CN105153821A - Adhesive for domestic outer security door prime paint and preparation method thereof - Google Patents
Adhesive for domestic outer security door prime paint and preparation method thereof Download PDFInfo
- Publication number
- CN105153821A CN105153821A CN201510589347.9A CN201510589347A CN105153821A CN 105153821 A CN105153821 A CN 105153821A CN 201510589347 A CN201510589347 A CN 201510589347A CN 105153821 A CN105153821 A CN 105153821A
- Authority
- CN
- China
- Prior art keywords
- parts
- preparation
- adhesive
- hours
- stirring reaction
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides an adhesive for a domestic outer security door prime paint and a preparation method thereof, relating to the technical field of home decoration material production. The invention is characterized in that the adhesive is prepared from the following materials in parts by weight: 4 parts of benzoin powder, 8 parts of n-butyl methylacrylate, 7 parts of hexamethylenetetramine, 11 parts of superfine titanium white, 10 parts of resorcinol, 13 parts of organosilicon leveling agent, 8 parts of low-density polyethylene resin and 13 parts of sodium carboxymethyl cellulose. The adhesive has the advantages of reasonable method and reasonable proportioning, and can prevent oxidization.
Description
Technical field:
The present invention relates to house decoration material produce technical field, be specifically related to tackiness agent of the outer antitheft door primer base of a kind of family expenses and preparation method thereof.
Background technology:
The full name of antitheft door is " anti-theft safety door ".It has both antitheft and safe performance.Specify according to " anti-theft safety door general technical specifications ", qualified antitheft door utilized the portable power tools such as ordinary hand tools and electric hand drill such as chisel, screwdriver, crowbar cannot pry open or open on door leaf the opening of 615 square millimeters in 15 minutes, or in the semicircle of keyed end 150 square millimeters, open the opening of 38 square millimeters.And the lockset that antitheft door uses must be through inspection center of the Ministry of Public Security and detect the qualified Special purpose lock for anti-theft door with anti-drilling function.Antitheft door can make of different materials, but it is qualified only to reach standard detection, and the Men Caineng getting safety precaution product standard product card is called antitheft door.
In life now, antitheft door not only wants excellent property, and its outward appearance is all very important with being convenient to degree of cleaning, has the many antitheft door time for a long time easily to fall paint, or wiping after touching and just have very serious scratch, is also unacceptable so for consumers.
Summary of the invention:
Technical problem to be solved by this invention be to overcome existing technological deficiency provide a kind of method rationally, reasonable ratio, can the tackiness agent and preparation method thereof of the outer antitheft door primer base of a kind of family expenses of anti-oxidation.
Technical problem to be solved by this invention adopts following technical scheme to realize:
Tackiness agent of the outer antitheft door primer base of a kind of family expenses and preparation method thereof, is characterized in that: be made up of the material of following weight part,
Benzoin 4 parts, n-BMA 8 parts, vulkacit H 7 parts, superfine titanium white 11 parts, Resorcinol 10 parts, organosilicon flow agent 13 parts, ldpe resin 8 parts, Xylo-Mucine 13 parts;
Its preparation method comprises,
Benzoin, n-BMA, vulkacit H, superfine titanium white are put into stainless steel cauldron by being warming up to 140 DEG C, stirring reaction 1.5 hours by I;
Resorcinol, organosilicon flow agent, ldpe resin are put into stainless steel cauldron by being warming up to 170 DEG C, stirring reaction 2 hours by II;
III starts working I after 0.5 hour in II work, after then completing at the same time, the material in I and II is put into a new reactor, and with the intensification stirring reaction 5 hours of 30 DEG C/h, the 2nd little adds Xylo-Mucine constantly;
IV after III step completes, and is taken out by material, and shakes mixing 20 minutes, then extruded by twin screw extruder, temperature controls at 100 DEG C, has then extruded rear material left 10 minutes, then put into pulverizer lapping powder and be broken into 130-165 object powder, packaging warehouse-in.
Beneficial effect of the present invention is: the more convenient and result of use of the processing of particle or pulverulence very good; and different materials is processed by various steps such as reaction, concussion, mixing; make the performance of product more excellent; and the service efficiency of material also can improve, so just make product more outstanding.The inventive method rationally, reasonable ratio, can anti-oxidation.
Embodiment:
The technique means realized to make the present invention, creation characteristic, reaching object and effect is easy to understand, setting forth the present invention further below.
Tackiness agent of the outer antitheft door primer base of a kind of family expenses and preparation method thereof, is characterized in that: be made up of the material of following weight part,
Benzoin 4 parts, n-BMA 8 parts, vulkacit H 7 parts, superfine titanium white 11 parts, Resorcinol 10 parts, organosilicon flow agent 13 parts, ldpe resin 8 parts, Xylo-Mucine 13 parts;
Its preparation method comprises,
Benzoin, n-BMA, vulkacit H, superfine titanium white are put into stainless steel cauldron by being warming up to 140 DEG C, stirring reaction 1.5 hours by I;
Resorcinol, organosilicon flow agent, ldpe resin are put into stainless steel cauldron by being warming up to 170 DEG C, stirring reaction 2 hours by II;
III starts working I after 0.5 hour in II work, after then completing at the same time, the material in I and II is put into a new reactor, and with the intensification stirring reaction 5 hours of 30 DEG C/h, the 2nd little adds Xylo-Mucine constantly;
IV after III step completes, and is taken out by material, and shakes mixing 20 minutes, then extruded by twin screw extruder, temperature controls at 100 DEG C, has then extruded rear material left 10 minutes, then put into pulverizer lapping powder and be broken into 130-165 object powder, packaging warehouse-in.
More than show and describe ultimate principle of the present invention and principal character and advantage of the present invention.The technician of the industry should understand; the present invention is not restricted to the described embodiments; what describe in above-described embodiment and specification sheets just illustrates principle of the present invention; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications, and these changes and improvements all fall in the claimed scope of the invention.Application claims protection domain is defined by appending claims and equivalent thereof.
Claims (1)
1. the tackiness agent and preparation method thereof of the outer antitheft door primer base of family expenses, is characterized in that: be made up of the material of following weight part,
Benzoin 4 parts, n-BMA 8 parts, vulkacit H 7 parts, superfine titanium white 11 parts, Resorcinol 10 parts, organosilicon flow agent 13 parts, ldpe resin 8 parts, Xylo-Mucine 13 parts;
Its preparation method comprises,
Benzoin, n-BMA, vulkacit H, superfine titanium white are put into stainless steel cauldron by being warming up to 140 DEG C, stirring reaction 1.5 hours by I;
Resorcinol, organosilicon flow agent, ldpe resin are put into stainless steel cauldron by being warming up to 170 DEG C, stirring reaction 2 hours by II;
III starts working I after 0.5 hour in II work, after then completing at the same time, the material in I and II is put into a new reactor, and with the intensification stirring reaction 5 hours of 30 DEG C/h, the 2nd little adds Xylo-Mucine constantly;
IV after III step completes, and is taken out by material, and shakes mixing 20 minutes, then extruded by twin screw extruder, temperature controls at 100 DEG C, has then extruded rear material left 10 minutes, then put into pulverizer lapping powder and be broken into 130-165 object powder, packaging warehouse-in.