CN105130254A - 一种高效水泥助磨剂及其水泥 - Google Patents
一种高效水泥助磨剂及其水泥 Download PDFInfo
- Publication number
- CN105130254A CN105130254A CN201510601448.3A CN201510601448A CN105130254A CN 105130254 A CN105130254 A CN 105130254A CN 201510601448 A CN201510601448 A CN 201510601448A CN 105130254 A CN105130254 A CN 105130254A
- Authority
- CN
- China
- Prior art keywords
- parts
- cement
- grinding aid
- sodium
- ligninsulfonate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种高效水泥助磨剂及其水泥，属于水泥制造领域。所述水泥助磨剂包括如下重量份数的原料：烷基多苷3～9份、三聚磷酸钠2～6份、三异丙醇胺2～6份、聚乙二醇3～9份、醋酸钠2～6份、不饱和聚酯树脂2～6份、二乙二醇胺4～12份、木质磺酸盐3～9份、硫代硫酸钠3～9份、羟乙基二亚乙基三胺2～6份、葡萄糖酸钠3～9份、甘油2～6份。同时，本发明还公开了一种包含如上所述增强型水泥助磨剂的水泥。本发明的高效水泥助磨剂，掺量低、增强效果好，能够改善水泥性能和台时产量，降低水泥生产的成本，本发明的水泥，熟料配比少，可减少环境污染，节约矿产资源。
Description
技术领域
本发明涉及一种高效水泥助磨剂及其水泥，属于水泥制造领域。
背景技术
水泥是人类生活和社会生产中不可缺少的一种建筑材料，其使用范围广，用量大，素有“建筑工业的粮食之称”。但是，水泥生产工业污染大，能源消耗大。为了节能降耗，最佳途径就是在粉磨过程中添加水泥助磨剂，一方面，水泥助磨剂能够提高水泥磨机的台时产量，从而直接降低了粉磨电耗；另一方面，水泥助磨剂还可以激发工业废渣的活性，降低水泥熟料的使用量，从而节省了因生产水泥熟料而造成的煤、电消耗，并降低了大气污染物的排放，提高了工业废渣的利用效率，使其资源化效率提高，在实现“节能”效果的同时，也达到了“减排”的目的。
目前我国助磨剂产品一直普遍存在的组分单一、成本高昂、产品质量稳定性差、对工艺条件适应性不佳等缺陷影响助磨剂的推广应用，因此亟需通过试验研究，开发一类具备助磨效果优异、成本低廉、产品性能稳定、普适性高兼具改善水泥物理性能、激发混合材活性、提高混合材掺量的多功能复合助磨剂。
发明内容
本发明的目的是弥补现有技术的不足，提供一种高效水泥助磨剂及其水泥。本发明的高效水泥助磨剂，掺量低、增强效果好，能够改善水泥性能和台时产量。
本发明解决上述技术问题的技术方案如下：一种高效水泥助磨剂，包括如下重量份数的原料：烷基多苷3～9份、三聚磷酸钠2～6份、三异丙醇胺2～6份、聚乙二醇3～9份、醋酸钠2～6份、不饱和聚酯树脂2～6份、二乙二醇胺4～12份、木质磺酸盐3～9份、硫代硫酸钠3～9份、羟乙基二亚乙基三胺2～6份、葡萄糖酸钠3～9份、甘油2～6份。
在上述技术方案的基础上，本发明还可以做如下改进。
进一步，包括如下重量份数的原料：烷基多苷6份、三聚磷酸钠4份、三异丙醇胺4份、聚乙二醇6份、醋酸钠4份、不饱和聚酯树脂4份、二乙二醇胺8份、木质磺酸盐6份、硫代硫酸钠6份、羟乙基二亚乙基三胺4份、葡萄糖酸钠6份、甘油4份。
进一步，包括如下重量份数的原料：烷基多苷3份、三聚磷酸钠6份、三异丙醇胺2份、聚乙二醇9份、醋酸钠2份、不饱和聚酯树脂6份、二乙二醇胺4份、木质磺酸盐9份、硫代硫酸钠3份、羟乙基二亚乙基三胺6份、葡萄糖酸钠3份、甘油6份。
进一步，包括如下重量份数的原料：烷基多苷9份、三聚磷酸钠2份、三异丙醇胺6份、聚乙二醇3份、醋酸钠6份、不饱和聚酯树脂2份、二乙二醇胺12份、木质磺酸盐3份、硫代硫酸钠9份、羟乙基二亚乙基三胺2份、葡萄糖酸钠9份、甘油2份。
一种包含如上任一项所述增强型水泥助磨剂的水泥。
在上述技术方案的基础上，本发明还可以做如下改进。
进一步，所述助磨剂的质量为水泥质量的0.02～0.1wt％。
进一步，所述助磨剂的质量为水泥质量的0.05wt％。
本发明的有益效果是：
(1)本发明的高效水泥助磨剂，掺量低、增强效果好，能够改善水泥性能和台时产量，降低水泥生产的成本。
(2)采用本发明的高效水泥助磨剂生产的水泥，熟料配比少，可减少环境污染，节约矿产资源。
(3)本发明的价格低廉、生产工艺简单、成本低，适合规模化生产。
具体实施方式
以下结合具体实施例对本发明的原理和特征进行描述，所举实例只用于解释本发明，并非用于限定本发明的范围。
实施例1：
一种高效水泥助磨剂，包括如下重量份数的原料：烷基多苷3份、三聚磷酸钠6份、三异丙醇胺2份、聚乙二醇9份、醋酸钠2份、不饱和聚酯树脂6份、二乙二醇胺4份、木质磺酸盐9份、硫代硫酸钠3份、羟乙基二亚乙基三胺6份、葡萄糖酸钠3份、甘油6份。
一种包含如上所述增强型水泥助磨剂的水泥，所述助磨剂的质量为水泥质量的0.02wt％。
实施例2：
一种高效水泥助磨剂，包括如下重量份数的原料：烷基多苷6份、三聚磷酸钠4份、三异丙醇胺4份、聚乙二醇6份、醋酸钠4份、不饱和聚酯树脂4份、二乙二醇胺8份、木质磺酸盐6份、硫代硫酸钠6份、羟乙基二亚乙基三胺4份、葡萄糖酸钠6份、甘油4份。
一种包含如上所述增强型水泥助磨剂的水泥，所述助磨剂的质量为水泥质量的0.05wt％。
实施例3：
一种高效水泥助磨剂，包括如下重量份数的原料：烷基多苷9份、三聚磷酸钠2份、三异丙醇胺6份、聚乙二醇3份、醋酸钠6份、不饱和聚酯树脂2份、二乙二醇胺12份、木质磺酸盐3份、硫代硫酸钠9份、羟乙基二亚乙基三胺2份、葡萄糖酸钠9份、甘油2份。
一种包含如上所述增强型水泥助磨剂的水泥，所述助磨剂的质量为水泥质量的0.1wt％。
以上所述仅为本发明的较佳实施例，并不用以限制本发明，凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。
Claims (7)
1.一种高效水泥助磨剂，其特征在于，包括如下重量份数的原料：烷基多苷3～9份、三聚磷酸钠2～6份、三异丙醇胺2～6份、聚乙二醇3～9份、醋酸钠2～6份、不饱和聚酯树脂2～6份、二乙二醇胺4～12份、木质磺酸盐3～9份、硫代硫酸钠3～9份、羟乙基二亚乙基三胺2～6份、葡萄糖酸钠3～9份、甘油2～6份。
2.根据权利要求1所述的一种高效水泥助磨剂，其特征在于，包括如下重量份数的原料：烷基多苷6份、三聚磷酸钠4份、三异丙醇胺4份、聚乙二醇6份、醋酸钠4份、不饱和聚酯树脂4份、二乙二醇胺8份、木质磺酸盐6份、硫代硫酸钠6份、羟乙基二亚乙基三胺4份、葡萄糖酸钠6份、甘油4份。
3.根据权利要求1所述的一种高效水泥助磨剂，其特征在于，包括如下重量份数的原料：烷基多苷3份、三聚磷酸钠6份、三异丙醇胺2份、聚乙二醇9份、醋酸钠2份、不饱和聚酯树脂6份、二乙二醇胺4份、木质磺酸盐9份、硫代硫酸钠3份、羟乙基二亚乙基三胺6份、葡萄糖酸钠3份、甘油6份。
4.根据权利要求1所述的一种高效水泥助磨剂，其特征在于，包括如下重量份数的原料：烷基多苷9份、三聚磷酸钠2份、三异丙醇胺6份、聚乙二醇3份、醋酸钠6份、不饱和聚酯树脂2份、二乙二醇胺12份、木质磺酸盐3份、硫代硫酸钠9份、羟乙基二亚乙基三胺2份、葡萄糖酸钠9份、甘油2份。
5.一种包含权利要求1-4任一项所述高效水泥助磨剂的水泥。
6.根据权利要求5所述的水泥，其特征在于，所述助磨剂的质量为水泥质量的0.02～0.1wt％。
7.根据权利要求6所述的水泥，其特征在于，所述助磨剂的质量为水泥质量的0.05wt％。