CN105350384A - 一种含有聚乳酸纤维的变压器用绝缘纸 - Google Patents
一种含有聚乳酸纤维的变压器用绝缘纸 Download PDFInfo
- Publication number
- CN105350384A CN105350384A CN201510739534.0A CN201510739534A CN105350384A CN 105350384 A CN105350384 A CN 105350384A CN 201510739534 A CN201510739534 A CN 201510739534A CN 105350384 A CN105350384 A CN 105350384A
- Authority
- CN
- China
- Prior art keywords
- acid fiber
- insulating paper
- polylactic
- deionized water
- polylactic acid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种含有聚乳酸纤维的变压器用绝缘纸,由以下重量份的原料制备制成:纳米二氧化钛10-12、酚醛树脂2-3、浆板500-550、羧甲基纤维素钠1-1.3、聚乳酸纤维3.8-4.4、苯并三氮唑0.6-0.8、硫脲0.2-0.4、镁橄榄石粉2-3、硼酸铝2.2-2.5、氯化石蜡0.3-0.6、去离子水适量;本发明的制备方法简单,性能优异,成本低,作为变压器的绝缘材料具有使用寿命长,绝缘效果好,应用前景广泛。
Description
技术领域
本发明涉及变压器技术领域,尤其涉及一种含有聚乳酸纤维的变压器用绝缘纸。
背景技术
绝缘纸广泛用作电机、电缆、电容器和变压器等设备的绝缘材料,也是层压制品、复合材料和预浸材料等绝缘材料的主要组成材料。由于绝缘纸的特殊用途,要求其必须具备一些不同于其它纸种的特性,主要包括机械性能、电气性能和热稳定性。而且由于各类电气设备使用环境的不同,如湿热条件下运行的电机、化工厂经常接触高浓度的腐蚀性化学介质的电机、在有放射性辐射下运行的电机等,要求绝缘纸还要有较好的物理化学性能和环境适应性。采用天然纤维素制备的绝缘纸从19世纪90年代开始就被广泛应用于各种油浸式的电力设备中作为绝缘材料,虽然现在的绝缘材料有了较大的变化和进步,但纤维素绝缘纸具有价格低、机械强度大、尺寸容易控制、浸油后电气性能优良、环境友好等诸多优点,仍然是油浸变压器的首选绝缘材料,在传统的造纸行业当中为了提高纸张的各种性能,利用多种物理化学方法对纸进行改性。利用无机填料来改性绝缘纸可以得到性能更加优异的绝缘纸,但是目前国内外对于这方面的研究很少。
纳米二氧化钛具有很大的比表面积,因此在其表面产生的羟基数量就多而纤维素表面也带有大量的羟基,就为纳米二氧化钛粒子与纤维素之间的紧密结合提供了条件,保证纳米二氧化钛在纤维素上的附着率,并且纳米二氧化钛还能对绝缘油的绝缘性能起到较好的作用。所以本发明选择纳米二氧化钛对绝缘纸进行改性。
发明内容
本发明目的就是为了弥补已有技术的缺陷,提供一种含有聚乳酸纤维的变压器用绝缘纸。
本发明是通过以下技术方案实现的:
一种含有聚乳酸纤维的变压器用绝缘纸,由以下重量份的原料制备制成:纳米二氧化钛10-12、酚醛树脂2-3、浆板500-550、羧甲基纤维素钠1-1.3、聚乳酸纤维3.8-4.4、苯并三氮唑0.6-0.8、硫脲0.2-0.4、镁橄榄石粉2-3、硼酸铝2.2-2.5、氯化石蜡0.3-0.6、去离子水适量。
所述一种含有聚乳酸纤维的变压器用绝缘纸,由以下具体步骤制备制成:
(1)将纳米二氧化钛在烘箱中于100°C下干燥30min,冷却后加到0.5Wt%硅烷偶联剂kh550无水乙醇溶液中,再加入镁橄榄石粉进行回流冷凝处理,取出后烘干碾磨待用;
(2)将固含量为15-20%的酚醛树脂和步骤(1)制备的产物混合均匀,再加热至80°C时搅拌反应0.5-1h,恒温保持再加入聚乳酸纤维浸泡4-5h,捞出后用蒸馏水清洗纤维条数遍后烘干备用;
(3)将浆板在去离子水中浸泡12h,浸泡充分后疏解6-8min后利用打浆机进行打浆,待浆料的打浆度到40-45°SR时停止打浆,将制备的浆料放入纤维解离器中,加入去离子水使浆料的浓度在2-2.5%内进行机械处理,得到纸浆悬浊液备用;
(4)将硼酸铝、苯并三氮唑、羧甲基纤维素钠、硫脲和氯化石蜡混合加入总倍量6-8倍量的去离子水混合搅拌均匀,将步骤(2)制备的产物加到步骤(3)制备的纸浆悬浊液中,再加入上述混合溶液以300转/分下进行搅拌,最后将纸浆悬浮液加到纸业成型设备中进行脱水成型,即可得到。
本发明的优点是:本发明采用将二氧化钛表面改性,不易聚集,使其在纸浆中分布均匀,且能大幅度提高绝缘纸的绝缘性能,并且还将纤维浸渍到绝缘树脂中,固化梳理然后利用粘胶溶液和纤维素纤维混合纺织,制备的复合纸大大提高了其机械性能、绝缘性、耐热老化性和强度等方面的作用,添加的聚乳酸纤维提高了绝缘纸的生物降解性,耐热性,不会对环境造成污染,添加的硼酸铝、苯并三氮唑和硫脲等相互作用效果好,明显增强了绝缘纸的抗紫外、阻燃、杀菌等方面的作用,本发明的制备方法简单,性能优异,成本低,作为变压器的绝缘材料具有使用寿命长,绝缘效果好,应用前景广泛。
具体实施方式
一种含有聚乳酸纤维的变压器用绝缘纸,由以下重量份(公斤)的原料制备制成:纳米二氧化钛10、酚醛树脂2、浆板500、羧甲基纤维素钠1、聚乳酸纤维3.8、苯并三氮唑0.6、硫脲0.2、镁橄榄石粉2、硼酸铝2.2、氯化石蜡0.3、去离子水适量。
所述一种含有聚乳酸纤维的变压器用绝缘纸,由以下具体步骤制备制成:
(1)将纳米二氧化钛在烘箱中于100°C下干燥30min,冷却后加到0.5Wt%硅烷偶联剂kh550无水乙醇溶液中,再加入镁橄榄石粉进行回流冷凝处理,取出后烘干碾磨待用;
(2)将固含量为15%的酚醛树脂和步骤(1)制备的产物混合均匀,再加热至80°C时搅拌反应0.5h,恒温保持再加入聚乳酸纤维浸泡4h,捞出后用蒸馏水清洗纤维条数遍后烘干备用;
(3)将浆板在去离子水中浸泡12h,浸泡充分后疏解6min后利用打浆机进行打浆,待浆料的打浆度到40°SR时停止打浆,将制备的浆料放入纤维解离器中,加入去离子水使浆料的浓度在2%内进行机械处理,得到纸浆悬浊液备用;
(4)将硼酸铝、苯并三氮唑、羧甲基纤维素钠、硫脲和氯化石蜡混合加入总倍量6倍量的去离子水混合搅拌均匀,将步骤(2)制备的产物加到步骤(3)制备的纸浆悬浊液中,再加入上述混合溶液以300转/分下进行搅拌,最后将纸浆悬浮液加到纸业成型设备中进行脱水成型,即可得到。
按照本实施例制备的绝缘纸其性能测试如下:击穿电压为3.9KV、介电强度为38KV/mm,绝缘纸的阻燃级别为V0级,纸白度≥80%,干抗拉强度为3.9KN/m,湿抗张强度为0.43KN/m,吸水高度55mm,透气度为20±4s,体积电阻率为0.9×106,表面电阻为4.3×104,介电常数为5.4,介电损耗因数为0.045。
Claims (2)
1.一种含有聚乳酸纤维的变压器用绝缘纸,其特征在于,由以下重量份的原料制备制成:纳米二氧化钛10-12、酚醛树脂2-3、浆板500-550、羧甲基纤维素钠1-1.3、聚乳酸纤维3.8-4.4、苯并三氮唑0.6-0.8、硫脲0.2-0.4、镁橄榄石粉2-3、硼酸铝2.2-2.5、氯化石蜡0.3-0.6、去离子水适量。
2.根据权利要求1所述一种含有聚乳酸纤维的变压器用绝缘纸,其特征在于,由以下具体步骤制备制成:
(1)将纳米二氧化钛在烘箱中于100°C下干燥30min,冷却后加到0.5Wt%硅烷偶联剂kh550无水乙醇溶液中,再加入镁橄榄石粉进行回流冷凝处理,取出后烘干碾磨待用;
(2)将固含量为15-20%的酚醛树脂和步骤(1)制备的产物混合均匀,再加热至80°C时搅拌反应0.5-1h,恒温保持再加入聚乳酸纤维浸泡4-5h,捞出后用蒸馏水清洗纤维条数遍后烘干备用;
(3)将浆板在去离子水中浸泡12h,浸泡充分后疏解6-8min后利用打浆机进行打浆,待浆料的打浆度到40-45°SR时停止打浆,将制备的浆料放入纤维解离器中,加入去离子水使浆料的浓度在2-2.5%内进行机械处理,得到纸浆悬浊液备用;
(4)将硼酸铝、苯并三氮唑、羧甲基纤维素钠、硫脲和氯化石蜡混合加入总倍量6-8倍量的去离子水混合搅拌均匀,将步骤(2)制备的产物加到步骤(3)制备的纸浆悬浊液中,再加入上述混合溶液以300转/分下进行搅拌,最后将纸浆悬浮液加到纸业成型设备中进行脱水成型,即可得到。