CN105036590A - 一种专用于流动性砂浆中的改性聚羧酸粉末减水剂 - Google Patents

一种专用于流动性砂浆中的改性聚羧酸粉末减水剂 Download PDF

Info

Publication number
CN105036590A
CN105036590A CN201510425758.4A CN201510425758A CN105036590A CN 105036590 A CN105036590 A CN 105036590A CN 201510425758 A CN201510425758 A CN 201510425758A CN 105036590 A CN105036590 A CN 105036590A
Authority
CN
China
Prior art keywords
superplasticizer
polycarboxylic acid
exclusively used
polycarboxylate
powder
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201510425758.4A
Other languages
English (en)
Other versions
CN105036590B (zh
Inventor
王香港
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SUZHOU XINGBANG CHEMICAL BUILDING MATERIALS Co Ltd
Original Assignee
SUZHOU XINGBANG CHEMICAL BUILDING MATERIALS Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SUZHOU XINGBANG CHEMICAL BUILDING MATERIALS Co Ltd filed Critical SUZHOU XINGBANG CHEMICAL BUILDING MATERIALS Co Ltd
Priority to CN201510425758.4A priority Critical patent/CN105036590B/zh
Publication of CN105036590A publication Critical patent/CN105036590A/zh
Application granted granted Critical
Publication of CN105036590B publication Critical patent/CN105036590B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种专用于流动性砂浆中的改性聚羧酸粉末减水剂，包括以下质量百分比的组分：聚羧酸减水剂原粉90.0-98.0%；超细滑石粉0.5-5.0%；抗吸附剂0.25-1.0%；高粘度生物合成胶原0.03-0.08%；原纤维合成纸浆0.3-0.5%；高聚合度缓凝剂0.5-2.0%。通过上述方式，本发明提供的专用于流动性砂浆中的改性聚羧酸粉末减水剂，通过物理复配，借助有效的、掺量低的助剂改善聚羧酸减水剂的流动性能，提高流动砂浆的铺展面积，延长聚羧酸减水剂作用力的释放时间，保持较好的施工工作度，提高了工作效率，完善了施工质量。

Description

一种专用于流动性砂浆中的改性聚羧酸粉末减水剂
技术领域
本发明涉及混凝土的领域，尤其涉及一种专用于流动性砂浆中的改性聚羧酸粉末减水剂。
背景技术
一般聚羧酸减水剂用于流动性的砂浆中，其发挥作用的时间点因材料的不同而有不同。换句话说，减水剂发挥最大效用的时间不一样，有的可以在15秒完全发挥作用，流动性能达到最好，有的需要延长搅拌时间至1分钟，才能达到最好的流动效果。虽然掺量相同，但是应用的领域就会有所不同。特别是，随着社会进步，劳动力价格越来越高，单纯依靠人工去完成一些工作，在效率和质量上都不能得到很好的保证。这就需要使用机械化施工，那就必须要配套合适的材料，进而要求配制性能优异的添加剂来满足工艺要求。
发明内容
本发明主要解决的技术问题是提供一种专用于流动性砂浆中的改性聚羧酸粉末减水剂，通过物理复配，借助有效的、掺量低的助剂改善聚羧酸减水剂的流动性能，提高流动砂浆的铺展面积，延长聚羧酸减水剂作用力的释放时间，保持较好的施工工作度，提高了工作效率，完善了施工质量，通过改性助剂，使得聚羧酸粉末减水剂增加保水增稠效果，能提高减水剂水的容忍度，降低泌水、离析，提高水泥浆体的自愈合性能。
为解决上述技术问题，本发明采用的一个技术方案是：提供了一种专用于流动性砂浆中的改性聚羧酸粉末减水剂，其特征在于，包括以下质量百分比的组分：
聚羧酸减水剂原粉90.0-98.0%；
超细滑石粉0.5-5.0%；
抗吸附剂0.25-1.0%；
高粘度生物合成胶原0.03-0.08%；
原纤维合成纸浆0.3-0.5%；
高聚合度缓凝剂0.5-2.0%。
在本发明一个较佳实施例中，所述的超细滑石粉的细度为600-1200目。
在本发明一个较佳实施例中，所述的高粘度生物合成胶原包括的组分有:温轮胶、高粘度纤维素醚以及骨胶原蛋白。
在本发明一个较佳实施例中，所述的原纤维合成纸浆采用高分散技术获得的低粘度的纤维状物质，其黏度在5-300mPa.s之间。
在本发明一个较佳实施例中，所述的高聚合度缓凝剂包括的组分有:有机合成具有若减水性能的聚合物、白糖以及葡萄糖酸钠
本发明的有益效果是：本发明的专用于流动性砂浆中的改性聚羧酸粉末减水剂，通过物理复配，借助有效的、掺量低的助剂改善聚羧酸减水剂的流动性能，提高流动砂浆的铺展面积，延长聚羧酸减水剂作用力的释放时间，保持较好的施工工作度，提高了工作效率，完善了施工质量，通过改性助剂，使得聚羧酸粉末减水剂增加保水增稠效果，能提高减水剂水的容忍度，降低泌水、离析，提高水泥浆体的自愈合性能。
具体实施方式
下面将对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅是本发明的一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其它实施例，都属于本发明保护的范围。
本发明实施例包括：
一种专用于流动性砂浆中的改性聚羧酸粉末减水剂，包括以下质量百分比的组分：
聚羧酸减水剂原粉90.0-98.0%；
超细滑石粉0.5-5.0%；
抗吸附剂0.25-1.0%；
高粘度生物合成胶原0.03-0.08%；
原纤维合成纸浆0.3-0.5%；
高聚合度缓凝剂0.5-2.0%。
上述中，所述的超细滑石粉的细度为600-1200目。超细滑石粉是由高纯度滑石矿加工而成的超细天然滑石粉末，强酸、强碱、在水溶液中呈碱性，PH值8-9，吸油性和遮盖力强，熔点高、比热大、导热率以及收缩率低。
进一步的，所述的高粘度生物合成胶原包括的组分有:温轮胶、高粘度纤维素醚以及骨胶原蛋白等；所述的原纤维合成纸浆采用一种国外通过高分散技术获得的低粘度的纤维状物质，类似于纤维素又不同于纤维素，其黏度在5-300mPa.s之间；所述的高聚合度缓凝剂包括的组分有:有机合成具有若减水性能的聚合物、白糖以及葡萄糖酸钠等。
综上所述，本发明的专用于流动性砂浆中的改性聚羧酸粉末减水剂，通过物理复配，借助有效的、掺量低的助剂改善聚羧酸减水剂的流动性能，提高流动砂浆的铺展面积，延长聚羧酸减水剂作用力的释放时间，保持较好的施工工作度，提高了工作效率，完善了施工质量，通过改性助剂，使得聚羧酸粉末减水剂增加保水增稠效果，能提高减水剂水的容忍度，降低泌水、离析，提高水泥浆体的自愈合性能。
以上所述仅为本发明的实施例，并非因此限制本发明的专利范围，凡是利用本发明说明书内容所作的等效结构或等效流程变换，或直接或间接运用在其它相关的技术领域，均同理包括在本发明的专利保护范围内。

Claims (5)

1.一种专用于流动性砂浆中的改性聚羧酸粉末减水剂，其特征在于，包括以下质量百分比的组分：
聚羧酸减水剂原粉90.0-98.0%；
超细滑石粉0.5-5.0%；
抗吸附剂0.25-1.0%；
高粘度生物合成胶原0.03-0.08%；
原纤维合成纸浆0.3-0.5%；
高聚合度缓凝剂0.5-2.0%。
2.根据权利要求1所述的专用于流动性砂浆中的改性聚羧酸粉末减水剂，其特征在于，所述的超细滑石粉的细度为600-1200目。
3.根据权利要求1所述的专用于流动性砂浆中的改性聚羧酸粉末减水剂，其特征在于，所述的高粘度生物合成胶原包括的组分有:温轮胶、高粘度纤维素醚以及骨胶原蛋白。
4.根据权利要求1所述的专用于流动性砂浆中的改性聚羧酸粉末减水剂，其特征在于，所述的原纤维合成纸浆采用高分散技术获得的低粘度的纤维状物质，其黏度在5-300mPa.s之间。
5.根据权利要求1所述的专用于流动性砂浆中的改性聚羧酸粉末减水剂，其特征在于，所述的高聚合度缓凝剂包括的组分有:有机合成具有若减水性能的聚合物、白糖以及葡萄糖酸钠。
CN201510425758.4A 2015-07-20 2015-07-20 一种专用于流动性砂浆中的改性聚羧酸粉末减水剂 Active CN105036590B (zh)