CN105220054A - The ruhmkorff coil material prescription of current transformer - Google Patents
The ruhmkorff coil material prescription of current transformer Download PDFInfo
- Publication number
- CN105220054A CN105220054A CN201510597249.XA CN201510597249A CN105220054A CN 105220054 A CN105220054 A CN 105220054A CN 201510597249 A CN201510597249 A CN 201510597249A CN 105220054 A CN105220054 A CN 105220054A
- Authority
- CN
- China
- Prior art keywords
- parts
- silicon
- current transformer
- magnesium
- prescription
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to the ruhmkorff coil material prescription of current transformer, its material composition is with parts by weight, and filling a prescription is made up of following component: 1 ~ 2 part, platinum, gold 0.2 ~ 0.5 part, silver 0.5 ~ 0.7 part, copper 4 ~ 7 parts, silicon 2 ~ 3 parts, 0.5 ~ 0.7 part, germanium, 3 ~ 6 parts, aluminium, gallium 1 ~ 2 part, 0.1 ~ 0.5 part, magnesium, scandium 3 ~ 5 parts, yttrium 0.2 ~ 0.3 part, titanium 0.4 ~ 0.6 part, molybdenum 2 ~ 3 parts, 2 ~ 3 parts, tungsten, 0.6 ~ 1.2 part, manganese, iron 2 ~ 4 parts, cobalt 3 ~ 5 parts, 6 ~ 7 parts, nickel, 4 ~ 5 parts, zinc, 3 ~ 4 parts, magnesium oxide, silicon-dioxide 2 ~ 5 parts, magnesium hydroxide 2 ~ 3 parts and Calucium Silicate powder 3 ~ 6 parts.
Description
Technical field
The present invention relates to current transformer technical field, particularly relate to the ruhmkorff coil material prescription of current transformer.
Background technology
In prior art, current transformer inside is provided with ruhmkorff coil, has the harmonic elimination effect of circuit, but the ruhmkorff coil that existing ruhmkorff coil material is made, and in the process used, be easy to aging, work-ing life is very low, and result of use is poor.
Summary of the invention
The present invention, according to the deficiencies in the prior art, provides one to increase the service life, the ruhmkorff coil material prescription of the current transformer that result of use is good.
The present invention realizes like this, the ruhmkorff coil material prescription of current transformer, its material composition is with parts by weight, and filling a prescription is made up of following component: 1 ~ 2 part, platinum, gold 0.2 ~ 0.5 part, silver 0.5 ~ 0.7 part, copper 4 ~ 7 parts, silicon 2 ~ 3 parts, 0.5 ~ 0.7 part, germanium, 3 ~ 6 parts, aluminium, gallium 1 ~ 2 part, 0.1 ~ 0.5 part, magnesium, scandium 3 ~ 5 parts, yttrium 0.2 ~ 0.3 part, titanium 0.4 ~ 0.6 part, molybdenum 2 ~ 3 parts, 2 ~ 3 parts, tungsten, 0.6 ~ 1.2 part, manganese, iron 2 ~ 4 parts, cobalt 3 ~ 5 parts, 6 ~ 7 parts, nickel, 4 ~ 5 parts, zinc, 3 ~ 4 parts, magnesium oxide, silicon-dioxide 2 ~ 5 parts, magnesium hydroxide 2 ~ 3 parts and Calucium Silicate powder 3 ~ 6 parts.
Further, its material composition is with parts by weight, and filling a prescription is made up of following component: 1 part, platinum, gold 0.2 part, silver 0.5 part, copper 7 parts, silicon 2 parts, 0.7 part, germanium, 6 parts, aluminium, gallium 2 parts, 0.5 part, magnesium, scandium 5 parts, yttrium 0.3 part, titanium 0.4 part, molybdenum 3 parts, 3 parts, tungsten, 0.6 part, manganese, iron 2 parts, cobalt 3 parts, 6 parts, nickel, 4 parts, zinc, 3 parts, magnesium oxide, silicon-dioxide 5 parts, magnesium hydroxide 3 parts and Calucium Silicate powder 6 parts.
The advantage of the ruhmkorff coil material prescription of current transformer provided by the invention is: the ruhmkorff coil of the current transformer that platinum, gold and silver, copper, silicon, germanium, aluminium, gallium, magnesium, scandium, yttrium, titanium, molybdenum, tungsten, manganese, iron, cobalt, nickel, zinc, magnesium oxide, silicon-dioxide, magnesium hydroxide and Calucium Silicate powder are prepared out according to proportioning by the present invention, can increase the service life, anti-aging degree is high, and withstand voltage is high, and Current Mutual Inductance effect is very good.
Embodiment
In order to make object of the present invention, technical scheme and advantage clearly understand, below in conjunction with embodiment, the present invention is further elaborated.Should be appreciated that specific embodiment described herein only in order to explain the present invention, be not intended to limit the present invention.
The ruhmkorff coil material prescription of current transformer, its material composition is with parts by weight, and filling a prescription is made up of following component: 1 ~ 2 part, platinum, gold 0.2 ~ 0.5 part, silver 0.5 ~ 0.7 part, copper 4 ~ 7 parts, silicon 2 ~ 3 parts, 0.5 ~ 0.7 part, germanium, 3 ~ 6 parts, aluminium, gallium 1 ~ 2 part, 0.1 ~ 0.5 part, magnesium, scandium 3 ~ 5 parts, yttrium 0.2 ~ 0.3 part, titanium 0.4 ~ 0.6 part, molybdenum 2 ~ 3 parts, 2 ~ 3 parts, tungsten, 0.6 ~ 1.2 part, manganese, iron 2 ~ 4 parts, cobalt 3 ~ 5 parts, 6 ~ 7 parts, nickel, 4 ~ 5 parts, zinc, 3 ~ 4 parts, magnesium oxide, silicon-dioxide 2 ~ 5 parts, magnesium hydroxide 2 ~ 3 parts and Calucium Silicate powder 3 ~ 6 parts.
In actually operating, its material composition is with parts by weight, and filling a prescription when being made up of following component is optimum regime: 1 part, platinum, gold 0.2 part, silver 0.5 part, copper 7 parts, silicon 2 parts, 0.7 part, germanium, 6 parts, aluminium, gallium 2 parts, 0.5 part, magnesium, scandium 5 parts, yttrium 0.3 part, titanium 0.4 part, molybdenum 3 parts, 3 parts, tungsten, 0.6 part, manganese, iron 2 parts, cobalt 3 parts, 6 parts, nickel, 4 parts, zinc, 3 parts, magnesium oxide, silicon-dioxide 5 parts, magnesium hydroxide 3 parts and Calucium Silicate powder 6 parts.
The advantage of the ruhmkorff coil material prescription of current transformer provided by the invention is: the ruhmkorff coil of the current transformer that platinum, gold and silver, copper, silicon, germanium, aluminium, gallium, magnesium, scandium, yttrium, titanium, molybdenum, tungsten, manganese, iron, cobalt, nickel, zinc, magnesium oxide, silicon-dioxide, magnesium hydroxide and Calucium Silicate powder are prepared out according to proportioning by the present invention, can increase the service life, anti-aging degree is high, and withstand voltage is high, and Current Mutual Inductance effect is very good.
The foregoing is only preferred embodiment of the present invention, not in order to limit the present invention, all any amendments done within the spirit and principles in the present invention, equivalent replacement and improvement etc., all should be included within protection scope of the present invention.
Claims (2)
1. the ruhmkorff coil material prescription of current transformer, it is characterized in that, its material composition is with parts by weight, and filling a prescription is made up of following component: 1 ~ 2 part, platinum, gold 0.2 ~ 0.5 part, silver 0.5 ~ 0.7 part, copper 4 ~ 7 parts, silicon 2 ~ 3 parts, 0.5 ~ 0.7 part, germanium, 3 ~ 6 parts, aluminium, gallium 1 ~ 2 part, 0.1 ~ 0.5 part, magnesium, scandium 3 ~ 5 parts, yttrium 0.2 ~ 0.3 part, titanium 0.4 ~ 0.6 part, molybdenum 2 ~ 3 parts, 2 ~ 3 parts, tungsten, 0.6 ~ 1.2 part, manganese, iron 2 ~ 4 parts, cobalt 3 ~ 5 parts, 6 ~ 7 parts, nickel, 4 ~ 5 parts, zinc, 3 ~ 4 parts, magnesium oxide, silicon-dioxide 2 ~ 5 parts, magnesium hydroxide 2 ~ 3 parts and Calucium Silicate powder 3 ~ 6 parts.
2. the ruhmkorff coil material prescription of current transformer according to claim 1, it is characterized in that, its material composition is with parts by weight, and filling a prescription is made up of following component: 1 part, platinum, gold 0.2 part, silver 0.5 part, copper 7 parts, silicon 2 parts, 0.7 part, germanium, 6 parts, aluminium, gallium 2 parts, 0.5 part, magnesium, scandium 5 parts, yttrium 0.3 part, titanium 0.4 part, molybdenum 3 parts, 3 parts, tungsten, 0.6 part, manganese, iron 2 parts, cobalt 3 parts, 6 parts, nickel, 4 parts, zinc, 3 parts, magnesium oxide, silicon-dioxide 5 parts, magnesium hydroxide 3 parts and Calucium Silicate powder 6 parts.