CN105174834A - 一种煤矸石轻骨料混凝土 - Google Patents
一种煤矸石轻骨料混凝土 Download PDFInfo
- Publication number
- CN105174834A CN105174834A CN201510527443.0A CN201510527443A CN105174834A CN 105174834 A CN105174834 A CN 105174834A CN 201510527443 A CN201510527443 A CN 201510527443A CN 105174834 A CN105174834 A CN 105174834A
- Authority
- CN
- China
- Prior art keywords
- coal
- gangue
- coal gangue
- aggregate
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种煤矸石轻骨料混凝土,它是由水、水泥、煤矸石骨料、煤矸石砂、减水剂和硅灰混合制作而成,所述的煤矸石骨料为煤矸石大粒径成分,所述的煤矸石砂为制作的煤矸石小粒径成分。本发明具有轻质、高强、保温和耐火等特点,并且变形性能良好,弹性模量较低,在一般情况下收缩和徐变也较大,且可减少基础荷载,因而可使整个建筑物自重减轻;可以将煤矿产生的大量的带有污染性质的煤矸石变废为宝,将其有效利用在道路铺设等市政、建筑施工中,降低了对环境的污染。
Description
技术领域
本发明涉及混凝土制品领域,具体涉及一种煤矸石轻骨料混凝土。
背景技术
煤矸石是煤矿在采掘和洗选过程中遗弃的工业废料,是一种在成煤过程中与煤层伴生的一种含碳量较低、比煤坚硬的黑灰色岩石。据估算,我国每年的排放数量约占煤炭总产量的10%,到目前为止,已累计堆存约48亿t,长期积存和逐年排弃不仅占用了大量的土地,而且在适合的条件下还会自燃,对大气及地下水造成严重的污染。为了高效利用煤矸石资源,而且我国现在正处于基础设施建设的集中期,隧使其替代传统的粗细骨料(碎石、河沙),研究将其利用到建筑行业的方法,以减少煤矸石对环境造成的不良影响,现有以煤矸石为骨料的混凝土在拌合过程中往往因为其质量过轻(具有空隙)会产生漂浮的现象,或者成型后其28d的抗压强度不符合混凝土抗压标准。
发明内容
本发明目的是提供一种煤矸石轻骨料混凝土,它能有效地解决背景技术中所存在的问题。
一种煤矸石轻骨料混凝土,它是由水、水泥、煤矸石骨料、煤矸石砂、减水剂和硅灰混合制作而成,所述的煤矸石骨料为煤矸石大粒径成分,所述的煤矸石砂为制作的煤矸石小粒径成分;
各组分的重量范围是:
由于采用了以上技术方案,本发明具有以下有益效果:具有轻质、高强、保温和耐火等特点,并且变形性能良好,弹性模量较低,在一般情况下收缩和徐变也较大,且可减少基础荷载,因而可使整个建筑物自重减轻;可以将煤矿产生的大量的带有污染性质的煤矸石变废为宝,将其有效利用在道路铺设等市政、建筑施工中,降低了对环境的污染。
具体实施方式
实施例1
一种煤矸石轻骨料混凝土,它是由水、水泥、煤矸石骨料、煤矸石砂、减水剂和硅灰混合制作而成;
各组分添加的重量为:
24小时蒸养后的抗压测试结果为16.6Mpa;
一种煤矸石轻骨料混凝土的制作方法:
1、称量2.6kg水并在水中加入0.013kg的减水剂搅拌均匀;
2、将6.47kg的煤矸石骨料、3.39kg的煤矸石砂、4.55kg的水泥倒入三十升搅拌机中搅拌均匀;
3、倒入2.6kg的水,并搅拌,每隔两三分钟静止一分钟使其充分吸收水分,搅拌三次后即可成型;
4、待24小时后方可拆除模具。
实施例2
一种煤矸石轻骨料混凝土,它是由水、水泥、煤矸石骨料、煤矸石砂、减水剂和硅灰混合制作而成;
各组分添加的重量为:
24小时蒸养后的抗压测试结果为20.8Mpa;
一种煤矸石轻骨料混凝土的制作方法:
1、称量2.3kg水并在水中加入0.05kg的减水剂搅拌均匀;
2、将6.47kg的煤矸石骨料、3.39kg的煤矸石砂、4.55kg的水泥倒入三十升搅拌机中搅拌均匀;
3、倒入2.3kg的水,并搅拌,每隔两三分钟静止一分钟使其充分吸收水分,搅拌三次后即可成型;
4、待24小时后方可拆除模具。
实施例3
一种煤矸石轻骨料混凝土,它是由水、水泥、煤矸石骨料、煤矸石砂、减水剂和硅灰混合制作而成;
各组分添加的重量为:
24小时蒸养后的抗压测试结果为24.1Mpa;
一种煤矸石轻骨料混凝土的制作方法:
1、称量2.4kg水并在水中加入0.035kg的减水剂搅拌均匀;
2、将5.51kg的煤矸石骨料、4.22kg的煤矸石砂、4.77kg的水泥倒入三十升搅拌机中搅拌均匀;
3、倒入2.4kg的水,并搅拌,每隔两三分钟静止一分钟使其充分吸收水分,搅拌三次后即可成型;
4、待24小时后方可拆除模具。
实施例4
一种煤矸石轻骨料混凝土,它是由水、水泥、煤矸石骨料、煤矸石砂、减水剂和硅灰混合制作而成;
各组分添加的重量为:
24小时蒸养后的抗压测试结果为36Mpa;
一种煤矸石轻骨料混凝土的制作方法:
1、称量2.2kg水并在水中加入0.0335kg的减水剂搅拌均匀;
2、将5.51kg的煤矸石骨料、4.5kg的煤矸石砂、4.7kg的水泥倒入三十升搅拌机中搅拌均匀;
3、倒入2.2kg的水,并搅拌,每隔两三分钟静止一分钟使其充分吸收水分,搅拌三次后即可成型;
4、待24小时后方可拆除模具。
最后应说明的是:以上实施例仅用以说明本发明的技术方案,而非对其限制;尽管参照前述实施例对本发明进行了详细的说明,本领域的普通技术人员应当理解,其依然可以对前述各实施例所记载的技术方案进行修改,或者对其中部分技术特征进行等同替换;而这些修改或者替换,并不使相应技术方案的本质脱离本发明各实施例技术方案的精神和范围。
Claims (1)
1.一种煤矸石轻骨料混凝土,其特征在于它是由水、水泥、煤矸石骨料、煤矸石砂、减水剂和硅灰混合制作而成,所述的煤矸石骨料为煤矸石大粒径成分,所述的煤矸石砂为制作的煤矸石小粒径成分;
各组分的重量范围是: