CN105249871A - Process for producing dacron composite fiber towels - Google Patents
Process for producing dacron composite fiber towels Download PDFInfo
- Publication number
- CN105249871A CN105249871A CN201510545976.1A CN201510545976A CN105249871A CN 105249871 A CN105249871 A CN 105249871A CN 201510545976 A CN201510545976 A CN 201510545976A CN 105249871 A CN105249871 A CN 105249871A
- Authority
- CN
- China
- Prior art keywords
- composite fibre
- grey cloth
- terylene composite
- dacron composite
- carried out
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the field of towel production, particularly to a process for producing dacron composite fiber towels. The process includes the following steps: performing a beam-warping process on dacron composite fibers; performing a sizing process on the dacron composite fibers after the beam-warping process; weaving the dacron composite fibers into grey cloths after the sizing process; soaking the grey cloths in a hot water tank, and washing away hydrosol filaments; performing a boiling and bleaching process on the grey cloths; performing a dyeing process on the grey cloths after the boiling and bleaching process; performing a drying process on the dyed grey cloths by using a drying device; cutting and sewing the dried grey cloths to obtain the dacron composite fiber towels. According to the invention, the dacron composite fiber towels have excellent moisture absorption and sweat releasing performances, have soft and comfortable performances, and excellent high temperature resistance and stink absorption and pollution discharge performances, are environmentally friendly, and are long in service life, the processing technology is simple, and the production efficiency is high.
Description
Technical field
The present invention relates to towel and make field, especially a kind of terylene composite fibre towel manufacture craft.
Background technology
Towel surface looped pile is intensive, soft, and water suction water storage is strong, and wear-resisting, thermal property is good, and therefore can directly be used for contacting skin, be one of most important daily necessities of daily life.Towel take textile fabric as raw material, the fabric with loop construction be interweaved by three system yarns.The yarn of these three systems be hair respectively through, warp and weft yarn.Along with the development of science and technology, occurred again through compiling towel cloth, this towel looped pile consolidation jail, but form is relatively single.On market, the overwhelming majority is woven towel, and the shortcomings such as filoplume is more, feel is poor easily appear in obtained towel, and the service life of towel is not long, and manufacture craft is also comparatively complicated.
Summary of the invention
The technical problem to be solved in the present invention is: for overcoming above-mentioned Problems existing, provides a kind of environmental protection, soft comfortable a kind of terylene composite fibre towel manufacture craft.
The technical solution adopted for the present invention to solve the technical problems is: a kind of terylene composite fibre towel manufacture craft, and technological process is as follows:
A. described terylene composite fibre is carried out warping process;
B. the terylene composite fibre after warping is carried out starching process;
C. grey cloth is woven into by through the terylene composite fibre described in starching process;
D. described grey cloth is immersed in hot water storgae, rinses and remove water-soluble silk;
E. described grey cloth is processed through over-cooking drift;
F. dyeing process is carried out by through over-cooking the grey cloth after drift;
G. the grey cloth after dyeing is carried out drying and processing through drying plant;
H. the grey cloth after oven dry is carried out cutting out and sew and obtain terylene composite fibre towel.
Further, described dyeing process is dyeed 25 minutes at 65 DEG C of temperature.
Further, the temperature that described drying and processing adopts is 80 DEG C ~ 90 DEG C.
The invention has the beneficial effects as follows, a kind of terylene composite fibre towel manufacture craft of the present invention has excellent moisture absorbing and sweat releasing performance, and there is the performance of soft comfortable, outstanding resistance to elevated temperatures and the smelly blowdown performance of suction, environmental protection, long service life, and processing technology is simple, and production efficiency is high.
Detailed description of the invention
A kind of terylene composite fibre towel manufacture craft, technological process is as follows:
A. terylene composite fibre is carried out warping process;
B. the terylene composite fibre after warping is carried out starching process;
C. grey cloth is woven into by through the terylene composite fibre described in starching process;
D. grey cloth is immersed in hot water storgae, rinses and remove water-soluble silk;
E. grey cloth is processed through over-cooking drift;
F. dyeing process is carried out by through over-cooking the grey cloth after drift;
G. the grey cloth after dyeing is carried out drying and processing through drying plant;
H. the grey cloth after oven dry is carried out cutting out and sew and obtain terylene composite fibre towel.
Further, dyeing process is dyeed 25 minutes at 65 DEG C of temperature.
Further, the temperature that drying and processing adopts is 80 DEG C ~ 90 DEG C.
With above-mentioned according to desirable embodiment of the present invention for enlightenment, by above-mentioned description, relevant staff in the scope not departing from this invention technological thought, can carry out various change and amendment completely.The technical scope of this invention is not limited to the content on description, must determine its technical scope according to right.
Claims (3)
1. a terylene composite fibre towel manufacture craft, it is characterized in that, technological process is as follows:
A. described terylene composite fibre is carried out warping process;
B. the terylene composite fibre after warping is carried out starching process;
C. grey cloth is woven into by through the terylene composite fibre described in starching process;
D. described grey cloth is immersed in hot water storgae, rinses and remove water-soluble silk;
E. described grey cloth is processed through over-cooking drift;
F. dyeing process is carried out by through over-cooking the grey cloth after drift;
G. the grey cloth after dyeing is carried out drying and processing through drying plant;
H. the grey cloth after oven dry is carried out cutting out and sew and obtain terylene composite fibre towel.
2. a kind of terylene composite fibre towel manufacture craft according to claim 1, is characterized in that: described dyeing process is dyeed 25 minutes at 65 DEG C of temperature.
3. a kind of terylene composite fibre towel manufacture craft according to claim 1, is characterized in that: the temperature that described drying and processing adopts is 80 DEG C ~ 90 DEG C.