CN104927444A - Oil paint resistant to weather - Google Patents

Abstract

Oil paint resistant to weather comprises, by weight, 12-22 parts of fluororesin, 7-11 parts of tripropylene glycol diacrylate, 1-4 parts of isocyanate, 8-13 parts of butyl acetate, 3-4 parts of ehylene glycol diglycidyl ether, 6-10 parts of precipitated barium sulphate, 3-6 parts of diacetone-acryloamide, 10-17 parts of acrylic resin, 6-8 parts of catalyst, 7-14 parts stearic acid, 2-4 parts of rust, 15-20 parts of plant color paste, 4-6 parts of silica solution, 10-15 parts of carbon monofluoride, 8-10 parts of tetramethyl thiocarbamide, 4-7 parts of adhesion promoter and 2-4 parts of amber. The oil paint resistant to weather has the advantages of high abrasive resistance, high fracture resistance, high smoothness, high weather resistance, high produced product quality, wide using range and no pollution.

Description

A kind of paint with good weatherability properties

Technical field

The present invention relates to a kind of paint with good weatherability properties.

Background technology

Paint or coating are all the decorative materials generally adopted during modern humans lives, and be by the macromolecular material of film forming and add auxiliary agent and solvent and combine as this decorative material material is many.Paint is be seen everywhere in daily life, it mainly plays protection and decoration, and according to different environments for use, the kind of paint is also varied, the demand of current people gets more and more, the performance requriements of paint is also got more and more, current paint performance can not meet the user demand of people, in life-time service, at moisture content, oxygen, under the attack of the conditions such as ultraviolet, polymer also can degraded slowly, namely so-called aging, illumination, high temperature and humidity cause paint coating loss of gloss, fade, xanthochromia, the major cause of efflorescence, the work-ing life of paint will be reduced.

Summary of the invention

For the deficiencies in the prior art, the problem to be solved in the present invention is, provides a kind of paint with good weatherability properties, has high-wearing feature and resistance to cracking, highly polished, excellent in weather, and the quality product of production is high, and use range is wide, does not pollute.

For solving prior art problem, technical scheme provided by the invention is, a kind of paint with good weatherability properties, and it is made up of the raw material of following parts by weight:

Fluoro-resin 12-22 part, tri (propylene glycol) diacrylate 7-11 part, isocyanic ester 1-4 part, butylacetate 8-13 part, ethylene glycol bis glycidyl ether 3-4 part, process white 6-10 part, diacetone-acryloamide(DAA) 3-6 part, acrylic resin 10-17 part, catalyzer 6-8 part, stearic acid 7-14 part, iron rust 2-4 part, plant mill base 15-20 part, silicon sol 4-6 part, fluorographite 10-15 part, tetramethyl thiourea 8-10 part, adhesion promoter 4-7 part, amber 2-4 part.

The invention has the beneficial effects as follows: the paint with good weatherability properties of the present invention, has high-wearing feature and resistance to cracking, highly polished, excellent in weather, and the quality product of production is high, and use range is wide, do not pollute.

Embodiment

embodiment 1

Have a paint for good weatherability properties, it is made up of the raw material of following parts by weight:

Fluoro-resin 12 parts, tri (propylene glycol) diacrylate 7 parts, isocyanic ester 1 part, butylacetate 8 parts, ethylene glycol bis glycidyl ether 3 parts, process white 6 parts, diacetone-acryloamide(DAA) 3 parts, acrylic resin 10 parts, catalyzer 6 parts, stearic acid 7 parts, 2 parts, iron rust, plant mill base 15 parts, silicon sol 4 parts, fluorographite 10 parts, tetramethyl thiourea 8 parts, adhesion promoter 4 parts, amber 2 parts.

embodiment 2

Have a paint for good weatherability properties, it is made up of the raw material of following parts by weight:

Fluoro-resin 22 parts, tri (propylene glycol) diacrylate 11 parts, isocyanic ester 4 parts, butylacetate 13 parts, ethylene glycol bis glycidyl ether 4 parts, process white 10 parts, diacetone-acryloamide(DAA) 6 parts, acrylic resin 17 parts, catalyzer 8 parts, stearic acid 14 parts, 4 parts, iron rust, plant mill base 20 parts, silicon sol 6 parts, fluorographite 15 parts, tetramethyl thiourea 10 parts, adhesion promoter 7 parts, amber 4 parts.

Claims (1)

1. there is a paint for good weatherability properties, it is characterized in that: it is made up of the raw material of following parts by weight:

Fluoro-resin 12-22 part, tri (propylene glycol) diacrylate 7-11 part, isocyanic ester 1-4 part, butylacetate 8-13 part, ethylene glycol bis glycidyl ether 3-4 part, process white 6-10 part, diacetone-acryloamide(DAA) 3-6 part, acrylic resin 10-17 part, catalyzer 6-8 part, stearic acid 7-14 part, iron rust 2-4 part, plant mill base 15-20 part, silicon sol 4-6 part, fluorographite 10-15 part, tetramethyl thiourea 8-10 part, adhesion promoter 4-7 part, amber 2-4 part.