CN105252164A - 一种抗氧化焊锡条 - Google Patents

一种抗氧化焊锡条 Download PDF

Info

Publication number
CN105252164A
CN105252164A CN201510850697.6A CN201510850697A CN105252164A CN 105252164 A CN105252164 A CN 105252164A CN 201510850697 A CN201510850697 A CN 201510850697A CN 105252164 A CN105252164 A CN 105252164A
Authority
CN
China
Prior art keywords
content
bismuth
tin
silver
nickel
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510850697.6A
Other languages
English (en)
Inventor
杨伟帅
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Suzhou Lotte Chemical Technology Co Ltd
Original Assignee
Suzhou Lotte Chemical Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Suzhou Lotte Chemical Technology Co Ltd filed Critical Suzhou Lotte Chemical Technology Co Ltd
Priority to CN201510850697.6A priority Critical patent/CN105252164A/zh
Publication of CN105252164A publication Critical patent/CN105252164A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种抗氧化焊锡条，包括锡、铋、铜、镍、银和金元素，所述铋的含量为0.022-0.12%，所述镍含量为0.55-0.65%，所述铜含量为5-6.5%，所述银含量为3.8-6.7%，所述金含量为0.3-0.75%，其余为锡，所述含量为重量百分比。通过上述方式，本发明抗氧化焊锡条具有良好的抗氧化能力，流动性高，焊接性强，融化时浮渣极少，焊接效果极佳。

Description

一种抗氧化焊锡条
技术领域
本发明涉及焊锡条领域，特别是涉及一种抗氧化焊锡条。
背景技术
为了保证焊锡焊接的美观度和牢固度，常常需要焊锡具有一定的抗氧化能力，而现有的焊锡条抗氧化能力较差。
发明内容
本发明主要解决的技术问题是提供一种抗氧化能力好、流动性高、焊接性强的抗氧化焊锡条。
为解决上述技术问题，本发明提供一种抗氧化焊锡条，包括锡、铋、铜、镍、银和金元素，所述铋的含量为0.022-0.12%，所述镍含量为0.55-0.65%，所述铜含量为5-6.5%，所述银含量为3.8-6.7%，所述金含量为0.3-0.75%，其余为锡，所述含量为重量百分比。
在本发明一个较佳实施例中，包括锡、铋、铜、镍、银和金元素，所述铋的含量为0.022%，所述镍含量为0.55%，所述铜含量为5%，所述银含量为6.7%，所述金含量为0.75%，其余为锡，所述含量为重量百分比。
在本发明一个较佳实施例中，包括锡、铋、铜、镍、银和金元素，所述铋的含量为0.12%，所述镍含量为0.65%，所述铜含量为6.5%，所述银含量为6.7%，所述金含量为0.75%，其余为锡，所述含量为重量百分比。
在本发明一个较佳实施例中，包括锡、铋、铜、镍、银和金元素，所述铋的含量为0.1%，所述镍含量为0.6%，所述铜含量为5%，所述银含量为4%，所述金含量为0.35%，其余为锡，所述含量为重量百分比。
本发明的有益效果是：本发明抗氧化焊锡条具有良好的抗氧化能力，流动性高，焊接性强，融化时浮渣极少，焊接效果极佳。
具体实施方式
下面将对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅是本发明的一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其它实施例，都属于本发明保护的范围。
实施例1
一种抗氧化焊锡条，包括锡、铋、铜、镍、银和金元素，所述铋的含量为0.022%，所述镍含量为0.55%，所述铜含量为5%，所述银含量为6.7%，所述金含量为0.75%，其余为锡，所述含量为重量百分比。
实施例2
一种抗氧化焊锡条，包括锡、铋、铜、镍、银和金元素，所述铋的含量为0.12%，所述镍含量为0.65%，所述铜含量为6.5%，所述银含量为6.7%，所述金含量为0.75%，其余为锡，所述含量为重量百分比。
实施例2
一种抗氧化焊锡条，包括锡、铋、铜、镍、银和金元素，所述铋的含量为0.1%，所述镍含量为0.6%，所述铜含量为5%，所述银含量为4%，所述金含量为0.35%，其余为锡，所述含量为重量百分比。
区别于现有技术，本发明抗氧化焊锡条具有良好的抗氧化能力，流动性高，焊接性强，融化时浮渣极少，焊接效果极佳。
以上所述仅为本发明的实施例，并非因此限制本发明的专利范围，凡是利用本发明说明书内容所作的等效结构或等效流程变换，或直接或间接运用在其它相关的技术领域，均同理包括在本发明的专利保护范围内。

Claims (4)

1.一种抗氧化焊锡条，其特征在于，包括锡、铋、铜、镍、银和金元素，所述铋的含量为0.022-0.12%，所述镍含量为0.55-0.65%，所述铜含量为5-6.5%，所述银含量为3.8-6.7%，所述金含量为0.3-0.75%，其余为锡，所述含量为重量百分比。
2.根据权利要求1所述的抗氧化焊锡条，其特征在于，包括锡、铋、铜、镍、银和金元素，所述铋的含量为0.022%，所述镍含量为0.55%，所述铜含量为5%，所述银含量为6.7%，所述金含量为0.75%，其余为锡，所述含量为重量百分比。
3.根据权利要求1所述的抗氧化焊锡条，其特征在于，包括锡、铋、铜、镍、银和金元素，所述铋的含量为0.12%，所述镍含量为0.65%，所述铜含量为6.5%，所述银含量为6.7%，所述金含量为0.75%，其余为锡，所述含量为重量百分比。
4.根据权利要求1所述的抗氧化焊锡条，其特征在于，包括锡、铋、铜、镍、银和金元素，所述铋的含量为0.1%，所述镍含量为0.6%，所述铜含量为5%，所述银含量为4%，所述金含量为0.35%，其余为锡，所述含量为重量百分比。
CN201510850697.6A 2015-11-30 2015-11-30 一种抗氧化焊锡条 Pending CN105252164A (zh)