CN105368282A - 一种用于铜管防锈的组合物 - Google Patents
一种用于铜管防锈的组合物 Download PDFInfo
- Publication number
- CN105368282A CN105368282A CN201410394274.3A CN201410394274A CN105368282A CN 105368282 A CN105368282 A CN 105368282A CN 201410394274 A CN201410394274 A CN 201410394274A CN 105368282 A CN105368282 A CN 105368282A
- Authority
- CN
- China
- Prior art keywords
- parts
- sodium sulfate
- copper pipe
- composition
- urea
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种用于铜管防锈的组合物，所述的配方成分重量份数为脂肪醇聚氧乙烯醚硫酸钠60-80份、聚氨酯乳液90-140份、聚烯烃类树脂6-8份、石油硫酸钠6-8份、无机酸或有机酸的胺/铵/金属盐25-30份、尿素5-10份、疏水剂5-10份、纳米填料5-10份，水100-150份。本发明克服了现有技术的不足，在配方设计方面增加防锈膜的疏水性，能够减弱水分子的透过率，从而提高防锈膜的防锈性能，处理防锈效果佳的防锈组合物配方。
Description
技术领域
本发明涉及制冷技术铜管防锈处理领域，具体属于一种用于铜管防锈的组合物。
背景技术
在制冷技术领域中，用于制冷设备的铜管，在其加工过程中，需要采用防锈剂对其内壁进行防锈处理，以保证产品质量较高，使用寿命较长，铜管内壁在长期使用过程中不会发生锈迹等情况出现。
发明内容
本发明的目的是提供了一种用于铜管防锈的组合物，克服了现有技术的不足，在配方设计方面增加防锈膜的疏水性，能够减弱水分子的透过率，从而提高防锈膜的防锈性能，处理防锈效果佳的防锈组合物配方。
本发明采用的技术方案如下：
一种用于铜管防锈的组合物，所述的配方成分重量份数为脂肪醇聚氧乙烯醚硫酸钠60-80份、聚氨酯乳液90-140份、聚烯烃类树脂6-8份、石油硫酸钠6-8份、无机酸或有机酸的胺/铵/金属盐25-30份、尿素5-10份、疏水剂5-10份、纳米填料5-10份，水100-150份。
所述的脂肪醇聚氧乙烯醚硫酸钠50份、聚氨酯乳液130份、聚烯烃类树脂10份、石油硫酸钠5份、无机酸或有机酸的胺/铵/金属盐25份、尿素10份、疏水剂5份、纳米填料8份。
所述的脂肪醇聚氧乙烯醚硫酸钠70份、聚氨酯乳液120份、聚烯烃类树脂10份、石油硫酸钠8份、无机酸或有机酸的胺/铵/金属盐25份、尿素8份、疏水剂8份、纳米填料8份。
所述的脂肪醇聚氧乙烯醚硫酸钠70份、聚氨酯乳液130份、聚烯烃类树脂8份、石油硫酸钠8份、无机酸或有机酸的胺/铵/金属盐25份、尿素8份、疏水剂5份、纳米填料8份。
一种用于铜管防锈的组合物的制备方法，将水加热到45～55℃，将上述配方加入，进行高速搅拌剪切，直至完全乳化分散。
与已有技术相比，本发明的有益效果如下：
本发明在配方设计方面增加防锈膜的疏水性，能够减弱水分子的透过率，从而提高防锈膜的防锈性能，处理防锈效果佳的防锈组合物配方。
具体实施方式
实施例1
一种用于铜管防锈的组合物，所述的配方组分重量份数为脂肪醇聚氧乙烯醚硫酸钠50份、聚氨酯乳液130份、聚烯烃类树脂10份、石油硫酸钠5份、无机酸或有机酸的胺/铵/金属盐25份、尿素10份、疏水剂5份、纳米填料8份，水80-150份。按上述配方，将水加热到45～55℃，将上述配方中成分加入，进行高速搅拌剪切，直至完全乳化分散，得到产品。
实施例2
一种用于铜管防锈的组合物，所述的配方组分重量份数为脂肪醇聚氧乙烯醚硫酸钠70份、聚氨酯乳液120份、聚烯烃类树脂10份、石油硫酸钠8份、无机酸或有机酸的胺/铵/金属盐25份、尿素8份、疏水剂8份，纳米填料8份，水80-150份，按上述配方，将水加热到45～55℃，将上述配方中成分加入，进行高速搅拌剪切，直至完全乳化分散，得到产品。
实施例3
一种用于铜管防锈的组合物，所述的配方组分重量份数为脂肪醇聚氧乙烯醚硫酸钠70份、聚氨酯乳液130份、聚烯烃类树脂8份、石油硫酸钠8份、无机酸或有机酸的胺/铵/金属盐25份、尿素8份、疏水剂5份，纳米填料8份，水80-150份，按上述配方，将水加热到45～55℃，将上述配方中成分加入，进行高速搅拌剪切，直至完全乳化分散，得到产品。
Claims (5)
1.一种用于铜管防锈的组合物，其特征在于：所述的配方成分重量份数为脂肪醇聚氧乙烯醚硫酸钠60-80份、聚氨酯乳液90-140份、聚烯烃类树脂6-8份、石油硫酸钠6-8份、无机酸或有机酸的胺/铵/金属盐25-30份、尿素5-10份、疏水剂5-10份、纳米填料5-10份，水100-150份。
2.根据权利要求1所述的一种用于铜管防锈的组合物，其特征在于：所述的脂肪醇聚氧乙烯醚硫酸钠50份、聚氨酯乳液130份、聚烯烃类树脂10份、石油硫酸钠5份、无机酸或有机酸的胺/铵/金属盐25份、尿素10份、疏水剂5份、纳米填料8份。
3.根据权利要求1所述的一种用于铜管防锈的组合物，其特征在于：所述的脂肪醇聚氧乙烯醚硫酸钠70份、聚氨酯乳液120份、聚烯烃类树脂10份、石油硫酸钠8份、无机酸或有机酸的胺/铵/金属盐25份、尿素8份、疏水剂8份、纳米填料8份。
4.根据权利要求1所述的一种用于铜管防锈的组合物，其特征在于：所述的脂肪醇聚氧乙烯醚硫酸钠70份、聚氨酯乳液130份、聚烯烃类树脂8份、石油硫酸钠8份、无机酸或有机酸的胺/铵/金属盐25份、尿素8份、疏水剂5份、纳米填料8份。
5.根据权利要求1-4其中之一所述的一种用于铜管防锈的组合物的制备方法，其特征在于：将水加热到45～55℃，将上述配方加入，进行高速搅拌剪切，直至完全乳化分散。