CN105367132A - Novel glaze material and application thereof - Google Patents
Novel glaze material and application thereof Download PDFInfo
- Publication number
- CN105367132A CN105367132A CN201410442298.1A CN201410442298A CN105367132A CN 105367132 A CN105367132 A CN 105367132A CN 201410442298 A CN201410442298 A CN 201410442298A CN 105367132 A CN105367132 A CN 105367132A
- Authority
- CN
- China
- Prior art keywords
- glaze
- parts
- glaze material
- novel
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a novel glaze material and application thereof. The glaze material is prepared from, by weight, 55-75 parts of SiO<2>, 10-20 parts of Al<2>O<3>, 0-3 parts of (K<2>O+Na<2>O), 5-10 parts of CaO, 0-5 parts of MgO, 2-5 parts of ZnO, 0-3 parts of BaO and 5-10 parts of ZrO<2>. According to the novel glaze material and the application thereof, the glaze material which is good in high temperature flowability is produced out through the steps of raw material selection, matching, high temperature firing and the like, moreover, raw materials which are large in surface tension are used, when the glaze is subjected to high temperature melting, surface tension of the glaze material is larger than that of a traditional glaze material, interaction is achieved, the glaze achieves a smooth effect, gas in the glaze material is easy to discharge, no trace is left by the discharged gas, and no small opening or hole is left, so that the glaze is easy to clean, most of flux used in the formula is alkaline-earth metal, introduction of alkali metal, namely potassium oxide and sodium oxide, is reduced, hardness of the glaze is improved, and wear resistance of the glaze is enhanced.
Description
Technical field
The invention belongs to ceramic field, be specifically related to a kind of Novel glaze material and application thereof.
Background technology
Existing full throwing glaze brick product just rises, and the exploitation of the glaze adapted with it relatively lags behind, and at present the full glaze brick product of throwing of great majority all adopts common fritted glaze, its shortcoming be glaze paint wear no resistance and hardness little, be difficult to meet service requirements.Thus develop new have better wear resistance and the high cover-coat enamel glaze of hardness become building field in the urgent need to.
Summary of the invention
One object of the present invention is to provide the Novel glaze material that a kind of hardness is high, wear resistance is good.
Another object of the present invention is to provide the method being prepared Novel glaze by above-mentioned glazing type material.
For solving the problems of the technologies described above, the technical solution used in the present invention is:
A kind of Novel glaze material, is made up of the raw material of following weight part: SiO
255-75 part, Al
2o
310-20 part, (K
2o+Na
2o) 0-3 part, CaO5-10 part, MgO0-5 part, ZnO2-5 part, BaO0-3 part, ZrO
25-10 part.
As preferably, described glazing type material is made up of the raw material of following weight part: SiO
262 parts, Al
2o
316 parts, K
2o1 part, Na
2o1 part, CaO7 part, MgO2 part, ZnO3 part, BaO1 part, ZrO
26 parts.
The preparation method of the above Novel glaze material, comprises the steps: raw material to add ball milling in ball mill, crosses 200 ~ 400 mesh sieves after ball milling, and be preferably 325 mesh sieves, excess is less than 0.1%.
A preparation method for Novel glaze, comprises the steps: that the above-mentioned Novel glaze material prepared burns till at 1100 DEG C-1200 DEG C, and is incubated more than 2 hours at the maximum temperature.
The invention has the beneficial effects as follows: the present invention is chosen by starting material, the steps such as proportioning and high temperature burn till, the temperature flowing performance of the glaze produced is good, add in raw material the raw material using surface tension larger, glaze is under high-temperature fusion, surface tension is large compared with traditional glaze, both interact, glaze paint just reaches a level and smooth effect, and gas is easily discharged in glaze, and expellant gas also can not be left a trace, small holes is not had to stay, make glaze paint easy to clean, the flux used in formula mostly is alkaline-earth metal, decrease basic metal potassium oxide, the introducing of sodium oxide, the hardness of glaze paint is improved, add the wear resistance of glaze paint.
Embodiment
Below in conjunction with embodiment, the present invention is further illustrated,
Embodiment 1
A kind of Novel glaze material, is made up of the raw material of following weight part: SiO
262 parts, Al
2o
316 parts, K
2o1 part, Na
2o1 part, CaO7 part, MgO2 part, ZnO3 part, BaO1 part, ZrO
26 parts.
Embodiment 2
A kind of Novel glaze material, is made up of the raw material of following weight part: SiO
255 parts, Al
2o
310 parts, K
2o1 part, Na
2o1 part, CaO10 part, ZnO5 part, BaO2 part, ZrO
210 parts.
Embodiment 3
A kind of Novel glaze material, is made up of the raw material of following weight part: SiO
275 parts, Al
2o
320 parts, CaO5 part, MgO5 part, ZnO2 part, BaO3 part, ZrO
25 parts.
Embodiment 4
A kind of Novel glaze material, is made up of the raw material of following weight part: SiO
260 parts, Al
2o
315 parts, K
2o1 part, Na
2o2 part, CaO8 part, MgO3 part, ZnO4 part, ZrO
28 parts.
The raw material of embodiment 1 ~ 4 is added ball milling in ball mill, and cross 325 mesh sieves after ball milling, excess is less than 0.1%.
The above-mentioned Novel glaze material prepared burns till at 1100 DEG C-1200 DEG C, and insulation can obtain a kind of Novel glaze in more than 2 hours at the maximum temperature.
The property of glaze obtained is fired as shown in table 1 by the glazing type material of embodiment 1 ~ 4.
Table 1
| Performance index | Fastness to rubbing (cc) | Mohs' hardness | Surface tension (dynes per centimeter) |
| Embodiment 1 | 4.0 | 7.5 | 390 |
| Embodiment 2 | 3.0 | 6.0 | 370 |
| Embodiment 3 | 2.5 | 6.5 | 375 |
| Embodiment 4 | 3.5 | 7.0 | 380 |
Above embodiment is only introduces preferred case of the present invention, to those skilled in the art, not deviating from any apparent changes and improvements of carrying out in the scope of spirit of the present invention, all should be regarded as a part of the present invention.
Claims (5)
1. a Novel glaze material, is characterized in that, described glazing type material is made up of the raw material of following weight part: SiO
255-75 part, Al
2o
310-20 part, (K
2o+Na
2o) 0-3 part, CaO5-10 part, MgO0-5 part, ZnO2-5 part, BaO0-3 part, ZrO
25-10 part.
2. according to claim 1, it is characterized in that, described glazing type material is made up of the raw material of following weight part: SiO
262 parts, Al
2o
316 parts, K
2o1 part, Na
2o1 part, CaO7 part, MgO2 part, ZnO3 part, BaO1 part, ZrO
26 parts.
3. the preparation method of Novel glaze material described in claim 1 or 2, comprises the steps: raw material to add ball milling in ball mill, and cross 200 ~ 400 mesh sieves after ball milling, excess is less than 0.1%.
4. preparation method according to claim 3,325 mesh sieves crossed by the raw material after ball milling, and excess is less than 0.1%.
5. a preparation method for Novel glaze, comprises the steps: that Novel glaze material claim 3 or 4 prepared burns till at 1100 DEG C-1200 DEG C, and is incubated more than 2 hours at the maximum temperature.