicate 2 parts, titanium dioxide 2 parts.
Embodiment 2:
A manufacture method for anti-sliding bamboo wood composite board, comprises the following steps:
(1) select materials: bamboo wood can select the leftover pieces after mao bamboon, assorted bamboo, small-bore bamboo or bamboo processing, and timber can select willow, willow or the timber leftover pieces after processing;
(2) dry: first raw material to be placed on natural seasoning place, when gas is done to moisture content 35%, send into dry kiln and carry out force drying, the humidity controlled in dry kiln is 90%, time is 5 ~ 6 days, and controlling the temperature of first day is 50 DEG C ~ 60 DEG C, and the programming rate of 10 DEG C of keeping heating up every day, until temperature reaches 100 DEG C, moisture content is made to be reduced to 11%;
(3) roll: the bamboo wood after step (2) is gone green grass or young crops, timber peeling, through cal rolling well-thought-out plan matter and wooden blank;
(4) again dry: the bamboo matter after cal rolling and wooden blank put into conditioning room, and control temperature is 30 DEG C ~ 45 DEG C, and humidity is 90%, makes moisture content be adjusted to 12%;
(5) compound of blank: first soluble polyurethane applying glue is carried out to bamboo matter blank, wooden blank, carry out hot-pressing processing subsequently: 1. heat pre-pressing stage: by heating plate and material surface contact, maintenance pressure is 1mpa ~ 1.5mpa, temperature is 90 DEG C ~ 100 DEG C, and the time is 2min ~ 3min; 2. packing stage: intensified pressure, make pressure be 3mpa ~ 5mpa, temperature is increased to 120 DEG C ~ 140 DEG C, and the time is 5min ~ 10min; 3. shape the stage: reduce pressure, make pressure be 1.5mpa ~ 2mpa, temperature is 80 DEG C ~ 100 DEG C, and the time is 2min ~ 6min; Finally cool to obtain bamboo-wood composite board, bamboo-wood composite board is composited by three layers, and upper and lower superficial layer is bamboo matter base layer, and sandwich layer is wooden base layer;
(6) health: by bamboo-wood composite board health 7 days;
(7) antislip paint is coated with: at bamboo-wood plyboard surface coating antislip paint, the constituent of antislip paint is: linear alkyl arylsulfonates 35 parts, 15 parts, phenolic resins, alkylphenol-polyethenoxy alcohol sulfuric ester sodium salt 60 parts, 1 part, sodium chloride, rosin 3 parts, ethanol 3 parts, sodium metasilicate 2 parts, titanium dioxide 2 parts.
It should be noted that, in this article, the such as relational terms of first and second grades and so on is only used for an entity or operation to separate with another entity or operating space, and not necessarily requires or imply the relation that there is any this reality between these entities or operation or sequentially.And, term " comprises ", " comprising " or its any other variant are intended to contain comprising of nonexcludability, thus make to comprise the process of a series of key element, method, article or equipment and not only comprise those key elements, but also comprise other key elements clearly do not listed, or also comprise by the intrinsic key element of this process, method, article or equipment.When not more restrictions, the key element limited by statement " comprising ... ", and be not precluded within process, method, article or the equipment comprising described key element and also there is other identical element.
Above embodiment is only in order to illustrate technical scheme of the present invention, be not intended to limit, although with reference to previous embodiment to invention has been detailed description, those of ordinary skill in the art is to be understood that: it still can be modified to the technical scheme described in foregoing embodiments, or carries out equivalent replacement to wherein portion of techniques feature; And these amendments or replacement, do not make the essence of appropriate technical solution depart from the spirit and scope of various embodiments of the present invention technical scheme.
Claims (7)
1. a manufacture method for anti-sliding bamboo wood composite board, is characterized in that, it comprises the following steps:
(1) select materials: bamboo wood can select the leftover pieces after mao bamboon, assorted bamboo, small-bore bamboo or bamboo processing, and timber can select willow, willow or the timber leftover pieces after processing;
(2) dry: above-mentioned raw materials being dried to moisture content is 9% ~ 11%;
(3) roll: the bamboo wood after step (2) is gone green grass or young crops, timber peeling, through cal rolling well-thought-out plan matter and wooden blank;
(4) again dry: it is 7% ~ 12% that the bamboo matter after step (3) and wooden blank are dried to moisture content;
(5) compound of blank: bamboo matter blank, wooden blank are carried out to applying glue, hot pressing, cooled to obtain bamboo-wood composite board;
(6) health: by bamboo-wood composite board health 3 ~ 7 days;
(7) antislip paint is coated with: at bamboo-wood plyboard surface coating antislip paint.
2. the manufacture method of anti-sliding bamboo wood composite board according to claim 1, it is characterized in that, described step (2) is: first raw material is placed on natural seasoning place, when gas is done to moisture content 35%, sends into dry kiln and carries out force drying, the humidity controlled in dry kiln is 70% ~ 90%, time is 5 ~ 6 days, and controlling the temperature of first day is 50 DEG C ~ 60 DEG C, and the programming rate of 10 DEG C of keeping heating up every day, until temperature reaches 100 DEG C, moisture content is made to be reduced to 9% ~ 11%.
3. the manufacture method of anti-sliding bamboo wood composite board according to claim 1, it is characterized in that, described step (4) is: the bamboo matter after cal rolling and wooden blank put into conditioning room, control temperature is 30 DEG C ~ 45 DEG C, humidity is 70% ~ 90%, makes moisture content be adjusted to 7% ~ 12%.
4. the manufacture method of anti-sliding bamboo wood composite board according to claim 1, is characterized in that, the adhesive that the Process of Applying Glue of described step (5) adopts is waterproof glue, and this waterproof glue selects modified phenolic or soluble polyurethane.
5. the manufacture method of anti-sliding bamboo wood composite board according to claim 1, is characterized in that, the hot pressing of described step (5) is:
1. heat pre-pressing stage: by heating plate and material surface contact, maintenance pressure is 1mpa ~ 1.5mpa, and temperature is 90 DEG C ~ 100 DEG C, and the time is 2min ~ 3min;
2. packing stage: intensified pressure, make pressure be 3mpa ~ 5mpa, temperature is increased to 120 DEG C ~ 140 DEG C, and the time is 5min ~ 10min;
3. shape the stage: reduce pressure, make pressure be 1.5mpa ~ 2mpa, temperature is 80 DEG C ~ 100 DEG C, and the time is 2min ~ 6min.
6. the manufacture method of anti-sliding bamboo wood composite board according to claim 1, it is characterized in that, the constituent of the antislip paint of described step (7) is: linear alkyl arylsulfonates 35 parts, 15 parts, phenolic resins, alkylphenol-polyethenoxy alcohol sulfuric ester sodium salt 60 parts, 1 part, sodium chloride, rosin 3 parts, ethanol 3 parts, sodium metasilicate 2 parts, titanium dioxide 2 parts.
7. the manufacture method of anti-sliding bamboo wood composite board according to claim 1, is characterized in that, bamboo-wood composite board is composited by three layers, and upper and lower superficial layer is bamboo matter base layer, and sandwich layer is wooden base layer.