CN105268617A - Manufacturing method of anti-microbial metal product - Google Patents
Manufacturing method of anti-microbial metal product Download PDFInfo
- Publication number
- CN105268617A CN105268617A CN201510569829.8A CN201510569829A CN105268617A CN 105268617 A CN105268617 A CN 105268617A CN 201510569829 A CN201510569829 A CN 201510569829A CN 105268617 A CN105268617 A CN 105268617A
- Authority
- CN
- China
- Prior art keywords
- antimicrobial component
- fabrication methods
- antibacterial metal
- copper
- metal article
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a manufacturing method of an anti-microbial metal product. The method comprises the steps that the surface of the metal product is coated with a coating layer containing anti-microbial constituents, the coating layer comprises particles containing the anti-microbial constituents, then the coating layer is ground and polished, and the surface of the coating layer is flat and smooth, wherein the anti-microbial constituents are the combination of one or more of copper, copper sulfate, copper chloride, silver oxide, silver fluoride, silver fluoride and phosphoric acid. The metal product manufactured through the method has a certain anti-microbial capability, and the metal product can be used for containing foods and other objects with the high requirement for sanitation.
Description
Technical field
The present invention relates to a kind of preparation method of antibacterial metal goods.
Background technology
Metallic article is widely used in production and life as aluminum products, stainless steel products etc., similarly is that some containers such as metal basin, box are widely used.Some are used to splendid attire food, and the antibacterial ability of these containers has the requirement of a bit, can ensure the safety and sanitation of food.Therefore, when these metallic articles of making, the making link considering the antibacterial ability increasing metallic article is needed.
Summary of the invention
The technical problem that the present invention mainly solves is to provide a kind of antibacterial metal article fabrication methods, and the metallic article made by the method has certain antibacterial ability, makes metallic article can be used for the article very high to hygienic requirements such as splendid attire food.
For solving the problems of the technologies described above, the technical scheme that the present invention adopts is: provide a kind of antibacterial metal article fabrication methods, its coating one deck of avoiding being included in metallic article contains the coat of antimicrobial component, the particle of antimicrobial component is included in described coat, then grinding and polishing is carried out to described coat, make described coat surfacing smooth.
In a preferred embodiment of the present invention, carry out during grinding and polishing in containing the solution of antimicrobial component, metallic article immerses 10-20cm under the liquid level of described solution.
In a preferred embodiment of the present invention, described antimicrobial component is the combination of one or more of following material: copper, copper sulphate, copper chloride, silver oxide, silver fluoride, copper sulfide or cupric phosphate.
In a preferred embodiment of the present invention, the thickness of described coat is 0.01-0.03mm.
In a preferred embodiment of the present invention, the described concentration containing the solution of antimicrobial component is that the weight content of antimicrobial component accounts for 1%-8%.
In a preferred embodiment of the present invention, the particle diameter of described antimicrobial component is 2-8 μm.
The invention has the beneficial effects as follows: the metallic article made by method of the present invention has certain antibacterial ability, make metallic article can be used for the article very high to hygienic requirements such as splendid attire food.
Detailed description of the invention
Be clearly and completely described to the technical scheme in the embodiment of the present invention below, obviously, described embodiment is only a part of embodiment of the present invention, instead of whole embodiments.Based on the embodiment in the present invention, those of ordinary skill in the art, not making other embodiments all obtained under creative work prerequisite, belong to the scope of protection of the invention.
The embodiment of the present invention comprises:
A kind of antibacterial metal article fabrication methods, comprise: metallic article avoid apply the coat that one deck contains antimicrobial component, include the particle of antimicrobial component in described coat, then grinding and polishing is carried out to described coat, make described coat surfacing smooth.
Preferably, carry out during grinding and polishing in containing the solution of antimicrobial component, metallic article immerses 10-20cm under the liquid level of described solution.When grinding and polishing, metallic article can bear certain hydraulic pressure like this, is conducive to the formation of coat.
Preferably, described antimicrobial component is the combination of one or more of following material: copper, copper sulphate, copper chloride, silver oxide, silver fluoride, copper sulfide or cupric phosphate.These compositions have good antibacterial action.
Preferably, the thickness of described coat is 0.01-0.03mm.
Preferably, the concentration of the described solution containing antimicrobial component is that the weight content of antimicrobial component accounts for 1%-8%.
Preferably, the particle diameter of described antimicrobial component is 2-8 μm.
The beneficial effect of antibacterial metal article fabrication methods of the present invention is:
The metallic article made by method of the present invention has certain antibacterial ability, makes metallic article can be used for the article very high to hygienic requirements such as splendid attire food.
The foregoing is only embodiments of the invention; not thereby the scope of the claims of the present invention is limited; every utilize description of the present invention to do equivalent structure or equivalent flow process conversion; or be directly or indirectly used in other relevant technical field, be all in like manner included in scope of patent protection of the present invention.
Claims (6)
1. an antibacterial metal article fabrication methods, it is characterized in that, the coating one deck of avoiding being included in metallic article contains the coat of antimicrobial component, includes the particle of antimicrobial component in described coat, then grinding and polishing is carried out to described coat, make described coat surfacing smooth.
2. antibacterial metal article fabrication methods according to claim 1, is characterized in that, carries out during grinding and polishing in containing the solution of antimicrobial component, and metallic article immerses 10-20cm under the liquid level of described solution.
3. antibacterial metal article fabrication methods according to claim 1, is characterized in that, the thickness of described coat is 0.01-0.03mm.
4. antibacterial metal article fabrication methods according to claim 1, is characterized in that, described antimicrobial component is the combination of one or more of following material: copper, copper sulphate, copper chloride, silver oxide, silver fluoride, copper sulfide or cupric phosphate.
5. antibacterial metal article fabrication methods according to claim 2, is characterized in that, the described concentration containing the solution of antimicrobial component is that the weight content of antimicrobial component accounts for 1%-8%.
6. antibacterial metal article fabrication methods according to claim 1, is characterized in that, the particle diameter of described antimicrobial component is 2-8 μm.