CN105255151A - Flame-retardant plastic material - Google Patents
Flame-retardant plastic material Download PDFInfo
- Publication number
- CN105255151A CN105255151A CN201510840279.9A CN201510840279A CN105255151A CN 105255151 A CN105255151 A CN 105255151A CN 201510840279 A CN201510840279 A CN 201510840279A CN 105255151 A CN105255151 A CN 105255151A
- Authority
- CN
- China
- Prior art keywords
- parts
- plastic material
- flame
- retardant
- flame retardant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a flame-retardant plastic material. The flame-retardant plastic material is prepared from, by weight, 28-40 parts of glass fibers, 10-15 parts of polycarbonate, 10-15 parts of poly-terephthalic acid, 5-7.5 parts of polyvinyl chloride resin, 1-5 parts of cadmium stearate, 5-10 parts of flame retardant, 1-5 parts of dispersed lubricant and 2-6 parts of gypsum. According to the flame-retardant plastic material, the plastic material achieves good flame-retardant performance on the premise that plastic achieves plasticity, and the plastic material can be used for the field with the high plastic flame-retardant requirement, and has wide market prospects.
Description
Technical field
The present invention relates to Material Field, particularly relate to a kind of Flame retardant plastic material.
Background technology
Plastic cement application widely, has become the indispensable parts raw material of all trades and professions.Along with the continuous enlargement of the demand of plastic parts, also tackle plastic cement products mutually and propose increasing requirement, the plastic cement products much with specific function arises at the historic moment.
Summary of the invention
The object of the present invention is to provide a kind of Flame retardant plastic material, be intended to solve the problem that current plastic cement products does not have flame retardant effect.
Technical scheme of the present invention is as follows:
A kind of Flame retardant plastic material, wherein, is made up of the material of following parts by weight:
Glass fibre 28-40 part;
Polycarbonate 10-15 part;
Poly terephthalic acid 10-15 part;
Polyvinyl chloride (PVC) RESINS 5-7.5 part;
Cadmium stearate 1-5 part;
Fire retardant 5-10 part;
Dispersed lubricant 1-5 part;
Gypsum 2-6 part.
Described Flame retardant plastic material, wherein, the weight proportion of described polycarbonate, poly terephthalic acid, polyvinyl chloride (PVC) RESINS is 2:2:1.
Described Flame retardant plastic material, wherein, described fire retardant is halogen-free expansion fire retardant.
Described Flame retardant plastic material, wherein, is made up of the material of following parts by weight:
35 parts, glass fibre;
Polycarbonate 12 parts;
Poly terephthalic acid 12 parts;
Polyvinyl chloride (PVC) RESINS 6 parts;
Cadmium stearate 2 parts;
Fire retardant 10 parts;
Dispersed lubricant 2 parts;
4 parts, gypsum.
Described Flame retardant plastic material, wherein, is made up of the material of following parts by weight:
40 parts, glass fibre;
Polycarbonate 10 parts;
Poly terephthalic acid 10 parts;
Polyvinyl chloride (PVC) RESINS 5 parts;
Cadmium stearate 5 parts;
Fire retardant 10 parts;
Dispersed lubricant 5 parts;
6 parts, gypsum.
Beneficial effect: the invention provides a kind of Flame retardant plastic material, plastic cement can be made to make plastic material itself have good flame retardant properties meeting under plastic prerequisite, make plastic material of the present invention can be used in the field high to plastic cement flame-retardancy requirements, there are wide market outlook.
Embodiment
For making object of the present invention, technical scheme and advantage clearly, clearly, the present invention is described in more detail below.
The invention provides a kind of Flame retardant plastic material, wherein, be made up of the material of following parts by weight:
Glass fibre 28-40 part;
Polycarbonate 10-15 part;
Poly terephthalic acid 10-15 part;
Polyvinyl chloride (PVC) RESINS 5-7.5 part;
Cadmium stearate 1-5 part;
Fire retardant 5-10 part;
Dispersed lubricant 1-5 part;
Gypsum 2-6 part.
Wherein, it is preferred that the weight proportion of described polycarbonate, poly terephthalic acid, polyvinyl chloride (PVC) RESINS is 2:2:1.In preferred embodiment, described fire retardant is halogen-free expansion fire retardant.
Further the present invention program is discussed below by embodiment.
Embodiment 1
Described Flame retardant plastic material, is made up of the material of following parts by weight:
35 parts, glass fibre;
Polycarbonate 12 parts;
Poly terephthalic acid 12 parts;
Polyvinyl chloride (PVC) RESINS 6 parts;
Cadmium stearate 2 parts;
Fire retardant 10 parts;
Dispersed lubricant 2 parts;
4 parts, gypsum.
Embodiment 2
Described Flame retardant plastic material, is made up of the material of following parts by weight:
40 parts, glass fibre;
Polycarbonate 10 parts;
Poly terephthalic acid 10 parts;
Polyvinyl chloride (PVC) RESINS 5 parts;
Cadmium stearate 5 parts;
Fire retardant 10 parts;
Dispersed lubricant 5 parts;
6 parts, gypsum.
The invention provides a kind of Flame retardant plastic material, plastic cement can be made to make plastic material itself have good flame retardant properties meeting under plastic prerequisite, make plastic material of the present invention can be used in the field high to plastic cement flame-retardancy requirements, there are wide market outlook.
Should be understood that, application of the present invention is not limited to above-mentioned citing, for those of ordinary skills, can be improved according to the above description or convert, and all these improve and convert the protection domain that all should belong to claims of the present invention.
Claims (5)
1. a Flame retardant plastic material, is characterized in that, is made up of the material of following parts by weight:
Glass fibre 28-40 part;
Polycarbonate 10-15 part;
Poly terephthalic acid 10-15 part;
Polyvinyl chloride (PVC) RESINS 5-7.5 part;
Cadmium stearate 1-5 part;
Fire retardant 5-10 part;
Dispersed lubricant 1-5 part;
Gypsum 2-6 part.
2. Flame retardant plastic material according to claim 1, is characterized in that, the weight proportion of described polycarbonate, poly terephthalic acid, polyvinyl chloride (PVC) RESINS is 2:2:1.
3. Flame retardant plastic material according to claim 1, is characterized in that, described fire retardant is halogen-free expansion fire retardant.
4. Flame retardant plastic material according to claim 2, is characterized in that, is made up of the material of following parts by weight:
35 parts, glass fibre;
Polycarbonate 12 parts;
Poly terephthalic acid 12 parts;
Polyvinyl chloride (PVC) RESINS 6 parts;
Cadmium stearate 2 parts;
Fire retardant 10 parts;
Dispersed lubricant 2 parts;
4 parts, gypsum.
5. Flame retardant plastic material according to claim 2, is characterized in that, is made up of the material of following parts by weight:
40 parts, glass fibre;
Polycarbonate 10 parts;
Poly terephthalic acid 10 parts;
Polyvinyl chloride (PVC) RESINS 5 parts;
Cadmium stearate 5 parts;
Fire retardant 10 parts;
Dispersed lubricant 5 parts;
6 parts, gypsum.