CN105176436A - 压敏胶粘带的制备方法 - Google Patents
压敏胶粘带的制备方法 Download PDFInfo
- Publication number
- CN105176436A CN105176436A CN201510635533.1A CN201510635533A CN105176436A CN 105176436 A CN105176436 A CN 105176436A CN 201510635533 A CN201510635533 A CN 201510635533A CN 105176436 A CN105176436 A CN 105176436A
- Authority
- CN
- China
- Prior art keywords
- acrylic acid
- parts
- powder
- preparation
- matte acrylic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明一种压敏胶粘带的制备方法,包括以下步骤:第一步.制备雾面丙烯酸胶黏剂:将微米级SiO2粉体、微米级Al2O3粉体和硅烷偶联剂加入丁酮中进行超声波处理获得预分散液;将纳米级SiO2粉体、纳米级Al2O3粉体和异氰酸酯加入预分散液中进行超声波处理获得调制后预分散液;将甲基丙烯酸甲酯、丙烯酸乙酯和二甲基二乙氧基硅烷加入甲苯中进行机械搅拌获得聚合物溶液;将调制后预分散液、聚合物溶液混合并依次加入松香树脂,帖烯树脂,偶氮化合物,获得雾面丙烯酸胶黏剂混合物;将获得的雾面丙烯酸胶黏剂涂覆于基材层的一表面形成雾面丙烯酸胶黏层;在获得的雾面丙烯酸胶黏层另一表面贴合离型材料层。本发明提高了胶黏剂粗糙度,避免了粉体团簇和沉降,提高了与基材结合力。
Description
技术领域
本发明涉及一种压敏胶粘带,特别涉及一种压敏胶粘带的制备方法。
背景技术
压敏胶以其独特的性能和特点已成为胶黏剂中用量最大,应用范围最广的产品。其制品几乎遍布包装、汽车、运输、通讯、电器、建材、机械、航空、轻工、卫生等各领域。目前国内年产量已达到40万吨以上。其中丙烯酸酯类压敏胶由于性能优越,操作方便,价格较低等原因,成为压敏胶中发展最快的主要产品。其制品包括压敏胶黏带、压敏胶黏标签纸和压敏胶黏片三大类,俗称胶带、不干胶标签纸、压敏胶片。制品在加工中包括送卷、涂胶、干燥、复合、收卷和分切等工序。使用粘胶带时,需要该粘胶带在温差变化大的情况下能一直维持粘性,且能容易将胶黏剂从薄膜上剥离。
发明内容
本发明提供一种压敏胶粘带的制备方法,该压敏胶粘带的制备方法在不增加颗粒直径的情况下提高了丙烯酸胶黏剂粗糙度,避免了团簇,也避免了SiO2粉体、Al2O3粉体在体系中的沉降,提高了与基材结合力。
为达到上述目的,本发明采用的技术方案是:一种压敏胶粘带的制备方法,包括以下步骤:
第一步.制备雾面丙烯酸胶黏剂,该雾面丙烯酸胶黏剂进一步通过以下工艺获得:
步骤1.将0.5份微米级SiO2粉体、0.3份微米级Al2O3粉体和1份硅烷偶联剂加入12份丁酮中进行超声波处理获得预分散液;
步骤2.将2.4份纳米级SiO2粉体、1.4份纳米级Al2O3粉体和异氰酸酯1份加入预分散液中进行超声波处理获得调制后预分散液;
步骤3.将甲基丙烯酸甲酯76份、丙烯酸乙酯32份和二甲基二乙氧基硅烷17份加入28份甲苯中进行机械搅拌获得聚合物溶液;
步骤4.将步骤2的调制后预分散液、步骤3的聚合物溶液混合并依次加入松香树脂5份,帖烯树脂4份,偶氮化合物1.4份,进行机械高速搅拌和超声波搅拌,从而获得雾面丙烯酸胶黏剂混合物;
步骤5.将步骤4的雾面丙烯酸胶黏剂混合物在密封的环境中加热获得所述雾面丙烯酸胶黏剂;
第二步.将第一步获得的雾面丙烯酸胶黏剂涂覆于基材层的一表面形成雾面丙烯酸胶黏层;
第三步.在第二步获得的雾面丙烯酸胶黏层另一表面贴合离型材料层。
上述技术方案中进一步改进的技术方案如下:
1.上述方案中,所述纳米级SiO2粉体平均直径为12nm,所述纳米级Al2O3粉体平均至今为30nm;所述微米级SiO2粉体平均直径为1.5~3μm,所述微米级Al2O3粉体平均直径为2~3μm。
2.上述方案中,所述基材层为PE薄膜层、PP薄膜层、PA薄膜层、PC薄膜层中的一种。
3.上述方案中,所述第一步中,将蒸发得到的溶剂收集,冷凝回收。
由于上述技术方案运用,本发明与现有技术相比具有下列优点和效果:
1.本发明压敏胶粘带的制备方法,其采用特定含量的纳米级和微米级SiO2粉体、纳米级和微米级Al2O3粉体和甲基丙烯酸甲酯76份,丙烯酸乙酯32份,二甲基二乙氧基硅烷17份与硅烷偶联剂1份、异氰酸酯1份共同作用,相对单一使用纳米级或微米级SiO2粉体、Al2O3粉体,提高了丙烯酸胶黏剂粗糙度,也有利于SiO2粉体、Al2O3粉体均匀分布和在体系中的分散,避免了团簇;其次,偶氮化合物1.2~1.5份的加入,也避免了微米级SiO2粉体、Al2O3粉体在体系中的沉降,提高了与基材结合力。
2.本发明压敏胶粘带的制备方法,其采用松香树脂5份,帖烯树脂4份与甲基丙烯酸甲酯76份,丙烯酸乙酯32份,二甲基二乙氧基硅烷17份共同作用,避免了了由SiO2粉体、Al2O3粉体加入导致的耐高温性能的下降,提高了耐高温性能,以及在温差变化下的粘度的稳定性,从而提高了产品的可靠性。
具体实施方式
下面结合实施例对本发明作进一步描述:
实施例:一种压敏胶粘带的制备方法,包括以下步骤:
第一步.制备雾面丙烯酸胶黏剂,该雾面丙烯酸胶黏剂进一步通过以下工艺获得:
步骤1.将0.5份微米级SiO2粉体、0.3份微米级Al2O3粉体和1份硅烷偶联剂加入12份丁酮中进行超声波处理获得预分散液;
步骤2.将2.4份纳米级SiO2粉体、1.4份纳米级Al2O3粉体和异氰酸酯1份加入预分散液中进行超声波处理获得调制后预分散液;
步骤3.将甲基丙烯酸甲酯76份、丙烯酸乙酯32份和二甲基二乙氧基硅烷17份加入28份甲苯中进行机械搅拌获得聚合物溶液;
步骤4.将步骤2的调制后预分散液、步骤3的聚合物溶液混合并依次加入松香树脂5份,帖烯树脂4份,偶氮化合物1.4份,进行机械高速搅拌和超声波搅拌,从而获得雾面丙烯酸胶黏剂混合物;
步骤5.将步骤4的雾面丙烯酸胶黏剂混合物在密封的环境中加热获得所述雾面丙烯酸胶黏剂;
第二步.将第一步获得的雾面丙烯酸胶黏剂涂覆于基材层的一表面形成雾面丙烯酸胶黏层;
第三步.在第二步获得的雾面丙烯酸胶黏层另一表面贴合离型材料层;
第四步.烘烤;
第五步.收卷。
上述第一步中,将蒸发得到的溶剂收集,冷凝回收。
上述基材层采用PA薄膜层。
采用上述制备工艺获得的压敏胶粘带,提高了丙烯酸胶黏剂粗糙度,也有利于SiO2粉体、Al2O3粉体均匀分布和在体系中的分散,避免了团簇;其次,偶氮化合物1.2~1.5份的加入,也避免了微米级SiO2粉体、Al2O3粉体在体系中的沉降,提高了与基材结合力。
上述实施例只为说明本发明的技术构思及特点,其目的在于让熟悉此项技术的人士能够了解本发明的内容并据以实施,并不能以此限制本发明的保护范围。凡根据本发明精神实质所作的等效变化或修饰,都应涵盖在本发明的保护范围之内。
Claims (3)
1.一种压敏胶粘带的制备方法,其特征在于:包括以下步骤:
第一步.制备雾面丙烯酸胶黏剂,该雾面丙烯酸胶黏剂进一步通过以下工艺获得:
步骤1.将0.5份微米级SiO2粉体、0.3份微米级Al2O3粉体和1份硅烷偶联剂加入12份丁酮中进行超声波处理获得预分散液;
步骤2.将2.4份纳米级SiO2粉体、1.4份纳米级Al2O3粉体和异氰酸酯1份加入预分散液中进行超声波处理获得调制后预分散液;
步骤3.将甲基丙烯酸甲酯76份、丙烯酸乙酯32份和二甲基二乙氧基硅烷17份加入28份甲苯中进行机械搅拌获得聚合物溶液;
步骤4.将步骤2的调制后预分散液、步骤3的聚合物溶液混合并依次加入松香树脂5份,帖烯树脂4份,偶氮化合物1.4份,进行机械高速搅拌和超声波搅拌,从而获得雾面丙烯酸胶黏剂混合物;
步骤5.将步骤4的雾面丙烯酸胶黏剂混合物在密封的环境中加热获得所述雾面丙烯酸胶黏剂;
第二步.将第一步获得的雾面丙烯酸胶黏剂涂覆于基材层的一表面形成雾面丙烯酸胶黏层;
第三步.在第二步获得的雾面丙烯酸胶黏层另一表面贴合离型材料层。
2.根据权利要求1所述的压敏胶粘带的制备方法,其特征在于:所述基材层为PA薄膜层。
3.根据权利要求1所述的压敏胶粘带的制备方法,其特征在于:所述第一步中,将蒸发得到的溶剂收集,冷凝回收。