CN104926242A - 一种混凝土裂缝修补灌浆料及其制备方法 - Google Patents

一种混凝土裂缝修补灌浆料及其制备方法 Download PDF

Info

Publication number
CN104926242A
CN104926242A CN201510290303.6A CN201510290303A CN104926242A CN 104926242 A CN104926242 A CN 104926242A CN 201510290303 A CN201510290303 A CN 201510290303A CN 104926242 A CN104926242 A CN 104926242A
Authority
CN
China
Prior art keywords
grouting material
concrete crack
parts
component
repairing concrete
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510290303.6A
Other languages
English (en)
Inventor
邓小旭
周强
程凯斌
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hubei Chidge Technology Co Ltd
Original Assignee
Hubei Chidge Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hubei Chidge Technology Co Ltd filed Critical Hubei Chidge Technology Co Ltd
Priority to CN201510290303.6A priority Critical patent/CN104926242A/zh
Publication of CN104926242A publication Critical patent/CN104926242A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种灌浆料及制备方法，属于工程材料领域，具体涉及一种混凝土裂缝修补灌浆料及制备方法。该混凝土裂缝修补灌浆料，包括如下重量份数的组分：水泥550～950份；玻璃微珠5～30份；方解石20～50份；膨胀组分50～200份；减水剂1～20份；消泡剂0.5～2份；稳定剂0.5～2份；缓凝组分0.5～10份；促凝组分0.1～2份。该混凝土裂缝修补灌浆料具有较好的流动性、快速凝结、稳定性、填充性、粘结性、早强、微膨胀性。

Description

一种混凝土裂缝修补灌浆料及其制备方法
技术领域
本发明涉及一种灌浆料及制备方法，属于工程材料领域，具体涉及一种混凝土裂缝修补灌浆料及制备方法。
背景技术
由于水泥混凝土材料的固有特性，在路面施工过程中受各种因素影响，产生裂缝是不可避免的。但是现有的混凝土裂缝修补灌浆料一般采用各种粒度和成分不同听水泥，这类材料刚度太大，而且界面粘结性能差，若要作为路面裂缝的修补材料，必须进行改性。
因此对于研究一种具有较好的流动性、快速凝结、稳定性、填充性、粘结性、早强、微膨胀性的用于混凝土裂缝修补的灌浆料具有重要的意义。
发明内容
本发明主要是解决现有技术所存在的上述的技术问题，提供了一种混凝土裂缝修补灌浆料及制备方法。该混凝土裂缝修补灌浆料具有较好的流动性、快速凝结、稳定性、填充性、粘结性、早强、微膨胀性。
为了解决上述问题，根据本发明的一个方面，提供了一种混凝土裂缝修补灌浆料，包括如下重量份数的组分：
优化的，上述的一种混凝土裂缝修补灌浆料，所述水泥包括如下重量份数的组分：
硫铝酸盐水泥   250～400份；
硅酸盐水泥     300～550份。
优化的，上述的一种混凝土裂缝修补灌浆料，所述膨胀组分为UEA膨胀剂或/和CSA膨胀剂。
优化的，上述的一种混凝土裂缝修补灌浆料，所述的减水剂为聚羧酸盐类高效减水剂、萘系高效减水剂、三聚氰胺高效减水剂、脂肪族高效减水剂、氨基磺酸系高效减水剂中的一种以上。
优化的，上述的一种混凝土裂缝修补灌浆料，所述稳定剂包括如下重量份数的组分：
优化的，上述的一种混凝土裂缝修补灌浆料，所述缓凝组分为柠檬酸、酒石酸、硼酸、钙糖和葡萄糖酸钠的一种或几种。
优化的，上述的一种混凝土裂缝修补灌浆料，所述促凝组分为甲酸钙、碳酸锂、硫酸钙和硫酸钠的一种或几种。
为了解决上述问题，根据本发明的另一个方面，提供了一种制备上述的混凝土裂缝修补灌浆料的方法，包括：将各组分混合均匀后，以0.24～0.28的水料比加水，使用制浆机快速搅拌制得混凝土裂缝修补灌浆料。
因此，本发明具有如下优点：该高强混凝土裂缝修补灌浆料具有较好的流动性、可操作时间长、稳定性、填充性、早强、高强、微膨胀性。
具体实施方式
以下通过实施例形式对本发明的上述内容再作进一步的详细说明，但不应将此理解为本发明上述主题的范围仅限于以下的实施例，凡基于本发明上述内容所实现的技术均属于本发明的范围。
实施例：
一种混凝土裂缝修补灌浆料，包括如下重量份数的组分：
其中，稳定剂包括如下重量份数的组分：
本实施例中的膨胀组份可选择UEA膨胀剂或/和CSA膨胀剂。减水剂为聚羧酸盐类高效减水剂、萘系高效减水剂、三聚氰胺高效减水剂、脂肪族高效减水剂、氨基磺酸系高效减水剂中的一种以上；缓凝组分为柠檬酸、酒石酸、硼酸、钙糖和葡萄糖酸钠的一种或几种。促凝组分为甲酸钙、碳酸锂、硫酸钙和硫酸钠的一种或几种。
使用时，将该材料加水直接高速搅拌，水与材料的重量比为0.24～0.28。该混凝土裂缝修补灌浆料具有较好的流动性、快速凝结、稳定性、填充性、粘结性、早强、微膨胀性。
该材料适用于混凝土由于材料干缩徐变、结构位移、温度应力、施工质量等原因而产生的混凝土梁、板、墙等结构裂缝修补，该材料现场加水高速搅拌制成灌浆浆液，通过钻孔埋设灌浆嘴，使用压力将其注入结构裂缝中，使其扩散、凝固，达到防水、堵漏、补强、加固的目的。
本文中所描述的具体实施例仅仅是对本发明精神作举例说明。本发明所属技术领域的技术人员可以对所描述的具体实施例做各种各样的修改或补充或采用类似的方式替代，但并不会偏离本发明的精神或者超越所附权利要求书所定义的范围。

Claims (8)

1.一种混凝土裂缝修补灌浆料，其特征在于，包括如下重量份数的组分：
2.根据权利要求1所述的一种混凝土裂缝修补灌浆料，其特征在于，所述水泥包括如下重量份数的组分：
硫铝酸盐水泥    250～400份；
硅酸盐水泥      300～550份。
3.根据权利要求1所述的一种混凝土裂缝修补灌浆料，其特征在于，所述膨胀组分为UEA膨胀剂或/和CSA膨胀剂。
4.根据权利要求1所述的一种混凝土裂缝修补灌浆料，其特征在于，所述的减水剂为聚羧酸盐类高效减水剂、萘系高效减水剂、三聚氰胺高效减水剂、脂肪族高效减水剂、氨基磺酸系高效减水剂中的一种以上。
5.根据权利要求1所述的一种混凝土裂缝修补灌浆料，其特征在于，所述稳定剂包括如下重量份数的组分：
6.根据权利要求1所述的一种混凝土裂缝修补灌浆料，其特征在于，所述缓凝组分为柠檬酸、酒石酸、硼酸、钙糖和葡萄糖酸钠的一种或几种。
7.根据权利要求1所述的一种混凝土裂缝修补灌浆料，其特征在于，所述促凝组分为甲酸钙、碳酸锂、硫酸钙和硫酸钠的一种或几种。
8.一种制备权利要求1所述的混凝土裂缝修补灌浆料的方法，其特征在于，将各组分混合均匀后，以0.24～0.28的水料比加水，使用制浆机快速搅拌制得混凝土裂缝修补灌浆料。
CN201510290303.6A 2015-05-29 2015-05-29 一种混凝土裂缝修补灌浆料及其制备方法 Pending CN104926242A (zh)