CN105130317A - 一种高强度碎屑加气砖 - Google Patents

一种高强度碎屑加气砖 Download PDF

Info

Publication number
CN105130317A
CN105130317A CN201510400785.6A CN201510400785A CN105130317A CN 105130317 A CN105130317 A CN 105130317A CN 201510400785 A CN201510400785 A CN 201510400785A CN 105130317 A CN105130317 A CN 105130317A
Authority
CN
China
Prior art keywords
parts
high strength
raw material
chip
minute
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510400785.6A
Other languages
English (en)
Inventor
王长富
毛东超
王玉童
刘伟
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI FUYANG FULONG BUILDING MATERIALS Co Ltd
Original Assignee
ANHUI FUYANG FULONG BUILDING MATERIALS Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI FUYANG FULONG BUILDING MATERIALS Co Ltd filed Critical ANHUI FUYANG FULONG BUILDING MATERIALS Co Ltd
Priority to CN201510400785.6A priority Critical patent/CN105130317A/zh
Publication of CN105130317A publication Critical patent/CN105130317A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种高强度碎屑加气砖，其是由下述重量份的原料制得：水泥18-28、矿粉5-7、粉煤灰5-8、碎屑70-75、木质素磺酸钙1-2、CTF混凝土增效剂1.8-2.5、铝粉0.3-0.5、羧基丁苯胶乳1-2、硫铝酸钙1-2、氯化石蜡0.2-0.3、硅藻土20-30、膨润土10-20、葡萄糖酸钠3.5-4.8、复配改性混凝土颗粒5-13。

Description

一种高强度碎屑加气砖
技术领域
本发明涉及加气砖领域，确切地说是一种高强度碎屑加气砖。
背景技术
加气砖即“蒸压加气混凝土砌块”，简称加气砖，是通过高温蒸压设备工艺生产的加气混凝土砌块。“加气砖”可以理解为一个简化的或是一个通用的名称。其涵盖的产品范围应该要大一点，即采用包括蒸压在内的其他各种工艺生产的砖品。
现在许多先进地区已经全面禁止红砖使用，设计单位在设计楼房的过程中就标明使用加气砖，如使用红砖，质检部门将不予验收，所以目前加气砖生产厂生产的产品供不应求。
发明内容
本发明的目的在于提供一种高强度碎屑加气砖。
上述目的通过以下方案实现：
一种高强度碎屑加气砖，其特征在于：其是由下述重量份的原料制得：
水泥18-28、矿粉5-7、粉煤灰5-8、碎屑70-75、木质素磺酸钙1-2、CTF混凝土增效剂1.8-2.5、铝粉0.3-0.5、羧基丁苯胶乳1-2、硫铝酸钙1-2、氯化石蜡0.2-0.3、硅藻土20-30、膨润土10-20、葡萄糖酸钠3.5-4.8、复配改性混凝土颗粒5-13;
复配改性混凝土颗粒由下述重量份的原料制得：
硬脂酸0.2-0.5，玉石粉5-7，石墨粉1-2、丙烯酸乳液1-2、页岩粉2-4、UEA混凝土膨胀剂1-2、凹凸棒土1-2、碳纳米管2-4、十二醇硫酸钠2.5-3.7、硼酸锌0.8-1.6、葡萄糖酸钠3.5-4.8、氧化铝1.5-2.4；
复配改性混凝土颗粒的制备方法为：
将所有原料混匀后，于500-700转/分下搅拌10-20分钟后，加适量水分，造粒，颗粒粒径在6-8mm，然后将制好的颗粒于900-920℃下闪烧8-10秒，再取出于200-300℃下烧制5-10分钟后，取出冷却，于浓度为3-6%的盐酸溶液中浸泡10-20分钟，取出，洗净，即得；
所述的一种高强度碎屑加气砖，其特征在于：
制备方法为：
（1)将按重量份混匀粉煤灰、碎屑、木质素磺酸钙、膨润土、葡萄糖酸钠，加入适量水，在30-40℃下200-300转/分钟搅拌5-10分钟后，再加入水泥，50-60转/分搅拌均匀，得混合水泥浆料；
（2）将所得混合水泥浆料与其余原料混匀，加入适量水，浇筑入模成型，后在40-50℃下预养3-5小时，脱模，切割，得砌块坯、蒸压养护后，入库即得。
本发明的有益效果为：本发明采用碎屑取代砂石，解决了加气砖混凝土粘聚性、保水性差的缺点，提高所制得加气砖的强度。
具体实施方式
一种高强度碎屑加气砖，其是由下述重量（kg)的原料制得：
水泥20、矿粉7、粉煤灰8、碎屑70、木质素磺酸钙2、CTF混凝土增效剂2.5、铝粉0.5、羧基丁苯胶乳1、硫铝酸钙2、氯化石蜡0.3、硅藻土20、膨润土20、葡萄糖酸钠4.8、复配改性混凝土颗粒5;
复配改性混凝土颗粒由下述重量（kg)的原料制得：
硬脂酸0.5，玉石粉7，石墨粉1、丙烯酸乳液2、页岩粉2、UEA混凝土膨胀剂2、凹凸棒土2、碳纳米管4、十二醇硫酸钠2.7、硼酸锌0.8、葡萄糖酸钠3.5、氧化铝2.4；
复配改性混凝土颗粒的制备方法为：
将所有原料混匀后，于500转/分下搅拌20分钟后，加适量水分，造粒，颗粒粒径为6-8mm，然后将制好的颗粒于920℃下闪烧10秒，再取出于300℃下烧制10分钟后，取出冷却，于浓度为6%的盐酸溶液中浸泡20分钟，取出，洗净，即得；
所述的一种高强度碎屑加气砖，
制备方法为：
（1)将按重量份混匀粉煤灰、碎屑、木质素磺酸钙、膨润土、葡萄糖酸钠，加入适量水，在40℃下300转/分钟搅拌10分钟后，再加入水泥，60转/分搅拌均匀，得混合水泥浆料；
（2）将所得混合水泥浆料与其余原料混匀，加入适量水，浇筑入模成型，后在50℃下预养5小时，脱模，切割，得砌块坯、蒸压养护后，入库即得。
本实施例所得加气砖的平均容重为580kg/m3,平均值抗压强度为8.8MPa。

Claims (2)

1.一种高强度碎屑加气砖，其特征在于：其是由下述重量份的原料制得：
水泥18-28、矿粉5-7、粉煤灰5-8、碎屑70-75、木质素磺酸钙1-2、CTF混凝土增效剂1.8-2.5、铝粉0.3-0.5、羧基丁苯胶乳1-2、硫铝酸钙1-2、氯化石蜡0.2-0.3、硅藻土20-30、膨润土10-20、葡萄糖酸钠3.5-4.8、复配改性混凝土颗粒5-13;
复配改性混凝土颗粒由下述重量份的原料制得：
硬脂酸0.2-0.5，玉石粉5-7，石墨粉1-2、丙烯酸乳液1-2、页岩粉2-4、UEA混凝土膨胀剂1-2、凹凸棒土1-2、碳纳米管2-4、十二醇硫酸钠2.5-3.7、硼酸锌0.8-1.6、葡萄糖酸钠3.5-4.8、氧化铝1.5-2.4；
复配改性混凝土颗粒的制备方法为：
将所有原料混匀后，于500-700转/分下搅拌10-20分钟后，加适量水分，造粒，颗粒粒径在6-8mm，然后将制好的颗粒于900-920℃下闪烧8-10秒，再取出于200-300℃下烧制5-10分钟后，取出冷却，于浓度为3-6%的盐酸溶液中浸泡10-20分钟，取出，洗净，即得。
2.根据权利要求1所述的一种高强度碎屑加气砖，其特征在于：
制备方法为：
（1)将按重量份混匀粉煤灰、碎屑、木质素磺酸钙、膨润土、葡萄糖酸钠，加入适量水，在30-40℃下200-300转/分钟搅拌5-10分钟后，再加入水泥，50-60转/分搅拌均匀，得混合水泥浆料；
（2）将所得混合水泥浆料与其余原料混匀，加入适量水，浇筑入模成型，后在40-50℃下预养3-5小时，脱模，切割，得砌块坯、蒸压养护后，入库即得。
CN201510400785.6A 2015-07-10 2015-07-10 一种高强度碎屑加气砖 Pending CN105130317A (zh)