CN105063996A - Environment-friendly dyeing and finishing technology for mulberry silk fabric - Google Patents
Environment-friendly dyeing and finishing technology for mulberry silk fabric Download PDFInfo
- Publication number
- CN105063996A CN105063996A CN201510498737.5A CN201510498737A CN105063996A CN 105063996 A CN105063996 A CN 105063996A CN 201510498737 A CN201510498737 A CN 201510498737A CN 105063996 A CN105063996 A CN 105063996A
- Authority
- CN
- China
- Prior art keywords
- light
- mulberry silk
- silk fabrics
- dyeing
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an environment-friendly dyeing and finishing technology for mulberry silk fabric. The technology comprises procedures of pretreatment, presetting, chitosan modification treatment, dyeing, mordant removal, soaping, fixation, after-treatment, drying, setting, calendaring and winding. According to the technology, helicase and alpha-amylase are adopted for pretreatment, chitosan modification treatment is adopted before dyeing, properties of the mulberry silk fabric are modified fundamentally, and the dye uptake of the fabric is increased; in the dyeing procedure, large amounts of alkaline substances and inorganic salt are not used, a leveling agent and a dispersing agent are added, the levelling property is improved, environmental pollution is avoided due to usage of natural dye, and the requirement of environment protection is met; self-cleaning treatment is added during after-treatment, so that the self-cleaning capability, the wrinkle resistance and the washing fastness of the fabric are improved; the whole technology is environment-friendly and pollution-free.
Description
Technical field
The present invention relates to a kind of environment-friendly type dyeing and finishing technology of Light of Mulberry Silk Fabrics.
Background technology
Fiber is divided into chemical fibre and natural fabric, chemical fibre has fast light, wear-resisting, easily wash easily dry, do not go rotten, the advantage such as not damaged by worms, be widely used in and manufacture clothing fabric, filter cloth, conveyer belt, rotary hose, rope, fishing net, electric insulated, medical treatment suture, tyre cord and parachute etc., natural fabric refer to nature exist and growth, there is the fiber that weaving is worth, chemical fibre is raw material with the macromolecular compound of natural polymer or Prof. Du Yucang, through preparing spinning solution, the fiber of what the operation such as spinning and post processing obtained have textile performance.
Mulberry silk fiber is senior textile raw material, fiber finer and soft, has preferably stretching property by force.As native protein fibrid, its fabric outward appearance elegant made, gloss gracefulness is soft, and the smooth exquisiteness of texture is worn elegant, smooth, ventilative, the dark favor by consumers in general, is therefore also widely used in clothing and manufactures field of textiles.
Traditional dyeing all adopts chemical dye to dye usually, but the pollution of chemical dye to environment is larger, in order to reduce environmental pollution, begin one's study at present and adopt natural dye to dye, and usually dye at a lower temperature when adopting natural dye to dye, also just lower to the requirement of equipment like this, energy consumption also can reduce.
But the Color of natural dye is poor, its fixing degree of the fabric dyed is lower, usually in dyeing course, a large amount of soda ash and inorganic salts are added in order to improve fixing degree, this brings larger difficulty to the treatment of dyeing wastewater of high salinity, can ecological environment be destroyed as directly discharged, causing the salinization of soil.Use natural dye usually also can use some mordants containing metal ion simultaneously; although the use of mordant can improve Color; if but mordant can not be removed completely in post processing; not only can bring pollution to environment; the coloured light of fabric also can be made simultaneously mostly to become dim, affect vividness and the aesthetic property of DYED FABRICS.In addition, in order to reduce the dyeing difficulty of follow-up dyeing, usually need before dyeing to carry out preliminary treatment to fabric, but current preliminary treatment is all adopt the alkaline solution such as sodium hydrosulfite, sodium carbonate to carry out High Temperature Pre process substantially, larger to the damage of fiber.Simultaneously; usually can notice in current fabric post-treatment operation that flexibility arranges; but otherwise arrangement is ignored; the automatically cleaning ability of such as fabric; if fabric has automatically cleaning ability; so its clean aspect after polluting again can be easier, can avoid adopting strong dirt-removing agent carry out decontamination or long-time immersion and make the life-span of fabric impaired.
Summary of the invention
Goal of the invention: the problems referred to above existed for prior art, the object of this invention is to provide a kind of environment-friendly type dyeing and finishing technology of Light of Mulberry Silk Fabrics.
Technical scheme: for achieving the above object, the technical solution used in the present invention is as follows:
An environment-friendly type dyeing and finishing technology for Light of Mulberry Silk Fabrics, comprises the following steps:
(1) pre-treatment: pre-treatment is carried out to Light of Mulberry Silk Fabrics, be specially: use urea 1-1.5g/L, non-phosphorus degreasing agent 4.5-5.5g/L, scouring agent 1-1.5g/L, 30% hydrogen peroxide 8-10g/L, glusulase 8-10g/L, α-amylase 8-10g/L, carry out ultrasonic process 1-2min; bath raio is 30:1; ultrasonic frequency is 45Hz, refill clear water and wash 2 times, then dry after process terminates in the ultrasound bath of 40 DEG C; Scouring agent is the ZJ-CH58 low-temperature refining agent that Guangzhou Zhuan Jie Chemical Co., Ltd. produces.
(2) pre-setting: pre-setting process is carried out to Light of Mulberry Silk Fabrics, add heat resistanceheat resistant flavescence agent 8-10g/L during sizing, setting temperature is 150-160 DEG C, and the speed of a motor vehicle is 20-30m/min, overfeeding 5-10%; The heat resistanceheat resistant xanthochromia agent FK-161 that Beijing Chemical Co., Ltd. in Textile produces;
(3) chitin modified process: to put into mass fraction be 0.5%(owf by the Light of Mulberry Silk Fabrics after sizing) chitosan solution carry out modification, bath raio 30:1, normal temperature process 60min, then washes, and finally dries at 100 DEG C;
(4) dye: Light of Mulberry Silk Fabrics is carried out dyeing process, be specially: under room temperature, fabric is immersed in the clear water of dyeing machine, then in water-bath, bleeding agent 1.5-2.5g/L is added, diffusant DN0.8-1.2g/L, levelling agent 1.5-2.5g/L, natural dye 1.5-2.5%(owf), mordant ferrous sulfate 3-5%(owf), imvite 3-5g/L, shitosan 3-5g/L, bath raio 20:1, and by pH buffer Acetic acid-sodium acetate, the pH value of dye liquor is adjusted to 5.5-6, cyclically charging material 20min, then dyeing machine heats up, programming rate is 1 DEG C/min, when temperature rises to 60 DEG C, insulation dyeing 20min, dyeing machine continues to heat up, programming rate is 0.5 DEG C/min, when being warming up to 70 DEG C, insulation dyeing 20min, dyeing machine continues to heat up, programming rate is 1 DEG C/min, when being warming up to 85 DEG C, insulation dyeing 40min, then dyeing machine cooling, cooling rate is 2 DEG C/min, when temperature is down to 40 DEG C, dyestuff is discharged also injected clear water again, 15min is rinsed with clear water, the levelling agent FK-482 that levelling agent adopts Beijing Chemical Co., Ltd. in Textile to produce,
(5) mordant is removed: the Light of Mulberry Silk Fabrics after dyeing being put into mass fraction is carry out mordant cleaning in the oxalic acid aqueous solution of 0.3-0.4%, and cleaning temperature is 70-80 DEG C, scavenging period 10min, rinses once after process terminates with clear water again;
(6) soap: will the Light of Mulberry Silk Fabrics lauryl sodium sulfate 1g/L after mordant be removed, polyvinylpyrrolidone 4.5g/L, AEO-94.5g/L, ethanol 10-20g/L; bath raio is 40:1, rinses 30min at 50-60 DEG C, finally rinses 15min with the clear water of 40-50 DEG C again;
(7) fixation: the Light of Mulberry Silk Fabrics after cleaning is put into fixation liquid and carries out fixation, described fixation liquid contains salt 3-5g/L, colophony powder 3-5g/L, ethanol 10-20g/L, bath raio is 20:1, color fixing temperature 50-60 DEG C, the fixation time is 30-40min, and then temperature reduces, and 40-50 DEG C is rinsed 15min with clear water, then by dryer at 80 DEG C of preliminary drying 4min, then bake 3min at 110 DEG C;
(8) Final finishing: Light of Mulberry Silk Fabrics is carried out Final finishing, is specially:
A () antibiotic finish: Light of Mulberry Silk Fabrics is carried out antibacterial treatment, uses shitosan 3-5g/L, citric acid 3-5g/L, softener 1-2g/L, ethanol 20-30g/L, in the water-bath of 30-40 DEG C, process 20-30min, and bath raio is 20:1;
B () mixing arranges: Light of Mulberry Silk Fabrics is put into mixed treating liquid and processes, use crease and shrink resistant finishing agent GFR-82-4g/L, UV resistance finishing agent UV-BS3-4g/L, in the water-bath of 30-40 DEG C, process 20-30min, bath raio is 20:1; Crease and shrink resistant finishing agent GFR-8 is that Nantong C&T Textile Technology Co., Ltd. produces; UV resistance finishing agent UV-BS is that Nantong C&T Textile Technology Co., Ltd. produces;
(c) flame-proof treatment: Light of Mulberry Silk Fabrics is put into fire-retardant treatment liquid and processes, with 2,3-epoxypropyltrimethylchloride chloride 20-30g/L, imvite 3-5g/L, isopropyl alcohol 15-20g/L, in the water-bath of 50-70 DEG C, process 40-60min, bath raio is 30:1;
(d) self-cleaning finishing: Light of Mulberry Silk Fabrics is put into containing the chloro-2-hydroxypropyl-trimethyl ammonium chloride 15-20g/L of 3-, flood 2-3h in the water-bath of NaOH 8-10g/L at 70-80 DEG C, then wash, then 85 DEG C of oven dry; Then the Light of Mulberry Silk Fabrics of oven dry is put into containing 1,2,3,4-BTCA 8-10g/L, sodium hypophosphite 8-10g/L, water-bath at 70-80 DEG C, flood 2-3h, then wash, then 85 DEG C of oven dry; Then Light of Mulberry Silk Fabrics is impregnated into TiO
2with SiO
2mol ratio be 50: 1, concentration is the TiO of 0.2mol/l
2/ SiO
2in the hydrosol, room temperature immersion 10min, then bakes and banks up with earth 3min at 120 DEG C, finally rinses 2 times with clear water again;
(9) dry: the Light of Mulberry Silk Fabrics after Final finishing is put into dryer and carries out drying and processing, bake out temperature 100-110 DEG C, locomotive speed is 65-70m/min;
(10) shape: the Light of Mulberry Silk Fabrics of oven dry is carried out heat treatment, adds heat resistanceheat resistant flavescence agent 8-10g/L during sizing, anti-phenol flavescence agent 8-10g/L, setting temperature 155-165 DEG C, locomotive speed is 25-30m/min, overfeeding 5-8%; The heat resistanceheat resistant xanthochromia agent FK-161 that Beijing Chemical Co., Ltd. in Textile produces and anti-phenol xanthochromia agent FK-162;
(11) calendering: the Light of Mulberry Silk Fabrics after sizing is put into calender and carries out calendering process, calendering temperature 115-125 DEG C, locomotive speed is 20-25m/min;
(12) rolling: Light of Mulberry Silk Fabrics is carried out rolling.
Non-phosphorus degreasing agent in described step 1 is that without phosphorus neutrality is deoiled clever TF-104M.The without phosphorus neutrality clever TF-104M that deoils is that the development of evil in febrile disease board that Zhejiang Province Chuanhua Co., Ltd produces deoils clever TF-104M.
Bleeding agent in described step 4 is penetrating agent JFC.
Natural dye in described step 4 is chrysanthemum.
Softener in described step 8 is ester based quaternary ammonium salt softener.Ester based quaternary ammonium salt softener can select the softeners such as EQ400 or EQ200 of Korea S LG chemistry, and harmless to skin gentleness, make Light of Mulberry Silk Fabrics fabric have flexibility and antistatic behaviour, environmentally friendly, soft effect is good.
Beneficial effect: compared with prior art, the present invention has following conspicuousness beneficial effect:
1, the present invention adopts ultrasonic wave to carry out pre-treatment when pre-treatment, and compared to the pre-treatment of routine, treatment temperature step-down, time shorten, the rate of destarch simultaneously improves, whiteness improves, and comprehensive pretreatment better effects if, does not add the material that the alkalescence of soda ash is stronger simultaneously, the pH value of pretreatment liquid is made finally to remain on neutral left and right, processing environment is gentle, little to the damage of Light of Mulberry Silk Fabrics, Environmentally-friephosphorus-free phosphorus-free degreaser centered by the degreaser simultaneously adopted, little to the pollution of environment, more environmental protection; Adopt simultaneously glusulase and α-amylase carry out with the use of, not only destarch is effective, can also improve the wettability of fabric simultaneously, and two kinds of enzymes coordinate the use of hydrogen peroxide, can improve the whiteness of fabric simultaneously, be beneficial to follow-up Color;
2, the present invention is before dyeing process, chitin modified process is carried out to fabric, fundamentally modification is carried out to the performance of Light of Mulberry Silk Fabrics, overcome some defects himself existed, also add the dye uptake of fabric simultaneously, reduce the difficulty of follow-up staining procedure, shitosan process simultaneously can also improve the anti-microbial property of fabric; After this step process, the dye-uptake of its fabric and degree of fixation can improve about 30%; Make it go for low salt dyeing simultaneously, reduce the difficulty of follow-up staining procedure, reduce the salt content in dyeing waste water, reduce environmental pollution;
3, the present invention is in dyeing process, do not use a large amount of alkaline matters and inorganic salts, have employed natural dye, avoid environmental pollution, meet the requirement of environmental protection, add dye leveller and bleeding agent, diffusant, equalization is improved, add imvite in dyeing course, play fire retardation; Add anti-creasing agent and play wrinkle resistant effect; Simultaneously in whole dyeing course, temperature is no more than 85 DEG C, and temperature is lower, lower to equipment requirement, and energy consumption is less;
4, the present invention is in dyeing process, strictly controls intensification rate of temperature fall, and dyeing time, and fabric is dyeed, and firmness is high, even dyeing, dye stability are good;
5, the present invention adds color fixing process after dyeing, have employed the natural color-fixing agent colophony powder of environmental protection, avoid environmental pollution, further increase the fixing degree of Light of Mulberry Silk Fabrics in color fixing process; What adopt before fixation soaps in technique, have employed lauryl sodium sulfate, polyvinylpyrrolidone and AEO-9 carries out composite, anti-staining, removal floating color are effective, make soap poststaining fabric color fastness to washing, colour fastness to rubbing simultaneously, especially fastness to wet rubbing all significantly strengthens, and also reduces simultaneously; Carry out going mordant process to fabric before technique of soaping, employing oxalic acid aqueous solution can get rid of the mordant that fabric adheres in dyeing course well completely, thus avoid environmental pollution, ensure that attractive in appearance, the vividness of fabric color, and oxalic acid belongs to organic monoacid, lower to human injury;
6, present invention adds Final finishing science and engineering skill, improve the performances such as the crease and shrink resistance performance of fabric, COLOR FASTNESS, pliability, uviolresistance, antibiotic property, resistance combustion; Simultaneously in arrangement process, when multiple finishing agent mixing, the various finishing agent selected is while playing respective effect, and can also play the effect strengthened mutually, cooperative effect is good; Select imvite as fire retardant, add quaternary ammonium salt simultaneously and modification is carried out to imvite, make flame retardant effect better, non-environmental-pollution; In addition, in finishing process, add self-cleaning finishing, first ionomer process is carried out to fabric, then adopts TiO
2/ SiO
2the hydrosol processes, and reaches the automatically cleaning ability that improve fabric, also improve its water-fastness firmness, and its wrinkle resistance is also further enhanced simultaneously, which greatly enhances the service life of fabric and overall combination property;
7, the present invention all employ the yellow reagent of resistance in pre-setting, sizing, makes final fabric be not easy to turn yellow;
8, the present invention have employed calendering process further, makes the bright and clean smooth of fabric, can improve feel further, makes feel more soft fluffy, ensures that washing shrinkage meets the demands simultaneously;
9, the temperature of several operation such as preliminary treatment of the present invention, dyeing, sizing is relatively more steady, and such process conditions jumping characteristic is less, and technics comparing is steady, makes the final performance of fabric more stable;
10, efficient, the environmental protection of dyeing of the present invention, technique are simple, and simple operation, can promote the use of.
Detailed description of the invention
Below in conjunction with embodiment, technical solution of the present invention is described in further detail and completely.
embodiment 1
An environment-friendly type dyeing and finishing technology for Light of Mulberry Silk Fabrics, comprises the following steps:
(1) pre-treatment: pre-treatment is carried out to Light of Mulberry Silk Fabrics, be specially: use urea 1g/L, non-phosphorus degreasing agent TF-104M4.5g/L, scouring agent 1g/L, 30% hydrogen peroxide 8g/L, glusulase 8g/L, α-amylase 8g/L, carry out ultrasonic process 1-2min; bath raio is 30:1; ultrasonic frequency is 45Hz, refill clear water and wash 2 times, then dry after process terminates in the ultrasound bath of 40 DEG C;
(2) pre-setting: pre-setting process is carried out to Light of Mulberry Silk Fabrics, add heat resistanceheat resistant flavescence agent FK-1618g/L during sizing, setting temperature is 150 DEG C, and the speed of a motor vehicle is 20m/min, overfeeding 5%;
(3) chitin modified process: to put into mass fraction be 0.5%(owf by the Light of Mulberry Silk Fabrics after sizing) chitosan solution carry out modification, bath raio 30:1, normal temperature process 60min, then washes, and finally dries at 100 DEG C;
(4) dye: Light of Mulberry Silk Fabrics is carried out dyeing process, be specially: under room temperature, fabric is immersed in the clear water of dyeing machine, then in water-bath, penetrating agent JFC 1.5g/L is added, diffusant DN0.8g/L, levelling agent 1.5g/L, natural dye chrysanthemum 1.5%(owf), mordant ferrous sulfate 3%(owf), imvite 3g/L, shitosan 3g/L, bath raio 20:1, and by pH buffer Acetic acid-sodium acetate, the pH value of dye liquor is adjusted to 5.5-6, cyclically charging material 20min, then dyeing machine heats up, programming rate is 1 DEG C/min, when temperature rises to 60 DEG C, insulation dyeing 20min, dyeing machine continues to heat up, programming rate is 0.5 DEG C/min, when being warming up to 70 DEG C, insulation dyeing 20min, dyeing machine continues to heat up, programming rate is 1 DEG C/min, when being warming up to 85 DEG C, insulation dyeing 40min, then dyeing machine cooling, cooling rate is 2 DEG C/min, when temperature is down to 40 DEG C, dyestuff is discharged also injected clear water again, 15min is rinsed with clear water,
(5) mordant is removed: the Light of Mulberry Silk Fabrics after dyeing being put into mass fraction is carry out mordant cleaning in the oxalic acid aqueous solution of 0.3%, and cleaning temperature is 70 DEG C, scavenging period 10min, rinses once after process terminates with clear water again;
(6) soap: will remove the Light of Mulberry Silk Fabrics lauryl sodium sulfate 1g/L after mordant, polyvinylpyrrolidone 4.5g/L, AEO-94.5g/L, ethanol 10g/L, bath raio is 40:1, at 50 DEG C, rinse 30min, finally rinse 15min with the clear water of 40 DEG C again;
(7) fixation: the Light of Mulberry Silk Fabrics after cleaning is put into fixation liquid and carries out fixation, described fixation liquid contains salt 3g/L, colophony powder 3g/L, ethanol 10g/L, bath raio is 20:1, color fixing temperature 50 DEG C, the fixation time is 30min, and then temperature reduces, and 40 DEG C are rinsed 15min with clear water, then by dryer at 80 DEG C of preliminary drying 4min, then bake 3min at 110 DEG C;
(8) Final finishing: Light of Mulberry Silk Fabrics is carried out Final finishing, is specially:
A () antibiotic finish: Light of Mulberry Silk Fabrics is carried out antibacterial treatment, uses shitosan 3g/L, citric acid 3g/L, softener EQ2001g/L, ethanol 20g/L, in the water-bath of 30 DEG C, process 20min, and bath raio is 20:1;
B () mixing arranges: Light of Mulberry Silk Fabrics is put into mixed treating liquid and processes, use crease and shrink resistant finishing agent GFR-82g/L, UV resistance finishing agent UV-BS3g/L, in the water-bath of 30 DEG C, process 20min, bath raio is 20:1;
(c) flame-proof treatment: Light of Mulberry Silk Fabrics is put into fire-retardant treatment liquid and processes, with 2,3-epoxypropyltrimethylchloride chloride 20g/L, imvite 3g/L, isopropyl alcohol 15g/L, in the water-bath of 50 DEG C, process 40min, bath raio is 30:1;
(d) self-cleaning finishing: Light of Mulberry Silk Fabrics is put into containing the chloro-2-hydroxypropyl-trimethyl ammonium chloride 15g/L of 3-, flood 3h in the water-bath of NaOH 8g/L at 70 DEG C, then wash, then 85 DEG C of oven dry; Then the Light of Mulberry Silk Fabrics of oven dry is put into containing 1,2,3,4-BTCA 8g/L, sodium hypophosphite 8g/L, water-bath at 70 DEG C, flood 3h, then wash, then 85 DEG C of oven dry; Then Light of Mulberry Silk Fabrics is impregnated into TiO
2with SiO
2mol ratio be 50: 1, concentration is the TiO of 0.2mol/l
2/ SiO
2in the hydrosol, room temperature immersion 10min, then bakes and banks up with earth 3min at 120 DEG C, finally rinses 2 times with clear water again;
(9) dry: the Light of Mulberry Silk Fabrics after Final finishing is put into dryer and carries out drying and processing, bake out temperature 100 DEG C, locomotive speed is 65m/min;
(10) shape: the Light of Mulberry Silk Fabrics of oven dry is carried out heat treatment, adds heat resistanceheat resistant flavescence agent FK-1618g/L during sizing, anti-phenol flavescence agent FK-1628g/L, setting temperature 155 DEG C, locomotive speed is 25m/min, overfeeding 5%;
(11) calendering: the Light of Mulberry Silk Fabrics after sizing is put into calender and carries out calendering process, calendering temperature 115 DEG C, locomotive speed is 20m/min;
(12) rolling: Light of Mulberry Silk Fabrics is carried out rolling.
embodiment 2
An environment-friendly type dyeing and finishing technology for Light of Mulberry Silk Fabrics, comprises the following steps:
(1) pre-treatment: pre-treatment is carried out to Light of Mulberry Silk Fabrics, be specially: use urea 1.2g/L, non-phosphorus degreasing agent TF-104M5g/L, scouring agent 1.2g/L, 30% hydrogen peroxide 9g/L, glusulase 9g/L, α-amylase 9g/L, carry out ultrasonic process 1-2min; bath raio is 30:1; ultrasonic frequency is 45Hz, refill clear water and wash 2 times, then dry after process terminates in the ultrasound bath of 40 DEG C;
(2) pre-setting: pre-setting process is carried out to Light of Mulberry Silk Fabrics, add heat resistanceheat resistant flavescence agent FK-1619g/L during sizing, setting temperature is 155 DEG C, and the speed of a motor vehicle is 25m/min, overfeeding 8%;
(3) chitin modified process: to put into mass fraction be 0.5%(owf by the Light of Mulberry Silk Fabrics after sizing) chitosan solution carry out modification, bath raio 30:1, normal temperature process 60min, then washes, and finally dries at 100 DEG C;
(4) dye: Light of Mulberry Silk Fabrics is carried out dyeing process, be specially: under room temperature, fabric is immersed in the clear water of dyeing machine, then in water-bath, penetrating agent JFC 2g/L is added, diffusant DN1g/L, levelling agent 2g/L, natural dye chrysanthemum 2%(owf), mordant ferrous sulfate 4%(owf), imvite 4g/L, shitosan 4g/L, bath raio 20:1, and by pH buffer Acetic acid-sodium acetate, the pH value of dye liquor is adjusted to 5.5-6, cyclically charging material 20min, then dyeing machine heats up, programming rate is 1 DEG C/min, when temperature rises to 60 DEG C, insulation dyeing 20min, dyeing machine continues to heat up, programming rate is 0.5 DEG C/min, when being warming up to 70 DEG C, insulation dyeing 20min, dyeing machine continues to heat up, programming rate is 1 DEG C/min, when being warming up to 85 DEG C, insulation dyeing 40min, then dyeing machine cooling, cooling rate is 2 DEG C/min, when temperature is down to 40 DEG C, dyestuff is discharged also injected clear water again, 15min is rinsed with clear water,
(5) mordant is removed: the Light of Mulberry Silk Fabrics after dyeing being put into mass fraction is carry out mordant cleaning in the oxalic acid aqueous solution of 0.35%, and cleaning temperature is 75 DEG C, scavenging period 10min, rinses once after process terminates with clear water again;
(6) soap: will remove the Light of Mulberry Silk Fabrics lauryl sodium sulfate 1g/L after mordant, polyvinylpyrrolidone 4.5g/L, AEO-94.5g/L, ethanol 15g/L, bath raio is 40:1, at 55 DEG C, rinse 30min, finally rinse 15min with the clear water of 45 DEG C again;
(7) fixation: the Light of Mulberry Silk Fabrics after cleaning is put into fixation liquid and carries out fixation, described fixation liquid contains salt 4g/L, colophony powder 4g/L, ethanol 15g/L, bath raio is 20:1, color fixing temperature 55 DEG C, the fixation time is 35min, and then temperature reduces, and 45 DEG C are rinsed 15min with clear water, then by dryer at 80 DEG C of preliminary drying 4min, then bake 3min at 110 DEG C;
(8) Final finishing: Light of Mulberry Silk Fabrics is carried out Final finishing, is specially:
A () antibiotic finish: Light of Mulberry Silk Fabrics is carried out antibacterial treatment, uses shitosan 4g/L, citric acid 4g/L, softener EQ2001.5g/L, ethanol 25g/L, in the water-bath of 35 DEG C, process 25min, and bath raio is 20:1;
B () mixing arranges: Light of Mulberry Silk Fabrics is put into mixed treating liquid and processes, use crease and shrink resistant finishing agent GFR-83g/L, UV resistance finishing agent UV-BS3.5g/L, in the water-bath of 35 DEG C, process 25min, bath raio is 20:1;
(c) flame-proof treatment: Light of Mulberry Silk Fabrics is put into fire-retardant treatment liquid and processes, with 2,3-epoxypropyltrimethylchloride chloride 25g/L, imvite 4g/L, isopropyl alcohol 18g/L, in the water-bath of 60 DEG C, process 50min, bath raio is 30:1;
(d) self-cleaning finishing: Light of Mulberry Silk Fabrics is put into containing the chloro-2-hydroxypropyl-trimethyl ammonium chloride 18g/L of 3-, flood 2.5h in the water-bath of NaOH 9g/L at 75 DEG C, then wash, then 85 DEG C of oven dry; Then the Light of Mulberry Silk Fabrics of oven dry is put into containing 1,2,3,4-BTCA 9g/L, sodium hypophosphite 9g/L, water-bath at 75 DEG C, flood 2.5h, then wash, then 85 DEG C of oven dry; Then Light of Mulberry Silk Fabrics is impregnated into TiO
2with SiO
2mol ratio be 50: 1, concentration is the TiO of 0.2mol/l
2/ SiO
2in the hydrosol, room temperature immersion 10min, then bakes and banks up with earth 3min at 120 DEG C, finally rinses 2 times with clear water again;
(9) dry: the Light of Mulberry Silk Fabrics after Final finishing is put into dryer and carries out drying and processing, bake out temperature 105 DEG C, locomotive speed is 68m/min;
(10) shape: the Light of Mulberry Silk Fabrics of oven dry is carried out heat treatment, adds heat resistanceheat resistant flavescence agent FK-1619g/L during sizing, anti-phenol flavescence agent FK-1629g/L, setting temperature 160 DEG C, locomotive speed is 28m/min, overfeeding 5-8%;
(11) calendering: the Light of Mulberry Silk Fabrics after sizing is put into calender and carries out calendering process, calendering temperature 120 DEG C, locomotive speed is 28m/min;
(12) rolling: Light of Mulberry Silk Fabrics is carried out rolling.
embodiment 3
An environment-friendly type dyeing and finishing technology for Light of Mulberry Silk Fabrics, comprises the following steps:
(1) pre-treatment: pre-treatment is carried out to Light of Mulberry Silk Fabrics, be specially: use urea 1.5g/L, non-phosphorus degreasing agent TF-104M5.5g/L, scouring agent 1.5g/L, 30% hydrogen peroxide 10g/L, glusulase 10g/L, α-amylase 10g/L, carry out ultrasonic process 1-2min; bath raio is 30:1; ultrasonic frequency is 45Hz, refill clear water and wash 2 times, then dry after process terminates in the ultrasound bath of 40 DEG C;
(2) pre-setting: pre-setting process is carried out to Light of Mulberry Silk Fabrics, add heat resistanceheat resistant flavescence agent FK-16110g/L during sizing, setting temperature is 160 DEG C, and the speed of a motor vehicle is 30m/min, overfeeding 10%;
(3) chitin modified process: to put into mass fraction be 0.5%(owf by the Light of Mulberry Silk Fabrics after sizing) chitosan solution carry out modification, bath raio 30:1, normal temperature process 60min, then washes, and finally dries at 100 DEG C;
(4) dye: Light of Mulberry Silk Fabrics is carried out dyeing process, be specially: under room temperature, fabric is immersed in the clear water of dyeing machine, then in water-bath, penetrating agent JFC 2.5g/L is added, diffusant DN1.2g/L, levelling agent 2.5g/L, natural dye chrysanthemum 2.5%(owf), mordant ferrous sulfate 5%(owf), imvite 5g/L, shitosan 5g/L, bath raio 20:1, and by pH buffer Acetic acid-sodium acetate, the pH value of dye liquor is adjusted to 5.5-6, cyclically charging material 20min, then dyeing machine heats up, programming rate is 1 DEG C/min, when temperature rises to 60 DEG C, insulation dyeing 20min, dyeing machine continues to heat up, programming rate is 0.5 DEG C/min, when being warming up to 70 DEG C, insulation dyeing 20min, dyeing machine continues to heat up, programming rate is 1 DEG C/min, when being warming up to 85 DEG C, insulation dyeing 40min, then dyeing machine cooling, cooling rate is 2 DEG C/min, when temperature is down to 40 DEG C, dyestuff is discharged also injected clear water again, 15min is rinsed with clear water,
(5) mordant is removed: the Light of Mulberry Silk Fabrics after dyeing being put into mass fraction is carry out mordant cleaning in the oxalic acid aqueous solution of 0.4%, and cleaning temperature is 80 DEG C, scavenging period 10min, rinses once after process terminates with clear water again;
(6) soap: will remove the Light of Mulberry Silk Fabrics lauryl sodium sulfate 1g/L after mordant, polyvinylpyrrolidone 4.5g/L, AEO-94.5g/L, ethanol 20g/L, bath raio is 40:1, at 60 DEG C, rinse 30min, finally rinse 15min with the clear water of 50 DEG C again;
(7) fixation: the Light of Mulberry Silk Fabrics after cleaning is put into fixation liquid and carries out fixation, described fixation liquid contains salt 5g/L, colophony powder 5g/L, ethanol 20g/L, bath raio is 20:1, color fixing temperature 60 DEG C, the fixation time is 40min, and then temperature reduces, and 50 DEG C are rinsed 15min with clear water, then by dryer at 80 DEG C of preliminary drying 4min, then bake 3min at 110 DEG C;
(8) Final finishing: Light of Mulberry Silk Fabrics is carried out Final finishing, is specially:
A () antibiotic finish: Light of Mulberry Silk Fabrics is carried out antibacterial treatment, uses shitosan 5g/L, citric acid 5g/L, softener EQ2002g/L, ethanol 30g/L, in the water-bath of 40 DEG C, process 30min, and bath raio is 20:1;
B () mixing arranges: Light of Mulberry Silk Fabrics is put into mixed treating liquid and processes, use crease and shrink resistant finishing agent GFR-84g/L, UV resistance finishing agent UV-BS4g/L, in the water-bath of 40 DEG C, process 30min, bath raio is 20:1;
(c) flame-proof treatment: Light of Mulberry Silk Fabrics is put into fire-retardant treatment liquid and processes, with 2,3-epoxypropyltrimethylchloride chloride 30g/L, imvite 5g/L, isopropyl alcohol 20g/L, in the water-bath of 70 DEG C, process 60min, bath raio is 30:1;
(d) self-cleaning finishing: Light of Mulberry Silk Fabrics is put into containing the chloro-2-hydroxypropyl-trimethyl ammonium chloride 20g/L of 3-, flood 2h in the water-bath of NaOH 10g/L at 80 DEG C, then wash, then 85 DEG C of oven dry; Then the Light of Mulberry Silk Fabrics of oven dry is put into containing 1,2,3,4-BTCA 10g/L, sodium hypophosphite 10g/L, water-bath at 80 DEG C, flood 2h, then wash, then 85 DEG C of oven dry; Then Light of Mulberry Silk Fabrics is impregnated into TiO
2with SiO
2mol ratio be 50: 1, concentration is the TiO of 0.2mol/l
2/ SiO
2in the hydrosol, room temperature immersion 10min, then bakes and banks up with earth 3min at 120 DEG C, finally rinses 2 times with clear water again;
(9) dry: the Light of Mulberry Silk Fabrics after Final finishing is put into dryer and carries out drying and processing, bake out temperature 110 DEG C, locomotive speed is 70m/min;
(10) shape: the Light of Mulberry Silk Fabrics of oven dry is carried out heat treatment, adds heat resistanceheat resistant flavescence agent FK-16110g/L during sizing, anti-phenol flavescence agent FK-16210g/L, setting temperature 165 DEG C, locomotive speed is 30m/min, overfeeding 8%;
(11) calendering: the Light of Mulberry Silk Fabrics after sizing is put into calender and carries out calendering process, calendering temperature 125 DEG C, locomotive speed is 25m/min;
(12) rolling: Light of Mulberry Silk Fabrics is carried out rolling.
The present invention adopts the technical scheme of above-described embodiment, and before dyeing process, adopt glusulase and α-amylase to carry out preliminary treatment to fabric, not only destarch is effective, can also improve the wettability of fabric simultaneously, before dyeing process, chitin modified process is carried out to fabric, fundamentally modification is carried out to the performance of Light of Mulberry Silk Fabrics, overcome some defects himself existed, also add the dye uptake of fabric simultaneously, reduce the difficulty of follow-up staining procedure, after this step process, the dye-uptake of its fabric and degree of fixation can improve about 30%, in dyeing course, do not use a large amount of alkaline matters and inorganic salts, have employed natural dye, add levelling agent and diffusant improves its equalization, avoid environmental pollution, meet the requirement of environmental protection, dyeing terminates to have carried out going mordant process to fabric afterwards, employing oxalic acid aqueous solution can get rid of the mordant that fabric adheres in dyeing course well completely, thus avoid environmental pollution, ensure that attractive in appearance, the vividness of fabric color, and oxalic acid belongs to organic monoacid, lower to human injury, final like this make dye after its dye-uptake of Light of Mulberry Silk Fabrics fabric more than 95%, greatly exceed the dye-uptake of like product, its degree of fixation also can reach about 95%, colour fixation is good, the fabric simultaneously obtained after dyeing, also it is carried out to the test of fixing degree and colour fastness to rubbing, test result shows, it is done, fastness to wet rubbing reaches more than 4 grades, fixing degree reaches more than 5 grades, also add flame-proof treatment operation simultaneously, the oxygen index (OI) LOI of final fabric is made to be 36%, this shows that its fire resistance is high, and the present invention is at pre-setting, the yellow reagent of resistance is all employ in sizing, final fabric is made to be not easy to turn yellow, also add crease and shrink resistance process simultaneously, fabric is not creased easily, the performance such as flexibility, uviolresistance is all better simultaneously, add self-cleaning finishing in finishing process, first ionomer process is carried out to fabric, then adopts TiO
2/ SiO
2the hydrosol processes, and reaches the automatically cleaning ability that improve fabric.
Finally need to herein means out: be only part preferred embodiment of the present invention above; can not be interpreted as limiting the scope of the invention, some nonessential improvement that those skilled in the art's foregoing according to the present invention is made and adjustment all belong to protection scope of the present invention.
Claims (5)
1. an environment-friendly type dyeing and finishing technology for Light of Mulberry Silk Fabrics, is characterized in that: comprise the following steps:
(1) pre-treatment: pre-treatment is carried out to Light of Mulberry Silk Fabrics, be specially: use urea 1-1.5g/L, non-phosphorus degreasing agent 4.5-5.5g/L, scouring agent 1-1.5g/L, 30% hydrogen peroxide 8-10g/L, glusulase 8-10g/L, α-amylase 8-10g/L, carry out ultrasonic process 1-2min; bath raio is 30:1; ultrasonic frequency is 45Hz, refill clear water and wash 2 times, then dry after process terminates in the ultrasound bath of 40 DEG C;
(2) pre-setting: pre-setting process is carried out to Light of Mulberry Silk Fabrics, add heat resistanceheat resistant flavescence agent 8-10g/L during sizing, setting temperature is 150-160 DEG C, and the speed of a motor vehicle is 20-30m/min, overfeeding 5-10%;
(3) chitin modified process: to put into mass fraction be 0.5%(owf by the Light of Mulberry Silk Fabrics after sizing) chitosan solution carry out modification, bath raio 30:1, normal temperature process 60min, then washes, and finally dries at 100 DEG C;
(4) dye: Light of Mulberry Silk Fabrics is carried out dyeing process, be specially: under room temperature, fabric is immersed in the clear water of dyeing machine, then in water-bath, bleeding agent 1.5-2.5g/L is added, diffusant DN0.8-1.2g/L, levelling agent 1.5-2.5g/L, natural dye 1.5-2.5%(owf), mordant ferrous sulfate 3-5%(owf), imvite 3-5g/L, shitosan 3-5g/L, bath raio 20:1, and by pH buffer Acetic acid-sodium acetate, the pH value of dye liquor is adjusted to 5.5-6, cyclically charging material 20min, then dyeing machine heats up, programming rate is 1 DEG C/min, when temperature rises to 60 DEG C, insulation dyeing 20min, dyeing machine continues to heat up, programming rate is 0.5 DEG C/min, when being warming up to 70 DEG C, insulation dyeing 20min, dyeing machine continues to heat up, programming rate is 1 DEG C/min, when being warming up to 85 DEG C, insulation dyeing 40min, then dyeing machine cooling, cooling rate is 2 DEG C/min, when temperature is down to 40 DEG C, dyestuff is discharged also injected clear water again, 15min is rinsed with clear water,
(5) mordant is removed: the Light of Mulberry Silk Fabrics after dyeing being put into mass fraction is carry out mordant cleaning in the oxalic acid aqueous solution of 0.3-0.4%, and cleaning temperature is 70-80 DEG C, scavenging period 10min, rinses once after process terminates with clear water again;
(6) soap: will the Light of Mulberry Silk Fabrics lauryl sodium sulfate 1g/L after mordant be removed, polyvinylpyrrolidone 4.5g/L, AEO-94.5g/L, ethanol 10-20g/L; bath raio is 40:1, rinses 30min at 50-60 DEG C, finally rinses 15min with the clear water of 40-50 DEG C again;
(7) fixation: the Light of Mulberry Silk Fabrics after cleaning is put into fixation liquid and carries out fixation, described fixation liquid contains salt 3-5g/L, colophony powder 3-5g/L, ethanol 10-20g/L, bath raio is 20:1, color fixing temperature 50-60 DEG C, the fixation time is 30-40min, and then temperature reduces, and 40-50 DEG C is rinsed 15min with clear water, then by dryer at 80 DEG C of preliminary drying 4min, then bake 3min at 110 DEG C;
(8) Final finishing: Light of Mulberry Silk Fabrics is carried out Final finishing, is specially:
A () antibiotic finish: Light of Mulberry Silk Fabrics is carried out antibacterial treatment, uses shitosan 3-5g/L, citric acid 3-5g/L, softener 1-2g/L, ethanol 20-30g/L, in the water-bath of 30-40 DEG C, process 20-30min, and bath raio is 20:1;
B () mixing arranges: Light of Mulberry Silk Fabrics is put into mixed treating liquid and processes, use crease and shrink resistant finishing agent GFR-82-4g/L, UV resistance finishing agent UV-BS3-4g/L, in the water-bath of 30-40 DEG C, process 20-30min, bath raio is 20:1;
(c) flame-proof treatment: Light of Mulberry Silk Fabrics is put into fire-retardant treatment liquid and processes, with 2,3-epoxypropyltrimethylchloride chloride 20-30g/L, imvite 3-5g/L, isopropyl alcohol 15-20g/L, in the water-bath of 50-70 DEG C, process 40-60min, bath raio is 30:1;
(d) self-cleaning finishing: Light of Mulberry Silk Fabrics is put into containing the chloro-2-hydroxypropyl-trimethyl ammonium chloride 15-20g/L of 3-, flood 2-3h in the water-bath of NaOH 8-10g/L at 70-80 DEG C, then wash, then 85 DEG C of oven dry; Then the Light of Mulberry Silk Fabrics of oven dry is put into containing 1,2,3,4-BTCA 8-10g/L, sodium hypophosphite 8-10g/L, water-bath at 70-80 DEG C, flood 2-3h, then wash, then 85 DEG C of oven dry; Then Light of Mulberry Silk Fabrics is impregnated into TiO
2with SiO
2mol ratio be 50: 1, concentration is the TiO of 0.2mol/l
2/ SiO
2in the hydrosol, room temperature immersion 10min, then bakes and banks up with earth 3min at 120 DEG C, finally rinses 2 times with clear water again;
(9) dry: the Light of Mulberry Silk Fabrics after Final finishing is put into dryer and carries out drying and processing, bake out temperature 100-110 DEG C, locomotive speed is 65-70m/min;
(10) shape: the Light of Mulberry Silk Fabrics of oven dry is carried out heat treatment, adds heat resistanceheat resistant flavescence agent 8-10g/L during sizing, anti-phenol flavescence agent 8-10g/L, setting temperature 155-165 DEG C, locomotive speed is 25-30m/min, overfeeding 5-8%;
(11) calendering: the Light of Mulberry Silk Fabrics after sizing is put into calender and carries out calendering process, calendering temperature 115-125 DEG C, locomotive speed is 20-25m/min;
(12) rolling: Light of Mulberry Silk Fabrics is carried out rolling.
2. the environment-friendly type dyeing and finishing technology of Light of Mulberry Silk Fabrics according to claim 1, is characterized in that: the non-phosphorus degreasing agent in described step 1 is that without phosphorus neutrality is deoiled clever TF-104M.
3. the environment-friendly type dyeing and finishing technology of Light of Mulberry Silk Fabrics according to claim 1, is characterized in that: the bleeding agent in described step 4 is penetrating agent JFC.
4. the environment-friendly type dyeing and finishing technology of Light of Mulberry Silk Fabrics according to claim 1, is characterized in that: the natural dye in described step 4 is chrysanthemum.
5. the environment-friendly type dyeing and finishing technology of Light of Mulberry Silk Fabrics according to claim 1, is characterized in that: the softener in described step 8 is ester based quaternary ammonium salt softener.