CN105330224A - 沥青混凝土 - Google Patents
沥青混凝土 Download PDFInfo
- Publication number
- CN105330224A CN105330224A CN201510928468.1A CN201510928468A CN105330224A CN 105330224 A CN105330224 A CN 105330224A CN 201510928468 A CN201510928468 A CN 201510928468A CN 105330224 A CN105330224 A CN 105330224A
- Authority
- CN
- China
- Prior art keywords
- parts
- epoxy resin
- coupling agent
- bituminous concrete
- mineral aggregate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种沥青混凝土,是由下述质量份数的成分制备而成的:废旧沥青料10~15份、矿料100~120份、环氧树脂0.5~3.0份、水泥10~30份、硫化钠0.5~2份、<b>活性炭</b>0.5~10份、磁铁矿0.5~5份和偶联剂0.02~0.1份。本发明具有路用性能优良、制备工艺简单、环保性能优越、原料无毒无害的特点。
Description
技术领域
本发明涉及道路工程材料领域,特别是涉及一种沥青混凝土。
背景技术
沥青路面具有良好的力学强度、耐磨耗、行车舒适、振动小、噪音低、施工简便等优点。随着公路工程建设的大规模铺开,沥青路面在高等级道路中所占比例越来越大,传统的沥青混凝土路面经常会出现裂缝现象,同时汽车数量的不断攀升,汽车尾气对环境造成的污染成为重要的社会问题,需大力治理。
发明内容
本发明主要解决的技术问题是提供一种沥青混凝土,具有路用性能优良、制备工艺简单、环保性能优越、原料无毒无害的特点。
为解决上述技术问题,本发明采用的一个技术方案是:
提供一种沥青混凝土,是由下述质量份数的成分制备而成的:废旧沥青料10~15份、矿料100~120份、环氧树脂0.5~3.0份、水泥10~30份、硫化钠0.5~2份、活性炭0.5~10份、磁铁矿0.5~5份和偶联剂0.02~0.1份。
在本发明一个较佳实施例中,所述环氧树脂为二酚基丙烷型环氧树脂。
在本发明一个较佳实施例中,所述矿料的粒径为15mm~30mm。
在本发明一个较佳实施例中,所述偶联剂为多元醇酯偶联剂。
在本发明一个较佳实施例中,是由下述质量份数的成分制备而成的:废旧沥青料10份、矿料120份、环氧树脂2.0份、水泥15份、硫化钠1.5份、活性炭3.5份、磁铁矿2.5份和偶联剂0.05份。
在本发明一个较佳实施例中,是由下述质量份数的成分制备而成的:废旧沥青料15份、矿料110份、环氧树脂1.5份、水泥25份、硫化钠1.0份、活性炭4.5份、磁铁矿1.5份和偶联剂0.08份。
本发明的有益效果是:本发明一种沥青混凝土,该配方制得的混凝土具有优良的环保性能,路用性能优良、制备工艺简单、原料无毒无害。
具体实施方式
下面对本发明的较佳实施例进行详细阐述,以使本发明的优点和特征能更易于被本领域技术人员理解,从而对本发明的保护范围做出更为清楚明确的界定。
实施例1:一种沥青混凝土,是由下述质量份数的成分制备而成的:废旧沥青料10份、矿料120份、环氧树脂2.0份、水泥15份、硫化钠1.5份、活性炭3.5份、磁铁矿2.5份和偶联剂0.05份。
所述环氧树脂为二酚基丙烷型环氧树脂,所述矿料的粒径为15mm~30mm,所述偶联剂为多元醇酯偶联剂。
实施例2:一种沥青混凝土,是由下述质量份数的成分制备而成的:废旧沥青料15份、矿料110份、环氧树脂1.5份、水泥25份、硫化钠1.0份、活性炭4.5份、磁铁矿1.5份和偶联剂0.08份。
其余成分同实施例1。
实施例3:一种沥青混凝土,是由下述质量份数的成分制备而成的:废旧沥青料12份、矿料100份、环氧树脂1.5份、水泥20份、硫化钠1.5份、活性炭3.8份、磁铁矿4.5份和偶联剂0.08份。
其余成分同实施例1。
上述实施例1~3中的沥青混凝土,按照各配比将成分混合后进入球磨机中研磨至产品要求的细度即可。
以上所述仅为本发明的实施例,并非因此限制本发明的专利范围,凡是利用本发明说明书内容所作的等效结构或等效流程变换,或直接或间接运用在其他相关的技术领域,均同理包括在本发明的专利保护范围内。
Claims (6)
1.一种沥青混凝土,其特征在于,是由下述质量份数的成分制备而成的:废旧沥青料10~15份、矿料100~120份、环氧树脂0.5~3.0份、水泥10~30份、硫化钠0.5~2份、活性炭0.5~10份、磁铁矿0.5~5份和偶联剂0.02~0.1份。
2.根据权利要求1所述的沥青混凝土,其特征在于,所述环氧树脂为二酚基丙烷型环氧树脂。
3.根据权利要求1所述的沥青混凝土,其特征在于,所述矿料的粒径为15mm~30mm。
4.根据权利要求1所述的沥青混凝土,其特征在于,所述偶联剂为多元醇酯偶联剂。
5.根据权利要求1所述的沥青混凝土,其特征在于,是由下述质量份数的成分制备而成的:废旧沥青料10份、矿料120份、环氧树脂2.0份、水泥15份、硫化钠1.5份、活性炭3.5份、磁铁矿2.5份和偶联剂0.05份。
6.根据权利要求1所述的沥青混凝土,其特征在于,是由下述质量份数的成分制备而成的:废旧沥青料15份、矿料110份、环氧树脂1.5份、水泥25份、硫化钠1.0份、活性炭4.5份、磁铁矿1.5份和偶联剂0.08份。