CN105001448A - High-temperature-resisting plasticizer - Google Patents
High-temperature-resisting plasticizer Download PDFInfo
- Publication number
- CN105001448A CN105001448A CN201510337659.0A CN201510337659A CN105001448A CN 105001448 A CN105001448 A CN 105001448A CN 201510337659 A CN201510337659 A CN 201510337659A CN 105001448 A CN105001448 A CN 105001448A
- Authority
- CN
- China
- Prior art keywords
- temperature
- high temperature
- parts
- plasticizer
- temperature plasticizer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a high-temperature-resisting plasticizer. The high-temperature-resisting plasticizer consists of, by weight, 94-99 parts of trimellitic anhydride, 324-327 parts of 2-ethyl hexanol, 1-4 parts of solid super-acid esterification catalyst, 1-3 parts of activated carbon and 40-42 parts of 3% NaOH solution. The high-temperature-resisting plasticizer can have better effect when being used in a processing environment adopting 100 DEG C of plastic production temperature. The improvement of the plastic yield and plastic quality is facilitated.
Description
Technical field
The present invention relates to a kind of high temperature plasticizer, belong to plastic plasticizer technical field.
Background technology
At present, plastic plasticizer a kind ofly increases the flexibility of plastics or make the additive of plastics liquefaction.When producing plastics, be widely used.But, in some plastics-production, often occur that production temperature is too high, the problem of softening agent poor effect.
Summary of the invention
Object: in order to overcome the deficiencies in the prior art, the invention provides a kind of high temperature plasticizer.
Technical scheme: for solving the problems of the technologies described above, the technical solution used in the present invention is:
A kind of high temperature plasticizer, is grouped into by the one-tenth of following weight part:
Inclined benzene three is acid anhydride 94-99,2-Ethylhexyl Alcohol 324-327, solid super strong acid esterification catalyst 1-4, gac 1-3,3%NaOH solution 40-42 partially.
Preferably, the inclined acid anhydride of described inclined benzene three is set to 96.
Preferably, described 2-Ethylhexyl Alcohol is set to 325.
Preferably, described solid super strong acid esterification catalyst is set to 2.
Preferably, described gac is set to 2.
Preferably, described 3%NaOH solution is set to 40.
Beneficial effect: a kind of high temperature plasticizer provided by the invention, uses in 100 degree of processing environments for plastics-production temperature, can reach better effect.Have to utilize and improve plastics output, improve plastic quality.
Embodiment
Below the present invention is further described.
A kind of high temperature plasticizer, is grouped into by the one-tenth of following weight part:
Inclined benzene three is acid anhydride 96,2-Ethylhexyl Alcohol 325, solid super strong acid esterification catalyst 2, gac 2,3%NaOH solution 40 partially.
The above is only the preferred embodiment of the present invention; be noted that for those skilled in the art; under the premise without departing from the principles of the invention, can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (6)
1. a high temperature plasticizer, is characterized in that, is grouped into by the one-tenth of following weight part:
Inclined benzene three is acid anhydride 94-99,2-Ethylhexyl Alcohol 324-327, solid super strong acid esterification catalyst 1-4, gac 1-3,3%NaOH solution 40-42 partially.
2. a kind of high temperature plasticizer according to claim 1, is characterized in that: described inclined benzene three partially acid anhydride is set to 96.
3. a kind of high temperature plasticizer according to claim 1, is characterized in that: described 2-Ethylhexyl Alcohol is set to 325.
4. a kind of high temperature plasticizer according to claim 1, is characterized in that: described solid super strong acid esterification catalyst is set to 2.
5. a kind of high temperature plasticizer according to claim 1, is characterized in that: described gac is set to 2.
6. a kind of high temperature plasticizer according to claim 1, is characterized in that: described 3%NaOH solution is set to 40.