CN104973832A - 一种抗裂砂浆及其制备方法 - Google Patents
一种抗裂砂浆及其制备方法 Download PDFInfo
- Publication number
- CN104973832A CN104973832A CN201510333002.7A CN201510333002A CN104973832A CN 104973832 A CN104973832 A CN 104973832A CN 201510333002 A CN201510333002 A CN 201510333002A CN 104973832 A CN104973832 A CN 104973832A
- Authority
- CN
- China
- Prior art keywords
- cement
- hpmc
- minute
- vinyl acetate
- anticracking grout
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及一种抗裂砂浆及其制备方法,抗裂砂浆可以按照重量百分比含有下列组份:水泥:28~30%,煤灰:10~6%或5%~10%的玻璃粉,重钙:5%,中粗砂:57~59%,HPMC:0.3%,乳胶粉:1.5~2%,慎水剂:0.2%,聚丙烯纤维:0.3%,其他添加剂:0-0.3%,其中,HPMC采用10万粘度羟丙基甲基纤维素。能够利用废弃物煤灰(玻璃粉),从而环保节能;砂浆流动性和保水性好,从而易于和拌;硬化砂浆的硬度、强度高;无毒害,稳定性能高。
Description
技术领域
本发明涉及建筑材料,具体涉及一种抗裂砂浆及其制备方法。
背景技术
砂浆是指建筑上砌砖使用的黏结物质,由一定比例的沙子和胶结材料(水泥、石灰膏、黏土等)加水和成,也叫灰浆,也作沙浆。砂浆是由胶凝材料(水泥、石灰、粘土等)和细骨料(砂)加水拌合而成。常用的有水泥砂浆、混合砂浆(或叫水泥石灰砂浆)、石灰砂浆和粘土砂浆。
混合砂浆以水泥和石膏粉为胶凝剂,具有柔软、保水性好、施工方便等优点,其缺点是耐水性差、收缩大、粘结度低、耐久性差、容易开裂和爆灰,并且不能用于潮湿环境和外墙粉刷;水泥砂浆虽然可以克服混合砂浆的缺陷,但它本身却存在着和易性差、沁水多、水泥用量高、硬化快的不足。传统的粘结砂浆通常分为单组分型与多组分型两种。单组分是指砂浆生产企业将多种组分混合、均化后包装成袋,在施工现场按配比规定的加水量加水,搅拌均匀即可使用;多组分砂浆是指由粉体组分与胶体组分等两种或两种以上的组分构成,在施工现场将两种或两种以上的组分按配比规定的比例混合,搅拌均匀即可使用。其中多组分砂浆由于其组分中至少有一种为液态,因此在运输、贮存等方面均暴露出不便捷的现象,同时冬季贮存困难。
发明内容
本发明的目的在于提供一种环保节能,易于运输并且易于和拌,稳定性能高的抗裂砂浆及其制备方法,具体技术方案如下:
一种抗裂砂浆,进一步地,按照重量百分比含有下列组份:
水泥:28~30%,
煤灰:3~5%,
玻璃粉:3%~5%,
重钙:5%,
中粗砂:57~59%,
HPMC:0.3%,
乳胶粉:1.5~2%,
慎水剂:0.2%,
聚丙烯纤维:0.3%,
其他添加剂:0-0.3%,
其中,
所述水泥中掺有高炉矿渣形成水泥混合物,其与水泥按照8:1的质量比掺和,高炉矿渣粉磨至比表面积450—500m2/kg,水泥混合物中掺加水泥混合物用量1-2%的含有引气作用复合高效砂浆发泡剂;
所述煤灰为经干法风选二级以上粉煤灰;
所述中粗砂采用以下粒径和级配要求:3-3.5mm含有0-3%重量比,1.8-2mm含有60-80%重量比,0.425~1.175mm含有25~35%重量比,0.001-0.424mm含有0~3%重量比;
所述乳胶粉为可再分散乳胶粉,包括:37%的醋酸乙烯酯与乙烯共聚胶粉,29%的乙烯与氯乙烯及月硅酸乙烯酯三元共聚胶粉,21%的醋酸乙烯酯与乙烯及高级脂肪酸乙烯酯三元共聚胶粉,11%的醋酸乙烯酯与高级脂肪酸乙烯酯共聚胶粉,以及2%的醋酸乙烯酯均聚胶粉的混合物;
所述聚丙烯纤维为长度5-10mm的抗裂纤维,包括78%的聚丙烯单丝纤维,12%的聚酯纤维以及10%的聚丙烯腈纤维;
所述HPMC中掺加HPMC用量2-2.7%的淀粉醚ST2100,HPMC采用10万粘度羟丙基甲基纤维素。
进一步地,聚丙烯纤维为长度9mm的抗裂纤维,中粗砂采用石英砂,其他添加剂采用β半水石膏,其掺量为0.3%。
进一步地,还包括0.4%的木质纤维,2%的聚合物乳液,以及0.2-0.4%的羟丙基纤维素。
进一步地,所述水泥为强度等级32.5级或42.5级的普通硅酸盐水泥。
进一步地,所述聚丙烯纤维为长度9mm的聚丙烯单丝纤维、聚酯纤维或聚丙烯腈纤维中一种或多种。
上述抗裂砂浆的制备方法,包括如下步骤:
(1)按照预定配比准备各个组分并称量;
(2)将1/3至一半的水泥,一半的煤灰,一半的玻璃粉,一半的重钙,一半的中粗砂,1/3至一半的HPMC投入搅拌机中,搅拌1-1.5分钟;
(3)将乳胶粉,慎水剂投入搅拌机中,搅拌1-1.5分钟;
(4)将剩余的水泥,煤灰,玻璃粉,重钙,中粗砂,HPMC投入搅拌机中,搅拌1-1.5分钟;
(5)将聚丙烯纤维,其他添加剂投入搅拌机中,搅拌1-3分钟;
(6)按照步骤(4)所得物料3-5:1的比例准备清水;
(7)将清水倒入容器中后将所述物料加入并搅拌3-10分钟至均匀;
(8)静置5-8分钟;
(9)再次搅拌1-3分钟。
进一步地,所述搅拌机为双卧轴锥形双螺旋搅拌机。
进一步地,步骤(2)中投入水泥时同时掺入水泥用量1%的发泡剂,HPMC中掺加HPMC用量2%的淀粉醚,以及0.3%的β半水石膏。
进一步地,步骤(5)中还加入0.4%的木质纤维,2%的聚合物乳液,以及0.2-0.4%的羟丙基纤维素。
与目前现有技术相比,本发明提供的抗裂砂浆其工艺简易、易于实现,生产效率高,配方设计合理,固化快,强度高,耐磨耗,同时具有较好的柔韧性,可抗冲击及震动,而且流动性好,易于施工;本发明提供的制备方法,工序简易,易于施工,大大缩短工期,提高施工效率,利于广泛推广应用。具体来说:(1)能够利用废弃物煤灰(玻璃粉),从而环保节能;(2)砂浆流动性和保水性好,从而易于和拌;(3)硬化砂浆的硬度、强度高;(4)无毒害,稳定性能高。
具体实施方式
下面对本发明进行详细描述,其为本发明多种实施方式中的一种优选实施例。
在一个实施例中的砂浆配方采用:
水泥:28~30%;
煤灰:10~6%(能够利用5%~10%的玻璃粉替代);
重钙:5%;
中粗砂:57~59%;
10万粘度HPMC(羟丙基甲基纤维素):0.3%;
乳胶粉:1.5~2%;
慎水剂:0.2%;
聚丙烯纤维:0.3%。
在一个优选实施例中,抗裂砂浆按照重量百分比含有下列组份:水泥:28~30%,煤灰:10~6%或5%~10%的玻璃粉,重钙:5%,中粗砂:57~59%,HPMC:0.3%,乳胶粉:1.5~2%,慎水剂:0.2%,聚丙烯纤维:0.3%,其他添加剂:0-0.3%,其中,HPMC采用10万粘度羟丙基甲基纤维素。水泥中掺加水泥用量2%的含有引气作用复合高效砂浆发泡剂,HPMC中掺加HPMC用量3.7%的淀粉醚,聚丙烯纤维为长度9mm的抗裂纤维,中粗砂采用石英砂,乳胶粉为可再分散乳胶粉,其掺量为1.7%-2.0%;此外,其他添加剂采用β半水石膏,其掺量为0.3%。还包括0.4%的木质纤维,2%的聚合物乳液,以及0.2-0.4%的羟丙基纤维素。所述水泥为强度等级32.5级或42.5级的普通硅酸盐水泥。可再分散乳胶粉为:37%的醋酸乙烯酯与乙烯共聚胶粉,29%的乙烯与氯乙烯及月硅酸乙烯酯三元共聚胶粉,21%的醋酸乙烯酯与乙烯及高级脂肪酸乙烯酯三元共聚胶粉,11%的醋酸乙烯酯与高级脂肪酸乙烯酯共聚胶粉,以及2%的醋酸乙烯酯均聚胶粉;所述减水剂为减水剂F10,所述淀粉醚为淀粉醚ST2100;所述可再分散乳胶粉为可再分散乳胶粉5010N。所述聚丙烯纤维为长度9mm的聚丙烯单丝纤维、聚酯纤维或聚丙烯腈纤维中一种或多种。
在一个优选的实施例中,制备方法包括如下步骤:
(1)按照预定配比准备各个组分并称量;
(2)将1/3至一半的水泥,一半的煤灰或玻璃粉,一半的重钙,一半的中粗砂,1/3至一半的HPMC投入双卧轴锥形双螺旋搅拌机中,搅拌1-1.5分钟,投入水泥时同时掺入水泥用量1%的发泡剂,HPMC中掺加HPMC用量2%的淀粉醚,以及0.3%的β半水石膏;
(3)将乳胶粉,慎水剂投入搅拌机中,搅拌1-1.5分钟;
(4)将剩余的水泥,煤灰或玻璃粉,重钙,中粗砂,HPMC投入搅拌机中,搅拌1-1.5分钟;
(5)将聚丙烯纤维,其他添加剂投入搅拌机中,搅拌1-3分钟,还加入0.4%的木质纤维,2%的聚合物乳液,以及0.2-0.4%的羟丙基纤维素;
(6)按照步骤(4)所得物料3-5:1的比例准备清水;
(7)将清水倒入容器中后将所述物料加入并搅拌3-10分钟至均匀;
(8)静置5-8分钟;
(9)再次搅拌1-3分钟。
上面对本发明进行了示例性描述,显然本发明具体实现并不受上述方式的限制,只要采用了本发明的方法构思和技术方案进行的各种改进,或未经改进直接应用于其它场合的,均在本发明的保护范围之内。
Claims (9)
1.一种抗裂砂浆,其特征在于,按照重量百分比含有下列组份:
水泥:28~30%,
煤灰:3~5%,
玻璃粉:3%~5%,
重钙:5%,
中粗砂:57~59%,
HPMC:0.3%,
乳胶粉:1.5~2%,
慎水剂:0.2%,
聚丙烯纤维:0.3%,
其他添加剂:0-0.3%,
其中,
所述水泥中掺有高炉矿渣形成水泥混合物,水泥与高炉矿渣按照8:1的质量比掺和,高炉矿渣粉磨至比表面积450—500m2/kg,水泥混合物中掺加水泥混合物用量1-2%的含有引气作用复合高效砂浆发泡剂;
所述煤灰为经干法风选二级以上粉煤灰;
所述中粗砂采用以下粒径和级配要求:3-3.5mm含有0-3%重量比,1.8-2mm含有60-80%重量比,0.425~1.175mm含有25~35%重量比,0.001-0.424mm含有0~3%重量比;
所述乳胶粉为可再分散乳胶粉,包括:37%的醋酸乙烯酯与乙烯共聚胶粉,29%的乙烯与氯乙烯及月硅酸乙烯酯三元共聚胶粉,21%的醋酸乙烯酯与乙烯及高级脂肪酸乙烯酯三元共聚胶粉,11%的醋酸乙烯酯与高级脂肪酸乙烯酯共聚胶粉,以及2%的醋酸乙烯酯均聚胶粉的混合物;
所述聚丙烯纤维为长度5-10mm的抗裂纤维,包括78%的聚丙烯单丝纤维,12%的聚酯纤维以及10%的聚丙烯腈纤维;
所述HPMC中掺加HPMC用量2-2.7%的淀粉醚ST2100,HPMC采用10万粘度羟丙基甲基纤维素。
2.如权利要求1所述的抗裂砂浆,其特征在于,聚丙烯纤维为长度9mm的抗裂纤维,中粗砂采用石英砂,其他添加剂采用β半水石膏,其掺量为0.3%。
3.如权利要求1或2所述的抗裂砂浆,其特征在于,还包括0.4%的木质纤维,2%的聚合物乳液,以及0.2-0.4%的羟丙基纤维素。
4.如权利要求1-3中任一项所述的抗裂砂浆,其特征在于,所述水泥为强度等级32.5级或42.5级的普通硅酸盐水泥。
5.如权利要求1-4中任一项所述的抗裂砂浆,其特征在于,所述聚丙烯纤维为长度9mm的聚丙烯单丝纤维、聚酯纤维或聚丙烯腈纤维中一种或多种。
6.如权利要求1-5所述抗裂砂浆的制备方法,其特征在于,包括如下步骤:
(1)按照预定配比准备各个组分并称量;
(2)将1/3至一半的水泥,一半的煤灰,一半的玻璃粉,一半的重钙,一半的中粗砂,1/3至一半的HPMC投入搅拌机中,搅拌1-1.5分钟;
(3)将乳胶粉,慎水剂投入搅拌机中,搅拌1-1.5分钟;
(4)将剩余的水泥,煤灰,玻璃粉,重钙,中粗砂,HPMC投入搅拌机中,搅拌1-1.5分钟;
(5)将聚丙烯纤维,其他添加剂投入搅拌机中,搅拌1-3分钟;
(6)按照步骤(4)所得物料3-5:1的比例准备清水;
(7)将清水倒入容器中后将所述物料加入并搅拌3-10分钟至均匀;
(8)静置5-8分钟;
(9)再次搅拌1-3分钟。
7.如权利要求6所述抗裂砂浆的制备方法,其特征在于,所述搅拌机为双卧轴锥形双螺旋搅拌机。
8.如权利要求6或7所述抗裂砂浆的制备方法,其特征在于,步骤(2)中投入水泥时同时掺入水泥用量1%的发泡剂,HPMC中掺加HPMC用量2%的淀粉醚,以及0.3%的β半水石膏。
9.如权利要求8所述抗裂砂浆的制备方法,其特征在于,步骤(5)中还加入0.4%的木质纤维,2%的聚合物乳液,以及0.2-0.4%的羟丙基纤维素。