CN105017978A - Adhesive - Google Patents
Adhesive Download PDFInfo
- Publication number
- CN105017978A CN105017978A CN201510389540.8A CN201510389540A CN105017978A CN 105017978 A CN105017978 A CN 105017978A CN 201510389540 A CN201510389540 A CN 201510389540A CN 105017978 A CN105017978 A CN 105017978A
- Authority
- CN
- China
- Prior art keywords
- parts
- glue
- glue paste
- maleic anhydride
- dibutyl phthalate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the field of adhesive design and preparation, and relates to the resign and preparation of an adhesive. The invention especially relates to an adhesive which is characterized in comprising the components of polyvinyl acetate, basalt fiber, butyl rubber, urea formaldehyde resin, polyvinyl butyral, dibutyl phthalate, polymer gel, epoxy resin, an adhesive, construction glue, maleic anhydride and acrylic acid.
Description
Technical field
The invention belongs to glue paste design preparation field, relate to a kind of design preparation of glue paste, particularly relate to a kind of glue paste.
Background technology
Instantly, CNG is a kind of optimal automobile-used substitute energy, and its utilisation technology reaches its maturity through many decades development.The features such as it is low that it has cost, high efficiency, pollution-free, and use safety is convenient, demonstrate powerful development potentiality just day by day.Natural gas filling station is generally divided into three base types, namely fills type fast, and common (at a slow speed) fills and both mixed type.CNG is also applied to gas cause, particularly resident living fuel.Along with the raising of living standards of the people and the enhancing of environmental consciousness, the demand of most of city to Sweet natural gas obviously increases.Sweet natural gas (pipe natural gas) is also greater than industrial fuel as the economic benefit of domestic fuel.
The vehicles of CNG equipment and equipment is used to get more and more in highway transportation, in the various vehicles, CNG equipment is installed and is connected the pipeline of CNG equipment to the power system of the vehicles and also gets more and more, but in prior art, the sealing of CNG pipeline or valve is just sealed with common sealing glue, do not reach for the distinctive technical requirements of CNG, there is the risk of gas leakage.
Summary of the invention
In order to solve problem in prior art, the invention provides a kind of glue paste.
A kind of glue paste, is characterized in that comprising following component: polyvinyl acetate (PVA), basalt fibre, isoprene-isobutylene rubber, urea-formaldehyde resin, polyvinyl butyral acetal, dibutyl phthalate, polymeric gel, epoxy, glue paste, building glue, maleic anhydride, vinylformic acid.
Described a kind of glue paste, is characterized in that comprising following component is calculated as follows according to mass fraction:
Polyvinyl acetate (PVA) 80-100 part
Basalt fibre 25-30 part
Isoprene-isobutylene rubber 10-15 part
Urea-formaldehyde resin 15-20 part
Polyvinyl butyral acetal 15-25 part
Dibutyl phthalate 5-10 part
Polymeric gel 12-15 part
Epoxy 20-25 part
Glue paste 3-5 part
Building glue 5-10 part
Maleic anhydride 15-20 part
Vinylformic acid 5-8 part.
Described a kind of glue paste, characterized by further comprising following component and is calculated as follows according to mass fraction:
Polyvinyl acetate (PVA) 80 parts
Basalt fibre 25 parts
Isoprene-isobutylene rubber 10 parts
Urea-formaldehyde resin 15 parts
Polyvinyl butyral acetal 15 parts
Dibutyl phthalate 5 parts
Polymeric gel 12 parts
Epoxy 20 parts
Glue paste 3 parts
Building glue 5 parts
Maleic anhydride 15 parts
5 parts, vinylformic acid.
Described a kind of glue paste, characterized by further comprising following component and is calculated as follows according to mass fraction:
Polyvinyl acetate (PVA) 100 parts
Basalt fibre 30 parts
Isoprene-isobutylene rubber 15 parts
Urea-formaldehyde resin 20 parts
Polyvinyl butyral acetal 25 parts
Dibutyl phthalate 10 parts
Polymeric gel 15 parts
Epoxy 25 parts
Glue paste 5 parts
Building glue 10 parts
Maleic anhydride 20 parts
8 parts, vinylformic acid.
concrete embodiment:
embodiment 1
A kind of glue paste, is characterized in that comprising following component: polyvinyl acetate (PVA), basalt fibre, isoprene-isobutylene rubber, urea-formaldehyde resin, polyvinyl butyral acetal, dibutyl phthalate, polymeric gel, epoxy, glue paste, building glue, maleic anhydride, vinylformic acid.
Described a kind of glue paste, is characterized in that comprising following component is calculated as follows according to mass fraction:
Polyvinyl acetate (PVA) 80-100 part
Basalt fibre 25-30 part
Isoprene-isobutylene rubber 10-15 part
Urea-formaldehyde resin 15-20 part
Polyvinyl butyral acetal 15-25 part
Dibutyl phthalate 5-10 part
Polymeric gel 12-15 part
Epoxy 20-25 part
Glue paste 3-5 part
Building glue 5-10 part
Maleic anhydride 15-20 part
Vinylformic acid 5-8 part.
embodiment 2
A kind of glue paste, characterized by further comprising following component and is calculated as follows according to mass fraction:
Polyvinyl acetate (PVA) 80 parts
Basalt fibre 25 parts
Isoprene-isobutylene rubber 10 parts
Urea-formaldehyde resin 15 parts
Polyvinyl butyral acetal 15 parts
Dibutyl phthalate 5 parts
Polymeric gel 12 parts
Epoxy 20 parts
Glue paste 3 parts
Building glue 5 parts
Maleic anhydride 15 parts
5 parts, vinylformic acid.
embodiment 3
A kind of glue paste, characterized by further comprising following component and is calculated as follows according to mass fraction:
Polyvinyl acetate (PVA) 100 parts
Basalt fibre 30 parts
Isoprene-isobutylene rubber 15 parts
Urea-formaldehyde resin 20 parts
Polyvinyl butyral acetal 25 parts
Dibutyl phthalate 10 parts
Polymeric gel 15 parts
Epoxy 25 parts
Glue paste 5 parts
Building glue 10 parts
Maleic anhydride 20 parts
8 parts, vinylformic acid.
Claims (4)
1. a glue paste, is characterized in that comprising following component: polyvinyl acetate (PVA), basalt fibre, isoprene-isobutylene rubber, urea-formaldehyde resin, polyvinyl butyral acetal, dibutyl phthalate, polymeric gel, epoxy, glue paste, building glue, maleic anhydride, vinylformic acid.
2. a kind of glue paste according to claim 1, is characterized in that comprising following component is calculated as follows according to mass fraction:
Polyvinyl acetate (PVA) 80-100 part
Basalt fibre 25-30 part
Isoprene-isobutylene rubber 10-15 part
Urea-formaldehyde resin 15-20 part
Polyvinyl butyral acetal 15-25 part
Dibutyl phthalate 5-10 part
Polymeric gel 12-15 part
Epoxy 20-25 part
Glue paste 3-5 part
Building glue 5-10 part
Maleic anhydride 15-20 part
Vinylformic acid 5-8 part.
3. a kind of glue paste according to claim 1, is characterized in that comprising following component is calculated as follows according to mass fraction:
Polyvinyl acetate (PVA) 80 parts
Basalt fibre 25 parts
Isoprene-isobutylene rubber 10 parts
Urea-formaldehyde resin 15 parts
Polyvinyl butyral acetal 15 parts
Dibutyl phthalate 5 parts
Polymeric gel 12 parts
Epoxy 20 parts
Glue paste 3 parts
Building glue 5 parts
Maleic anhydride 15 parts
5 parts, vinylformic acid.
4. a kind of glue paste according to claim 1, is characterized in that comprising following component is calculated as follows according to mass fraction:
Polyvinyl acetate (PVA) 100 parts
Basalt fibre 30 parts
Isoprene-isobutylene rubber 15 parts
Urea-formaldehyde resin 20 parts
Polyvinyl butyral acetal 25 parts
Dibutyl phthalate 10 parts
Polymeric gel 15 parts
Epoxy 25 parts
Glue paste 5 parts
Building glue 10 parts
Maleic anhydride 20 parts
8 parts, vinylformic acid.