CN105038358A - 一种免打磨型腻子粉 - Google Patents

一种免打磨型腻子粉 Download PDF

Info

Publication number
CN105038358A
CN105038358A CN201510294032.1A CN201510294032A CN105038358A CN 105038358 A CN105038358 A CN 105038358A CN 201510294032 A CN201510294032 A CN 201510294032A CN 105038358 A CN105038358 A CN 105038358A
Authority
CN
China
Prior art keywords
powder
parts
polishing
putty powder
polyvinyl alcohol
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201510294032.1A
Other languages
English (en)
Other versions
CN105038358B (zh
Inventor
陈贤耿
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guangdong Jing Long Construction Group Co., Ltd.
Original Assignee
GUANGZHOU JINGLONG DECORATION ENGINEERING CO LTD
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by GUANGZHOU JINGLONG DECORATION ENGINEERING CO LTD filed Critical GUANGZHOU JINGLONG DECORATION ENGINEERING CO LTD
Priority to CN201510294032.1A priority Critical patent/CN105038358B/zh
Publication of CN105038358A publication Critical patent/CN105038358A/zh
Application granted granted Critical
Publication of CN105038358B publication Critical patent/CN105038358B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种免打磨型腻子粉，其配方按质量份配比如下：改性聚乙烯醇5～8份、滑石粉15～20份、碳酸钙粉40～45份、硅酸盐粉5～15份、硫酸钙粉10～12份、硫酸钠0.1～0.3份、添加剂0.2～0.3份，还同时公开了其配制方法，先将添加剂、硫酸钠、硫酸钙粉混合均匀，再将改性聚乙烯醇、滑石粉、碳酸钙粉、硅酸盐粉、硫酸钙粉、硫酸钠、添加剂一并加入，混合均匀后成为成品，将成品与水按质量比1：0.3～0.4混合成胶状料，采用刷墙工具直接将胶状料涂抹于墙上。本发明提供一种免打磨型腻子粉，其除符合国家外墙检测标准外，还具有优秀的施工性，该腻子粉作用于墙壁表面光滑、平整、无气孔，并且与墙壁的交接性良好，不容易掉粉，施工后无需砂纸打磨即可进行表面涂料施工。

Description

一种免打磨型腻子粉
技术领域
本发明涉及建筑工程中的装饰材料，特别是一种免打磨型腻子粉。
背景技术
现有的腻子粉是以石膏粉为主要成份，做成的腻子，主要问题是附着力差。表现之一是不容易刮涂在载体上，要反复涂刮，工作效率低；其二是已刮涂在载体上的腻子干燥后，经不起撞击，容易与载体脱离。由于腻子与载体脱离，已上油漆的物体表面就易出现斑斑点点的原形，很不美观。其次是现有腻子粉做成的腻子，质地松软，强度差，涂刷的漆面经不起碰撞，如铅笔等稍硬的物品就能在漆面上划出印迹来，使漆面失去平整光滑的美感。所以，要使漆面长期保持平整光滑的光泽，首先是要解决腻子的质量问题，人们都希望有好的腻子问世，使通过精心装饰的家俱等物品，能永远保持漆面的光泽。
本发明的目的在于针对上述腻子的问题，提供一种质量优于现有腻子，并能广泛用于金属制品、木制品、塑料制品、砼等制品的油漆前刮用的腻子粉，并且腻子粉作用于各种制品后能保持表面平整光滑，无需进行后续打磨。
发明内容
本发明的目的在于克服现有技术之缺陷，提供了一种免打磨型腻子粉，该腻子粉具有高的施工性，施工后表面光滑、平整、无气孔，并且与墙壁的交接性好。
本发明的技术方案为：
一种免打磨型腻子粉，其配方按质量份配比如下：
改性聚乙烯醇5～8份
滑石粉15～20份
碳酸钙粉40～45份
硅酸盐粉5～15份
硫酸钙粉10～12份
硫酸钠0.1～0.3份
添加剂0.2～0.3份
其调配方法如下：
先将添加剂、硫酸钠、硫酸钙粉混合均匀，再将改性聚乙烯醇、滑石粉、碳酸钙粉、硅酸盐粉、硫酸钙粉、硫酸钠、添加剂的粉体一并加入，混合均匀后成为成品，将成品与水按质量比1：0.3～0.4混合成胶状料，采用刷墙工具直接将胶状料涂抹于墙上。
所述的改性聚乙烯醇为疏水性聚乙烯醇，所述的疏水性聚乙烯醇为聚乙烯醇添加甲醛反应而得到的产物。
所述的滑石粉、碳酸钙粉的粒度均为2000目。
所述的添加剂为增稠剂或保水剂。
所述的增稠剂为纤维素或改性淀粉粉体。
所述的保水剂为聚丙烯酰胺或聚丙烯酸钾粉体。
本发明的有益效果：
本发明提供一种免打磨型腻子粉，其除符合国家外墙检测标准外，还具有优秀的施工性，该腻子粉作用于墙壁表面光滑、平整、无气孔，并且与墙壁的交接性良好，不容易掉粉，施工后无需砂纸打磨即可进行表面涂料施工。
具体实施方式
下面将结合本发明实施例对技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其它实施例，都属于本发明保护的范围。
以下结合实施例对本发明作进一步详细描述。
实施例1
聚乙烯醇缩甲醛(改性聚乙烯醇)5份
滑石粉15份
碳酸钙粉40份
硅酸盐粉5份
硫酸钙粉10份
硫酸钠0.1份
纤维素0.2份
其中，改性聚乙烯醇为甲醛改性聚乙烯醇形成产物。其改性方法为在盐酸催化的作用下，高分子链上的羟基进行缩醛化反应形成聚乙烯醇缩甲醛。
免打磨型腻子粉刷墙的配制方法，其步骤如下：
先将添加剂、硫酸钠、硫酸钙粉混合均匀，再将改性聚乙烯醇、滑石粉、碳酸钙粉、硅酸盐粉、硫酸钙粉、硫酸钠、纤维素所有粉体一并加入，混合均匀后成为成品，将成品与水按质量比1：0.3～0.4混合成胶状料，采用刷墙工具直接将胶状料涂抹于裸墙上。
实施例2
聚乙烯醇缩甲醛(改性聚乙烯醇)6份
滑石粉18份
碳酸钙粉42份
硅酸盐粉10份
硫酸钙粉11份
硫酸钠0.2份
改性淀粉0.15份
聚丙烯酰胺0.1份
本实施例采用改性淀粉0.15份加上聚丙烯酰胺0.1份代替实施例1中纤维素0.2份，并且与实施例1相比，本实施例还更改了免打磨型腻子粉配方中各成分的比例。
其中，改性聚乙烯醇为甲醛改性聚乙烯醇形成产物。其改性方法为在盐酸催化的作用下，高分子链上的羟基进行缩醛化反应形成聚乙烯醇缩甲醛。
免打磨型腻子粉刷墙的配制方法，其步骤如下：
先将添加剂、硫酸钠、硫酸钙粉混合均匀，再将改性聚乙烯醇、滑石粉、碳酸钙粉、硅酸盐粉、硫酸钙粉、硫酸钠、纤维素一并加入，混合均匀后成为成品，将成品与水按质量比1：0.3～0.4混合成胶状料，采用刷墙工具直接将胶状料涂抹于裸墙上。
实施例3
聚乙烯醇缩甲醛(改性聚乙烯醇)8份
滑石粉20份
碳酸钙粉45份
硅酸盐粉15份
硫酸钙粉12份
硫酸钠0.3份
聚丙烯酸钾0.3份
本实施例采用聚丙烯酸钾0.3份代替实施例1中纤维素0.2份，并且与实施例1相比，本实施例还更改了免打磨型腻子粉配方中各成分的比例。
其中，改性聚乙烯醇为甲醛改性聚乙烯醇形成产物。其改性方法为在盐酸催化的作用下，高分子链上的羟基进行缩醛化反应形成聚乙烯醇缩甲醛。
免打磨型腻子粉刷墙的配制方法，其步骤如下：
先将添加剂、硫酸钠、硫酸钙粉混合均匀，再将改性聚乙烯醇、滑石粉、碳酸钙粉、硅酸盐粉、硫酸钙粉、硫酸钠、纤维素一并加入，混合均匀后成为成品，将成品与水按质量比1：0.3～0.4混合成胶状料，采用刷墙工具直接将胶状料涂抹于墙上。
实施例4
聚乙烯醇缩甲醛(改性聚乙烯醇)6份
滑石粉18份
碳酸钙粉42份
硅酸盐粉10份
硫酸钙粉11份
硫酸钠0.2份
改性淀粉0.15份
聚丙烯酰胺0.1份
本实施例采用改性淀粉0.15份加上聚丙烯酰胺0.1份代替实施例1中纤维素0.2份，并且与实施例1相比，本实施例还更改了免打磨型腻子粉配方中各成分的比例。
改性聚乙烯醇为甲醛改性聚乙烯醇形成产物。其改性方法为在盐酸催化的作用下，高分子链上的羟基进行缩醛化反应形成聚乙烯醇缩甲醛。
免打磨型腻子粉刷墙的配制方法，其步骤如下：
先将添加剂、硫酸钠、硫酸钙粉混合均匀，再将改性聚乙烯醇、滑石粉、碳酸钙粉、硅酸盐粉、硫酸钙粉、硫酸钠、纤维素一并加入，混合均匀后成为成品，将成品与水按质量比1：0.3～0.4混合成胶状料，采用刷墙工具直接将胶状料涂抹于墙上。
针对实施例1～4中的腻子粉进行测试，依据JG/T157-2009《建筑外墙用腻子》进行检验，腻子粉的各项性能均符合《建筑外墙用腻子》的规定，该规定的各项指标如下：
另外，通过检测，实施例1～4中的腻子粉干燥时间为0.3h，远比标准要求中≤5h快，而在快速干燥后，墙壁表面光滑、平整、无气孔，并且与墙壁的交接性良好，不容易掉粉，施工后无需砂纸打磨即可进行表面涂料施工。

Claims (6)

1.一种免打磨型腻子粉，其特征在于，配方中各成分按质量份配比如下：
改性聚乙烯醇5～8份
滑石粉15～20份
碳酸钙粉40～45份
硅酸盐粉5～15份
硫酸钙粉10～12份
硫酸钠0.1～0.3份
添加剂0.2～0.3份
其配制方法如下：
先将添加剂、硫酸钠、硫酸钙粉混合均匀，再将改性聚乙烯醇、滑石粉、碳酸钙粉、硅酸盐粉、硫酸钙粉、硫酸钠、添加剂一并加入，混合均匀后成为成品，将成品与水按质量比1：0.3～0.4混合成胶状料，采用刷墙工具直接将胶状料涂抹于裸墙上。
2.根据权利要求1所述的免打磨型腻子粉，其特征在于：所述的改性聚乙烯醇为疏水性聚乙烯醇，所述的疏水性聚乙烯醇为聚乙烯醇添加甲醛反应而得到的产物。
3.根据权利要求1所述的免打磨型腻子粉，其特征在于：所述的滑石粉、碳酸钙粉的粒度均为2000目。
4.根据权利要求1所述的免打磨型腻子粉，其特征在于：所述的添加剂为增稠剂或保水剂。
5.根据权利要求4所述的免打磨型腻子粉，其特征在于：所述的增稠剂为纤维素或改性淀粉。
6.根据权利要求4所述的免打磨型腻子粉，其特征在于：所述的保水剂为聚丙烯酰胺或聚丙烯酸钾。
CN201510294032.1A 2015-06-01 2015-06-01 一种免打磨型腻子粉 Active CN105038358B (zh)