CN105385145A - Wear-resistant polyurethane film - Google Patents
Wear-resistant polyurethane film Download PDFInfo
- Publication number
- CN105385145A CN105385145A CN201510959729.6A CN201510959729A CN105385145A CN 105385145 A CN105385145 A CN 105385145A CN 201510959729 A CN201510959729 A CN 201510959729A CN 105385145 A CN105385145 A CN 105385145A
- Authority
- CN
- China
- Prior art keywords
- wear
- parts
- polyurethane film
- content
- accounts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a wear-resistant polyurethane film, which comprises the following chemical components by mass: 50-60 parts of polyurethane, 8-14 parts of stearic acid, 2-6 parts of a coupling agent, 3-5 parts of graphite powder, 12-18 parts of toluene diisocyanate, 16-22 parts of a tackifier, and 10-20 parts of a wear-resistance aid, wherein the wear-resistance aid is prepared by mixing 24-28% by mass of sodium lignin sulfonate and 72-76% of polytetrafluoroethylene. According to the present invention, the wear-resistant polyurethane film has advantages of high strength, wear resistance, strong adhesion, and substantially-improved use value.
Description
Technical field
The present invention relates to a kind of macromolecular material, particularly a kind of wear-resistant type polyurethane film.
Background technology
Along with the adjustment of expanding economy and the structure of rural undertaking, the market requirement of China's all trades and professions to plastics film constantly rises, wherein, polyurethane film because of its superior performance and environmental protection concept day by day welcomed by the people, polyurethane film not only can with various cloth pasting, clear-cut can also be produced by the method for vacuum thermoforming, the product of dimensional stabilizing, then in the process used, film is all plated on product surface, therefore the wear resistance for film requires very harsh, and traditional film is more difficult meets its requirement.
Summary of the invention
The technical problem that the present invention mainly solves is to provide a kind of wear-resistant type polyurethane film, can have the advantage of high strength, wear-resisting, strong adhesion, significantly improve use value.
For solving the problems of the technologies described above, the technical scheme that the present invention adopts is: provide a kind of wear-resistant type polyurethane film, the mass fraction of its chemical composition is specific as follows:
Urethane 50-60 part, stearic acid 8-14 part, coupling agent 2-6 part, Graphite Powder 99 3-5 part, tolylene diisocyanate 12-18 part, tackifier 16-22 part, antiwear assistant 10-20 part;
Described antiwear assistant is mixed by sodium lignosulfonate and tetrafluoroethylene, and calculate according to mass percent, the content of described sodium lignosulfonate accounts for 24-28%, and the content of described tetrafluoroethylene accounts for 72-76%.
In a preferred embodiment of the present invention, described coupling agent is aminopropyl triethoxysilane.
In a preferred embodiment of the present invention, described tackifier are aliphatic hydrocarbon resin.
In a preferred embodiment of the present invention, in described antiwear assistant, the concrete proportioning of composition is: the content of described sodium lignosulfonate accounts for 26%, and the content of described tetrafluoroethylene accounts for 74%.
The invention has the beneficial effects as follows: the present invention can have the advantage of high strength, wear-resisting, strong adhesion, significantly improves use value.
Embodiment
Below preferred embodiment of the present invention is described in detail, can be easier to make advantages and features of the invention be readily appreciated by one skilled in the art, thus more explicit defining is made to protection scope of the present invention.
Embodiment 1:
A kind of wear-resistant type polyurethane film, the mass fraction of chemical composition is specific as follows:
Urethane 50 parts, stearic acid 14 parts, aminopropyl triethoxysilane 2 parts, Graphite Powder 99 5 parts, tolylene diisocyanate 12 parts, aliphatic hydrocarbon resin 22 parts, antiwear assistant 10 parts;
Described antiwear assistant is mixed by sodium lignosulfonate and tetrafluoroethylene, and calculate according to mass percent, the content of described sodium lignosulfonate accounts for 24%, and the content of described tetrafluoroethylene accounts for 76%.
Embodiment 2:
A kind of wear-resistant type polyurethane film, the mass fraction of chemical composition is specific as follows:
Urethane 60 parts, stearic acid 8 parts, aminopropyl triethoxysilane 6 parts, Graphite Powder 99 3 parts, tolylene diisocyanate 18 parts, aliphatic hydrocarbon resin 16 parts, antiwear assistant 20 parts;
Described antiwear assistant is mixed by sodium lignosulfonate and tetrafluoroethylene, and calculate according to mass percent, the content of described sodium lignosulfonate accounts for 28%, and the content of described tetrafluoroethylene accounts for 72%.
Embodiment 3:
A kind of wear-resistant type polyurethane film, the mass fraction of chemical composition is specific as follows:
Urethane 55 parts, stearic acid 11 parts, aminopropyl triethoxysilane 4 parts, Graphite Powder 99 4 parts, tolylene diisocyanate 15 parts, aliphatic hydrocarbon resin 19 parts, antiwear assistant 15 parts;
Described antiwear assistant is mixed by sodium lignosulfonate and tetrafluoroethylene, and calculate according to mass percent, the content of described sodium lignosulfonate accounts for 26%, and the content of described tetrafluoroethylene accounts for 74%.
The preparation method of a kind of wear-resistant type of the present invention polyurethane film is as follows:
(1), first above-mentioned batching is proportionally stirred in charging basket;
(2), adopt dehumidifier to be dried by above-mentioned materials, control water ratio and be less than or equal to 0.05%;
(3), after extruder screw plasticizing, from the extrusion moulding of die head die orifice;
(4), cool finally by inside and outside vane, rolling forms after rotation traction traction, deckle machine deckle, both sides trimming again.
Be different from prior art, the present invention can have the advantage of high strength, wear-resisting, strong adhesion, significantly improves use value.
The foregoing is only embodiments of the invention; not thereby the scope of the claims of the present invention is limited; every utilize description of the present invention to do equivalent structure or equivalent flow process conversion; or be directly or indirectly used in other relevant technical fields, be all in like manner included in scope of patent protection of the present invention.
Claims (4)
1. a wear-resistant type polyurethane film, is characterized in that, the mass fraction of its chemical composition is specific as follows:
Urethane 50-60 part, stearic acid 8-14 part, coupling agent 2-6 part, Graphite Powder 99 3-5 part, tolylene diisocyanate 12-18 part, tackifier 16-22 part, antiwear assistant 10-20 part;
Described antiwear assistant is mixed by sodium lignosulfonate and tetrafluoroethylene, and calculate according to mass percent, the content of described sodium lignosulfonate accounts for 24-28%, and the content of described tetrafluoroethylene accounts for 72-76%.
2. wear-resistant type polyurethane film according to claim 1, is characterized in that, described coupling agent is aminopropyl triethoxysilane.
3. wear-resistant type polyurethane film according to claim 1, is characterized in that, described tackifier are aliphatic hydrocarbon resin.
4. wear-resistant type polyurethane film according to claim 1, is characterized in that, in described antiwear assistant, the concrete proportioning of composition is: the content of described sodium lignosulfonate accounts for 26%, and the content of described tetrafluoroethylene accounts for 74%.