CN105063677A - 一种电镀镍溶液及其电镀方法 - Google Patents

一种电镀镍溶液及其电镀方法 Download PDF

Info

Publication number
CN105063677A
CN105063677A CN201510520392.9A CN201510520392A CN105063677A CN 105063677 A CN105063677 A CN 105063677A CN 201510520392 A CN201510520392 A CN 201510520392A CN 105063677 A CN105063677 A CN 105063677A
Authority
CN
China
Prior art keywords
plating solution
nickel plating
nickel
hydroxymethylacrylate
asccharin
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510520392.9A
Other languages
English (en)
Inventor
沈秋
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wuxi Qingyang Machinery Manufacturing Co Ltd
Original Assignee
Wuxi Qingyang Machinery Manufacturing Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuxi Qingyang Machinery Manufacturing Co Ltd filed Critical Wuxi Qingyang Machinery Manufacturing Co Ltd
Priority to CN201510520392.9A priority Critical patent/CN105063677A/zh
Publication of CN105063677A publication Critical patent/CN105063677A/zh
Pending legal-status Critical Current

Abstract

本发明提供了一种电镀镍溶液及其电镀方法。该电镀镍溶液包含硫酸镍100～150g/L、氯化镍20～40g/L、亚磷酸20～45g/L、烯丙基磺酸钠20～35g/L、羟甲基丙烯酸20～30g/L、糖精0.1～0.3g/L。本发明电镀镍溶液降低了镍的含量，提高了稳定性，电镀得到的镀层具有良好的光亮度和耐腐蚀性。

Description

一种电镀镍溶液及其电镀方法
技术领域
本发明涉及电镀液技术领域，尤其涉及一种电镀镍溶液及其电镀方法。
背景技术
随着科技的不断发展，对产品的要求越来越严格，单一元素的镀层难以满足电镀产品的需求，科研工作者逐渐将目光投向合金电镀。
镀镍工艺广泛应用于电镀行业的各个方面，用于金属器件进行防腐、装饰为目的的表面处理。但由于镍资源属不可再生自然，随着镍消费量的不断增加，供给已严重不足，造成价格飙升。各电镀企业镀镍成本居高不下。电镀企业纷纷寻求节镍、代镍的新工艺。
发明内容
有鉴于此，本发明一方面提供一种电镀镍溶液，该电镀镍溶液降低了镍的含量，提高了电镀镍溶液稳定性。
本发明采用以下技术方案实现。
一种电镀镍溶液，包含硫酸镍100～150g/L、氯化镍20～40g/L、亚磷酸20～45g/L、烯丙基磺酸钠20～35g/L、羟甲基丙烯酸20～30g/L、糖精0.1～0.3g/L。
优选地，包含硫酸镍100～120g/L、氯化镍20～30g/L、亚磷酸35～45g/L、烯丙基磺酸钠30～35g/L、羟甲基丙烯酸25～30g/L、糖精0.1～0.2g/L。
优选地，包含硫酸镍115g/L、氯化镍25g/L、亚磷酸40g/L、烯丙基磺酸钠32g/L、羟甲基丙烯酸28g/L、糖精0.2g/L。
优选地，所述电镀镍溶液PH为3～4。
本发明另一方面提供一种使用上述电镀镍溶液电镀的方法，采用该方法电镀得到的镀层具有良好的光亮度和耐腐蚀性。
一种使用上述电镀镍溶液电镀的方法，包括以下步骤：
(1)将硫酸镍、氯化镍和烯丙基磺酸钠溶解于去离子水中，制得混合液，向混合液中加入亚磷酸、羟甲基丙烯酸和糖精，混合均匀，制得电镀镍溶液，其中，硫酸镍100～150g/L、氯化镍20～40g/L、亚磷酸20～45g/L、烯丙基磺酸钠20～35g/L、羟甲基丙烯酸20～30g/L、糖精0.1～0.3g/L。
(2)用钛-氧化物惰性阳极为阳极，工件做阴极，进行电镀，得到镍银镀层。
优选地，所述步骤(2)中电镀过程在温度40～50℃，电流密度为70～90mA/cm2条件下进行。
优选地，所述步骤(2)中阴极与阳极的面积比为(1/2～2)：1。
与现有技术相比，本发明的有益效果：本发明的电镀镍溶液，包含硫酸镍100～150g/L、氯化镍20～40g/L、亚磷酸20～45g/L、烯丙基磺酸钠20～35g/L、羟甲基丙烯酸20～30g/L、糖精0.1～0.3g/L。本发明电镀镍溶液降低了镍的含量，提高了稳定性，电镀得到的镀层具有良好的光亮度和耐腐蚀性。
具体实施方式
下面分别结合实施例来进一步说明本发明的技术方案。
以下实施例中所涉及的原料均为市售。
实施例1：本实施例的电镀镍溶液包含以下组分：
使用上述电镀镍溶液电镀方法如下:
将硫酸镍、氯化镍和烯丙基磺酸钠溶解于去离子水中，制得混合液，向混合液中加入亚磷酸、羟甲基丙烯酸和糖精，混合均匀，制得电镀镍溶液，其中，硫酸镍100g/L、氯化镍20g/L、亚磷酸20g/L、烯丙基磺酸钠20g/L、羟甲基丙烯酸20g/L、糖精0.1g/L。
用钛-氧化物惰性阳极为阳极，工件做阴极，在电镀液温度为40℃、电流密度为70mA/cm2、阴极与阳极的面积比为1：1下，进行电镀，得到镍银镀层。
实施例2：本实施例的电镀镍溶液包含以下组分：
使用上述电镀镍溶液电镀方法如下:
将硫酸镍、氯化镍和烯丙基磺酸钠溶解于去离子水中，制得混合液，向混合液中加入亚磷酸、羟甲基丙烯酸和糖精，混合均匀，制得电镀镍溶液，其中，硫酸镍120g/L、氯化镍30g/L、亚磷酸35g/L、烯丙基磺酸钠30g/L、羟甲基丙烯酸25g/L、糖精0.1g/L。
用钛-氧化物惰性阳极为阳极，工件做阴极，在电镀液温度为40℃、电流密度为70mA/cm2、阴极与阳极的面积比为1：1下，进行电镀，得到镍银镀层。
实施例3：本实施例的电镀镍溶液包含以下组分：
使用上述电镀镍溶液电镀方法如下:
将硫酸镍、氯化镍和烯丙基磺酸钠溶解于去离子水中，制得混合液，向混合液中加入亚磷酸、羟甲基丙烯酸和糖精，混合均匀，制得电镀镍溶液，其中，硫酸镍115g/L、氯化镍25g/L、亚磷酸40g/L、烯丙基磺酸钠32g/L、羟甲基丙烯酸28g/L、糖精0.2g/L。
用钛-氧化物惰性阳极为阳极，工件做阴极，在电镀液温度为40℃、电流密度为70mA/cm2、阴极与阳极的面积比为1：1下，进行电镀，得到镍银镀层。
本发明电镀镍溶液降低了镍的含量，提高了稳定性，电镀得到的镀层具有良好的光亮度和耐腐蚀性。
应该注意到并理解，在不脱离后附的权利要求所要求保护的本发明的精神和范围的情况下，能够对上述详细描述的本发明做出各种修改和改进。因此，要求保护的技术方案的范围不受所给出的任何特定示范教导的限制。
申请人声明，本发明通过上述实施例来说明本发明的详细工艺设备和工艺流程，但本发明并不局限于上述详细工艺设备和工艺流程，即不意味着本发明必须依赖上述详细工艺设备和工艺流程才能实施。所属技术领域的技术人员应该明了，对本发明的任何改进，对本发明产品各原料的等效替换及辅助成分的添加、具体方式的选择等，均落在本发明的保护范围和公开范围之内。

Claims (7)

1.一种电镀镍溶液，其特征在于，包含硫酸镍100～150g/L、氯化镍20～40g/L、亚磷酸20～45g/L、烯丙基磺酸钠20～35g/L、羟甲基丙烯酸20～30g/L、糖精0.1～0.3g/L。
2.根据权利要求1所述的电镀镍溶液，其特征在于，包含硫酸镍100～120g/L、氯化镍20～30g/L、亚磷酸35～45g/L、烯丙基磺酸钠30～35g/L、羟甲基丙烯酸25～30g/L、糖精0.1～0.2g/L。
3.根据权利要求1所述的电镀镍溶液，其特征在于，包含硫酸镍115g/L、氯化镍25g/L、亚磷酸40g/L、烯丙基磺酸钠32g/L、羟甲基丙烯酸28g/L、糖精0.2g/L。
4.根据权利要求1所述的电镀镍溶液，其特征在于，所述电镀镍溶液PH为3～4。
5.一种使用权利要求1所述的电镀镍溶液电镀的方法，其特征在于，包括以下步骤：
(1)将硫酸镍、氯化镍和烯丙基磺酸钠溶解于去离子水中，制得混合液，向混合液中加入亚磷酸、羟甲基丙烯酸和糖精，混合均匀，制得电镀镍溶液，其中，硫酸镍100～150g/L、氯化镍20～40g/L、亚磷酸20～45g/L、烯丙基磺酸钠20～35g/L、羟甲基丙烯酸20～30g/L、糖精0.1～0.3g/L。
(2)用钛-氧化物惰性阳极为阳极，工件做阴极，进行电镀，得到镍银镀层。
6.根据权利要求5所述的方法，其特征在于，所述步骤(2)中电镀过程在温度40～50℃，电流密度为70～90mA/cm2条件下进行。
7.根据权利要求5所述的方法，其特征在于，所述步骤(2)中阴极与阳极的面积比为(1/2～2)：1。
CN201510520392.9A 2015-08-21 2015-08-21 一种电镀镍溶液及其电镀方法 Pending CN105063677A (zh)