CN105295573A - Waterproof base layer coating, waterproof base layer and coating method of waterproof base layer - Google Patents
Waterproof base layer coating, waterproof base layer and coating method of waterproof base layer Download PDFInfo
- Publication number
- CN105295573A CN105295573A CN201510633422.7A CN201510633422A CN105295573A CN 105295573 A CN105295573 A CN 105295573A CN 201510633422 A CN201510633422 A CN 201510633422A CN 105295573 A CN105295573 A CN 105295573A
- Authority
- CN
- China
- Prior art keywords
- waterproof
- coating
- seam
- matrix
- mylar
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a waterproof base layer coating which is prepared from the following components in parts by weight: 100 to 120 parts of elastic emulsion, 80 to 90 parts of heavy calcium, 20 to 30 parts of silica fume, 0.4 to 0.5 part of defoaming agent, 0.5 to 0.6 part of dispersing agent, 0.4 to 0.5 part of fungicide and 15 parts of water. The components contained in the waterproof base layer coating are better in extension, good in elasticity and higher in adhesive force; the waterproof base layer coating can form a dense waterproof layer in a to-be-treated area; in addition, the waterproof base layer coating is wider in application range, and can provide better waterproof effects for daylighting panels of a metal roof, deep roof pipelines, fan openings, metal plate lapped seams, reinforcing screws, roof gutters and other weak waterproof parts.
Description
Technical field
The present invention relates to building material field, specifically the coating process of a kind of waterproof matrix coating, the waterproof matrix formed by waterproof matrix coatings and coating waterproof matrix.
Background technology
Traditional water-proof material mainly contains the flexible waterproof materials such as waterproof roll, waterproof paint, sealing cement, and based on cement matrix, adds the rigidity water-proofing material of liquid medicine agent and other auxiliary agent.Conventional waterproof coating is used for roof waterproof, easily cause aging, dry and cracked, be out of shape, fracture, the phenomenon such as layering; For indoor waterproof, for complex-shaped place, constructional difficulties, and to Seepage, quality is more difficult to ensure, people will spend a large amount of funds and labor force to reprocess every several years, not only confuse the orthobiosis of people, work and the production order, and affect the work-ing life of whole building buildings.And traditional waterproof paint is directly be coated with at pending place in use, and there is region all unfairnesses of infiltration in major part, adopts to carry out coating in this way and can cause waterproof loosely, easily again occurs seepage; In addition the waterproof scope of application of this mode is narrower, to the waterproof effect of some flattened region still can, but be difficult to carry out effective waterproof to blower fan mouth, metal sheet seam lap etc.
Summary of the invention
The technical problem to be solved in the present invention is, a kind of waterproof matrix coating is provided, the component extensibility that it comprises is better, good springiness, sticking power are stronger, the waterproof layer of one deck densification can be formed on pending region, and its scope of application is comparatively wide, good waterproof can be provided for the plane skylight of metal Roof, depths roof pipeline, blower fan mouth, metal sheet seam lap, reinforcing screw, gutter and other waterproof weak parts.
A kind of waterproof matrix coating, the part by weight proportioning of the component comprised and each component is as follows: elastic emulsion 100-120 part, coarse whiting 80-90 part, wollastonite powder 20-30 part, defoamer 0.4-0.5 part, dispersion agent 0.5-0.6 part, sterilant 0.4-0.5 part, 15 parts, water.
Preferred as such scheme, also comprise dibutylester, its weight proportion is 1-2 part.
Preferred as such scheme, also comprise thickening material, its weight proportion is 0.6-1 part.
Preferred as such scheme, also comprises appropriate mill base.
Preferred as such scheme, described elastic emulsion is phenylpropyl alcohol elastic emulsion, and the granularity of described coarse whiting is 800 orders, and the granularity of described wollastonite powder is 1250 orders.
The present invention also provides a kind of waterproof matrix, and comprise waterproof layer one from inside to outside successively, seam knits mylar, waterproof layer two, described waterproof layer one, waterproof layer two form by the waterproof matrix coatings described in above-mentioned any one.This waterproof matrix comprises waterproof layer and seam knits mylar, seam knits mylar water-permeable and air permeable better performances, can ensure that waterproof matrix coating perviousness is wherein better, make that waterproof matrix globality is comparatively strong, tack is better, the ventilation property of knitting mylar due to seam is better, the water vapour formed due to temperature variation in waterproof matrix can be discharged in time, thus the cohesive force of waterproof matrix and metal Roof is not by the impact of steam, extends the work-ing life of waterproof matrix.
The present invention also provides a kind of coating process of waterproof matrix, and its concrete steps comprise: a, and the waterproof matrix coating as described in as arbitrary in claim 1 to 5 in the coating of pending region, forms waterproof layer one; B, knits mylar and is laid on described waterproof layer one by seam; C, described seam knit mylar is coated with as arbitrary in claim 1 to 5 as described in waterproof matrix coating formed waterproof layer two.The waterproof matrix be coated with by this step, its waterproof effect is better.
Preferred as such scheme, described step b is specially: knit mylar according to the size cutting seam in pending region, seam suitable for size is knitted mylar and be laid on described waterproof layer one.
Preferred as such scheme, described step c is specially: lay seam and knit mylar and be coated with waterproof layer two, make waterproof matrix coating soak full seam and knit mylar.
The present invention also provides a kind of waterproof layer, to comprising waterproof matrix, waterproof top layer successively outward in many, described waterproof top layer is coated with by waterproof watch coating and is formed, the part by weight proportioning of the component that described waterproof watch coating comprises and each component is as follows: elastic emulsion 300-350 part, coarse whiting 150-250 part, pure-acrylic emulsion 100-120 part, titanium dioxide 70-80 part, kaolin 50-70 part, softening agent 10-15 part, ethylene glycol 10-15 part, dispersion agent 7-10 part, defoamer 3-5 part, sterilant 2-4 part, neutralizing agent 1-3 part, 217 parts, water.
Preferred as such scheme, described waterproof watch coating also comprises wetting agent, and its weight proportion is 2-5 part.
Preferred as such scheme, described waterproof watch coating also comprises thickening material, and its weight proportion is 8-10 part.
The present invention reoffers a kind of coating process of waterproof layer, comprises the steps: a, forms waterproof matrix; B, after waterproof matrix drying, described waterproof matrix is coated with above-mentioned waterproof watch coating and forms waterproof top layer.The waterproof layer with waterproof top layer can be formed by this coating process.
Embodiment
Be described below in detail embodiments of the invention, wherein same or similar label represents same or similar element or has element that is identical or similar functions from start to finish.The following examples are exemplary, only for explaining the present invention, and can not be interpreted as limitation of the present invention.
In describing the invention, it will be appreciated that, the orientation of the instruction such as term " " center ", " on ", D score, "front", "rear", "left", "right", " vertically ", " level ", " top ", " end " " interior ", " outward " or position relationship; be only the present invention for convenience of description and simplified characterization; instead of the device of instruction or hint indication or element must have specific orientation, with specific azimuth configuration and operation, therefore can not be interpreted as limitation of the present invention.
In describing the invention, it should be noted that, unless otherwise clearly defined and limited, term " installation ", " being connected ", " setting " should be interpreted broadly, and such as, can be fixedly linked, arrange, also can be removably connect, arrange, or connect integratedly, arrange.For the ordinary skill in the art, particular case above-mentioned term concrete meaning in the present invention can be understood.
Embodiment one
A kind of waterproof matrix coating, the part by weight proportioning of the component comprised and each component is as follows: stupid acrylate elastic emulsion 100g, 800 order coarse whiting 80g, 1250 order wollastonite powder 20g, defoamer 0.4g, dispersion agent 0.5g, sterilant 0.4g, water 15g, dibutylester 1g, thickening material 0.6g.
A kind of waterproof matrix, comprise waterproof layer one from inside to outside successively, seam knits mylar, waterproof layer two, described waterproof layer one, waterproof layer two form by above-mentioned waterproof matrix coatings.
A coating process for waterproof matrix, comprises the steps:
A, is coated with above-mentioned waterproof matrix coating in pending region, forms waterproof layer one;
B, knits mylar and is laid on described waterproof layer one by seam;
C, knits on mylar at described seam and is coated with above-mentioned waterproof matrix coating formation waterproof layer two.
The present invention also provides a kind of waterproof layer, comprises waterproof matrix, waterproof top layer from inside to outside successively, and described waterproof top layer is coated with by waterproof watch coating and is formed, the part by weight proportioning of the component that described waterproof watch coating comprises and each component is as follows: phenylpropyl alcohol elastic emulsion 300g, 1250 order coarse whiting 200g, pure-acrylic emulsion 100g, titanium dioxide 75g, 1250 order kaolin 60g, softening agent 10g, ethylene glycol 15g, dispersion agent 7g, defoamer 3g, sterilant 2g, neutralizing agent 1g, 217 parts, water.
The present invention reoffers a kind of coating process of waterproof layer, comprises the steps: a, forms waterproof matrix; B, after waterproof matrix drying, described waterproof matrix is coated with above-mentioned waterproof watch coating and forms waterproof top layer.
Embodiment two
A kind of waterproof matrix coating, the part by weight proportioning of the component comprised and each component is as follows: phenylpropyl alcohol elastic emulsion 105g, 800 order coarse whiting 85g, 1250 order wollastonite powder 25g, defoamer 0.45g, dispersion agent 0.54g, sterilant 0.45g, water 15g, dibutylester 1.2g, thickening material 0.8g, mill base is appropriate.
A kind of waterproof matrix, comprise waterproof layer one from inside to outside successively, seam knits mylar, waterproof layer two, described waterproof layer one, waterproof layer two are formed by above-mentioned waterproof matrix coatings.
A coating process for waterproof matrix, comprises the steps:
A, is coated with waterproof matrix coating described above in pending region, forms waterproof layer one;
B, knits mylar according to the size cutting seam in pending region, seam suitable for size is knitted mylar and be laid on described waterproof layer one;
C, knits on mylar at described seam and is coated with above-mentioned waterproof matrix coating formation waterproof layer two.
The present invention also provides a kind of waterproof layer, comprises waterproof matrix, waterproof top layer from inside to outside successively, and described waterproof top layer is coated with by waterproof watch coating and is formed, the part by weight proportioning of the component that described waterproof watch coating comprises and each component is as follows: phenylpropyl alcohol elastic emulsion 310g, 1250 order coarse whiting 180g, pure-acrylic emulsion 100g, titanium dioxide 80g, 1250 order kaolin 60g, softening agent 10g, ethylene glycol 15g, dispersion agent 7g, defoamer 3g, sterilant 2g, neutralizing agent 1g, 217 parts, water, wetting agent 2g.
The present invention reoffers a kind of coating process of waterproof layer, comprises the steps: a, forms waterproof matrix; B, after waterproof matrix drying, described waterproof matrix is coated with above-mentioned waterproof watch coating and forms waterproof top layer, described waterproof top layer is multilayer, the waterproof watch coating that multilayer flashing top layer is coated with by different time is formed, the coating of adjacent waterproof top layer interval greater than 4 hours.
Embodiment three
A kind of waterproof matrix coating, the part by weight proportioning of the component comprised and each component is as follows: phenylpropyl alcohol elastic emulsion 108g, 800 order coarse whiting 88g, 1250 order wollastonite powder 28g, defoamer 0.48g, dispersion agent 0.56g, sterilant 0.48g, water 15g, dibutylester 1.5g, thickening material 0.9g.
A kind of waterproof matrix, comprise waterproof layer one from inside to outside successively, seam knits mylar, waterproof layer two, described waterproof layer one, waterproof layer two are formed by above-mentioned waterproof matrix coatings.
A coating process for waterproof matrix, comprises the steps:
A, is coated with waterproof matrix coating described above in pending region, forms waterproof layer one;
B, knits mylar according to the size cutting seam in pending region, seam suitable for size is knitted mylar and be laid on described waterproof layer one;
C, the strong mylar of described seam is coated with above-mentioned waterproof matrix coating and forms waterproof layer two, and limit is laid seam and knitted polyester selvedge coating waterproof layer two, makes waterproof matrix coating soak full seam and knits mylar.
The present invention also provides a kind of waterproof layer, comprise waterproof matrix, waterproof top layer from inside to outside successively, described waterproof top layer is coated with by waterproof watch coating and is formed, the part by weight proportioning of the component that described waterproof watch coating comprises and each component is as follows: phenylpropyl alcohol elastic emulsion 325g, 1250 order coarse whiting 200g, pure-acrylic emulsion 110g, titanium dioxide 78g, 1250 order kaolin 50g, softening agent 12g, ethylene glycol 15g, dispersion agent 8g, defoamer 5g, sterilant 3g, neutralizing agent 2g, 217 parts, water, wetting agent 4g, thickening material 9g.
The present invention reoffers a kind of coating process of waterproof layer, comprises the steps: a, forms waterproof matrix; B, after waterproof matrix drying, described waterproof matrix is coated with above-mentioned waterproof watch coating and forms waterproof top layer.
Embodiment four
A kind of waterproof matrix coating, the part by weight proportioning of the component comprised and each component is as follows: phenylpropyl alcohol elastic emulsion 115g, 800 order coarse whiting 85g, 1250 order wollastonite powder 27g, defoamer 0.46g, dispersion agent 0.56g, sterilant 0.46g, water 15g, dibutylester 1.3g, thickening material 0.9g, mill base is appropriate.
A kind of waterproof matrix, comprise waterproof layer one from inside to outside successively, seam knits mylar, waterproof layer two, described waterproof layer one, waterproof layer two are formed by above-mentioned waterproof matrix coatings.
A coating process for waterproof matrix, comprises the steps:
A, is coated with waterproof matrix coating described above in pending region, forms waterproof layer one;
B, knits mylar and is laid on described waterproof layer one by seam;
C, the strong mylar of described seam is coated with above-mentioned waterproof matrix coating and forms waterproof layer two, and limit is laid seam and knitted polyester selvedge coating waterproof layer two, makes waterproof matrix coating soak full seam and knits mylar.
The present invention also provides a kind of waterproof layer, comprise waterproof matrix, waterproof top layer from inside to outside successively, described waterproof top layer is coated with by waterproof watch coating and is formed, the part by weight proportioning of the component that described waterproof watch coating comprises and each component is as follows: phenylpropyl alcohol elastic emulsion 340g, 1250 order coarse whiting 225g, pure-acrylic emulsion 115g, titanium dioxide 72g, 1250 order kaolin 55g, softening agent 11g, ethylene glycol 13g, dispersion agent 8g, defoamer 4g, sterilant 4g, neutralizing agent 1.8g, 217 parts, water, wetting agent 5g, thickening material 8g.
The present invention reoffers a kind of coating process of waterproof layer, comprises the steps: a, forms waterproof matrix; B, after waterproof matrix drying, described waterproof matrix is coated with above-mentioned waterproof watch coating and forms waterproof top layer.
Embodiment five
A kind of waterproof matrix coating, the part by weight proportioning of the component comprised and each component is as follows: phenylpropyl alcohol elastic emulsion 120g, 800 order coarse whiting 90g, 1250 order wollastonite powder 30g, defoamer 0.5g, dispersion agent 0.6g, sterilant 0.5g, water 15g, dibutylester 2g, thickening material 1g, mill base is appropriate.
A kind of waterproof matrix, comprise waterproof layer one from inside to outside successively, seam knits mylar, waterproof layer two, described waterproof layer one, waterproof layer two are formed by above-mentioned waterproof matrix coatings.
A coating process for waterproof matrix, comprises the steps:
A, is coated with waterproof matrix coating described above in pending region, forms waterproof layer one;
B, knits mylar according to the size cutting seam in pending region, seam suitable for size is knitted mylar and be laid on described waterproof layer one;
C, the strong mylar of described seam is coated with above-mentioned waterproof matrix coating and forms waterproof layer two, and limit is laid seam and knitted polyester selvedge coating waterproof layer two, makes waterproof matrix coating soak full seam and knits mylar.
The present invention also provides a kind of waterproof layer, comprise waterproof matrix, waterproof top layer from inside to outside successively, described waterproof top layer is coated with by waterproof watch coating and is formed, the part by weight proportioning of the component that described waterproof watch coating comprises and each component is as follows: phenylpropyl alcohol elastic emulsion 350g, 1250 order coarse whiting 250g, pure-acrylic emulsion 110g, titanium dioxide 70g, 1250 order kaolin 50g, softening agent 14g, ethylene glycol 13g, dispersion agent 8g, defoamer 5g, sterilant 3g, neutralizing agent 3g, 217 parts, water, wetting agent 4g, thickening material 10g.
The present invention reoffers a kind of coating process of waterproof layer, comprises the steps: a, forms waterproof matrix; B, after waterproof matrix drying, described waterproof matrix is coated with above-mentioned waterproof watch coating and forms waterproof top layer, described waterproof top layer is multilayer, the protective coating that multilayer flashing top layer is coated with by different time is formed, the coating of adjacent waterproof top layer interval greater than 4 hours.
Although illustrate and describe embodiments of the invention, those having ordinary skill in the art will appreciate that: can carry out multiple change, amendment, replacement and modification to these embodiments when not departing from principle of the present invention and aim, scope of the present invention is by claim and equivalents thereof.
Claims (9)
1. a waterproof matrix coating, is characterized in that, the part by weight proportioning of the component comprised and each component is as follows: elastic emulsion 100-120 part, coarse whiting 80-90 part, wollastonite powder 20-30 part, defoamer 0.4-0.5 part, dispersion agent 0.5-0.6 part, sterilant 0.4-0.5 part, 15 parts, water.
2. waterproof matrix coating according to claim 1, is characterized in that, also comprise dibutylester, and its weight proportion is 1-2 part.
3. waterproof matrix coating according to claim 1, is characterized in that, also comprise thickening material, and its weight proportion is 0.6-1 part.
4. waterproof matrix coating according to claim 1, is characterized in that, also comprises appropriate mill base.
5. waterproof matrix coating according to claim 1, is characterized in that, described elastic emulsion is phenylpropyl alcohol elastic emulsion, and the granularity of described coarse whiting is 800 orders, and the granularity of described wollastonite powder is 1250 orders.
6. a waterproof matrix, is characterized in that, comprise waterproof layer one from inside to outside successively, seam knits mylar, waterproof layer two, described waterproof layer one, waterproof layer two form by the waterproof matrix coatings according to any one of claim 1-5.
7. a coating process for waterproof matrix, is characterized in that, comprises the steps:
A, the waterproof matrix coating as described in as arbitrary in claim 1 to 5 in the coating of pending region, forms waterproof layer one;
B, knits mylar and is laid on described waterproof layer one by seam;
C, described seam knit mylar is coated with as arbitrary in claim 1 to 5 as described in waterproof watch coating formed waterproof layer two.
8. waterproof matrix coating process according to claim 7, is characterized in that, described step b is specially: knit mylar according to the size cutting seam in pending region, seam suitable for size is knitted mylar and be laid on described waterproof layer one.
9. waterproof matrix coating process according to claim 7, is characterized in that, described step c is specially: lay seam and knit mylar and be coated with waterproof layer two, makes waterproof matrix coating soak full seam and knits mylar.