CN105001809A - 一种生物粘结木材胶 - Google Patents

一种生物粘结木材胶 Download PDF

Info

Publication number
CN105001809A
CN105001809A CN201510366997.7A CN201510366997A CN105001809A CN 105001809 A CN105001809 A CN 105001809A CN 201510366997 A CN201510366997 A CN 201510366997A CN 105001809 A CN105001809 A CN 105001809A
Authority
CN
China
Prior art keywords
parts
mixing
liquid
raw material
bio
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510366997.7A
Other languages
English (en)
Inventor
张洪滨
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
BENGBU HONGAN PRECISION MACHINERY Co Ltd
Original Assignee
BENGBU HONGAN PRECISION MACHINERY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by BENGBU HONGAN PRECISION MACHINERY Co Ltd filed Critical BENGBU HONGAN PRECISION MACHINERY Co Ltd
Priority to CN201510366997.7A priority Critical patent/CN105001809A/zh
Publication of CN105001809A publication Critical patent/CN105001809A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种生物粘结木材胶，它是由下述重量份的原料组成的：十二烷基肌氨酸钠0.2-0.4、聚二甲基硅氧烷0.1-0.3、三丁基三氯化锡0.1-0.2、骨炭2-3、硫代二丙酸双十八醇酯2-4、海螺壳粉3-5、亚油酸0.4-1、马来酸二丁酯3-4、过氯乙烯树脂5-7、氯磺化聚乙烯80-86、过氧甲酸叔丁酯0.6-1、松节油0.3-1、生物粘结剂5-6，本发明的生物粘结剂采用榆树皮粉作为结构增强剂，配合高粘度的聚丙烯酰胺，使得形成的凝胶具有纤维的特征，使凝胶具有一定的韧性，在提高成品粘度的同时，又提高了成品的韧性。

Description

一种生物粘结木材胶
技术领域
    本发明主要涉及胶领域，尤其涉及一种生物粘结木材胶。
背景技术
    目前木材胶粘剂的种类很多，人造板厂主要用尿醛树脂、酚醛树脂等胶粘剂生产纤维板、胶合板、刨花板等板材，有的是在原来的聚醋酸乙烯酯乳液、丙烯酸乳液、聚氨酯胶粘剂等的基础上，陆续研发出大豆基木材胶粘剂、淀粉基木材胶粘剂、其他农作物基木材粘剂、改性异氰酸酯胶粘剂等胶种，虽然都有一定的粘结性，但是依然存在很多的缺点，有的耐候性差，耐沸水性不强，抗冻、抗酸等性不好，都可以使得胶体变质，从而失去粘结效果。
发明内容
本发明目的就是提供一种生物粘结木材胶。
本发明是通过以下技术方案实现的：
一种生物粘结木材胶，其特征在于它是由下述重量份的原料组成的：
十二烷基肌氨酸钠0.2-0.4、聚二甲基硅氧烷0.1-0.3、三丁基三氯化锡0.1-0.2、骨炭2-3、硫代二丙酸双十八醇酯2-4、海螺壳粉3-5、亚油酸0.4-1、马来酸二丁酯3-4、过氯乙烯树脂5-7、氯磺化聚乙烯80-86、过氧甲酸叔丁酯0.6-1、松节油0.3-1、生物粘结剂5-6；
所述的生物粘结剂是由下述重量份的原料组成的：
亚硫酸钠0.4-0.5、结构增强剂4-5、醋酸酯淀粉10-11、丙二醇苯醚4-5、聚丙烯酰胺4-6、柠檬酸铝0.7-2、烷基糖苷1-2、水溶性酚醛树脂1-3、水180-200；
将聚丙烯酰胺加入到6-10倍水中，配制成溶液，加入水溶性酚醛树脂，调节PH为6-8，加入结构增强剂、亚硫酸钠，搅拌均匀，得液a；将醋酸酯淀粉、丙二醇苯醚混合，加入到剩余水重量的80-90%，60-70℃下搅拌混合10-14分钟，得液b；将剩余各原料混合，搅拌均匀，得液c；将液a与液b混合，300-350转/分搅拌分散6-10分钟，加入液c，搅拌均匀后置于80-85℃的水浴中恒温加热10-12 小时，即得所述生物粘结剂；
所述的结构增强剂的制备方法是将榆树皮磨粉后放入30-40%的氢氧化钠溶液中浸泡2-3小时，取出烘干。
所述的生物粘结木材胶的制备方法，其特征在于包括以下步骤：
将骨炭、马来酸二丁酯、过氯乙烯树脂混合，搅拌均匀，得基料；
将过氧甲酸叔丁酯、聚二甲基硅氧烷混合，搅拌均匀后加入到上述基料中，升高温度为60-80℃，加入亚油酸，保温静置20-30分钟，加入硫代二丙酸双十八醇酯，搅拌至常温；
将上述处理后的各原料与剩余各原料混合，送入高速混合机，混炼均匀后送入开炼机混炼，待混炼充分后拉出胶膜冷却，将胶粘膜铺设在木材单板之间，压制条件：压力1-2Mpa，温度110-170℃，时间2-10min。
本发明的优点是：
本发明的生物粘结剂采用榆树皮粉作为结构增强剂，配合高粘度的聚丙烯酰胺，使得形成的凝胶具有纤维的特征，使凝胶具有一定的韧性，在提高成品粘度的同时，又提高了成品的韧性；本发明的木材胶对木制品的粘结效果强，不易脱落，耐候性好，使用寿命长。
具体实施方式
实施例1
一种生物粘结木材胶，它是由下述重量份的原料组成的：
十二烷基肌氨酸钠0.4、聚二甲基硅氧烷0.3、三丁基三氯化锡0.1、骨炭3、硫代二丙酸双十八醇酯4、海螺壳粉5、亚油酸1、马来酸二丁酯4、过氯乙烯树脂7、氯磺化聚乙烯86、过氧甲酸叔丁酯1、松节油0.3、生物粘结剂6；
所述的生物粘结剂是由下述重量份的原料组成的：
亚硫酸钠0.4、结构增强剂4、醋酸酯淀粉11、丙二醇苯醚5、聚丙烯酰胺4、柠檬酸铝0.7、烷基糖苷2、水溶性酚醛树脂2、水200；
将聚丙烯酰胺加入到6倍水中，配制成溶液，加入水溶性酚醛树脂，调节PH为8，加入结构增强剂、亚硫酸钠，搅拌均匀，得液a；将醋酸酯淀粉、丙二醇苯醚混合，加入到剩余水重量的80%， 70℃下搅拌混合14分钟，得液b；将剩余各原料混合，搅拌均匀，得液c；将液a与液b混合，300转/分搅拌分散10分钟，加入液c，搅拌均匀后置于85℃的水浴中恒温加热10小时，即得所述生物粘结剂；
所述的结构增强剂的制备方法是将榆树皮磨粉后放入30%的氢氧化钠溶液中浸泡3小时，取出烘干。
所述的生物粘结木材胶的制备方法，包括以下步骤：
将骨炭、马来酸二丁酯、过氯乙烯树脂混合，搅拌均匀，得基料；
将过氧甲酸叔丁酯、聚二甲基硅氧烷混合，搅拌均匀后加入到上述基料中，升高温度为80℃，加入亚油酸，保温静置30分钟，加入硫代二丙酸双十八醇酯，搅拌至常温；
将上述处理后的各原料与剩余各原料混合，送入高速混合机，混炼均匀后送入开炼机混炼，待混炼充分后拉出胶膜冷却，将胶粘膜铺设在木材单板之间，压制条件：压力2Mpa，温度160℃，时间2min。
上述实施例的压板测试结果，胶合强度大于0.80Mpa，符合国家标准。

Claims (2)

1.一种生物粘结木材胶，其特征在于它是由下述重量份的原料组成的：
十二烷基肌氨酸钠0.2-0.4、聚二甲基硅氧烷0.1-0.3、三丁基三氯化锡0.1-0.2、骨炭2-3、硫代二丙酸双十八醇酯2-4、海螺壳粉3-5、亚油酸0.4-1、马来酸二丁酯3-4、过氯乙烯树脂5-7、氯磺化聚乙烯80-86、过氧甲酸叔丁酯0.6-1、松节油0.3-1、生物粘结剂5-6；
所述的生物粘结剂是由下述重量份的原料组成的：
亚硫酸钠0.4-0.5、结构增强剂4-5、醋酸酯淀粉10-11、丙二醇苯醚4-5、聚丙烯酰胺4-6、柠檬酸铝0.7-2、烷基糖苷1-2、水溶性酚醛树脂1-3、水180-200；
将聚丙烯酰胺加入到6-10倍水中，配制成溶液，加入水溶性酚醛树脂，调节PH为6-8，加入结构增强剂、亚硫酸钠，搅拌均匀，得液a；将醋酸酯淀粉、丙二醇苯醚混合，加入到剩余水重量的80-90%，60-70℃下搅拌混合10-14分钟，得液b；将剩余各原料混合，搅拌均匀，得液c；将液a与液b混合，300-350转/分搅拌分散6-10分钟，加入液c，搅拌均匀后置于80-85℃的水浴中恒温加热10-12 小时，即得所述生物粘结剂；
所述的结构增强剂的制备方法是将榆树皮磨粉后放入30-40%的氢氧化钠溶液中浸泡2-3小时，取出烘干。
2.一种如权利要求1所述的生物粘结木材胶的制备方法，其特征在于包括以下步骤：
将骨炭、马来酸二丁酯、过氯乙烯树脂混合，搅拌均匀，得基料；
将过氧甲酸叔丁酯、聚二甲基硅氧烷混合，搅拌均匀后加入到上述基料中，升高温度为60-80℃，加入亚油酸，保温静置20-30分钟，加入硫代二丙酸双十八醇酯，搅拌至常温；
将上述处理后的各原料与剩余各原料混合，送入高速混合机，混炼均匀后送入开炼机混炼，待混炼充分后拉出胶膜冷却，将胶粘膜铺设在木材单板之间，压制条件：压力1-2Mpa，温度110-170℃，时间2-10min。
CN201510366997.7A 2015-06-26 2015-06-26 一种生物粘结木材胶 Pending CN105001809A (zh)