CN105127568A - 一种双金属复合管焊接技术 - Google Patents
一种双金属复合管焊接技术 Download PDFInfo
- Publication number
- CN105127568A CN105127568A CN201510484849.5A CN201510484849A CN105127568A CN 105127568 A CN105127568 A CN 105127568A CN 201510484849 A CN201510484849 A CN 201510484849A CN 105127568 A CN105127568 A CN 105127568A
- Authority
- CN
- China
- Prior art keywords
- welding
- weld
- gtaw
- weldingvoltage
- speed
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种双金属复合管焊接技术,涉及焊接技术领域,主要包括焊前准备、焊接、焊后热处理三个步骤。本发明的双金属复合管焊接技术能获得较高质量的焊接接头,焊接后无损检测合格率高,能满足高腐蚀环境下复合管的焊接要求。
Description
技术领域
本发明涉及焊接技术领域,更具体地说是一种双金属复合管焊接技术。
背景技术
20钢+316L双金属复合管属于机械复合产品,对焊接质量要求高,主要用于天然气输送,现有的焊接工艺焊接时易产生裂纹和气孔,在高温、高压、高流速、高二氧化碳的腐蚀环境下,双金属复合管容易发生爆管,给气井安全生产和环境带来安全隐患。
发明内容
本发明的目的是为了弥补现有技术的不足,提供一种双金属复合管焊接技术。
本发明的目的是通过以下技术方案实现的:
一种双金属复合管焊接技术,双金属复合管是由基管(20钢)和内衬层(316L不锈钢)两部分组成,包括以下步骤:
(1)焊前准备
第一,焊接方式和焊接材料的选择,焊接分为封焊、根焊、过渡焊、填充层、盖面层五层焊接,封焊采用手工钨极氩弧焊,焊材选用ER309LMo焊丝,焊丝直径为1.6mm;根焊采用手工钨极氩弧焊,焊材选用TR316L焊条,焊条直径为2.6mm;过渡焊采用手工钨极氩弧焊,焊材选用ER309LMo焊丝,焊丝直径为2.0mm;填充层采用焊条手工电弧焊,焊材选用E4315焊条,焊条直径为3.2mm;盖面层采用焊条手工电弧焊,焊材选用E4315焊条,焊条直径为3.2mm;
第二,对管道开V型坡口,对口间隙为2mm,钝边为2mm,坡口大小为60°;
第三,将管道内的杂物清除干净,将坡口内外表面50mm内及层间油污、毛刺、油漆等清除干净,显露出金属光泽;
第四,将焊条在350℃下保温1小时,将焊接坡口两侧150-200mm范围进行150-200℃的预热;
(2)焊接
第一,封焊,采用手工钨极氩弧焊以6-7cm/min的速度进行焊接,焊接电流为70-75A,焊接电压为11-12V;
第二,根焊,采用手工钨极氩弧焊以8-9cm/min的速度进行焊接,焊接电流为80-85A,焊接电压为11-12V;
第三,过渡焊,采用手工钨极氩弧焊以5-6cm/min的速度进行焊接,焊接电流为80-90A,焊接电压为12V;
第四,填充层焊接,采用焊条手工电弧焊以6-7cm/min的速度进行焊接,焊接电流为85-95A,焊接电压为22-26V;
第五,盖面层焊接,采用焊条手工电弧焊以5-6cm/min的速度进行焊接,焊接电流为90-95A,焊接电压为22-26V;
(3)焊后热处理
焊接完毕后立即对焊缝进行保温,保温温度为200-250℃,保温时间为75-90分钟。
本发明的优点在于:
本发明的双金属复合管焊接技术能获得较高质量的焊接接头,焊接后无损检测合格率高,能满足高腐蚀环境下复合管的焊接要求。
具体实施方式
一种双金属复合管焊接技术,双金属复合管是由基管(20钢)和内衬层(316L不锈钢)两部分组成,包括以下步骤:
(1)焊前准备
第一,焊接方式和焊接材料的选择,焊接分为封焊、根焊、过渡焊、填充层、盖面层五层焊接,封焊采用手工钨极氩弧焊,焊材选用ER309LMo焊丝,焊丝直径为1.6mm;根焊采用手工钨极氩弧焊,焊材选用TR316L焊条,焊条直径为2.6mm;过渡焊采用手工钨极氩弧焊,焊材选用ER309LMo焊丝,焊丝直径为2.0mm;填充层采用焊条手工电弧焊,焊材选用E4315焊条,焊条直径为3.2mm;盖面层采用焊条手工电弧焊,焊材选用E4315焊条,焊条直径为3.2mm;
第二,对管道开V型坡口,对口间隙为2mm,钝边为2mm,坡口大小为60°;
第三,将管道内的杂物清除干净,将坡口内外表面50mm内及层间油污、毛刺、油漆等清除干净,显露出金属光泽;
第四,将焊条在350℃下保温1小时,将焊接坡口两侧150mm范围进行150℃的预热;
(2)焊接
第一,封焊,采用手工钨极氩弧焊以6cm/min的速度进行焊接,焊接电流为70A,焊接电压为11V;
第二,根焊,采用手工钨极氩弧焊以8cm/min的速度进行焊接,焊接电流为80A,焊接电压为11V;
第三,过渡焊,采用手工钨极氩弧焊以5cm/min的速度进行焊接,焊接电流为80A,焊接电压为12V;
第四,填充层焊接,采用焊条手工电弧焊以6cm/min的速度进行焊接,焊接电流为85A,焊接电压为22V;
第五,盖面层焊接,采用焊条手工电弧焊以5cm/min的速度进行焊接,焊接电流为90A,焊接电压为22V;
(3)焊后热处理
焊接完毕后立即对焊缝进行保温,保温温度为200℃,保温时间为75分钟。
Claims (1)
1.一种双金属复合管焊接技术,双金属复合管是由基管(20钢)和内衬层(316L不锈钢)两部分组成,其特征在于:包括以下步骤:
(1)焊前准备
第一,焊接方式和焊接材料的选择,焊接分为封焊、根焊、过渡焊、填充层、盖面层五层焊接,封焊采用手工钨极氩弧焊,焊材选用ER309LMo焊丝,焊丝直径为1.6mm;根焊采用手工钨极氩弧焊,焊材选用TR316L焊条,焊条直径为2.6mm;过渡焊采用手工钨极氩弧焊,焊材选用ER309LMo焊丝,焊丝直径为2.0mm;填充层采用焊条手工电弧焊,焊材选用E4315焊条,焊条直径为3.2mm;盖面层采用焊条手工电弧焊,焊材选用E4315焊条,焊条直径为3.2mm;
第二,对管道开V型坡口,对口间隙为2mm,钝边为2mm,坡口大小为60°;
第三,将管道内的杂物清除干净,将坡口内外表面50mm内及层间油污、毛刺、油漆等清除干净,显露出金属光泽;
第四,将焊条在350℃下保温1小时,将焊接坡口两侧150-200mm范围进行150-200℃的预热;
(2)焊接
第一,封焊,采用手工钨极氩弧焊以6-7cm/min的速度进行焊接,焊接电流为70-75A,焊接电压为11-12V;
第二,根焊,采用手工钨极氩弧焊以8-9cm/min的速度进行焊接,焊接电流为80-85A,焊接电压为11-12V;
第三,过渡焊,采用手工钨极氩弧焊以5-6cm/min的速度进行焊接,焊接电流为80-90A,焊接电压为12V;
第四,填充层焊接,采用焊条手工电弧焊以6-7cm/min的速度进行焊接,焊接电流为85-95A,焊接电压为22-26V;
第五,盖面层焊接,采用焊条手工电弧焊以5-6cm/min的速度进行焊接,焊接电流为90-95A,焊接电压为22-26V;
(3)焊后热处理
焊接完毕后立即对焊缝进行保温,保温温度为200-250℃,保温时间为75-90分钟。