CN105063874A - Preparation method of cationic spandex single jersey knitted fabric - Google Patents
Preparation method of cationic spandex single jersey knitted fabric Download PDFInfo
- Publication number
- CN105063874A CN105063874A CN201510503493.5A CN201510503493A CN105063874A CN 105063874 A CN105063874 A CN 105063874A CN 201510503493 A CN201510503493 A CN 201510503493A CN 105063874 A CN105063874 A CN 105063874A
- Authority
- CN
- China
- Prior art keywords
- fabric
- cationic
- preparation
- spandex
- prefinishing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to the field of textile technologies and particularly relates to a preparation method of cationic spandex single jersey knitted fabric. The fabric is composed of 25 wt% of dacron, 70 wt% of acrylic fibers and 5 wt% of spandex. The preparation process includes the steps of yarn forming and fabric pre-treatment. A dyestuff additive used in the fabric pre-treatment process comprises, 0.1-0.3 wt% of cationic blue BG-ED, 0.05-0.10% of cationic red GRL-ED, 0.12-0.25 wt% of cationic yellow 3RL-ED, 0.8-1.3 wt% of glacial acetic acid, 1.5-3.5 wt% of anhydrous sodium sulphate, 0.8-1.5 wt% of ammonium sulfate and the balance water. After the twist of yarn in the fabric yarn forming process is controlled and special dyeing and finishing are conducted, the fabric has the stereoscopic feeling, and a cloth cover is active, not rigid, smooth in hand feeling, good in drooping feeling, breathable and capable of absorbing moisture and releasing sweat. The fabric is easy to dry after being washed, not prone to wrinkling, free of deformation and suitable for being used as summer coat garment materials.
Description
Technical field
The invention belongs to textile technology field, be specifically related to a kind of preparation method of CATION spandex undershirt cloth knit fabric.
Background technology
Knit fabric utilizes knitting needle by yarn bends lopping and mutually go here and there to overlap and the fabric of formation.Knit fabric and the difference of shuttle-woven fabric are that the form of yarn in fabric is different.Knitting be divided into weft knitting and through compile.At present, knit fabric is widely used in garment material and lining, and family to be spun etc. in product, is subject to liking of consumers in general.The grey cloth of fiber crops is comfortable and easy to wear, and absorbing sweat is easily done, and is excellent jacket garment material in summer.But common fiber crops ash cloth dyed after, cloth cover effect third dimension is strong, more inflexible, limits its development.
Summary of the invention
The object of the invention is to for the deficiencies in the prior art, a kind of preparation method of CATION spandex undershirt cloth knit fabric is provided.The twist size of twisting during by controlling resultant yarn, and select suitable dyeing and finishing technology, obtained a kind of third dimension strong, the fiber crops ash cloth that cloth cover relatively enlivens, adapts to jacket garment material in summer.
For achieving the above object, the present invention adopts following technical scheme:
A preparation method for CATION spandex undershirt cloth knit fabric, described fabric is by 25wt% terylene, and 70wt% acrylic fibers and 5wt% spandex form; Its preparation process comprises: resultant yarn, fabric prefinishing, and other techniques are consistent with common process; Dye addictive during fabric prefinishing is: cationic blue BG-ED0.1 ~ 0.3wt%, cationic red GRL-ED0.05 ~ 0.10wt%, cationic yellow 3RL-ED0.12 ~ 0.25wt%, glacial acetic acid 0.8 ~ 1.3wt%, glauber salt 1.5 ~ 3.5wt%, ammonium sulfate 0.8 ~ 1.5wt%, surplus is water.
Described resultant yarn, the twist of terylene and acrylic fibers twisting is 10-15.
Described its design parameter of fabric prefinishing is: dyeing temperature 125 ~ 130 DEG C, dyeing time 25 ~ 35 minutes; Setting temperature 155 ~ 165 DEG C, the speed of a motor vehicle is 30 ~ 40m/min.
beneficial effect of the present invention is:
1) when resultant yarn, the twist size of terylene and acrylic fibers twisting must be grasped, the twist is excessive or too small, cloth cover third dimension after dyeing is not strong, and with common fiber crops ash cloth indifference, the twist must control in a rational scope, after dyeing and finishing, just have third dimension, cloth cover is more active, not inflexible;
2) fabric of the present invention is through prefinishing, and cloth cover stereoeffect is given prominence to, and feel is sliding glutinous, and sagging sense is well, moisture absorbing and sweat releasing, ventilative, easily dry after washing, does not crease easily, indeformable, adapts to jacket garment material in summer.
Detailed description of the invention
The present invention's the following example further illustrates the present invention, but protection scope of the present invention is not limited to the following example.
embodiment 1
A preparation method for CATION spandex undershirt cloth knit fabric, described fabric is by 25wt% terylene, and 70wt% acrylic fibers and 5wt% spandex form;
Dye addictive during fabric prefinishing is: cationic blue BG-ED0.15wt%, cationic red GRL-ED0.08wt%, cationic yellow 3RL-ED0.18wt%, glacial acetic acid 1wt%, glauber salt 2wt%, ammonium sulfate 1wt%, and surplus is water.
During resultant yarn, the twist of terylene and acrylic fibers twisting is 10.
Described its design parameter of fabric prefinishing is: dyeing temperature 130 DEG C, dyeing time 30 minutes; Setting temperature 160 DEG C, the speed of a motor vehicle is 35m/min.
embodiment 2
A preparation method for CATION spandex undershirt cloth knit fabric, described fabric is by 25wt% terylene, and 70wt% acrylic fibers and 5wt% spandex form;
Dye addictive during fabric prefinishing is: cationic blue BG-ED0.3wt%, cationic red GRL-ED0.05wt%, cationic yellow 3RL-ED0.25wt%, glacial acetic acid 0.8wt%, glauber salt 3.5wt%, ammonium sulfate 0.8wt%, and surplus is water.
During resultant yarn, the twist of terylene and acrylic fibers twisting is 12.
Described its design parameter of fabric prefinishing is: dyeing temperature 128 DEG C, dyeing time 25 minutes; Setting temperature 155 DEG C, the speed of a motor vehicle is 30m/min.
embodiment 3
A preparation method for CATION spandex undershirt cloth knit fabric, described fabric is by 25wt% terylene, and 70wt% acrylic fibers and 5wt% spandex form;
Dye addictive during fabric prefinishing is: cationic blue BG-ED0.1wt%, cationic red GRL-ED0.10wt%, cationic yellow 3RL-ED0.12wt%, glacial acetic acid 1.3wt%, glauber salt 1.5wt%, ammonium sulfate 1.5wt%, and surplus is water.
During resultant yarn, the twist of terylene and acrylic fibers twisting is 15.
Described its design parameter of fabric prefinishing is: dyeing temperature 125 DEG C, dyeing time 35 minutes; Setting temperature 165 DEG C, the speed of a motor vehicle is 40m/min.
The foregoing is only preferred embodiment of the present invention, all equalizations done according to the present patent application the scope of the claims change and modify, and all should belong to covering scope of the present invention.
Claims (3)
1. a preparation method for CATION spandex undershirt cloth knit fabric, is characterized in that: described fabric is by 25wt% terylene, and 70wt% acrylic fibers and 5wt% spandex form; Its preparation process comprises: resultant yarn, fabric prefinishing; Dye addictive during fabric prefinishing is: cationic blue BG-ED0.1 ~ 0.3wt%, cationic red GRL-ED0.05 ~ 0.10wt%, cationic yellow 3RL-ED0.12 ~ 0.25wt%, glacial acetic acid 0.8 ~ 1.3wt%, glauber salt 1.5 ~ 3.5wt%, ammonium sulfate 0.8 ~ 1.5wt%, surplus is water.
2. the preparation method of CATION spandex undershirt cloth knit fabric according to claim 1, is characterized in that: described resultant yarn, and the twist of terylene and acrylic fibers twisting is 10-15.
3. the preparation method of CATION spandex undershirt cloth knit fabric according to claim 1, is characterized in that: described its design parameter of fabric prefinishing is: dyeing temperature 125 ~ 130 DEG C, dyeing time 25 ~ 35 minutes; Setting temperature 155 ~ 165 DEG C, the speed of a motor vehicle is 30 ~ 40m/min.