CN105219209A - For the environment-friendly type negative ion trimeric cyanamide functional resin of impregnated bond paper - Google Patents
For the environment-friendly type negative ion trimeric cyanamide functional resin of impregnated bond paper Download PDFInfo
- Publication number
- CN105219209A CN105219209A CN201510702308.5A CN201510702308A CN105219209A CN 105219209 A CN105219209 A CN 105219209A CN 201510702308 A CN201510702308 A CN 201510702308A CN 105219209 A CN105219209 A CN 105219209A
- Authority
- CN
- China
- Prior art keywords
- negative ion
- agent
- environment
- bond paper
- friendly type
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to the environment-friendly type negative ion trimeric cyanamide functional resin for impregnated bond paper.After the resin that object is to provide is applied to impregnated bond paper, a large amount of negative ion can be produced, thus effective environmental protect Air quality, and do not affect the decorative pattern sharpness of impregnated bond paper.Technical scheme is: a kind of environment-friendly type negative ion trimeric cyanamide functional resin for impregnated bond paper, and included composition and corresponding weight part are: amine aldehyde resin 100, permeate agent 0.1-0.5, releasing agent 0.15-0.25, solidifying agent 0.08-0.12, rare earth 6-14, tourmaline powder 4-8; K-S dispersion agent 20-30.The composition that this resin comprises and corresponding weight part are: amine aldehyde resin 100, permeate agent 0.3, releasing agent 0.2, solidifying agent 0.1, rare earth 10, tourmaline powder 4, dispersion agent 25.
Description
Technical field
The present invention relates to a kind of trimeric cyanamide functional resin, in particular for the environment-friendly type negative ion trimeric cyanamide functional resin of impregnated bond paper.
Background technology
The environmental issue that existing finishing material all exists, just not single burst size of methanal problem, also has the problem of negatron in a large amount of adsorption chamber.Because new dalle is with a large amount of positive charges, the negatron in air and environment must be absorbed at use these positive charges of starting stage, thus occur in environment that negative ions is not unbalance, cause people's for want of negative ion and occur dizzy uncomfortable sensation in newly-decorated house.Existing market has the method for positron-electron in several balance chamber, and a kind of is the inside this anion function homogenize material being applied to wood-base fibre and particle panel material dash board, and such functional material is closed in sheet material inside, is discharged by penetration of electrons, and effect is poor; Another kind method is that functional material is added into wearing layer, although effect is pretty good, functional material is main affects wearing layer sharpness, the transparency, can change original decorative pattern or color like this; The third method such as adds the measure of negative ion equipment, adds spending but limited efficiency.
Summary of the invention
Technical problem to be solved by this invention is, overcome above-mentioned background technology Problems existing, a kind of environment-friendly type negative ion trimeric cyanamide functional resin of impregnated bond paper is provided, after this resin is applied to impregnated bond paper, a large amount of negative ion can be produced, thus effective environmental protect Air quality, and do not affect the decorative pattern sharpness of impregnated bond paper.
Technical scheme provided by the invention is: a kind of environment-friendly type negative ion trimeric cyanamide functional resin for impregnated bond paper, and included composition and corresponding weight part are:
Amine aldehyde resin 100, permeate agent 0.1-0.5, releasing agent 0.15-0.25, solidifying agent 0.08-0.12, rare earth 6-14, tourmaline powder 4-8; K-S dispersion agent 20-30 (breeze is inorganic materials, and resin is organic materials, and interface must have link bridge to combine, so must add K-S dispersion agent).
The composition that this resin comprises and corresponding weight part are: amine aldehyde resin 100, permeate agent 0.3, releasing agent 0.2, solidifying agent 0.1, rare earth 10, tourmaline powder 4, dispersion agent 25.
The fineness of described rare earth is 200-250 order; The fineness of described tourmaline powder is 200-250 order.
Described rare earth is the one in hamartite, xenotime.
Described solidifying agent be CT0014,710, one in CT0012, HS710.
Described releasing agent is 189, one in W523,856.
Described permeate agent is the one in 883,959.
For the using method of the environment-friendly type negative ion trimeric cyanamide functional resin of impregnated bond paper, for coating the back side of impregnated bond paper.
The invention has the beneficial effects as follows:
1) impregnated bond paper of resin-coated acquisition provided by the invention, overlay process middle-weight rare earths in oven dry to be subject to exciting and to produce a large amount of negatron (negative ion quantity reaches 2000-3000) with tourmaline powder, thus the positive ion balanced in bond paper and base material, maintain positron-electron in ambient air, eliminate peculiar smell, allow new decoration household bring fresh comfortable sensation.
2) rare earth that adopts of the present invention and tourmaline powder, make itself and amine resin have integration, be uniformly dispersed by K-S dispersion agent; Adopt backsize technique thus can not affect wood grain decorative paper sharpness, do not produce aberration, ensure that original using function.
Embodiment
Domestic and international all impregnated bond paper industries are all devoted to reduce free formaldehyde and are reduced burst size and effort, but industry development needs science and technology to walk abreast with innovation to advance, along with the negative ion exploitation being called as VITAMIN in air, Environmental Health and negative ion are valued by the people day by day.For this reason, the present invention adopts and produces the rare earth of negative ion and the tourmaline powder environment-friendly type negative ion trimeric cyanamide functional resin by being mixed to form with amine resin, for printing ornament paper (preferably by immersion coating process, environment-friendly type negative ion trimeric cyanamide functional resin is coated the back side of impregnated bond paper), gained impregnated bond paper is in the former using function situation of guarantee, do not affect the printed decor decorative pattern sharpness on impregnated bond paper surface, through dipping, overlay, airing, rare earth and tourmaline powder is made to produce a large amount of negatron (or illumination excites negative ion), to reach air positive and negative charge balance, eliminate the effects such as peculiar smell.
All raw materials that the present invention adopts are the convenient source that buyable obtains; Wherein: rare earth is hamartite (light rare earths has radioactivity) or xenotime; Permeate agent 883 production firm is Changzhou Jin Yue auxiliary agent company limited; Releasing agent 189 production firm is Changzhou Jin Yue auxiliary agent company limited; Solidifying agent CT0014,710 production firms are Guangzhou Fen Teng Chemical Co., Ltd., and solidifying agent CT0012, HS710 production firm is Dongguan Wei Bang finishing material company limited; K-S dispersion agent production firm is Chuzhou Smet Compound Materials Co., Ltd..
Further illustrate below in conjunction with specific embodiment.
Embodiment 1
One, environment-friendly type negative ion trimeric cyanamide functional resin, the composition comprised and corresponding weight part are:
Amine aldehyde resin 100, permeate agent 0.3, releasing agent 0.2, solidifying agent 0.1, hamartite 10, tourmaline powder 5; K-S dispersion agent.
Two, coating process:
1) dipping decorative paper
Raw material containing following weight part in steeping fluid: leaching urea-formaldehyde resin 100, permeate agent (883) 0.3, solidifying agent (CT0014) 0.2, set time 8 points;
2) be coated with
Adopt the decorative paper (being coated on the back side of decorative paper) after environment-friendly type negative ion trimeric cyanamide functional resin coating dipping, set time 6 points.
Embodiment 2
One, environment-friendly type negative ion trimeric cyanamide functional resin, the composition comprised and corresponding weight part are:
Amine aldehyde resin 100, permeate agent 0.2, releasing agent 0.15, solidifying agent 0.12, hamartite 6, tourmaline powder 4; K-S dispersion agent 20.
Two, coating process:
1) dipping decorative paper
Raw material containing following weight part in steeping fluid: leaching urea-formaldehyde resin 100, permeate agent (883) 0.25, solidifying agent (CT0014) 0.3, set time 10 points;
2) be coated with
Adopt the decorative paper (being coated on the back side of decorative paper) after environment-friendly type negative ion trimeric cyanamide functional resin coating dipping, set time 7 points.
Embodiment 3
One, environment-friendly type negative ion trimeric cyanamide functional resin, the composition comprised and corresponding weight part are:
Amine aldehyde resin 100, permeate agent 0.4, releasing agent 0.25, solidifying agent 0.08, hamartite 14, tourmaline powder 8; K-S dispersion agent 30.
Two, coating process:
1) dipping decorative paper
Raw material containing following weight part in steeping fluid: leaching urea-formaldehyde resin 100, permeate agent (883) 0.35, solidifying agent (CT0014) 0.25, set time 9 points;
2) be coated with
Adopt the decorative paper (being coated on the back side of decorative paper) after environment-friendly type negative ion trimeric cyanamide functional resin coating dipping, set time 8 points.
Embodiment 4
One, environment-friendly type negative ion trimeric cyanamide functional resin, the composition comprised and corresponding weight part are:
Amine aldehyde resin 100, permeate agent 0.4, releasing agent 0.25, solidifying agent 0.08, xenotime 14, tourmaline powder 8; K-S dispersion agent 30.
Two, coating process:
1) dipping decorative paper
Raw material containing following weight part in steeping fluid: leaching urea-formaldehyde resin 100, permeate agent (883) 0.35, solidifying agent (CT0014) 0.25, set time 7 points;
2) be coated with
Adopt the decorative paper (being coated on the back side of decorative paper) after environment-friendly type negative ion trimeric cyanamide functional resin coating dipping, set time 7 points.
Comparison and detection data (be coated with after 48 hours and detect)
Claims (8)
1., for an environment-friendly type negative ion trimeric cyanamide functional resin for impregnated bond paper, included composition and corresponding weight part are:
Amine aldehyde resin 100, permeate agent 0.1-0.5, releasing agent 0.15-0.25, solidifying agent 0.08-0.12, rare earth 6-14, tourmaline powder 4-8; K-S dispersion agent 20-30.
2. the environment-friendly type negative ion trimeric cyanamide functional resin for impregnated bond paper according to claim 1, it is characterized in that: the composition that this resin comprises and corresponding weight part are: amine aldehyde resin 100, permeate agent 0.3, releasing agent 0.2, solidifying agent 0.1, rare earth 10, tourmaline powder 4, dispersion agent 25.
3. the environment-friendly type negative ion trimeric cyanamide functional resin for impregnated bond paper according to claim 1 and 2, is characterized in that: described rare earth is the one in hamartite, xenotime.
4. the environment-friendly type negative ion trimeric cyanamide functional resin for impregnated bond paper according to claim 3, is characterized in that: the fineness of described rare earth is 200-250 order; The fineness of described tourmaline powder is 200-250 order.
5. the environment-friendly type negative ion trimeric cyanamide functional resin for impregnated bond paper according to claim 4, is characterized in that: described solidifying agent be CT0014,710, one in CT0012, HS710.
6. the environment-friendly type negative ion trimeric cyanamide functional resin for impregnated bond paper according to claim 5, is characterized in that: described releasing agent is 189, one in W523,856.
7. the environment-friendly type negative ion trimeric cyanamide functional resin for impregnated bond paper according to claim 6, is characterized in that: described permeate agent is 883, one in A959.
8. the using method of the environment-friendly type negative ion trimeric cyanamide functional resin for impregnated bond paper according to claim 1, for coating the back side of impregnated bond paper.