CN105038461A - Environment-friendly pesticidal antibacterial paint - Google Patents
Environment-friendly pesticidal antibacterial paint Download PDFInfo
- Publication number
- CN105038461A CN105038461A CN201510530698.2A CN201510530698A CN105038461A CN 105038461 A CN105038461 A CN 105038461A CN 201510530698 A CN201510530698 A CN 201510530698A CN 105038461 A CN105038461 A CN 105038461A
- Authority
- CN
- China
- Prior art keywords
- environment protection
- protection type
- agent
- type insecticidal
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides an environment-friendly pesticidal antibacterial paint which comprises 25-40% of acrylic acid emulsion, 18.8-30% of water, 2.6-5% of porous SiO2 hollow microsphere, 0.01-0.24% of hydroxymethyl cellulose, 1-2.6% of bentonite, 0.01-0.2% of titanium white, 6.8-18.8% of high-efficiency cyfluthrin, 6.1-10.5% of brofenvalerate, 1.5-3.5% of assistant, 0.01-0.06% of anion antimicrobial agent, 0.3-1.9% of water-based adhesion promoter and 2.4-5.6% of pH regulator. The environment-friendly pesticidal antibacterial paint has the advantages of high pesticidal efficiency, long release time, microbe resistance, environment friendliness and low toxicity.
Description
Technical field
The present invention relates to a kind of environment protection type insecticidal antibiotic paint.
Background technology
Along with expanding economy, the raising day by day of people's material and cultural life, the awareness of environment protection and health generally strengthens, more and more higher to the requirement of the safety and comfort degree of living environment, build room air pure and fresh, invade and harass without mosquitos and flies, without a habitat environment of the pure and fresh easiness of germ harm, be the target that people pursue, insecticidal and antibacterial coating can help people to realize this wonderful dream always.Insecticidal coating is mainly added in coating that desinsection component prepares, desinsection component in insecticidal coating must have evenly long-term and discharge from coatingsurface lentamente, in addition, desinsection component is necessary low low residue also, to human body fanout free region in use procedure.
Traditional solvent-borne coating, because its contained a large amount of volatile organic compounds (VOC) and hazardous air pollutants, uses and is more and more restricted.Therefore, the attention rate suffered by free of contamination water-borne coatings is more and more higher.Water-borne coatings is a kind of more novel coating on Coating Market, more traditional solvent-based paints coating, water-borne coatings take water as solvent, VOC in production and use procedure is well below solvent-based paints, little to human injury, therefore, water-borne coatings more saving resource, reduction pollution, low toxic and environment-friendly.Use coating progressively replaces solvent-based paints coating to represent the developing direction of coating industry.
Summary of the invention
For solving above-mentioned Problems existing, the object of the present invention is to provide one to have efficient insecticide, release is lasting, the antibacterial and aqueous, environmental protective insecticidal and antibacterial coating of environmental protection low toxicity.
For achieving the above object, technical scheme of the present invention is:
A kind of environment protection type insecticidal antibiotic paint, described environment protection type insecticidal antibiotic paint comprises: ACRYLIC EMULSION: 25 ~ 40%, water: 18.8 ~ 30%, porous SiO
2hollow microsphere: 2.6 ~ 5%, Walocel MT 20.000PV: 0.01 ~ 0.24%, wilkinite: 1 ~ 2.6%, titanium dioxide: 0.01 ~ 0.2%, betacyfluthrin: 6.8 ~ 18.8%, brofenvalerate: 6.1 ~ 10.5%; Auxiliary agent: 1.5 ~ 3.5%, negative ion antibiotic agent: 0.01 ~ 0.06%, aqueous adhesive force promotor: 0.3 ~ 1.9%, pH adjusting agent: 2.4 ~ 5.6%.
Described environment protection type insecticidal antibiotic paint comprises: ACRYLIC EMULSION: 30 ~ 38%, water: 24 ~ 30%, porous SiO
2hollow microsphere: 3.5 ~ 4.5%, Walocel MT 20.000PV: 0.05 ~ 0.18%, wilkinite: 1.5 ~ 2.2%, titanium dioxide: 0.05 ~ 0.2%, betacyfluthrin: 8.5 ~ 12%, brofenvalerate: 6.6 ~ 10%; Auxiliary agent: 2 ~ 3.1%, negative ion antibiotic agent: 0.02 ~ 0.05%, aqueous adhesive force promotor: 0.8 ~ 1.7%, pH adjusting agent: 3.5 ~ 4.2%.
Described environment protection type insecticidal antibiotic paint comprises: ACRYLIC EMULSION: 37%, water: 30%, porous SiO
2hollow microsphere: 4.3%, Walocel MT 20.000PV: 0.13%, wilkinite: 1.85%, titanium dioxide: 0.1%, betacyfluthrin: 11.5%, brofenvalerate: 7.3%; Auxiliary agent: 2.14%, negative ion antibiotic agent: 0.03%, aqueous adhesive force promotor: 1.5%, pH adjusting agent: 4.15%.
Again, described water is deionized water.
Separately, described porous SiO
2the aperture of hollow microsphere is 45 ~ 60nm.
Separately have, described auxiliary agent is flow agent and defoamer.
And described aqueous adhesive force promotor is epoxy modified silicone compound.
Meanwhile, described pH adjusting agent is made up of SODIUM PHOSPHATE, MONOBASIC and Sodium phosphate dibasic.
Beneficial effect of the present invention is:
Described environment protection type insecticidal antibiotic paint selects porous SiO
2hollow microsphere is as slow-released carrier, and aperture is homogeneous, can effectively adsorb sterilant betacyfluthrin and brofenvalerate, wrap up, and is carried out slow releasing to coating surface, thus reaches the object of deinsectization; Porous SiO
2hollow microsphere can also make the scrub performance of coating and ageing resistance be improved.In addition, add negative ion antibiotic agent, the bacterium of carrying when stining attached coating surface to mosquito, virus have very strong killing action, more ensure that the hygienic safety of indoor environment.Meanwhile, select water as paint solvent, raw material is easy to get, and more low toxic and environment-friendly.
Embodiment
Below by specific embodiment, the present invention is described further, but embodiment does not limit the scope of the invention.
Embodiment one:
A kind of environment protection type insecticidal antibiotic paint comprises: ACRYLIC EMULSION: 37%, water: 30%, porous SiO
2hollow microsphere: 4.3%, Walocel MT 20.000PV: 0.13%, wilkinite: 1.85%, titanium dioxide: 0.1%, betacyfluthrin: 11.5%, brofenvalerate: 7.3%; Auxiliary agent: 2.14%, negative ion antibiotic agent: 0.03%, aqueous adhesive force promotor: 1.5%, pH adjusting agent: 4.15%.
Embodiment two:
A kind of environment protection type insecticidal antibiotic paint comprises: ACRYLIC EMULSION: 25%, water: 30%, porous SiO
2hollow microsphere: 5%, Walocel MT 20.000PV: 0.2%, wilkinite: 2.5%, titanium dioxide: 0.18%, betacyfluthrin: 18.5%, brofenvalerate: 10.3%; Auxiliary agent: 3.4%, negative ion antibiotic agent: 0.05%, aqueous adhesive force promotor: 1.8%, pH adjusting agent: 3.07%.
Embodiment three:
A kind of environment protection type insecticidal antibiotic paint comprises: ACRYLIC EMULSION: 40%, water: 21%, porous SiO
2hollow microsphere: 3.8%, Walocel MT 20.000PV: 0.09%, wilkinite: 1.5%, titanium dioxide: 0.08%, betacyfluthrin: 15.5%, brofenvalerate: 9.6%; Auxiliary agent: 2.2%, negative ion antibiotic agent: 0.02%, aqueous adhesive force promotor: 1.1%, pH adjusting agent: 5.11%.
The results of property of coating in embodiment:
| Test event | Embodiment one | Embodiment two | Embodiment three |
| Abrasion resistance | 1000 non-bottom drain materials | 1000 non-bottom drain materials | 1000 non-bottom drain materials |
| Condition in container | Without caking, evenly | Without caking, evenly | Without caking, evenly |
| Acid resistance | 24h is without exception | 24h is without exception | 24h is without exception |
| Alkali resistance | 24h is without exception | 24h is without exception | 24h is without exception |
| KT 50/min | 7.8 | 8.2 | 8.0 |
| KT 95/min | 16.8 | 17.1 | 17.0 |
| 24h mortality ratio/% | 98 | 96 | 96 |
It should be noted that, above embodiment is only in order to illustrate technical scheme of the present invention and unrestricted.Although with reference to preferred embodiment to invention has been detailed description, those of ordinary skill in the art is to be understood that, can modify to the technical scheme of invention or equivalent replacement, and not depart from the scope of technical solution of the present invention, it all should be encompassed in right of the present invention.
Claims (8)
1. an environment protection type insecticidal antibiotic paint, is characterized in that, described environment protection type insecticidal antibiotic paint comprises: ACRYLIC EMULSION: 25 ~ 40%, water: 18.8 ~ 30%, porous SiO
2hollow microsphere: 2.6 ~ 5%, Walocel MT 20.000PV: 0.01 ~ 0.24%, wilkinite: 1 ~ 2.6%, titanium dioxide: 0.01 ~ 0.2%, betacyfluthrin: 6.8 ~ 18.8%, brofenvalerate: 6.1 ~ 10.5%; Auxiliary agent: 1.5 ~ 3.5%, negative ion antibiotic agent: 0.01 ~ 0.06%, aqueous adhesive force promotor: 0.3 ~ 1.9%, pH adjusting agent: 2.4 ~ 5.6%.
2. a kind of environment protection type insecticidal antibiotic paint according to claim 1, is characterized in that, described environment protection type insecticidal antibiotic paint comprises: ACRYLIC EMULSION: 30 ~ 38%, water: 24 ~ 30%, porous SiO
2hollow microsphere: 3.5 ~ 4.5%, Walocel MT 20.000PV: 0.05 ~ 0.18%, wilkinite: 1.5 ~ 2.2%, titanium dioxide: 0.05 ~ 0.2%, betacyfluthrin: 8.5 ~ 12%, brofenvalerate: 6.6 ~ 10%; Auxiliary agent: 2 ~ 3.1%, negative ion antibiotic agent: 0.02 ~ 0.05%, aqueous adhesive force promotor: 0.8 ~ 1.7%, pH adjusting agent: 3.5 ~ 4.2%.
3. a kind of environment protection type insecticidal antibiotic paint according to claim 1, is characterized in that, described environment protection type insecticidal antibiotic paint comprises: ACRYLIC EMULSION: 37%, water: 30%, porous SiO
2hollow microsphere: 4.3%, Walocel MT 20.000PV: 0.13%, wilkinite: 1.85%, titanium dioxide: 0.1%, betacyfluthrin: 11.5%, brofenvalerate: 7.3%; Auxiliary agent: 2.14%, negative ion antibiotic agent: 0.03%, aqueous adhesive force promotor: 1.5%, pH adjusting agent: 4.15%.
4. a kind of environment protection type insecticidal antibiotic paint according to claim 1 or 2 or 3, is characterized in that, described water is deionized water.
5. a kind of environment protection type insecticidal antibiotic paint according to claim 1 or 2 or 3, is characterized in that, described porous SiO
2the aperture of hollow microsphere is 45 ~ 60nm.
6. a kind of environment protection type insecticidal antibiotic paint according to claim 1 or 2 or 3, is characterized in that, described auxiliary agent is flow agent and defoamer.
7. a kind of environment protection type insecticidal antibiotic paint according to claim 1 or 2 or 3, is characterized in that, described aqueous adhesive force promotor is epoxy modified silicone compound.
8. a kind of environment protection type insecticiding paint according to claim 1 or 2 or 3, it is characterized in that, described pH adjusting agent is made up of SODIUM PHOSPHATE, MONOBASIC and Sodium phosphate dibasic.