CN105177244A - Decarbonization preventing paint for workpiece - Google Patents
Decarbonization preventing paint for workpiece Download PDFInfo
- Publication number
- CN105177244A CN105177244A CN201510538036.XA CN201510538036A CN105177244A CN 105177244 A CN105177244 A CN 105177244A CN 201510538036 A CN201510538036 A CN 201510538036A CN 105177244 A CN105177244 A CN 105177244A
- Authority
- CN
- China
- Prior art keywords
- workpiece
- parts
- coating
- decarbonization
- onsio
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses decarbonization preventing paint for a workpiece. The decarbonization preventing paint consists of Na2O.SiO2, Al2O3, Cr2O3, SiC, poly-internal-olefin and graphite powder. According to the decarbonization preventing paint, common industrial raw materials are reasonably mixed, so that oxidation and decarbonization during thermal treatment is greatly reduced; after the workpiece is heated, the paint can be automatically peeled off from the surface of a basal body; and the paint is low in price, and has a good application prospect.
Description
Technical field
The present invention relates to metal heating processing technology field of material technology, particularly relate to the anti-decarburizing coating of a kind of workpiece.
Background technology
In iron and steel heat treatment process, the harm of oxidation and decarburization is very serious, and it makes steel material surface form zone of oxidation, causes the waste of material, increases machining operations amount, and due to the loss of carbon, makes the every mechanical property reduction of steel.Coating protection method has less investment, does not need the features such as complex apparatus, working method are simple, cost is low, adaptability is stronger, applies when being particularly suitable for medium and small sized enterprises' thermal treatment.But automatic spalling resistance when current coating protecting performance and cooling needs to improve.
Summary of the invention
Object of the present invention is exactly defect for above-mentioned existence and provides a kind of workpiece anti-decarburizing coating.The present invention adopts conventional industrial raw material to carry out rational allocation, oxidation and decarbonization during thermal treatment significantly can be reduced, and after workpiece heat, coating can peel off voluntarily from matrix surface, and coating price is cheap simultaneously, has good application prospect.
The anti-decarburizing coating technical scheme of a kind of workpiece of the present invention is that this coating is by Na
2oSiO
2, Al
2o
3, Cr
2o
3, SiC, poly-internal olefin, Graphite Powder 99 composition.
Further, by Na by weight
2onSiO
230-50 part, Al
2o
310-20 part, Cr
2o
310-20 part, SiC10-25 part, poly-internal olefin 20-40 part, Graphite Powder 99 10-30 part composition.
Preferably, by Na by weight
2onSiO
240 parts, Al
2o
315 parts, Cr
2o
315 parts, SiC18 part, poly-internal olefin 30 parts, Graphite Powder 99 20 parts composition.
Or, by Na by weight
2onSiO
245 parts, Al
2o
320 parts, Cr
2o
310 parts, SiC15 part, poly-internal olefin 35 parts, Graphite Powder 99 25 parts composition.
Na
2onSiO
2middle n is 1.2-3.N is preferably 1.8.
Coating smearing thickness on workpiece is 1-3mm.Be preferably 2mm.
Adopt coating of the present invention to carry out workpiece protection, be incorporated to stove and be heated to austenitizing, quenching of coming out of the stove after insulation terminates, the workpiece surface after quenching is sparkling clean, protected non-oxidation, decarburization phenomenon.
A kind of workpiece of the present invention anti-decarburizing coating beneficial effect is: coating material preparation technology of the present invention is simple, screening characteristics is good, oxidation and decarbonization during thermal treatment is significantly reduced, the process redundancy needing heat treated part can be reduced, thus, the non-oxidation decarburization thermal treatment of workpiece can be realized, and after workpiece heat, coating can peel off voluntarily from matrix surface, thus de-scaling operation when decreasing rolling, do not affect steel rolling precision; Coating price is cheap simultaneously, therefore has good application prospect.
embodiment:
In order to understand the present invention better, describe technical scheme of the present invention in detail with specific examples below, but the present invention is not limited thereto.
Embodiment 1
The anti-decarburizing coating of a kind of workpiece of the present invention, by Na by weight
2onSiO
240 parts, Al
2o
315 parts, Cr
2o
315 parts, SiC18 part, poly-internal olefin 30 parts, Graphite Powder 99 20 parts composition.
Na
2onSiO
2middle n is 1.8.
Thickness is 2mm.
Adopt coating of the present invention to carry out workpiece protection, be incorporated to stove and be heated to austenitizing, quenching of coming out of the stove after insulation terminates, the workpiece surface after quenching is sparkling clean, protected non-oxidation, decarburization phenomenon.
Embodiment 2
The anti-decarburizing coating technical scheme of a kind of workpiece of the present invention is, by Na by weight
2onSiO
245 parts, Al
2o
320 parts, Cr
2o
310 parts, SiC15 part, poly-internal olefin 35 parts, Graphite Powder 99 25 parts composition.
Na
2onSiO
2middle n is 1.6.
Coating smearing thickness on workpiece is 2mm.
Adopt coating of the present invention to carry out workpiece protection, be incorporated to stove and be heated to austenitizing, quenching of coming out of the stove after insulation terminates, the workpiece surface after quenching is sparkling clean, protected non-oxidation, decarburization phenomenon.
Embodiment 3
The anti-decarburizing coating technical scheme of a kind of workpiece of the present invention is, by Na by weight
2onSiO
230 parts, Al
2o
310 parts, Cr
2o
320 parts, SiC25 part, poly-internal olefin 20 parts, Graphite Powder 99 10 parts composition.
Na
2onSiO
2middle n is 3.
Coating smearing thickness on workpiece is 1mm.
Adopt coating of the present invention to carry out workpiece protection, be incorporated to stove and be heated to austenitizing, quenching of coming out of the stove after insulation terminates, the workpiece surface after quenching is sparkling clean, protected non-oxidation, decarburization phenomenon.
Claims (8)
1. the anti-decarburizing coating of workpiece, is characterized in that, by Na
2oSiO
2, Al
2o
3, Cr
2o
3, SiC, poly-internal olefin, Graphite Powder 99 composition.
2. the anti-decarburizing coating of a kind of workpiece according to claim 1, is characterized in that, by Na by weight
2onSiO
230-50 part, Al
2o
310-20 part, Cr
2o
310-20 part, SiC10-25 part, poly-internal olefin 20-40 part, Graphite Powder 99 10-30 part composition.
3. the anti-decarburizing coating of a kind of workpiece according to claim 1, is characterized in that, by Na by weight
2onSiO
240 parts, Al
2o
315 parts, Cr
2o
315 parts, SiC18 part, poly-internal olefin 30 parts, Graphite Powder 99 20 parts composition.
4. the anti-decarburizing coating of a kind of workpiece according to claim 1, is characterized in that, by Na by weight
2onSiO
245 parts, Al
2o
320 parts, Cr
2o
310 parts, SiC15 part, poly-internal olefin 35 parts, Graphite Powder 99 25 parts composition.
5. the anti-decarburizing coating of a kind of workpiece according to claim 1, is characterized in that, Na
2onSiO
2middle n is 1.2-3.
6. the anti-decarburizing coating of a kind of workpiece according to claim 1, is characterized in that, Na
2onSiO
2middle n is 1.8.
7. the anti-decarburizing coating of a kind of workpiece according to claim 1, is characterized in that, coating smearing thickness on workpiece is 1-3mm.
8. the anti-decarburizing coating of a kind of workpiece according to claim 1, is characterized in that, coating smearing thickness on workpiece is 2mm.