CN105254218A - Green, environmentally-friendly and discoloration and fading-free gap filler, and preparation method and use method thereof - Google Patents
Green, environmentally-friendly and discoloration and fading-free gap filler, and preparation method and use method thereof Download PDFInfo
- Publication number
- CN105254218A CN105254218A CN201510597371.7A CN201510597371A CN105254218A CN 105254218 A CN105254218 A CN 105254218A CN 201510597371 A CN201510597371 A CN 201510597371A CN 105254218 A CN105254218 A CN 105254218A
- Authority
- CN
- China
- Prior art keywords
- spackling
- water
- parts
- iron oxide
- oxide pigment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a green, environmentally-friendly and discoloration and fading-free gap filler. A preparation method of the gap filler comprises the following steps: 1, preparing a base material: crushing quartz sand and an air purifying decoration material named Kasongshi to 300-500 meshes, adding glazed hollow beads, hydroxypropyl methyl cellulose, an inorganic aluminum salt waterproof agent and ferrous sulfate, and uniformly stirring; 2, preparing an auxiliary material: mixing an ethylene-vinyl acetate copolymer, acrylic resin, fumed silica, RTV organic silica gel and an antioxidant 1076, and uniformly stirring; and 3, selecting an iron oxide pigment according to the color type of the gap filler, adding the base material to a high speed shearing stirrer, sequentially adding the auxiliary material and the iron oxide pigment in a shearing stirring state, stirring at a shearing speed of 6000-8000RPM for 45-90min, and discharging to obtain the gap filler. Gap filling spaces are cleaned, gap filling seams are sprinkled with water until moisture, the gap filler and water are mixed according to a mass ratio of 1:(0.4-0.6) and are blended to form a viscous material, the viscous material is filled between tiles, water is sprinkled after the viscous material is dried, and then natural drying is carried out.
Description
Technical field
The present invention relates to a kind of spackling for building, is that a kind of environmental protection is without variable color, the spackling that fades, preparation method and using method specifically.
Background technology
Because spackling perfectly can repair cracking or the breakage of ground surface, also can prepare various colors rich color voluntarily, thus more and more favor by guest.And existing spackling mostly adopts cement to prepare, be equipped with the additive that cement is conventional, there is the defect in resistance to environment, environmental protection, greatly sex-limited in application scenario and use safety, life-span lasting arrangement, long oxidation is easy to change, fade.
Summary of the invention
For the deficiencies in the prior art, the invention provides a kind of resistance to environment, environmental protection, without variable color, without spackling, preparation method and the using method of fading.
The technical solution used in the present invention is: a kind of environmental protection without variable color, fade spackling, comprises quartz sand 40-50 part, card song stone 10-15 part, ethylene-vinyl acetate copolymer 2-3 part, glass bead 8-12 part, aerosil 2-2.4 part, acrylic resin 1-1.5 part, Vltra tears 3-6 part, inorganic aluminate water-proof agent 1-1.3 part, ferrous sulfate 0.5-1.5 part, RTV organic silica gel 1.5-1.9 part, antioxidant 1076 0.4-0.6 part and iron oxide pigment 1.8-2.2 part by mass fraction.
Environmental protection, without a preparation method for variable color, the spackling that fades, first weighs following raw material: comprise quartz sand 40-50 part, card song stone 10-15 part, ethylene-vinyl acetate copolymer 2-3 part, glass bead 8-12 part, aerosil 2-2.4 part, acrylic resin 1-1.5 part, Vltra tears 3-6 part, inorganic aluminate water-proof agent 1-1.3 part, ferrous sulfate 0.5-1.5 part, RTV organic silica gel 1.5-1.9 part, antioxidant 1076 0.4-0.6 part and iron oxide pigment 1.8-2.2 part by mass fraction; Prepare base-material: first quartz sand, quartz sand are added glass bead after pulverizing 300-500 order, Vltra tears, inorganic aluminate water-proof agent, ferrous sulfate stir; Prepare auxiliary material: by ethylene-vinyl acetate copolymer, acrylic resin, aerosil, RTV organic silica gel and antioxidant 1076 mixing and stirring; Choose iron oxide pigment by spackling color classification, base-material is added high shear agitation machine, under shear agitation state, add auxiliary material and iron oxide pigment successively, velocity of shear 6000-8000RPM, time 45min ~ 90min, stir discharging and be spackling.
A kind of environmental protection is without the using method of variable color, the spackling that fades, cleaning joint filling space, and water is successively sprayed in joint filling seam, with moistening, again by spackling and water 1:(0.4-0.6 in mass ratio) mix and furnishing material of sticky shape, fill between ceramic tile and ceramic tile, spray a water after to be dried again, seasoning.
After adopting technique scheme, the invention has the beneficial effects as follows: in spackling, increase RTV organo-silicone rubber, effectively can strengthen hydrophobic nature and the migration of hydrophobicity of spackling, make spackling have self-cleaning property, not easily adhesive dust, ensure that the result of use of spackling.Ethylene-vinyl acetate copolymer improves water tolerance, its closedcells structure, do not absorb water, moistureproof, water resistance is good, improve erosion resistance: the chemical such as sea water resistance, grease, acid, alkali corrodes, antibacterial, nontoxic, tasteless, pollution-free, be convenient to carry out cutting out processing, there is good shockproof, shock-absorbing capacity, heat insulation, heat-insulating and cold and low temperature performance excellent, can be cold-resistant and tan by the sun.Glass bead, as filler aggregate, improves its Jue Re ﹑ Fang Huo ﹑ Xi Yin ﹑ heat-insulating property further.Filler aggregate and Jue Re ﹑ Fang Huo ﹑ Xi Yin ﹑ lagging material.Add card song stone, effectively to absorb, indoor decoration obnoxious flavour of demarcate, raising green safety performance.Aerosil, as the auxiliary agent of anti-settling, thickening, sag prevention, regulates unrestricted flow and improves powder properties as anti-caking agent, having the multiple effects such as good reinforcement, thickening, thixotroping, delustring, uvioresistant and sterilization.Acrylic resin effectively promotes outdoor ageing resistance. Vltra tears can make slurry because of so dry that to chap too soon, can not strengthen the rear intensity of sclerosis after smearing as toughener, water-holding agent simultaneously.Inorganic aluminate water-proof agent improves its water resistance, improves spackling stability, guarantees use safety health.In conjunction with antioxidant 1076, ferrous sulfate guarantees that spackling has good antioxidant property, avoid the variable color of life-time service, fade.
Embodiment
Below in conjunction with embodiment, the invention will be further described.
Embodiment one
A kind of environmental protection without variable color, fade spackling, comprises quartz sand 40 parts, card song 10 parts, stone, ethylene-vinyl acetate copolymer 2 parts, glass bead 8 parts, aerosil 2 parts, acrylic resin 1 part, Vltra tears 3 parts, inorganic aluminate water-proof agent 1 part, 0.5 part, ferrous sulfate, RTV organic silica gel 1.5 parts, antioxidant 1076 0.4 part and iron oxide pigment 1.8 parts by mass fraction.
Its preparation method is: first weigh following raw material: comprise quartz sand 40 parts, card song 10 parts, stone, ethylene-vinyl acetate copolymer 2 parts, glass bead 8 parts, aerosil 2 parts, acrylic resin 1 part, Vltra tears 3 parts, inorganic aluminate water-proof agent 1 part, 0.5 part, ferrous sulfate, RTV organic silica gel 1.5 parts, antioxidant 1076 0.4 part and iron oxide pigment 1.8 parts by mass fraction.
Prepare base-material: first quartz sand, quartz sand are added glass bead after pulverizing 300 orders, Vltra tears, inorganic aluminate water-proof agent, ferrous sulfate stir;
Prepare auxiliary material: by ethylene-vinyl acetate copolymer, acrylic resin, aerosil, RTV organic silica gel and antioxidant 1076 mixing and stirring;
Choose iron oxide pigment by spackling color classification, base-material is added high shear agitation machine, under shear agitation state, add auxiliary material and iron oxide pigment successively, velocity of shear 9000RPM, time 45min, stir discharging and be spackling.
Using method is: cleaning joint filling space, and in joint filling seam, sprays water successively, with moistening, again by spackling and water in mass ratio 1:0.4 mix and furnishing material of sticky shape, fill between ceramic tile and ceramic tile, spray a water after to be dried again, seasoning.
Embodiment two
A kind of environmental protection without variable color, fade spackling, comprises quartz sand 50 parts, card song 15 parts, stone, ethylene-vinyl acetate copolymer 3 parts, glass bead 12 parts, aerosil 2.4 parts, acrylic resin 1.5 parts, Vltra tears 6 parts, inorganic aluminate water-proof agent 1.3 parts, 1.5 parts, ferrous sulfate, RTV organic silica gel 1.9 parts, antioxidant 1076 0.6 part and iron oxide pigment 2.2 parts by mass fraction.
Its preparation method is: first weigh following raw material: comprise quartz sand 50 parts, card song 15 parts, stone, ethylene-vinyl acetate copolymer 3 parts, glass bead 12 parts, aerosil 2.4 parts, acrylic resin 1.5 parts, Vltra tears 6 parts, inorganic aluminate water-proof agent 1.3 parts, 1.5 parts, ferrous sulfate, RTV organic silica gel 1.9 parts, antioxidant 1076 0.6 part and iron oxide pigment 2.2 parts by mass fraction.
Prepare base-material: first quartz sand, quartz sand are added glass bead after pulverizing 500 orders, Vltra tears, inorganic aluminate water-proof agent, ferrous sulfate stir;
Prepare auxiliary material: by ethylene-vinyl acetate copolymer, acrylic resin, aerosil, RTV organic silica gel and antioxidant 1076 mixing and stirring;
Choose iron oxide pigment by spackling color classification, base-material is added high shear agitation machine, under shear agitation state, add auxiliary material and iron oxide pigment successively, velocity of shear 8000RPM, time 45min, stir discharging and be spackling.
Using method is: cleaning joint filling space, and in joint filling seam, sprays water successively, with moistening, again by spackling and water in mass ratio 1:0.6 mix and furnishing material of sticky shape, fill between ceramic tile and ceramic tile, spray a water after to be dried again, seasoning.
Embodiment three
A kind of environmental protection without variable color, fade spackling, comprises quartz sand 45 parts, card song 12 parts, stone, ethylene-vinyl acetate copolymer 2.5 parts, glass bead 11 parts, aerosil 2.3 parts, acrylic resin 1.35 parts, Vltra tears 5 parts, inorganic aluminate water-proof agent 1.2 parts, 1.2 parts, ferrous sulfate, RTV organic silica gel 1.8 parts, antioxidant 1076 0.5 part and iron oxide pigment 2 parts by mass fraction.
Its preparation method is: first weigh following raw material: comprise quartz sand 45 parts, card song 12 parts, stone, ethylene-vinyl acetate copolymer 2.5 parts, glass bead 11 parts, aerosil 2.3 parts, acrylic resin 1.35 parts, Vltra tears 5 parts, inorganic aluminate water-proof agent 1.2 parts, 1.2 parts, ferrous sulfate, RTV organic silica gel 1.8 parts, antioxidant 1076 0.5 part and iron oxide pigment 2 parts by mass fraction.
Prepare base-material: first quartz sand, quartz sand are added glass bead after pulverizing 450 orders, Vltra tears, inorganic aluminate water-proof agent, ferrous sulfate stir;
Prepare auxiliary material: by ethylene-vinyl acetate copolymer, acrylic resin, aerosil, RTV organic silica gel and antioxidant 1076 mixing and stirring;
Choose iron oxide pigment by spackling color classification, base-material is added high shear agitation machine, under shear agitation state, add auxiliary material and iron oxide pigment successively, velocity of shear 7000RPM, time 60min, stir discharging and be spackling.
Using method is: cleaning joint filling space, and in joint filling seam, sprays water successively, with moistening, again by spackling and water in mass ratio 1:0.5 mix and furnishing material of sticky shape, fill between ceramic tile and ceramic tile, spray a water after to be dried again, seasoning.
Claims (3)
1. environmental protection without variable color, fade a spackling, it is characterized in that: comprise quartz sand 40-50 part, card song stone 10-15 part, ethylene-vinyl acetate copolymer 2-3 part, glass bead 8-12 part, aerosil 2-2.4 part, acrylic resin 1-1.5 part, Vltra tears 3-6 part, inorganic aluminate water-proof agent 1-1.3 part, ferrous sulfate 0.5-1.5 part, RTV organic silica gel 1.5-1.9 part, antioxidant 1076 0.4-0.6 part and iron oxide pigment 1.8-2.2 part by mass fraction.
2. environmental protection is without variable color, a spackling preparation method of fading, and first weighs following raw material: comprise quartz sand 40-50 part, card song stone 10-15 part, ethylene-vinyl acetate copolymer 2-3 part, glass bead 8-12 part, aerosil 2-2.4 part, acrylic resin 1-1.5 part, Vltra tears 3-6 part, inorganic aluminate water-proof agent 1-1.3 part, ferrous sulfate 0.5-1.5 part, RTV organic silica gel 1.5-1.9 part, antioxidant 1076 0.4-0.6 part and iron oxide pigment 1.8-2.2 part by mass fraction; Prepare base-material: first quartz sand, quartz sand are added glass bead after pulverizing 300-500 order, Vltra tears, inorganic aluminate water-proof agent, ferrous sulfate stir; Prepare auxiliary material: by ethylene-vinyl acetate copolymer, acrylic resin, aerosil, RTV organic silica gel and antioxidant 1076 mixing and stirring; Choose iron oxide pigment by spackling color classification, base-material is added high shear agitation machine, under shear agitation state, add auxiliary material and iron oxide pigment successively, velocity of shear 6000-8000RPM, time 45min ~ 90min, stir discharging and be spackling.
3. an environmental protection is without variable color, spackling using method of fading, cleaning joint filling space, and water is successively sprayed in joint filling seam, with moistening, again by spackling and water 1:(0.4-0.6 in mass ratio) mix and furnishing material of sticky shape, fill between ceramic tile and ceramic tile, spray a water after to be dried again, seasoning.