CN105296045A - 一种高粘度型煤防水复合粘结剂 - Google Patents
一种高粘度型煤防水复合粘结剂 Download PDFInfo
- Publication number
- CN105296045A CN105296045A CN201510814096.XA CN201510814096A CN105296045A CN 105296045 A CN105296045 A CN 105296045A CN 201510814096 A CN201510814096 A CN 201510814096A CN 105296045 A CN105296045 A CN 105296045A
- Authority
- CN
- China
- Prior art keywords
- parts
- binding agent
- moulded coal
- high viscosity
- compound binding
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种高粘度型煤防水复合粘结剂,包括以下重量份的原料:预糊化淀粉350~?400份、氧化镁400~450份、粉煤灰100~150份、赤泥50~100份、纯碱6~8份和聚丙烯酰胺4~6份。本发明粘结剂的粘度≥20000Mpa.s、粒度200目达85%、水分≤10%和pH值为8.5~9.0。使用本发明粘结剂生产的型煤不仅具有很强的防水性能,还具有易燃、热稳定性好、冷热强度高、反应活性高、热效率高、环保优点,同时还具有原料来源广泛、成本低、制备工艺简单等优点,具有很好的社会、生态和经济效益,容易实现大规模化生产。
Description
技术领域
本发明涉及粘结剂技术领域,尤其是一种高粘度型煤防水复合粘结剂。
背景
型煤是以粉煤为主要原料,按具体用途所要求的配比,机械强度,和形状大小经机械加工压制成型的,具有一定强度和尺寸及形状各异的煤成品。型煤冷压成型工艺中,粘结剂的研制是关键技术之一,它直接决定型煤的冷、热态强度、防水性、热稳定性和燃烧性等指标。当前开发的型煤粘结剂主要分为有机、无机和复合粘结剂三大类。有机粘结剂的粘结性能好,型煤干燥固化以后具有较高的机械强度;但是,由于有机粘结剂中的有机物在高温下易分解和燃烧,会丧失粘结力,因此,型煤的热态强度一般较差。另外,有些有机粘结剂具有一定的吸水性,因而型煤易潮解。无机粘结剂制得的型煤具有较高的机械强度,而且热态强度也较高。其缺点是增加了型煤中的非可燃无机成分,从而降低了型煤的发热量。复合粘结剂是同时使用两种不同类型的粘结剂,可相互弥补单一粘结剂存在的不足,使型煤达到最佳效果。复合型粘结剂是近年来型煤粘结剂发展的研究方向。
中国专利CN103571561A公开了一种可再生型煤液体粘结剂,其配方包括如下成分:预糊化淀粉11.0%、变性生物秸杆4.0%、木质素0.7%、氯化钠0.5%、草木灰0.2%、纯碱1.0%和水82.6%。该发明具有原料来源广泛、成本低、可再生等优点。但是,粘结剂存在粘度低,生产型煤困难,成型率低,容易吸水,使得大多数型煤易潮解等不足。
中国专利CN102796585B公开了一种新型防水复合型煤粘结剂,按照重量份数比,包括以下组分:膨润土400-600份、增粘剂5-10份、烟囱灰300-400份和碱木素100-150份;所述增粘剂由海藻酸钠1-5份、羟甲基纤维素1-5份、薯渣类细粉2-5份、交联剂0.1-1份、氢氧化钙0.1-1份和丙烯酸甲酯0.05-0.5份混合制成。该发明的粘结剂不仅具备400倍以上的强吸水率,而且原料来源广泛,成本低,加入该粘结剂的型煤机械强度高,热稳定性和反应活性好。但也存在产品粘度不高、生产型煤成型率较低、使型煤的灰分增加、发热量降低等不足。
中国专利CN103710065B公开了一种新型防水复合型煤粘结剂,各原料组分重量比例为:膨润土40-45%、淀粉3-4%、特种树脂1-3%、有机高分子材料6-9%、水泥40-50%。其中,所述的特种树脂为热塑性酚醛树脂;所述的有机高分子材料为聚乙烯醇、羧甲基纤维素钠或者聚丙烯酰胺。该发明粘结剂的添加量低、制备工艺简单、无任何二次污染优点,但也存在原料成本高、热稳定性能差等不足。
目前市场上使用各种各样的粘结剂,粘结剂的发展有了一定的技术基础,但是从型煤冷强度、热强度、耐水性、固定碳、经济性的指标要求,还没有一种理想的粘结剂。因此,研究型煤粘结剂显得尤为重要。
发明内容
本发明的目的在于针对现有型煤粘结剂存在粘度低、成本高、热稳定性能差、防水性能差等不足,提供一种高粘度型煤防水复合粘结剂。
为了实现以上目的,本发明是通过以下技术方案实现:
一种高粘度型煤防水复合粘结剂,包括以下重量份的原料:
预糊化淀粉350~400份、氧化镁400~450份、粉煤灰100~150份、赤泥50~100份、纯碱6~8份和聚丙烯酰胺4~6份。
作为本发明优选的方案:以上所述的高粘度型煤防水复合粘结剂,包括以下重量份的原料:
预糊化淀粉400份、氧化镁450份、粉煤灰120份、赤泥100份、纯碱8份和聚丙烯酰胺6份。
以上所述高粘度型煤防水复合粘结剂的制备方法,包括以下步骤:
按重量份数计,称取预糊化淀粉350~400份、氧化镁400~450份、粉煤灰100~150份、赤泥50~100份、纯碱6~8份和聚丙烯酰胺4~6份,将各组分加入粉碎机分别粉碎至150~250目,再将各组分加入搅拌机,在转速为80~120r/min下搅拌10~20min,即可得到高粘度型煤防水复合粘结剂。
以上所述粘结剂的粘度≥20000Mpa.s、粒度200目达85%、水分≤10%和pH值为8.5~9.0。
以上所述高粘度型煤防水复合粘结剂的应用中,粘结剂的加入量为煤粉重量的3~5%。
与现有技术相比,本发明取得的有益效果为:
1、本发明的配方以预糊化淀粉、氧化镁、粉煤灰、赤泥为主要原料,再加入聚丙烯酰胺配成复合粘结剂,本粘结剂的粘度大于20000Mpa.s、粒度200目达85%水分≤10%和pH值为8.5~9.0,其应用在型煤生产过程中,可增加煤粒间的内聚力,从而提高型煤的成型率,型煤成型率可达到95%。
2、本发明的粘结剂,具备600倍以上的强吸水率作用,保证雨雪和南方回潮湿天气都能制备型煤,满足了企业全年都能生产。该粘结剂生产的型煤,不怕风吹雨打,可露天堆放,制成的煤球在水中浸泡一个月不溃散,且具有很好的稳定性能,浸泡后的煤球干燥后仍能恢复较高的抗压能力,解决了南方潮湿对型煤的影响。
3、本发明以氧化镁为主要原料,在型煤燃烧过程中能起到助燃作用,使型煤的反应活性得到提高,型煤球达到充分完全燃烧的效果;氧化镁在反应过程中起到固硫的作用,使型煤的二氧化硫反应生成硫酸镁,从而减少二氧化硫废气的排放;同时还具有粘结、防水及增强的效果。
4、本发明的粘结剂在型煤生产过程中,粘结剂的加入量仅为煤粉重量的3~5%,降低了型煤的生产成本。
5、使用本发明粘结剂生产的型煤不仅具有很强的防水性能,还具有易燃、热稳定性好、冷热强度高、反应活性高、热效率高、环保等优点;使用时不需加碱,不需蒸煮和沤制,工人劳动强度减少、降低成本。其中使用本粘结剂生产的型煤的发热量为26.46MJ/kg、冷抗压强度达到85kg/个以上、热抗压强度达30kg/个以上、浸水强度达15kg/个以上、浸水一个月后复干强度60kg/个以上和灰分(以干基计)小于20%。
6、本发明的复合粘结剂还具有原料来源广泛、成本低、制备工艺简单等优点,具有很好的社会、生态和经济效益,容易实现大规模化生产。
具体实施方式
下面将结合具体实施例对本发明进一步说明,但不限于本发明的保护范围。
实施例1
一种高粘度型煤防水复合粘结剂,包括以下重量份的原料:预糊化淀粉350份、氧化镁400份、粉煤灰120份、赤泥60份、纯碱6份和聚丙烯酰胺4份。
其制备方法,包括以下步骤:
按重量份数计,称取预糊化淀粉350份、氧化镁400份、粉煤灰120份、赤泥60份、纯碱6份和聚丙烯酰胺4份,将各组分加入粉碎机分别粉碎至150目,再将各组分加入搅拌机,在转速为80r/min下搅拌20min,即可得到高粘度型煤防水复合粘结剂。
实施例2
一种高粘度型煤防水复合粘结剂,包括以下重量份的原料:预糊化淀粉350份、氧化镁420份、粉煤灰100份、赤泥80份、纯碱6份和聚丙烯酰胺5份。
制备方法,包括以下步骤:
按重量份数计,称取氧化镁420份、预糊化淀粉350份、粉煤灰100份、赤泥80份、纯碱6份和聚丙烯酰胺5份,将各组分加入粉碎机分别粉碎至200目,再将各组分加入搅拌机,在转速为100r/min下搅拌15min,即可得到高粘度型煤防水复合粘结剂。
实施例3
一种高粘度型煤防水复合粘结剂,包括以下重量份的原料:预糊化淀粉380份、氧化镁420份、粉煤灰150份、赤泥50份、纯碱7份和聚丙烯酰胺5份。
制备方法,包括以下步骤:
按重量份数计,称取预糊化淀粉380份、氧化镁420份、粉煤灰150份、赤泥50份、纯碱7份和聚丙烯酰胺5份,将各组分加入粉碎机分别粉碎至250目,再将各组分加入搅拌机,在转速为120r/min下搅拌10min,即可得到高粘度型煤防水复合粘结剂。
实施例4
一种高粘度型煤防水复合粘结剂,包括以下重量份的原料:预糊化淀粉400份、氧化镁450份、粉煤灰120份、赤泥100份、纯碱8份和聚丙烯酰胺6份。
制备方法,包括以下步骤:
按重量份数计,称取预糊化淀粉400份、氧化镁450份、粉煤灰120份、赤泥100份、纯碱8份和聚丙烯酰胺6份,将各组分加入粉碎机分别粉碎至200目,再将各组分加入搅拌机,在转速为100r/min下搅拌15min,即可得到高粘度型煤防水复合粘结剂。
经过检测,本发明实施例1~4复合粘结剂的产品质量指标如表1所示。
表1:.复合粘结剂的产品质量指标
粘度(Mpa.s) | 粒度200目 | 水分(%) | pH值 | 外观 | |
实施例1 | 20000 | 87 | 10 | 8.5 | 灰白色 |
实施例2 | 20000 | 85 | 8.5 | 8.9 | 灰白色 |
实施例3 | 21000 | 89 | 9 | 8.8 | 灰白色 |
实施例4 | 23000 | 86 | 8 | 9.0 | 灰白色 |
国家对型煤粘结剂的标准为:粘度≥3500Mpa.s、粒度60目≥80、pH值8~9和水分≤12%。从上表可知,本发明复合粘结剂的均优于我国Q/LH001-2010《DF-1煤复合粘结剂》标准。
应用实施例
实施例1
将实施例1的复合粘结剂应用在型煤的生产中,具体的生产步骤如下:在煤粉中分别加入3%的粘结剂,搅拌混合均匀,在压力为6MPa、温度为30℃下进行冷压成型,成型后在90℃下烘干,即可得到型煤。
实施例2
将实施例2的复合粘结剂应用在型煤的生产中,具体的生产步骤如下:在煤粉中分别加入5%的粘结剂,搅拌混合均匀,在压力为6MPa、温度为30℃下进行冷压成型,成型后在90℃下烘干,即可得到型煤。
实施例3
将实施例3的复合粘结剂应用在型煤的生产中,具体的生产步骤如下:在煤粉中分别加入4%的粘结剂,搅拌混合均匀,在压力为6MPa、温度为30℃下进行冷压成型,成型后在90℃下烘干,即可得到型煤。
实施例4
将实施例4的复合粘结剂应用在型煤的生产中,具体的生产步骤如下:在煤粉中分别加入5%的粘结剂,搅拌混合均匀,在压力为6MPa、温度为30℃下进行冷压成型,成型后在90℃下烘干,即可得到型煤。
将上述实施例制备的型煤经检测,其结果如表2和表3所示。
表2:型煤的产品质量检测结果
表3:型煤的燃烧试验结果
Claims (5)
1.一种高粘度型煤防水复合粘结剂,其特征在于:包括以下重量份的原料:预糊化淀粉350~400份、氧化镁400~450份、粉煤灰100~150份、赤泥50~100份、纯碱6~8份和聚丙烯酰胺4~6份。
2.根据权利要求1所述的一种高粘度型煤防水复合粘结剂,其特征在于:包括以下重量份的原料:预糊化淀粉400份、氧化镁450份、粉煤灰120份、赤泥100份、纯碱8份和聚丙烯酰胺6份。
3.根据权利要求1或2所述的一种高粘度型煤防水复合粘结剂的制备方法,其特征在于:包括以下步骤:按重量份数计,称取预糊化淀粉350~400份、氧化镁400~450份、粉煤灰100~150份、赤泥50~100份、纯碱6~8份和聚丙烯酰胺4~6份,将各组分加入粉碎机分别粉碎至150~250目,再将各组分加入搅拌机,在转速为80~120r/min下搅拌10~20min,即可得到高粘度型煤防水复合粘结剂。
4.根据权利要求1~3任何一项所述的一种高粘度型煤防水复合粘结剂,其特征在于:所述粘结剂的粘度≥20000Mpa.s、粒度200目达85%、水分≤10%和pH值为8.5~9.0。
5.根据权利要求1所述一种高粘度型煤防水复合粘结剂的应用,其特征在于:所述的粘结剂的加入量是煤粉重量的3~5%。