CN105036678A - 一种含有碳纤维的轻质加气砖 - Google Patents
一种含有碳纤维的轻质加气砖 Download PDFInfo
- Publication number
- CN105036678A CN105036678A CN201510396100.5A CN201510396100A CN105036678A CN 105036678 A CN105036678 A CN 105036678A CN 201510396100 A CN201510396100 A CN 201510396100A CN 105036678 A CN105036678 A CN 105036678A
- Authority
- CN
- China
- Prior art keywords
- parts
- add
- concrete
- sodium
- carbon fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种含有碳纤维的轻质加气砖,其是由下述重量份的原料制得:硅烷偶联剂KH792?1-2、醋酸钠1-2、粉煤灰25-30、石膏8-9、电石渣3-5、碳化硅1-1.6、污酸渣4-6、电气石粉10-20、聚乙烯蜡1.2-1.5、碳纤维3-5、改性废弃混凝土23-35、水泥10-15、氯化钠2-4、尿素1-2、锌粉0.4-0.8、水适量。本发明抗冻性能、抗压强度性能优良,碳纤维纤维材料的加入,协助混凝土承担、传递拉应力,提高了该混凝土抗冻能力。
Description
技术领域
本发明涉及加气砖领域,确切地说是一种含有碳纤维的轻质加气砖。
背景技术
加气砖因为具有空心特性,所以具有伸缩性,而建筑主体是靠钢筋混凝土结构作为支撑的,砖块只起填充作用。在地震发生时,钢筋混凝土结构会因此变形,如果是实心砖,钢筋混凝土结构变形积压时则无处伸缩,会爆裂,弹塌。使用空心砖可以给钢筋混凝土结构留下很好伸缩空间。
现有的加气砖由于个物料之前相容性不好,因此容易发脆,强度不够长,使用寿命不够长,同时不够环保。
发明内容
本发明的目的在于提供一种含有碳纤维的轻质加气砖。
上述目的通过以下方案实现:
一种含有碳纤维的轻质加气砖,其特征在于:其是由下述重量份的原料制得:硅烷偶联剂KH7921-2、醋酸钠1-2、粉煤灰25-30、石膏8-9、电石渣3-5、碳化硅1-1.6、污酸渣4-6、电气石粉10-20、聚乙烯蜡1.2-1.5、碳纤维3-5、改性废弃混凝土23-35、水泥10-15、氯化钠2-4、尿素1-2、锌粉0.4-0.8、水适量;
所述的改性废弃混凝土由下述重量份的原料制得:
废弃混凝土30-40、柠檬酸钠1.2-2.5、硬脂酸单甘油酯1-2、松香酸聚氧乙烯酯1.6-2.8、二丁基萘磺酸钠1-2、十二烷基苯磺酸钠1-2、纳米二氧化硅3-5、卵磷脂4-8;
所述的改性废弃混凝土的制备方法为:
(1)废弃混凝土紫外线辐照8-12h,与适量水混匀后,再加入硬脂酸单甘油酯,搅拌均匀,再研磨1-2小时,再加入纳米二氧化硅于40-45℃下搅拌均匀后,再加入除卵磷脂外其余原料搅拌均匀,50-60℃下干燥40-50h,后在80-100℃下真空干燥,得复配粉体;
(2)再将步骤(1)所得复配粉体置于转鼓上,40-50转/分下50-55℃下预热25-30min,再将卵磷脂加热,雾化,均匀喷于粉体上,静置冷却后,即得。
所述的一种含有碳纤维的轻质加气砖,其特征在于:制备方法包括以下步骤:
(1)将硅烷偶联剂KH792、醋酸钠、粉煤灰、石膏、电石渣按重量份混匀,加入适量水,在55-60℃下搅拌6-10分钟后,再加入水泥,搅拌均匀,再加入电气石粉、聚乙烯蜡、碳纤维、改性废弃混凝土于常温下搅拌30-50分钟,得混合水泥浆料;
(2)将所得混合水泥浆料与其余原料混匀,加入适量水,浇筑入模成型,后预养,脱模,切割,得砖坯;
(3)将砖坯按照常规工艺蒸压养护后,入库即得。
本发明的有益效果为:
本发明抗冻性能、抗压强度性能优良,碳纤维纤维材料的加入,协助混凝土承担、传递拉应力,提高了该混凝土抗冻能力。
本发明使用改性废弃混凝土,使得所得加气砖具有一定的孔隙,同时能够增加各原料的相容性,从而能够在不影响韧性的情况下多添加废弃混凝土增加强度,能够使得本发明轻质,强度高,保温性能好;
本发明通过先酸化再紫外线辐照,能够对废弃混凝土起到一定的杀菌、消毒作用,同时清除废弃混凝土孔隙中的垃圾,增加孔隙,通过添加添加剂在改性废弃混凝土中,提高所得加气砖的强度以及抗冻性能。
本发明通过加入硬脂酸单甘油酯等对废弃混凝土进行一次分散、均匀分散搅拌同时改性,再加入纳米二氧化硅使得纳米二氧化硅能够均匀得分散于废弃混凝土表面,增加补强的作用,再加入其余添加剂等进行二次分散,有效地防止微细化粒子的自聚,增加其在加气砖中的相容性和分散性;采用真空干燥的方法,使避免改性废弃混凝土粉体二次团聚;本发明采用在转鼓中雾化喷淋的方式在废弃混凝土表面喷涂熔融的卵磷脂,使得其在改性废弃混凝土表面均匀得涂布。
具体实施方式
一种含有碳纤维的轻质加气砖,其是由下述重量(kg)的原料制得:硅烷偶联剂KH7922、醋酸钠1、粉煤灰25、石膏8、电石渣5、碳化硅1、污酸渣4、电气石粉20、聚乙烯蜡1.5、碳纤维5、改性废弃混凝土35、水泥15、氯化钠2、尿素1、锌粉0.4、水适量;
所述的改性废弃混凝土由下述重量(kg)的原料制得:
废弃混凝土30、柠檬酸钠1.2、硬脂酸单甘油酯1、松香酸聚氧乙烯酯1.6、二丁基萘磺酸钠1、十二烷基苯磺酸钠1、纳米二氧化硅3、卵磷脂5;
所述的改性废弃混凝土的制备方法为:
(1)废弃混凝土紫外线辐照12h,与适量水混匀后,再加入硬脂酸单甘油酯,搅拌均匀,再研磨1小时,再加入纳米二氧化硅于40℃下搅拌均匀后,再加入除卵磷脂外其余原料搅拌均匀,50℃下干燥40h,后在80℃下真空干燥,得复配粉体;
紫外线光源采用功率1000W,光谱范围365-450nm,峰值365nm的高压汞灯灯管;
(2)再将步骤(1)所得复配粉体置于转鼓上,40转/分下55℃下预热30min,再将卵磷脂加热,雾化,均匀喷于粉体上,静置冷却后,即得。
所述的一种含有碳纤维的轻质加气砖,制备方法包括以下步骤:
(1)将硅烷偶联剂KH792、醋酸钠、粉煤灰、石膏、电石渣按重量份混匀,加入适量水,在60℃下搅拌10分钟后,再加入水泥,搅拌均匀,再加入电气石粉、聚乙烯蜡、碳纤维、改性废弃混凝土于常温下搅拌50分钟,得混合水泥浆料;
(2)将所得混合水泥浆料与其余原料混匀,加入适量水,浇筑入模成型,后预养,脱模,切割,得砖坯;
(3)将砖坯按照常规工艺蒸压养护后,入库即得。
制得的50份加气砖送检测试,得出:本加气砖的平均容重为590kg/m3,平均值抗压强度为9.5MPa。
Claims (2)
1.一种含有碳纤维的轻质加气砖,其特征在于:其是由下述重量份的原料制得:硅烷偶联剂KH7921-2、醋酸钠1-2、粉煤灰25-30、石膏8-9、电石渣3-5、碳化硅1-1.6、污酸渣4-6、电气石粉10-20、聚乙烯蜡1.2-1.5、碳纤维3-5、改性废弃混凝土23-35、水泥10-15、氯化钠2-4、尿素1-2、锌粉0.4-0.8、水适量;
所述的改性废弃混凝土由下述重量份的原料制得:
废弃混凝土30-40、柠檬酸钠1.2-2.5、硬脂酸单甘油酯1-2、松香酸聚氧乙烯酯1.6-2.8、二丁基萘磺酸钠1-2、十二烷基苯磺酸钠1-2、纳米二氧化硅3-5、卵磷脂4-8;
所述的改性废弃混凝土的制备方法为:
(1)废弃混凝土紫外线辐照8-12h,与适量水混匀后,再加入硬脂酸单甘油酯,搅拌均匀,再研磨1-2小时,再加入纳米二氧化硅于40-45℃下搅拌均匀后,再加入除卵磷脂外其余原料搅拌均匀,50-60℃下干燥40-50h,后在80-100℃下真空干燥,得复配粉体;
(2)再将步骤(1)所得复配粉体置于转鼓上,40-50转/分下50-55℃下预热25-30min,再将卵磷脂加热,雾化,均匀喷于粉体上,静置冷却后,即得。
2.根据权利要求1所述的一种含有碳纤维的轻质加气砖,其特征在于:制备方法包括以下步骤:
(1)将硅烷偶联剂KH792、醋酸钠、粉煤灰、石膏、电石渣按重量份混匀,加入适量水,在55-60℃下搅拌6-10分钟后,再加入水泥,搅拌均匀,再加入电气石粉、聚乙烯蜡、碳纤维、改性废弃混凝土于常温下搅拌30-50分钟,得混合水泥浆料;
(2)将所得混合水泥浆料与其余原料混匀,加入适量水,浇筑入模成型,后预养,脱模,切割,得砖坯;
(3)将砖坯按照常规工艺蒸压养护后,入库即得。