CN105153781B - 一种铝合金门窗划痕修补腻子及其制备方法 - Google Patents
一种铝合金门窗划痕修补腻子及其制备方法 Download PDFInfo
- Publication number
- CN105153781B CN105153781B CN201510573853.9A CN201510573853A CN105153781B CN 105153781 B CN105153781 B CN 105153781B CN 201510573853 A CN201510573853 A CN 201510573853A CN 105153781 B CN105153781 B CN 105153781B
- Authority
- CN
- China
- Prior art keywords
- component
- aluminum alloy
- alloy doors
- tdi
- putty
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种铝合金门窗划痕修补腻子及其制备方法,所述腻子包括A组分和B组分,所述A组分由环氧改性无油醇酸树脂、醋酸丁酯、分散剂、聚酰胺蜡、重质碳酸钙、滑石粉、打磨剂以及二甲基乙醇胺组成,所述B组分为六亚甲基二异氰酸酯(HDI)‑甲苯二异氰酸酯(TDI)混合三聚体,所述A组分与B组分的质量配比为10:1。本发明提供的铝合金门窗划痕修补腻子以环氧改性无油聚酯为基料,对铝合金底材附着力强;干性好、易打磨;易批刮、填充性好;以六亚甲基二异氰酸酯和甲苯二异氰酸酯混合三聚体为交联剂,兼顾了腻子层的干性、柔韧性、打磨性和耐黄变性;混合物料活化期长,施工性能好。
Description
技术背景
在现代建筑外墙面、屋顶、阳台等部位的装饰装修过程中,一些铝合金门窗不可避免地受到刮擦、磕碰,使金属表面产生划痕,影响美观。对于铝合金,铁等金属表面的划伤修复,一般使用双组份腻子(环氧腻子、原子灰),单组份(硝基腻子),醇酸调合腻子。环氧腻子虽然坚固、附着力强,但粘性重、不好批刮,易泛黄;原子灰是不饱和聚酯腻子,施工性好、干燥快、易打磨,但活性稀释剂苯乙烯挥发性强,有毒,且混合好的物料活化期短,易胶化;单组份硝基腻子在金属表面附着力差,腻子层易收缩、塌陷。醇酸腻子干燥慢、附着力差、不易打磨。由于铝合金表面能低,一般的涂料腻子在上面难附着,其金属表面的修复很难,影响其装饰功能,开发一种适用于铝合金门窗表面划痕修补的专用腻子,有着广泛的市场应用前景。
发明内容
为了解决以上存在的技术问题,本发明的目的在于提供一种铝合金门窗划痕修补腻子及其制备方法。
为此,本发明采用如下技术方案:
一种铝合金门窗划痕修补腻子,所述腻子包括A组分和B组分,所述A组分由以下组分组成:
以上百分比为质量百分比;
所述B组分为六亚甲基二异氰酸酯(HDI)-甲苯二异氰酸酯(TDI)混合三聚体。
改性醇酸树脂系指在醇酸树脂中除脂肪酸、多元醇、苯二甲酸酐(或间苯二甲酸)之外,再添加其他成分,经过化学反应构成的新醇酸树脂,如松香改性醇酸树脂、苯乙烯改性醇酸树脂、苯甲酸改性醇酸树脂等,脂肪酸如全部为其他成分所取代,则称之为无油醇酸树脂。
进一步地,所述A组分中环氧改性无油醇酸树脂的酸值≤15mg KOH/g,固体份为63~67%。
进一步地,所述A组分中分散剂为EFKA4010或BYK104S或两者的组合。
进一步地,所述A组分中聚酰胺蜡为帝司巴隆的HX6900-HV或4200或两者的组合。
进一步地,所述A组分中打磨剂为硬脂酸锌或聚乙烯蜡或两者的组合。
进一步地,所述A组分的细度≤50μm。
一种铝合金门窗划痕修补腻子的制备方法,所述制备方法提供铝合金门窗划痕修补腻子,并按照如下步骤制备:
将A组分中的环氧改性无油醇酸树脂、醋酸丁酯以及分散剂投入制漆缸内,在搅拌速度为1200rpm/min下加入聚酰胺蜡并持续搅拌30min,然后依次向制漆缸内投入重质碳酸钙、滑石粉以及打磨剂,在转速为2500rpm/min下高速分散直至细度小于等于50μm,然后再投入二甲基乙醇胺,搅拌均匀;
所述B组分为六亚甲基二异氰酸酯(HDI)-甲苯二异氰酸酯(TDI)混合三聚体;
所述A组分与B组分的质量配比为10:1。
本发明采用如上技术方案,具有如下的优点:
(1)以环氧改性无油聚酯为基料,对铝合金底材附着力强;
(2)干性好、易打磨;
(3)易批刮、填充性好;
(4)以六亚甲基二异氰酸酯和甲苯二异氰酸酯混合三聚体为交联剂,兼顾了腻子层的干性、柔韧性、打磨性和耐黄变性;
(5)混合物料活化期长,施工性能好。
具体实施方式
参照具体实施例对本发明作进一步地详细说明。
实施例1
本实施例中A组分由以下组分组成:
以上百分比为质量百分比;
B组分为六亚甲基二异氰酸酯(HDI)-甲苯二异氰酸酯(TDI)混合三聚体。
一种铝合金门窗划痕修补腻子的制备方法,所述制备方法包括如下制备步骤:
将A组分中的环氧改性无油醇酸树脂、醋酸丁酯以及分散剂投入制漆缸内,在搅拌速度为1200rpm/min下加入聚酰胺蜡并持续搅拌30min,然后依次向制漆缸内投入重质碳酸钙、滑石粉以及打磨剂,在转速为2500rpm/min下高速分散直至细度小于等于50μm,然后再投入二甲基乙醇胺,搅拌均匀;
所述B组分为六亚甲基二异氰酸酯(HDI)-甲苯二异氰酸酯(TDI)混合三聚体;
所述A组分与B组分的质量配比为10:1。
实施例2
本实施例中A组分由以下组分组成:
以上百分比为质量百分比;
B组分为六亚甲基二异氰酸酯(HDI)-甲苯二异氰酸酯(TDI)混合三聚体。
一种铝合金门窗划痕修补腻子的制备方法,所述制备方法包括如下制备步骤:
将A组分中的环氧改性无油醇酸树脂、醋酸丁酯以及分散剂投入制漆缸内,在搅拌速度为1200rpm/min下加入聚酰胺蜡并持续搅拌30min,然后依次向制漆缸内投入重质碳酸钙、
滑石粉以及打磨剂,在转速为2500rpm/min下高速分散直至细度小于等于50μm,然后再投入二甲基乙醇胺,搅拌均匀;
所述B组分为六亚甲基二异氰酸酯(HDI)-甲苯二异氰酸酯(TDI)混合三聚体;
所述A组分与B组分的质量配比为10:1。
实施例3
本实施例中A组分由以下组分组成:
以上百分比为质量百分比;
B组分为六亚甲基二异氰酸酯(HDI)-甲苯二异氰酸酯(TDI)混合三聚体。
一种铝合金门窗划痕修补腻子的制备方法,所述制备方法包括如下制备步骤:
将A组分中的环氧改性无油醇酸树脂、醋酸丁酯以及分散剂投入制漆缸内,在搅拌速度为1200rpm/min下加入聚酰胺蜡并持续搅拌30min,然后依次向制漆缸内投入重质碳酸钙、滑石粉以及打磨剂,在转速为2500rpm/min下高速分散直至细度小于等于50μm,然后再投入二甲基乙醇胺,搅拌均匀;
所述B组分为六亚甲基二异氰酸酯(HDI)-甲苯二异氰酸酯(TDI)混合三聚体;
所述A组分与B组分的质量配比为10:1。
如上述配方及制备方法制备的铝合金门窗划痕修补腻子,涂料性能测试如下表:
Claims (7)
1.一种铝合金门窗划痕修补腻子,其特征在于,所述腻子包括A组分和B组分,所述A组分由以下组分组成:
以上百分比为质量百分比;
所述B组分为六亚甲基二异氰酸酯(HDI)-甲苯二异氰酸酯(TDI)混合三聚体。
2.根据权利要求1所述的一种铝合金门窗划痕修补腻子,其特征在于,所述A组分中环氧改性无油醇酸树脂的酸值≤15mg KOH/g,固体份为63~67%。
3.根据权利要求1所述的一种铝合金门窗划痕修补腻子,其特征在于,所述A组分中分散剂为EFKA4010或BYK104S或两者的组合。
4.根据权利要求1所述的一种铝合金门窗划痕修补腻子,其特征在于,所述A组分中聚酰胺蜡为帝司巴隆的HX6900-HV或4200或两者的组合。
5.根据权利要求1所述的一种铝合金门窗划痕修补腻子,其特征在于,所述A组分中打磨剂为硬脂酸锌或聚乙烯蜡或两者的组合。
6.根据权利要求1所述的一种铝合金门窗划痕修补腻子,其特征在于,所述A组分的细度≤50μm。
7.一种铝合金门窗划痕修补腻子的制备方法,其特征在于,所述制备方法提供权利要求1所述的铝合金门窗划痕修补腻子,并按照如下步骤制备:
将A组分中的环氧改性无油醇酸树脂、醋酸丁酯以及分散剂投入制漆缸内,在搅拌速度为1200rpm/min下加入聚酰胺蜡并持续搅拌30min,然后依次向制漆缸内投入重质碳酸钙、滑石粉以及打磨剂,在转速为2500rpm/min下高速分散直至细度小于等于50μm,然后再投入二甲基乙醇胺,搅拌均匀;
所述B组分为六亚甲基二异氰酸酯(HDI)-甲苯二异氰酸酯(TDI)混合三聚体;
所述A组分与B组分的质量配比为10:1。