CN105086907A - Mildew-proof sealant and preparation method thereof - Google Patents
Mildew-proof sealant and preparation method thereof Download PDFInfo
- Publication number
- CN105086907A CN105086907A CN201510644757.9A CN201510644757A CN105086907A CN 105086907 A CN105086907 A CN 105086907A CN 201510644757 A CN201510644757 A CN 201510644757A CN 105086907 A CN105086907 A CN 105086907A
- Authority
- CN
- China
- Prior art keywords
- parts
- calcium carbonate
- evacuated
- add
- light calcium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention provides a mildew-proof sealant and a preparation method thereof. The mildew-proof sealant adopts a system totally different from a silicone adhesive structure, overcomes the defect of a poor mildew-proof effect of traditional mildew-proof silicone sealants, has brightness like a ceramic glaze after the product is cured, is applied to ground and wall pointing and internal corner trimming of high-grade home space, hotels and business places as well as trimming and beautifying of closestools, kitchen countertops, partitions of shower rooms, balconies, windowsills and the like, and can completely eliminate household hygiene dead angles, and the mildew-proof, the anti-fouling and anti-yellowing performance and the like are improved substantially. Besides the above-mentioned effects, the storage stability is high, and the use performance is basically unchanged after the sealant is stored for two years.
Description
Technical field
The present invention relates to seal gum field, be specifically related to a kind of mildewproof sealant and preparation method thereof.
Background technology
Silicone sealant is the macromolecular compound of polymethyl siloxane and silicone cross-linked formation siloxane bond (Si-O key) tridimensional network, its Si-O key bond energy is up to 425KJ/mol, be far longer than carbon-carbon bond (C-C key) bond energy (345KJ/mol) and carbon-oxygen bond (C-O key) bond energy (351KJ/mol), therefore good stability.There is very strong weathering resistance, add polysiloxane molecule volume large, cohesive energy density(CED) is low, it is made to have excellent stain resistant, resistant of high or low temperature, height hydrophobicity and good ventilation property etc., can within the scope of-60 ~ 200 DEG C life-time service, its mechanical property is as very little in changes such as tensile strength, tear strength, elongation, hardness, is therefore widely used in building, electronics, automobile and other industries.
Since the eighties in 20th century, along with prefabricated, the high stratification of domestic construction and a large amount of employings of glass, metal curtain wall flexible structure and large-scale frame cladding panel structure, larger demand is proposed to high-grade resilient silicone seal gum, and to the balance of its quality, over-all properties, all propose requirements at the higher level to the aspect such as adaptability and operation performance of base material and varying environment, greatly facilitate the fast development of domestic resilient silicone seal gum, the application as the important branch product-mildew-resistant silicone sealant of silicone adhesive also extend to rapidly house ornamentation field.
Along with socioeconomic development, people's quality of the life is improving constantly, also more and more harsher to the requirement of house decoration details.Mildew-resistant silicone sealant has played irreplaceable effect in house decoration as sealing material, but, there is following shortcoming in traditional mildewproof sealant on the market: mildew-resistant timeliness is short, generally within some months to year, loses antimildew function gradually.As seal gum is applied in dark or moist environment such as the interface of Kitchen tap tank and table top, toilet wash platform and body of wall interface, waterproof sealing between bathtub and body of wall, toilet and the interface area on ground, the interface area between living room floors and metope etc., easily produce after short period that mould causes colloid surface to turn black, jaundice, greening or the inconsistent color of other and colloid, affect attractive in appearance.For this reason, above problem is solved in the urgent need to a kind of mildewproof sealant of efficient stable in market, to keep the perfection of fitting up details, allows bacterium spot have no place to hide, and makes healthy clean space.
In addition, also there is the shortcoming of poor storage stability in current mildewproof sealant, the storage life is low, and within general about 1 year, namely performance declines to a great extent, and affects the use of product.
Summary of the invention
The object of the present invention is to provide a kind of mildewproof sealant, adopt and the complete different system of silicone adhesive structure, coordinate high-effective antimold, products solidifying rear surface forms Ceramic glaze fast, fundamentally stopped the possibility of mould-growth, the anti-mold effect of seal gum significantly improves.
For achieving the above object, the present invention by the following technical solutions.
A kind of mildewproof sealant, comprise the component A according to weight ratio 1:1 mixing and B component, wherein, by weight, component A comprises E-44 epoxy resin (viscosity be 20,000 centipoises, oxirane value be 0.44) 30 ~ 35 parts, E-35 epoxy resin (viscosity be 80,000 centipoises, oxirane value be 0.35) 4 ~ 8 parts, 4 ~ 10 parts, softening agent, light calcium carbonate 23 ~ 35 parts, water-ground limestone 20.5 ~ 28 parts, mould inhibitor 0.5 ~ 2 part; B component comprises alkaline curing agent 28 ~ 36 parts, 4 ~ 9 parts, softening agent, polyamide resin 0.5 ~ 3 part, light calcium carbonate 30 ~ 50 parts, water-ground limestone 10 ~ 29.5 parts.
Further, one or more preferably in dinoctyl phthalate (DOP), di-sec-octyl phthalate (DCP), dibutyl phthalate (DBP) of above-mentioned softening agent.
Further, the particle diameter of above-mentioned light calcium carbonate is 50 ~ 90nm.
Further, above-mentioned water-ground limestone is 1000 ~ 2000 orders.
In component A and B component, different softening agent, light calcium carbonate, water-ground limestone can be selected respectively.
Further, above-mentioned mould inhibitor is selected from one or more in 5-chloro-2-methyl-1-isothiazoline-3-ketone, 2-methyl isophthalic acid-isothiazoline-3-ketone, CMIT or MIT.
Further, above-mentioned alkaline curing agent can select the various alkaline curing agent being applicable to epoxy-resin systems, one or more in such as quadrol, hexanediamine, diethylenetriamine, triethylene tetramine, diethylaminopropylamine.
Further, above-mentioned polyamide resin preferred amines value is 300 ~ 350mgKOH/g, 25 DEG C of viscosity is the polyamide resin (relative density preferably 0.98 ± 0.02) of 6000 ~ 10000 centipoises.
Further, the present invention also provides a kind of preparation method of above-mentioned mildewproof sealant, wherein, the preparation method of component A is: E-44 epoxy resin, E-35 epoxy resin, softening agent and mould inhibitor are added planet machine by (1), be evacuated to-0.09MPa, stir 10 minutes under the rotating speed of 150r/min; (2) add light calcium carbonate (before feeding in raw material, feed in raw material again after planet machine internal pressure first returns back to normal pressure at every turn, be again evacuated to specified vacuum degree after reinforced, be lower same), be evacuated to-0.09MPa, stir under the rotating speed of 150r/min; Add water-ground limestone again, be evacuated to-0.09MPa, stir under the rotating speed of 150r/min; In order to improve the degree mixed, several times can be divided to add light calcium carbonate and water-ground limestone, such as, first light calcium carbonate is divided into some parts, add a light calcium carbonate at every turn, be evacuated to-0.09MPa, stir 10 minutes under the rotating speed of 150r/min, and then add lower portion, until light calcium carbonate all adds, again water-ground limestone is divided into some parts, add portion at every turn, be evacuated to-0.09MPa, stir 10 minutes under the rotating speed of 150r/min, and then add lower portion, until water-ground limestone all adds; (3) after light calcium carbonate and water-ground limestone add, be evacuated to-0.09MPa, stir 30 minutes under the rotating speed of 150r/min, discharging, obtains component A;
The preparation method of B component is: alkaline curing agent, softening agent, polyamide resin are added planet machine by (1), are evacuated to-0.09MPa, stirs 10 minutes under the rotating speed of 150r/min; (2) add light calcium carbonate, be evacuated to-0.09MPa, stir under the rotating speed of 150r/min; Add water-ground limestone again, be evacuated to-0.09MPa, stir under the rotating speed of 150r/min; Several times can be divided to add light calcium carbonate and water-ground limestone, such as, first light calcium carbonate is divided into some parts, add a light calcium carbonate at every turn, be evacuated to-0.09MPa, stir 10 minutes under the rotating speed of 150r/min, and then add lower portion, until light calcium carbonate all adds, then water-ground limestone is divided into some parts, adds portion at every turn, be evacuated to-0.09MPa, stir 10 minutes under the rotating speed of 150r/min, and then add lower portion, until water-ground limestone all adds; (3) after light calcium carbonate and water-ground limestone add, be evacuated to-0.09MPa, stir 30 minutes under the rotating speed of 150r/min, discharging, obtains B component.
Compared with prior art, mildewproof sealant of the present invention has the following advantages:
(1) defect of traditional mildew-resistant silicone sealant anti-mold effect difference is overcome, there is after products solidifying the luminance brightness as Ceramic glaze, significantly improve the performances such as mildew-resistant, anti-soil, anti-yellowing change, be applicable to the receipts limit such as high-grade home room, hotel, the metope jointing of commercial location ground, inner corner trim receipts limit, toilet, kitchen countertop, shower house partition, balcony, windowsill beautify, thoroughly solve home care dead angle.
(2) stability in storage is high, and it is substantially constant that product preserves use properties after 2 years.
Embodiment
Embodiment 1:
(hereafter all refer to weight part about component content) by weight, component A comprises: E-44 epoxy resin 30 parts, E-35 epoxy resin 4 parts, 10 parts, DOP softening agent, 50nm light calcium carbonate 35 parts, 1000 order water-ground limestone 20.5 parts, 5-chloro-2-methyl-1-isothiazoline-3-ketone 0.5 part
Preparation method:
(1) in material cylinder, drop into E-44, E-35, DOP and 5-chloro-2-methyl-1-isothiazoline-3-ketone, push planet machine, start, turns fast 150r/min, is evacuated to-0.09MPa and stirs 10 minutes.
(2) first light calcium carbonate is added, divide and add for 5 times, after adding 7 weight part light calcium carbonate powder, start (turns fast 150r/min at every turn, following mixing speed is same), be evacuated to after-0.09MPa stirs 10 minutes and add again next time, to add after light calcium carbonate then medium solid calcium carbonate 10.5 weight part, be evacuated to after-0.09MPa stirs 10 minutes, then add 10 weight part water-ground limestones.
Be evacuated to-0.09MPa after (3) two kinds of calcium carbonate add and stir discharging in 30 minutes, obtain component A.
B component comprises: quadrol 28 parts, 9 parts, DCP softening agent, polyamide resin [amine value (mgKOH/g): 320, viscosity (centipoise/25 DEG C): 6000] 3 parts, 50nm light calcium carbonate 50 parts, 1000 order water-ground limestone 10 parts.
Preparation method:
(1) in material cylinder, drop into quadrol, DCP, polyamide resin, push planet machine, start, turns fast 150r/min, is evacuated to-0.09MPa and stirs 10 minutes.
(2) first light calcium carbonate is added, divide and add for 5 times, after adding 10 weight part light calcium carbonate powder, start (turns fast 150r/min at every turn, following mixing speed is same), be evacuated to after-0.09MPa stirs 10 minutes and add again next time, to add after light calcium carbonate then medium solid calcium carbonate 10 weight part.
Be evacuated to-0.09MPa after (3) two kinds of calcium carbonate add and stir discharging in 30 minutes, obtain B component.
During construction, component A mixes with the weight ratio of B component by 1:1.
Embodiment 2:
Component A comprises: E-44 epoxy resin 35 parts, E-35 epoxy resin 8 parts, 4 parts, DBP softening agent, 90nm light calcium carbonate 23 parts, 2000 order water-ground limestone 28 parts, 2-methyl isophthalic acid-isothiazoline-3-ketone 2 parts.
Preparation method:
(1) in material cylinder, drop into E-44, E-35, DBP and 2-methyl isophthalic acid-isothiazoline-3-ketone, push planet machine, start, turns fast 150r/min, is evacuated to-0.09MPa and stirs 10 minutes.
(2) first light calcium carbonate is added, divide and add for 4 times, after adding 5.75 weight part light calcium carbonate powder, start (turns fast 150r/min at every turn, following mixing speed is same), be evacuated to after-0.09MPa stirs 10 minutes and add again next time, to add after light calcium carbonate then medium solid calcium carbonate 15 weight part, be evacuated to after-0.09MPa stirs 10 minutes and add 13 weight parts again.
Be evacuated to-0.09MPa after (3) two kinds of calcium carbonate add and stir discharging in 30 minutes, obtain component A.
B component comprises: diethylenetriamine 36 parts, 4 parts, DBP softening agent, polyamide resin [amine value (mgKOH/g): 350, viscosity (centipoise/25 DEG C): 10000] 0.5 part, 90nm light calcium carbonate 30 parts, 2000 order water-ground limestone 29.5 parts.
Preparation method:
(1) in material cylinder, drop into diethylenetriamine, DBP, polyamide resin, push planet machine, start, turns fast 150r/min, is evacuated to-0.09MPa and stirs 10 minutes.
(2) first light calcium carbonate is added, divide and add for 5 times, after adding 6 weight part light calcium carbonate powder, start (turns fast 150r/min at every turn, following mixing speed is same), be evacuated to after-0.09MPa stirs 10 minutes and add again next time, to add after light calcium carbonate then medium solid calcium carbonate 15 weight part, be evacuated to after-0.09MPa stirs 10 minutes and add 14.5 weight parts again.
Be evacuated to-0.09MPa after (3) two kinds of calcium carbonate add and stir discharging in 30 minutes, obtain B component.
During construction, component A mixes with the weight ratio of B component by 1:1.
Embodiment 3:
Component A comprises: E-44 epoxy resin 32 parts, E-35 epoxy resin 6 parts, 8 parts, DOP softening agent, 65nm light calcium carbonate 30 parts, 1500 order water-ground limestone 23 parts, CMIT 1 part.
Preparation method:
In material cylinder, drop into E-44, E-35, DOP and CMIT, push planet machine, start, turns fast 150r/min, is evacuated to-0.09MPa and stirs 10 minutes.
First add light calcium carbonate, divide and add for 5 times, after adding 6 weight part light calcium carbonate powder, start (turns fast 150r/min at every turn, following mixing speed is same), be evacuated to after-0.09MPa stirs 10 minutes and add again next time, to add after light calcium carbonate then medium solid calcium carbonate 13 weight part, be evacuated to after-0.09MPa stirs 10 minutes and add 10 weight parts again.
Be evacuated to-0.09MPa after two kinds of calcium carbonate add and stir discharging in 30 minutes, obtain component A.
B component comprises: triethylene tetramine 32 parts, 6.4 parts, DOP softening agent, polyamide resin [amine value (mgKOH/g): 300 viscosity (centipoise/25 DEG C): 8000] 1.6 parts, 65nm light calcium carbonate 40 parts, 1500 order water-ground limestone 20 parts.
Preparation method:
(1) in material cylinder, drop into triethylene tetramine, DOP, polyamide resin, push planet machine, start, turns fast 150r/min, is evacuated to-0.09MPa and stirs 10 minutes.
(2) first light calcium carbonate is added, divide and add for 5 times, after adding 8 weight part light calcium carbonate powder, start (turns fast 150r/min at every turn, following mixing speed is same), be evacuated to after-0.09MPa stirs 10 minutes and add again next time, to add after light calcium carbonate then medium solid calcium carbonate 10 weight part, be evacuated to after-0.09MPa stirs 10 minutes and add 10 weight parts again.
Be evacuated to-0.09MPa after (3) two kinds of calcium carbonate add and stir discharging in 30 minutes, obtain B component.
During construction, component A mixes with the weight ratio of B component by 1:1.
Comparative example 1:
Formula composition: α, alpha, omega-dihydroxy polydimethyl siloxane 30 parts (viscosity is 80,000 centipoises), 3# white oil 10 parts, 60nm active carbonic acid Ca45 part, 1000 order water-ground limestone 15 parts, 5-chloro-2-methyl-1-isothiazoline-3-ketone 2 parts, methyl tributanoximo silane 3.5 parts, vinyl tributyl ketoximyl silane 0.5 part, 3-aminopropyl triethoxysilane 0.6 part, 3-(2,3-epoxy third oxygen) propyl trimethoxy silicane 0.2 part, dibutyl tin laurate 0.08 part.
Preparation method:
(1) first throw α, alpha, omega-dihydroxy polydimethyl siloxane, 3# white oil, to kneader, are opened stirring (turn fast 35r/min, below mediate mixing speed same), are opened intensification valve simultaneously, stir 10 minutes.
(2) divide and add activated Calcium carbonate three times, add at every turn 15 parts afterwards stir within 10 minutes, add again next time.
(3) the follow-up temperature of continuing rising of medium solid calcium carbonate stirs.After material temperature reaches 105 DEG C, be evacuated to-0.09MPa and stir 120 minutes.
(4) shut down, behind emptying shovel limit, continue stirring discharging in 30 minutes.Obtain 1# base-material after grinding, be cooled to normal temperature for subsequent use.
(5) get above-mentioned 1# base-material 100 parts and drop into planet machine material cylinder, drop into 5-chloro-2-methyl-1-isothiazoline-3-ketone, push planet machine.Fast 150r/min (following stirring velocity is same) is turned in start, is evacuated to-0.09MPa (simultaneously ON cycle refrigerated water) and stirs 10 minutes.
(6) shut down, add methyl tributanoximo silane and vinyl tributyl ketoximyl silane under nitrogen protection, vacuumize stirring 15 minutes.
(7) shut down; add 3-aminopropyl triethoxysilane, 3-(2 under nitrogen protection; 3-epoxy third oxygen) propyl trimethoxy silicane and dibutyl tin laurate; vacuumize stirring 25 minutes; stop circulated refrigerated water; continue to vacuumize stirring discharging in 15 minutes, mildew-resistant silicone sealant can be obtained.
Comparative example 2:
Formula composition: α, alpha, omega-dihydroxy polydimethyl siloxane 40 parts (viscosity is 50,000 centipoises), 350 centipoise methyl-silicone oil 5 parts, 80nm activated Calcium carbonate 42 parts, 2000 order water-ground limestone 13 parts, 2-methyl isophthalic acid-isothiazoline-3-ketone 0.5 part, methyl tributanoximo silane 4 parts, vinyl tributyl ketoximyl silane 0.8 part, 3-aminopropyl triethoxysilane 0.6 part, 3-(2,3-epoxy third oxygen) propyl trimethoxy silicane 0.2 part, dibutyl tin laurate 0.06 part.
Preparation method:
(1) first throw α, alpha, omega-dihydroxy polydimethyl siloxane, methyl-silicone oil, to kneader, are opened stirring (turn fast 35r/min, below mediate mixing speed same), are opened intensification valve simultaneously, stir 10 minutes.
(2) divide and add activated Calcium carbonate three times, add at every turn 14 parts afterwards stir within 10 minutes, add again next time.
(3) the follow-up temperature of continuing rising of medium solid calcium carbonate stirs.After material temperature reaches 105 DEG C, be evacuated to-0.09MPa and stir 120 minutes.
(4) shut down, behind emptying shovel limit, continue stirring discharging in 30 minutes.Obtain 2# base-material after grinding, be cooled to normal temperature for subsequent use.
(5) get above-mentioned 2# base-material 100 parts and drop into planet machine material cylinder, drop into 2-methyl isophthalic acid-isothiazoline-3-ketone, push planet machine.Fast 150r/min (following stirring velocity is same) is turned in start, is evacuated to-0.09MPa (simultaneously ON cycle refrigerated water) and stirs 10 minutes.
(6) shut down, add methyl tributanoximo silane and vinyl tributyl ketoximyl silane under nitrogen protection, vacuumize stirring 15 minutes.
(7) shut down; add 3-aminopropyl triethoxysilane, 3-(2 under nitrogen protection; 3-epoxy third oxygen) propyl trimethoxy silicane and dibutyl tin laurate; vacuumize stirring 25 minutes; stop circulated refrigerated water; continue to vacuumize stirring discharging in 15 minutes, mildew-resistant silicone sealant can be obtained.
Comparative example 3:
Formula composition: α, alpha, omega-dihydroxy polydimethyl siloxane 45 parts (viscosity is 50,000 centipoises), 350 centipoise methyl-silicone oil 5 parts, 70nm activated Calcium carbonate 40 parts, 1500 order water-ground limestone 10 parts, CMIT 1 part, methyl tributanoximo silane 5 parts, vinyl tributyl ketoximyl silane 1 part, 3-aminopropyl triethoxysilane 0.5 part, 3-(2,3-epoxy third oxygen) propyl trimethoxy silicane 0.1 part, dibutyl tin laurate 0.05 part.
Preparation method:
(1) first throw α, alpha, omega-dihydroxy polydimethyl siloxane, methyl-silicone oil, to kneader, are opened stirring (turn fast 35r/min, below mediate mixing speed same), are opened intensification valve simultaneously, stir 10 minutes.
(2) divide and add activated Calcium carbonate three times, add at every turn 13.3 parts afterwards stir within 10 minutes, add again next time.
(3) add the follow-up temperature of continuing rising of water-ground limestone to stir.After material temperature reaches 105 DEG C, be evacuated to-0.09MPa and stir 120 minutes.
(4) shut down, behind emptying shovel limit, continue stirring discharging in 30 minutes.Obtain 3# base-material after grinding, be cooled to normal temperature for subsequent use.
(5) get above-mentioned 3# base-material 100 parts and drop into planet machine material cylinder, drop into CMIT, push planet machine.Fast 150r/min (following stirring velocity is same) is turned in start, is evacuated to-0.09MPa (simultaneously ON cycle refrigerated water) and stirs 10 minutes.
(6) shut down, add methyl tributanoximo silane and vinyl tributyl ketoximyl silane under nitrogen protection, vacuumize stirring 15 minutes.
(7) shut down; add 3-aminopropyl triethoxysilane, 3-(2 under nitrogen protection; 3-epoxy third oxygen) propyl trimethoxy silicane and dibutyl tin laurate; vacuumize stirring 25 minutes; stop circulated refrigerated water; continue to vacuumize stirring discharging in 15 minutes, mildew-resistant silicone sealant can be obtained.
Comparative example 4:
Component A comprises: E-44 epoxy resin 28 parts, 16 parts, DOP softening agent, 50nm light calcium carbonate 35 parts, 1000 order water-ground limestone 17.5 parts, pyrocatechol (mould inhibitor) 3.5 parts
Preparation method:
(1) in material cylinder, drop into E-44, DOP and pyrocatechol, push planet machine, start, turns fast 150r/min, is evacuated to-0.09MPa and stirs 10 minutes.
(2) first light calcium carbonate is added, divide and add for 5 times, after adding 7 weight part light calcium carbonate powder, start (turns fast 150r/min at every turn, following mixing speed is same), be evacuated to after-0.09MPa stirs 10 minutes and add again next time, to add after light calcium carbonate then medium solid calcium carbonate 10 weight part, be evacuated to after-0.09MPa stirs 10 minutes, then add 7.5 parts by weight water-ground limestones.
Be evacuated to-0.09MPa after (3) two kinds of calcium carbonate add and stir discharging in 30 minutes, obtain component A.
B component comprises: quadrol 31 parts, 9 parts, DCP softening agent, 50nm light calcium carbonate 50 parts, 1000 order water-ground limestone 10 parts.
Preparation method:
(1) in material cylinder, drop into quadrol, DCP, push planet machine, start, turns fast 150r/min, is evacuated to-0.09MPa and stirs 10 minutes.
(2) first light calcium carbonate is added, divide and add for 5 times, after adding 10 weight part light calcium carbonate powder, start (turns fast 150r/min at every turn, following mixing speed is same), be evacuated to after-0.09MPa stirs 10 minutes and add again next time, to add after light calcium carbonate then medium solid calcium carbonate 10 weight part.
Be evacuated to-0.09MPa after (3) two kinds of calcium carbonate add and stir discharging in 30 minutes, obtain B component.
During construction, component A mixes with the weight ratio of B component by 1:1.
Comparative example 5:
Component A comprises: E-44 epoxy resin 38 parts, E-51 epoxy resin 10 parts, 4 parts, DBP softening agent, 90nm light calcium carbonate 23 parts, 2000 order water-ground limestone 24.7 parts, Whitfield's ointment (mould inhibitor) 0.3 part.
Preparation method:
(1) in material cylinder, drop into E-44, E-51, DBP and Whitfield's ointment, push planet machine, start, turns fast 150r/min, is evacuated to-0.09MPa and stirs 10 minutes.
(2) first light calcium carbonate is added, divide and add for 4 times, after adding 5.75 weight part light calcium carbonate powder, start (turns fast 150r/min at every turn, following mixing speed is same), be evacuated to after-0.09MPa stirs 10 minutes and add again next time, to add after light calcium carbonate then medium solid calcium carbonate 12.7 weight part, be evacuated to after-0.09MPa stirs 10 minutes and add 12 weight parts again.
Be evacuated to-0.09MPa after (3) two kinds of calcium carbonate add and stir discharging in 30 minutes, obtain component A.
B component comprises: diethylenetriamine 36.5 parts, 4 parts, DBP softening agent, 90nm light calcium carbonate 30 parts, 2000 order water-ground limestone 29.5 parts.
Preparation method:
(1) in material cylinder, drop into diethylenetriamine, DBP, push planet machine, start, turns fast 150r/min, is evacuated to-0.09MPa and stirs 10 minutes.
(2) first light calcium carbonate is added, divide and add for 5 times, after adding 6 weight part light calcium carbonate powder, start (turns fast 150r/min at every turn, following mixing speed is same), be evacuated to after-0.09MPa stirs 10 minutes and add again next time, to add after light calcium carbonate then medium solid calcium carbonate 15 weight part, be evacuated to after-0.09MPa stirs 10 minutes and add 14.5 weight parts again.
Be evacuated to-0.09MPa after (3) two kinds of calcium carbonate add and stir discharging in 30 minutes, obtain B component.
During construction, component A mixes with the weight ratio of B component by 1:1.
Comparative example 6:
Component A comprises: E-35 epoxy resin 38 parts, 8 parts, DOP softening agent, 65nm light calcium carbonate 30 parts, 1500 order water-ground limestone 23 parts, copper 8-quinolinolate 1 part.
Preparation method:
In material cylinder, drop into E-35, DOP and copper 8-quinolinolate, push planet machine, start, turns fast 150r/min, is evacuated to-0.09MPa and stirs 10 minutes.
First add light calcium carbonate, divide and add for 5 times, after adding 6 weight part light calcium carbonate powder, start (turns fast 150r/min at every turn, following mixing speed is same), be evacuated to after-0.09MPa stirs 10 minutes and add again next time, to add after light calcium carbonate then medium solid calcium carbonate 13 weight part, be evacuated to after-0.09MPa stirs 10 minutes and add 10 weight parts again.
Be evacuated to-0.09MPa after two kinds of calcium carbonate add and stir discharging in 30 minutes, obtain component A.
B component comprises: triethylene tetramine 32 parts, 8 parts, DOP softening agent, 65nm light calcium carbonate 40 parts, 1500 order water-ground limestone 20 parts.
Preparation method:
(1) in material cylinder, drop into triethylene tetramine, DOP, push planet machine, start, turns fast 150r/min, is evacuated to-0.09MPa and stirs 10 minutes.
(2) first light calcium carbonate is added, divide and add for 5 times, after adding 8 weight part light calcium carbonate powder, start (turns fast 150r/min at every turn, following mixing speed is same), be evacuated to after-0.09MPa stirs 10 minutes and add again next time, to add after light calcium carbonate then medium solid calcium carbonate 10 weight part, be evacuated to after-0.09MPa stirs 10 minutes and add 10 weight parts again.
Be evacuated to-0.09MPa after (3) two kinds of calcium carbonate add and stir shutdown shovel limit after 10 minutes, continue to be evacuated to-0.09MPa and stir discharging in 30 minutes, obtain B component.
During construction, component A mixes with the weight ratio of B component by 1:1.
Mildew resistance contrasts
1, detect according to GB/T1741-2007 paint film fungus resistance assay method, result is as follows:
2, mildew-resistant limit test is on the spot observed:
Method: above-mentioned sample glue is beaten adhesive tape respectively on solid wood block, makes test specimen, adhesive tape diameter 6 millimeters, solidify after 7 days, under test specimen being placed in public hand washing sink water tap, water tap and hand washing sink use as usual, the mouldy situation of adhesive tape of record different time sections, Details as Follows:
Stability in storage track data:
1, data are detected in three days after sample making:
2, the sample storage detection data of 6 months:
3, the sample storage detection data of 12 months:
4, the sample storage detection data of 24 months:
In above-mentioned comparative example, comparative example 1 ~ 3 is conventional mildew-resistant silicone sealant formula, and comparative example 4 ~ 6 is conventional mildew-resistant epoxy sealing glue formula.No matter can be found out by above Data Comparison, be silicone sealant or epoxy sealing glue, the general very difficult requirement simultaneously meeting high-effect anti-mould, standing storage.The present invention is by the optimization to formula, and not only have the luminance brightness as Ceramic glaze after sealing glue solidifying, significantly improve the performances such as mildew-resistant, anti-soil, anti-yellowing change, also have good preservation stability, after product preserves 2 years, use properties is substantially constant.
Claims (8)
1. a mildewproof sealant, it is characterized in that, comprise the component A according to weight ratio 1:1 mixing and B component, wherein, by weight, component A comprises E-44 epoxy resin 30 ~ 35 parts, E-35 epoxy resin 4 ~ 8 parts, 4 ~ 10 parts, softening agent, light calcium carbonate 23 ~ 35 parts, water-ground limestone 20.5 ~ 28 parts, mould inhibitor 0.5 ~ 2 part; B component comprises alkaline curing agent 28 ~ 36 parts, 4 ~ 9 parts, softening agent, polyamide resin 0.5 ~ 3 part, light calcium carbonate 30 ~ 50 parts, water-ground limestone 10 ~ 29.5 parts.
2. mildewproof sealant as claimed in claim 1, it is characterized in that, described softening agent is selected from one or more in dinoctyl phthalate, di-sec-octyl phthalate, dibutyl phthalate.
3. mildewproof sealant as claimed in claim 1, it is characterized in that, the particle diameter of described light calcium carbonate is 50 ~ 90nm.
4. mildewproof sealant as claimed in claim 1, it is characterized in that, described water-ground limestone is 1000 ~ 2000 orders.
5. mildewproof sealant as claimed in claim 1, it is characterized in that, described mould inhibitor is selected from one or more in 5-chloro-2-methyl-1-isothiazoline-3-ketone, 2-methyl isophthalic acid-isothiazoline-3-ketone, CMIT or MIT.
6. mildewproof sealant as claimed in claim 1, it is characterized in that, described alkaline curing agent is selected from one or more in quadrol, hexanediamine, diethylenetriamine, triethylene tetramine, diethylaminopropylamine.
7. mildewproof sealant as claimed in claim 1, is characterized in that, the amine value of described polyamide resin is 300 ~ 350mgKOH/g, 25 DEG C of viscosity are 6000 ~ 10000 centipoises.
8. the preparation method of the mildewproof sealant as described in as arbitrary in claim 1 ~ 7, is characterized in that,
The preparation method of component A is: E-44 epoxy resin, E-35 epoxy resin, softening agent and mould inhibitor are added planet machine by (1), are evacuated to-0.09MPa, stirs 10 minutes under the rotating speed of 150r/min; (2) add light calcium carbonate, be evacuated to-0.09MPa, stir under the rotating speed of 150r/min; Add water-ground limestone again, be evacuated to-0.09MPa, stir under the rotating speed of 150r/min; (3) after light calcium carbonate and water-ground limestone add, be evacuated to-0.09MPa, stir 30 minutes under the rotating speed of 150r/min, discharging, obtains component A;
The preparation method of B component is: alkaline curing agent, softening agent, polyamide resin are added planet machine by (1), are evacuated to-0.09MPa, stirs 10 minutes under the rotating speed of 150r/min; (2) add light calcium carbonate, be evacuated to-0.09MPa, stir under the rotating speed of 150r/min; Add water-ground limestone again, be evacuated to-0.09MPa, stir under the rotating speed of 150r/min; (3) after light calcium carbonate and water-ground limestone add, be evacuated to-0.09MPa, stir 30 minutes under the rotating speed of 150r/min, discharging, obtains B component.