CN104942218A - 一种大型钢铸件用高强度型砂 - Google Patents

一种大型钢铸件用高强度型砂 Download PDF

Info

Publication number
CN104942218A
CN104942218A CN201510310792.7A CN201510310792A CN104942218A CN 104942218 A CN104942218 A CN 104942218A CN 201510310792 A CN201510310792 A CN 201510310792A CN 104942218 A CN104942218 A CN 104942218A
Authority
CN
China
Prior art keywords
parts
molding sand
large steel
sand
strength
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510310792.7A
Other languages
English (en)
Inventor
张福新
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Spheroidal Graphite Cast-Iron Factory Of Hanshan County Xingda
Original Assignee
Spheroidal Graphite Cast-Iron Factory Of Hanshan County Xingda
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Spheroidal Graphite Cast-Iron Factory Of Hanshan County Xingda filed Critical Spheroidal Graphite Cast-Iron Factory Of Hanshan County Xingda
Priority to CN201510310792.7A priority Critical patent/CN104942218A/zh
Publication of CN104942218A publication Critical patent/CN104942218A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种大型钢铸件用高强度型砂，本发明采用石英砂为基料，粘土为主料，辅料包含蛭石、十二烷基苯磺酸、二烷基二硫代磷酸锌、漂珠、三氧化二铝、氢化松香等原料，通过粉碎、搅拌、造粒、预热、烧结、研磨等步骤制备产品。本发明产品增加了型砂颗粒的强度和耐热性，能够防止型砂结块，降低回收的难度，铸件表面光滑，不易落砂，同时，本发明制备工艺简单易行，产品溃散性好，粒径大小合适，粘结性好，可塑性好，透气性好、流动性好、分散性好等。

Description

一种大型钢铸件用高强度型砂
技术领域
本发明涉及铸造领域，具体涉及一种大型钢铸件用高强度型砂。
背景技术
目前型砂存在的主要问题有:1、粒径大小难控制，如果型砂粒径太大，虽然透气性较好，但是铸件表面比较粗糙，光洁度不好；如果型砂料径太小，导致砂型透气性不好，铸件有气孔产生。2、散热不良，激冷效果差，复杂铸件内部易出现缩松、缩孔现象。3、分散性、流动性不好，易结块、起砂豆。4、落砂严重，报废率高。5、对于不同种类的铸件缺少专门的型砂。
传统粘土型砂主要存在不易回收利用，透气性差、流动性不好、分散性不好、溃散性差、散热不好、环境污染严重的缺点。
鉴于以上现有技术中存在的缺陷，有必要将现有装置进一步改进，使其更具备实用性，才能符合实际使用情况。
发明内容
为了克服上述现有技术的缺陷，本发明的目的是提供.一种大型钢铸件用高强度型砂。
本发明是采取以下技术方案来实现的：一种大型钢铸件用高强度型砂，采用石英砂为基料，粘土为主料，辅料包括以下重量份的原料制备而成：
蛭石  20-40份、             十二烷基苯磺酸5-7份
二烷基二硫代磷酸锌 10-14份、  漂珠2-5份
三氧化二铝3-6份、           氢化松香1-3份
增韧剂PPB-8101 15-18 份、   稳定剂RWS  0.01-0.15份
偶联剂   0.1-0.3份、        酚醛树脂  10-20份
HoCu2       2-4份、                  成核剂 0.1-0.3份
氧化钴6-8份、               焦磷酸钠10-14份
四甲基溴化铵3-4份、        莫来石晶须10-25份。
    本发明辅料包括以下重量份的原料制备而成：
蛭石  30份、             十二烷基苯磺酸6份
二烷基二硫代磷酸锌 10-14份、  漂珠4份
三氧化二铝4份、          氢化松香2份
增韧剂PPB-8101 17份、   稳定剂RWS  0.12份
偶联剂   0.15份、        酚醛树脂  15份
HoCu2   3份、                  成核剂 0.2份
氧化钴7份、              焦磷酸钠12份
四甲基溴化铵3份、        莫来石晶须15份。
本发明制备工艺，它包括以下步骤制备：粉碎、搅拌、造粒、预热、烧结、研磨、成型。
综上所述本发明具有以下有益效果：本发明采用石英砂为基料，粘土为主料，辅料包含蛭石、十二烷基苯磺酸、二烷基二硫代磷酸锌、漂珠、三氧化二铝、氢化松香等原料，增加了型砂颗粒的强度和耐热性，能够防止型砂结块，降低回收的难度，铸件表面光滑，不易落砂，同时，本发明制备工艺简单易行，产品溃散性好，粒径大小合适，粘结性好，可塑性好，透气性好、流动性好、分散性好等。
具体实施方式
为使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解，下面结合具体实施方式，进一步阐述本发明。
 本发明是采取以下技术方案来实现的：一种大型钢铸件用高强度型砂，采用石英砂为基料，粘土为主料，辅料包括以下重量份的原料制备而成：
蛭石  20-40份、             十二烷基苯磺酸5-7份
二烷基二硫代磷酸锌 10-14份、  漂珠2-5份
三氧化二铝3-6份、           氢化松香1-3份
增韧剂PPB-8101 15-18 份、   稳定剂RWS  0.01-0.15份
偶联剂   0.1-0.3份、        酚醛树脂  10-20份
HoCu2       2-4份、                  成核剂 0.1-0.3份
氧化钴6-8份、               焦磷酸钠10-14份
四甲基溴化铵3-4份、        莫来石晶须10-25份。
 作为优选方案，本发明辅料包括以下重量份的原料制备而成：
蛭石  30份、             十二烷基苯磺酸6份
二烷基二硫代磷酸锌 10-14份、  漂珠4份
三氧化二铝4份、          氢化松香2份
增韧剂PPB-8101 17份、   稳定剂RWS  0.12份
偶联剂   0.15份、        酚醛树脂  15份
HoCu2   3份、                  成核剂 0.2份
氧化钴7份、              焦磷酸钠12份
四甲基溴化铵3份、        莫来石晶须15份。
作为优选方案，本发明制备工艺，它包括以下步骤制备：粉碎、搅拌、造粒、预热、烧结、研磨、成型。
以上所述是本发明的实施例，故凡依本发明申请范围所述的构造、特征及原理所做的等效变化或修饰，均包括于本发明专利申请范围内。

Claims (3)

1.一种大型钢铸件用高强度型砂，其特征在于：采用石英砂为基料，粘土为主料，辅料包括以下重量份的原料制备而成：
蛭石  20-40份、             十二烷基苯磺酸5-7份
二烷基二硫代磷酸锌 10-14份、  漂珠2-5份
三氧化二铝3-6份、           氢化松香1-3份
增韧剂PPB-8101 15-18 份、   稳定剂RWS  0.01-0.15份
偶联剂   0.1-0.3份、        酚醛树脂  10-20份
HoCu2       2-4份、                  成核剂 0.1-0.3份
氧化钴6-8份、               焦磷酸钠10-14份
四甲基溴化铵3-4份、        莫来石晶须10-25份。
2.根据权利要求1所述的一种大型钢铸件用高强度型砂，其特征在于：所述辅料包括以下重量份的原料制备而成：
蛭石  30份、             十二烷基苯磺酸6份
二烷基二硫代磷酸锌 10-14份、  漂珠4份
三氧化二铝4份、          氢化松香2份
增韧剂PPB-8101 17份、   稳定剂RWS  0.12份
偶联剂   0.15份、        酚醛树脂  15份
HoCu2   3份、                  成核剂 0.2份
氧化钴7份、              焦磷酸钠12份
四甲基溴化铵3份、        莫来石晶须15份。
3.根据权利要求1所述的一种大型钢铸件用高强度型砂制备工艺，其特征在于：它包括以下步骤制备：粉碎、搅拌、造粒、预热、烧结、研磨、成型。
CN201510310792.7A 2015-06-09 2015-06-09 一种大型钢铸件用高强度型砂 Pending CN104942218A (zh)