CN105363662A - Mosquito-resisting PVC coating film material and coating knife-scraping process thereof - Google Patents
Mosquito-resisting PVC coating film material and coating knife-scraping process thereof Download PDFInfo
- Publication number
- CN105363662A CN105363662A CN201510646383.4A CN201510646383A CN105363662A CN 105363662 A CN105363662 A CN 105363662A CN 201510646383 A CN201510646383 A CN 201510646383A CN 105363662 A CN105363662 A CN 105363662A
- Authority
- CN
- China
- Prior art keywords
- mosquito
- coating
- pvc
- paste resin
- film material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a mosquito-resisting PVC coating film material and a coating knife-scraping process thereof. The mosquito-resisting PVC coating film material comprises a base cloth layer. The front face of the base cloth layer is coated with a first base coat, and the back face of the base cloth layer is coated with a second base coat. The surface of the first base coat is coated with a first mosquito-resisting coating, and the surface of the second base coat is coated with a second mosquito-resisting coating. The base cloth layer is composed of base cloth. The mosquito-resisting PVC coating film material is prepared through the coating knife-scraping process; and due to the fact that the prepared mosquito-resisting PVC coating film material can repel mosquitoes, the situation that insects are gathered on the surface of the PVC coating film material one by one, the coating film material is corroded, the color of the appearance is changed in less serious cases, and the film material is aged and scraped in advance in serious cases is avoided.
Description
Technical field
The present invention relates to field of new, more particularly, relate to and a kind ofly there is the PVC coated film material of anti-mosquito function and prepare the cutter scraping coating technique of this anti-mosquito PVC coated film material.
Background technology
PVC coated film material as a kind of soft PVC product, in its formula system, containing various plasticizer and auxiliary agent.And this is for mosquito moth etc., be a kind of well trophosome, particularly in summer, under the attraction of light, above insect is gathered in PVC coated film material one after another, etching resist film material, and the lighter causes appearance color change, and severe one causes film material premature aging to scrap.Therefore, from the service life of improving coated film material, enough attention must be caused to this problem, and solve.
Summary of the invention
The technical problem to be solved in the present invention is, for the above-mentioned defect of prior art, a kind of PVC coated film material with anti-mosquito function and preparation method thereof is provided, the present invention adopts cutter scraping coating technique to prepare anti-mosquito PVC coated film material, obtained PVC coated film material owing to dispersing mosquito, thus prevents insect to be gathered in PVC coated film material surface one after another, etching resist film material, the lighter causes appearance color change, and severe one causes film material premature aging to scrap.
The technical solution adopted for the present invention to solve the technical problems is: provide a kind of anti-mosquito PVC coated film material, comprise base cloth layer, the first priming coat is coated with in base cloth layer front, the second priming coat is had at base cloth layer backsize, be coated with the first anti-mosquito coating on the surface of the first priming coat, be coated with the second anti-mosquito coating on the surface of the second priming coat; Described base cloth layer is made up of base cloth.
Anti-mosquito PVC coated film material of the present invention, wherein, described first priming coat and the second priming coat are PVC paste resin layer, described PVC paste resin layer is formed by the PVC paste resin blade coating doped with adhesive, PVC paste resin select K value be 60 ~ 80 PVC paste resin, the isocyanates that adhesive is is medium with dibutyl phthalate or diisononyl phthalate; Described adhesive is (2-6) with the ratio of the consumption of PVC paste resin: 100; The coating weight of described first priming coat and the second priming coat is 50-100g/m
2.
Anti-mosquito PVC coated film material of the present invention, wherein, described first anti-mosquito coating and the second anti-mosquito coating are anti-mosquito PVC paste resin bed, and described anti-mosquito PVC paste resin bed is formed by anti-mosquito PVC paste resin slurry blade coating; The coating weight of described first anti-mosquito coating is 200-300g/m
2, the coating weight of the second anti-mosquito coating is 150-250g/m
2.
Anti-mosquito PVC coated film material of the present invention, wherein, described anti-mosquito PVC paste resin slurry is by the component of following parts by weight:
Anti-mosquito PVC coated film material of the present invention, wherein, described anti-mosquito PVC paste resin slurry is by the component of following parts by weight:
Anti-mosquito PVC coated film material of the present invention, wherein, described first anti-mosquito auxiliary agent be selected from pyrethrins, carbamate insecticides and third generation organophosphorus insecticide one or more.
Anti-mosquito PVC coated film material of the present invention, wherein, described carbamate insecticides is the one in dimethylcarbamate, methyl carbamic acid aromatic ester, methyl carbamic acid oxime ester, acyl N-methyl carbamate, hydroxyl sulfenyl N-methyl carbamate; Described third generation organophosphorus insecticide is the one in metrifonate, DDVP, DDVP calcium, 2-dichloroethylk dimethyl phosphate, malathion, Entex.
Anti-mosquito PVC coated film material of the present invention, wherein, described PVC paste resin is selected K value to be the PVC paste resin of 60 ~ 80 or is the PVC paste resin of 60 ~ 80 doped with the K value of blending resin; Phthalic ester plasticizer selected by described plasticizer; Described stabilizing agent selects powdery or liquid composite stabilizing agent; Inorganic filler selected by described filler; Described pigment is inorganic or organic pigment.
The present invention also provides a kind of cutter scraping coating technique preparing anti-mosquito PVC coated film material described above, comprises the steps:
(1) base cloth is prepared: the tiling of base cloth is formed base cloth layer;
(2) painting bottom coating: the front coating PVC paste resin of the base cloth layer in step (1), obtain the first priming coat, at the backsize PVC paste resin of base cloth layer, obtain the second priming coat, then deliver to heating in the first baking oven;
(3) blade coating anti-mosquito coating: adopt cutter to scrape and anti-mosquito PVC paste resin slurry is coated with the surface of scraping the first priming coat obtained in step (2), obtain the first anti-mosquito coating, deliver to subsequently in the second baking oven and heat, make the gelation of anti-mosquito PVC paste resin slurry; Then adopt cutter to scrape anti-mosquito PVC paste resin slurry painting is scraped on the surface of the second priming coat, obtain the second anti-mosquito coating, deliver to subsequently in the 3rd baking oven and heat, make the gelation of anti-mosquito PVC paste resin slurry; Last press polish, trimming, receive and roll up greatly; Obtain anti-mosquito PVC coated film material.
The cutter scraping coating technique of anti-mosquito PVC coated film material of the present invention, wherein, in step (2), the coating weight of the first priming coat and the second priming coat is 50-100g/m
2, the temperature of described first baking oven is 120-180 DEG C, and described in step (3), the temperature of the second baking oven is 150-180 DEG C, and the temperature of the 3rd baking oven is 160-200 DEG C; The coating weight of described first anti-mosquito coating is 200-300g/m
2, the coating weight of the second anti-mosquito coating is 150-250g/m
2.
Implement one of the present invention anti-mosquito PVC coated film material and cutter scraping coating technique thereof, there is following beneficial effect:
(1) the present invention adopts cutter scraping coating technique to prepare anti-mosquito PVC coated film material, obtained PVC coated film material is owing to dispersing mosquito, thus prevent insect to be gathered in PVC coated film material surface one after another, etching resist film material, the lighter causes appearance color change, and severe one causes film material premature aging to scrap.
(2) in addition, anti-mosquito PVC coated film material not only has excellent anti-pollution characteristic, and intercept the migration of plasticizer and good weather resistance, and its mosquito repellent rate can reach 30-80%, warp direction stretching load can reach 2800-5000N/5cm.
(3) of the present invention simple with the raw material of anti-mosquito PVC coated film material composition, its preparation methods steps is simple, the mosquito repellent rate of the anti-mosquito PVC coated film material prepared and warp direction stretching load performance excellence.Meanwhile, the inventive method production equipment used is simple, and the construction cost of production line is low, to human-body safety, little to the pollution of environment, and easy to operate, product favorable reproducibility, can be used for the outer widely used tent cloth of make-up room and building film material.
Detailed description of the invention
Below, in conjunction with detailed description of the invention, the present invention is described further:
One of the present invention anti-mosquito PVC coated film material, comprise base cloth layer, be coated with the first priming coat in base cloth layer front, have the second priming coat at base cloth layer backsize, be coated with the first anti-mosquito coating on the surface of the first priming coat, be coated with the second anti-mosquito coating on the surface of the second priming coat; Described base cloth layer is made up of base cloth.Wherein, described base cloth layer is polyester screen cloth, this polyester screen cloth is fracture strength >=7.0cN/dtex, the high-strength low-shrinkage type polyester filament of 177 DEG C of dry-hot shrinkage≤2.2% adopts embryo cloth that is woven or warp knitting technology braiding, this embryo cloth has certain thread count requirement, as 1100dtex23*23/inch, 1100dtex28*26/inch, 1100dtex30*30/inch etc.Adopt above-mentioned high-strength low-shrinkage type polyester filament significantly can improve the hot strength of embryo cloth, the physical properties such as this resistance to spalling, and then improve the mechanical performance of film material, effectively can reduce the contraction that embryo cloth produces because gel polyvinyl chlorideization is heated with plasticizing in process simultaneously, the thread count of embryo cloth requires should meet finished product mechanical property requirements, again by good textile technology adaptability.
Described first priming coat and the second priming coat are PVC paste resin layer, described PVC paste resin layer is formed by the PVC paste resin blade coating doped with adhesive, PVC paste resin select K value be 60 ~ 80 PVC paste resin, the isocyanates that adhesive is is medium with dibutyl phthalate or diisononyl phthalate, as bright Sheng (Lanxess) 2001, the one in middle Shandong water chestnut TP101 or VP203 etc.; Described adhesive is (2-6) with the ratio of the consumption of PVC paste resin: 100; The coating weight of described first priming coat and the second priming coat is 50-100g/m
2.
Described first anti-mosquito coating and the second anti-mosquito coating are anti-mosquito PVC paste resin bed, and described anti-mosquito PVC paste resin bed is formed by anti-mosquito PVC paste resin slurry blade coating; The coating weight of described first anti-mosquito coating is 200-300g/m
2, the coating weight of the second anti-mosquito coating is 150-250g/m
2.
Described anti-mosquito PVC paste resin slurry is made up of the component of following parts by weight:
Preferably, described anti-mosquito PVC paste resin slurry is made up of the component of following parts by weight:
Wherein, described first anti-mosquito auxiliary agent is selected from one or more in pyrethrins, carbamate insecticides and third generation organophosphorus insecticide.Described carbamate insecticides is the one in dimethylcarbamate, methyl carbamic acid aromatic ester, methyl carbamic acid oxime ester, acyl N-methyl carbamate, hydroxyl sulfenyl N-methyl carbamate; Described third generation organophosphorus insecticide is the one in metrifonate, DDVP (DDVP), DDVP calcium, 2-dichloroethylk dimethyl phosphate, malathion (marathon), Entex; The present invention carries out modification by the first anti-mosquito auxiliary agent is added PVC paste slurry, make the first anti-mosquito auxiliary agent and plasticized PVC paste material compatibility good, have stronger action of contace poison, power of knocking down is strong, and drug effect is rapid, to positive light and thermally stable.
The PVC paste resin that the present invention selects in anti-mosquito PVC paste resin slurry is K value to be the PVC paste resin of 60 ~ 80 or to be the PVC paste resin of 60 ~ 80 doped with the K value of blending resin, preferably, the PVC paste resin that K value is 62 ~ 75 is selected from; As PVC paste resin selects one or more the mixing in the PVC paste resin of Shenyang chemical industry Psm-31, Tianjin chemical industry P440, Chenzhou magnificent Hunan CPM-31, Korea S Han Hua KM-31.Phthalic ester plasticizer selected by plasticizer, preferably, be selected from dioctyl phthalate (DOP) or dinonyl phthalate (DINP) one or more.Stabilizing agent selects powdery or liquid composite stabilizing agent, as barium/zinc, and calcium/zinc etc.Inorganic filler selected by filler, as calcium carbonate, wollastonite, barium sulfate etc.Pigment is inorganic or organic pigment, as titanium dioxide, and phthalocyanine blue etc.
The present invention also provides a kind of cutter scraping coating technique preparing above-mentioned anti-mosquito PVC coated film material, comprises the steps:
(1) prepare base cloth: choose fracture strength >=7.0cN/dtex, the high-strength low-shrinkage type polyester filament of 177 DEG C of dry-hot shrinkage≤2.2% adopts embryo cloth that is woven or warp knitting technology braiding, and embryo cloth is paved formation base cloth layer;
(2) painting bottom coating: the front coating PVC paste resin of the base cloth layer in step (1), obtains the first priming coat, at the backsize PVC paste resin of base cloth layer, obtain the second priming coat; Then deliver to heating in the first baking oven, the first oven temperature is 120-180 DEG C; The coating weight of described first priming coat and the second priming coat is 50-100g/m
2.
(3) blade coating anti-mosquito coating: adopt cutter to scrape and anti-mosquito PVC paste resin slurry is coated with the surface of scraping the first priming coat obtained in step (2), obtain the first anti-mosquito coating, deliver to subsequently in the second baking oven and heat, be heated to 150-180 DEG C, make the gelation of anti-mosquito PVC paste resin slurry; Then adopt cutter to scrape anti-mosquito PVC paste resin slurry painting is scraped on the surface of the second priming coat, obtain the second anti-mosquito coating, deliver to subsequently in the 3rd baking oven and heat, be heated to 160-200 DEG C, make the gelation of anti-mosquito PVC paste resin slurry; Last press polish, trimming, receive and roll up greatly; Obtain anti-mosquito PVC coated film material.Wherein, the coating weight of described first anti-mosquito coating is 200-300g/m
2, the coating weight of the second anti-mosquito coating is 150-250g/m
2.
Preferably, the temperature of the second baking oven is 160-170 DEG C, and the temperature of the 3rd baking oven is 170-195 DEG C; The coating weight of the first anti-mosquito coating is 250-280g/m
2, the coating weight of the second anti-mosquito coating is 180-200g/m
2.
embodiment 1
A kind of anti-mosquito PVC coated film material, comprise base cloth layer, be coated with the first priming coat in base cloth layer front, have the second priming coat at base cloth layer backsize, be coated with the first anti-mosquito coating on the surface of the first priming coat, be coated with the second anti-mosquito coating on the surface of the second priming coat; Described base cloth layer is made up of base cloth.Described first priming coat and the second priming coat are PVC paste resin layer, described PVC paste resin layer is formed by the PVC paste resin blade coating doped with adhesive, PVC paste resin select K value be 75 PVC paste resin, adhesive selects bright Sheng (Lanxess) 2001, and the ratio of the consumption that adhesive is set with Welvic is 3:100.
Wherein, the formula of anti-mosquito PVC paste resin slurry is as follows:
The formula of the anti-mosquito PVC paste resin slurry of table 1 embodiment 1
The present embodiment carries out modification by pyrethrins being added PVC paste slurry, make the first anti-mosquito auxiliary agent and plasticized PVC paste material compatibility good, have stronger action of contace poison, power of knocking down is strong, and drug effect is rapid, to positive light and thermally stable.
The preparation method of this anti-mosquito PVC coated film material, comprises the steps:
(1) prepare base cloth, choose fracture strength >=7.0cN/dtex, the high-strength low-shrinkage type polyester filament of 177 DEG C of dry-hot shrinkage≤2.2% adopts embryo cloth that is woven or warp knitting technology braiding, and the tiling of embryo cloth is formed base cloth layer;
(2) painting bottom coating: the front coating PVC paste resin of the base cloth layer in step (1), obtains the first priming coat, at the backsize PVC paste resin of base cloth layer, obtain the second priming coat; The coating weight of described first priming coat and the second priming coat is 70g/m
2.
(3) anti-mosquito PVC paste resin slurry is scraped in painting: adopt cutter to scrape and anti-mosquito PVC paste resin slurry is coated with the back side of scraping the priming coat obtained in step (2), then deliver in the first baking oven, be heated to 160 DEG C, make the gelation of anti-mosquito PVC paste resin slurry; Then adopt cutter to scrape and anti-mosquito PVC paste resin slurry is coated with the front of scraping at priming coat, then deliver in the second baking oven, be heated to 185 DEG C, make the gelation of anti-mosquito PVC paste resin slurry; Last press polish, trimming, receive and roll up greatly; The film material scribbling anti-mosquito PVC paste resin slurry must be scraped; The coating weight of described first anti-mosquito coating is 250g/m
2, the coating weight of the second anti-mosquito coating is 200g/m
2.
embodiment 2-10
Proportioning respectively according to the form below 3 weighs raw material, is prepared according to the step in embodiment 1, and difference is that added pulp furnish is different, and preparing product specifically refers to the formula consumption of anti-mosquito PVC paste resin slurry in table 3:
The formula of the anti-mosquito PVC paste resin slurry of table 3 embodiment 2-10
Below, the anti-mosquito PVC coated film material that Example 1-10 is obtained, detects its anti-mosquito function and warp direction stretching load performance.
1, the test of anti-mosquito function
The anti-mosquito PVC coated film material that Example 1-10 is obtained, film material is cut into respectively the small pieces of 50 × 50mm, then test according to standard GB/T/T13917.9-2009 " evaluating the repellent action of mosquito ", the sample that comparative examples adopts is common PVC film material, and test result is in table 5.
Concrete grammar is as follows: in the mosquito cage of 40cm × 30cm × 30cm, put into about 300 Culex quinquefasciatus (Cx.pipiensquinquefasciatus) female insects of not sucking blood for 5-7 days after sprouting wings, mosquito repellent cloth and undressed control sample (long × wide is 5cm × 5cm) are fixed on diameter 4cm, the glass body side of high 12cm, and in vial, be warming up to 43 DEG C, semiconductor point thermometer is used to measure shell temperature, keep shell temperature about 36 DEG C, be placed in mosquito cage, when observing counting 2min, sample with contrast the mosquito number stopping falling, 8 repetitions are established in test.Test is temperature 26 DEG C ± 2 DEG C, and relative humidity is carry out under the condition of 70 ﹪ ± 10 ﹪.Calculate the scattering ratio of mosquito as evaluating mosquito-proof effect with publicity once.
Scattering ratio=(contrast stop falling mosquito number-sample stop the mosquito number that falls)/contrast stops mosquito number × 100% that falls
2, the test of warp direction stretching performance
The anti-mosquito PVC coated film material that Example 1-12 is obtained, then conventional in the industry method of testing carries out warp direction stretching Road test, and the sample that comparative examples adopts is common PVC film material, and test result is in table 5.
Table 5 embodiment 1-12 properties of product test result:
| Scattering ratio (%) | Warp direction stretching load (N/5cm) | |
| Comparative examples | 0 | 2900 |
| Embodiment 1 | 38.2 | 3800 |
| Embodiment 2 | 57.55 | 3500 |
| Embodiment 3 | 35.14 | 2500 |
| Embodiment 4 | 39.32 | 2750 |
| Embodiment 5 | 48.80 | 3500 |
| Embodiment 6 | 75.94 | 5000 |
| Embodiment 7 | 40.61 | 3300 |
| Embodiment 8 | 35.63 | 3250 |
| Embodiment 9 | 42.15 | 2800 |
| Embodiment 10 | 36.58 | 3520 |
Through inspection, the mosquito repellent rate of the anti-mosquito PVC coated film material of this embodiment 1-10 can reach 30-80%, and warp direction stretching load can reach 2800-5000N/5cm; As can be seen from data in upper table, the product of embodiments of the invention 6 is to mosquito repellent rate and warp direction stretching load performance excellence, although the product of all the other embodiments also has reasonable mosquito repellent rate and warp direction stretching load performance, mosquito repellent rate and warp direction stretching load performance are not so good as the product of embodiment 6.
In addition, the present invention first in base cloth the effect of blade coating common PVC be mainly to improve peel strength between PVC coating and embryo cloth as priming coat; The effect of blade coating anti-mosquito PVC paste resin slurry is all be that the finished product ensureing to obtain has anti-mosquito effect.Of the present invention simple with the raw material of anti-mosquito PVC coated film material composition, its preparation methods steps is simple, the mosquito repellent rate of the anti-mosquito PVC coated film material prepared and warp direction stretching load performance excellence.Meanwhile, the inventive method production equipment used is simple, and the construction cost of production line is low, to human-body safety, little to the pollution of environment, and easy to operate, product favorable reproducibility.
To one skilled in the art, according to technical scheme described above and design, other various corresponding change and deformation can be made, and all these change and deformation all should belong within the protection domain of the claims in the present invention.
Claims (10)
1. an anti-mosquito PVC coated film material, it is characterized in that, comprise base cloth layer, the first priming coat is coated with in base cloth layer front, the second priming coat is had at base cloth layer backsize, be coated with the first anti-mosquito coating on the surface of the first priming coat, be coated with the second anti-mosquito coating on the surface of the second priming coat; Described base cloth layer is made up of base cloth.
2. anti-mosquito PVC coated film material according to claim 1, it is characterized in that, described first priming coat and the second priming coat are PVC paste resin layer, described PVC paste resin layer is formed by the PVC paste resin blade coating doped with adhesive, PVC paste resin select K value be 60 ~ 80 PVC paste resin, the isocyanates that adhesive is is medium with dibutyl phthalate or diisononyl phthalate; Described adhesive is (2-6) with the ratio of the consumption of PVC paste resin: 100; The coating weight of described first priming coat and the second priming coat is 50-100g/m
2.
3. anti-mosquito PVC coated film material according to claim 1, is characterized in that, described first anti-mosquito coating and the second anti-mosquito coating are anti-mosquito PVC paste resin bed, and described anti-mosquito PVC paste resin bed is formed by anti-mosquito PVC paste resin slurry blade coating; The coating weight of described first anti-mosquito coating is 200-300g/m
2, the coating weight of the second anti-mosquito coating is 150-250g/m
2.
4. anti-mosquito PVC coated film material according to claim 3, is characterized in that, described anti-mosquito PVC paste resin slurry is by the component of following parts by weight:
5. anti-mosquito PVC coated film material according to claim 3, is characterized in that, described anti-mosquito PVC paste resin slurry is by the component of following parts by weight:
6. the anti-mosquito PVC coated film material according to claim 4 or 5, is characterized in that, described first anti-mosquito auxiliary agent be selected from pyrethrins, carbamate insecticides and third generation organophosphorus insecticide one or more.
7. anti-mosquito PVC coated film material according to claim 6, it is characterized in that, described carbamate insecticides is the one in dimethylcarbamate, methyl carbamic acid aromatic ester, methyl carbamic acid oxime ester, acyl N-methyl carbamate, hydroxyl sulfenyl N-methyl carbamate; Described third generation organophosphorus insecticide is the one in metrifonate, DDVP, DDVP calcium, 2-dichloroethylk dimethyl phosphate, malathion, Entex.
8. the anti-mosquito PVC coated film material according to claim 4 or 5, is characterized in that, described PVC paste resin is selected K value to be the PVC paste resin of 60 ~ 80 or is the PVC paste resin of 60 ~ 80 doped with the K value of blending resin; Phthalic ester plasticizer selected by described plasticizer; Described stabilizing agent selects powdery or liquid composite stabilizing agent; Inorganic filler selected by described filler; Described pigment is inorganic or organic pigment.
9. prepare a cutter scraping coating technique for anti-mosquito PVC coated film material as claimed in claim 1, it is characterized in that, comprise the steps:
(1) base cloth is prepared: the tiling of base cloth is formed base cloth layer;
(2) painting bottom coating: the front coating PVC paste resin of the base cloth layer in step (1), obtain the first priming coat, at the backsize PVC paste resin of base cloth layer, obtain the second priming coat, then deliver to heating in the first baking oven;
(3) blade coating anti-mosquito coating: adopt cutter to scrape and anti-mosquito PVC paste resin slurry is coated with the surface of scraping the first priming coat obtained in step (2), obtain the first anti-mosquito coating, deliver to subsequently in the second baking oven and heat, make the gelation of anti-mosquito PVC paste resin slurry; Then adopt cutter to scrape anti-mosquito PVC paste resin slurry painting is scraped on the surface of the second priming coat, obtain the second anti-mosquito coating, deliver to subsequently in the 3rd baking oven and heat, make the gelation of anti-mosquito PVC paste resin slurry; Last press polish, trimming, receive and roll up greatly; Obtain anti-mosquito PVC coated film material.
10. a cutter scraping coating technique for anti-mosquito PVC coated film material as claimed in claim 9, it is characterized in that, in step (2), the coating weight of the first priming coat and the second priming coat is 50-100g/m
2, the temperature of described first baking oven is 120-180 DEG C; Described in step (3), the temperature of the second baking oven is 150-180 DEG C, and the temperature of the 3rd baking oven is 160-200 DEG C; The coating weight of described first anti-mosquito coating is 200-300g/m
2, the coating weight of the second anti-mosquito coating is 150-250g/m
2.