CN104908140A - Method for manufacturing decorative sheet by eucalypt leftover materials - Google Patents
Method for manufacturing decorative sheet by eucalypt leftover materials Download PDFInfo
- Publication number
- CN104908140A CN104908140A CN201510286185.1A CN201510286185A CN104908140A CN 104908140 A CN104908140 A CN 104908140A CN 201510286185 A CN201510286185 A CN 201510286185A CN 104908140 A CN104908140 A CN 104908140A
- Authority
- CN
- China
- Prior art keywords
- gained
- decorative sheet
- eucalypt
- base bar
- timber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a method for manufacturing a decorative sheet by eucalypt leftover materials, and relates to the field of decorative sheet processing methods. The method for manufacturing the decorative sheet by the eucalypt leftover materials comprises the steps of drying, two-side planing, splicing, pressing, material cutting and tooth combing, tooth connecting, pasting, horizontal band sawing, four-side planing, modeling, sanding and sawing off to obtain a finished decorative sheet product. According to the method for manufacturing the decorative sheet by the eucalypt leftover materials, the economic value of eucalypt is improved after the eucalypt leftover materials are effectively utilized to manufacture the decorative sheet; the production costs of an enterprise are reduced, and the enterprise profit is improved. The decorative sheet produced by the method provided by the invention has strong toughness, can resist deforming, warping and cracking, also has a function of resisting moths and ants, and is durable in use.
Description
Technical field
The present invention relates to a kind of dalle processing method field, especially a kind of method making decorative panel of eucalyptus clout.
Background technology
Nowadays dalle processing enterprise gets more and more, compete more and more fierce, add the bullish factor of the costs such as artificial, raw material, profit margin is more and more less, how to reduce costs, enhance productivity make profit maximization be enterprise be not eliminated in competition process even can run business big and strong key factor.
Eucalyptus is fast, cycle of rotational cutting is short, is a kind of important economic timber, and 50-60% is used for fiber and wood pulp material, and 20% for solid wood.Again because Eucalyptus Wood can prevent ant in worm effectively, the solid wood furniture be therefore made into also can be mothproof, durable in use.But eucalyptus rotary-cut clout is if eucalyptus core is because density is low, material is softer, contracting wrinkle rate is relatively high, if make solid wood board, easily ftracture, affect quality and attractive in appearance, tradition Application way is according to being worth the bundle that can do mop, broom from high to low respectively, do raw material or the papermaking material of fiberboard and do firewood and artificial carbon, economic worth is low, and price is cheap.
So using the raw material of eucalyptus core as Wood panel for decoration, can not only reduce enterprise and become to produce cost, improve profit, promoting enterprise is enhanced competitiveness, and can also effectively utilize eucalyptus clout, improves eucalyptus economic worth.
Summary of the invention
The invention provides a kind of method making decorative panel of eucalyptus clout, the problem not only solve and effectively utilize eucalyptus clout, improving eucalyptus economic worth, also reduces enterprise's production cost, improves enterprise profit.
In order to solve the problem, the technical solution adopted in the present invention is: this method making decorative panel of eucalyptus clout, is characterized in that including following steps:
A, drying: eucalyptus rotary-cut clout is carried out drying, being dried to moisture content is less than 10%;
B, both sides of plane part: after being cooled by steps A gained timber, carry out both sides of plane part process;
C, splicing: planing surface glue being coated in step B gained timber, and the described timber filling glue by planing surface and planing surface bonding;
D, compacting: the timber that step C gained has spliced is put and suppresses 12 hours to obtain blanket in a mold;
E, fracture comb: step D gained blanket is pressed different size sawed-off, and comb process is carried out to two ends obtain base bar;
F, toe joint: polylith step e gained base bar is pressed comb splicing by different size;
G, pasting: the mortar for filling cracks is smeared to the spliced base bar of step F gained;
H, horizontal band resaw: horizontal band resaw is carried out to step G gained base bar by different-thickness specification;
J, shaping: by the requirement of final products, through the base bar of horizontal band resaw, four side moulder to be carried out to step H gained, moulding, sanding, sawed-off process obtain decorative panel finished product.
Owing to have employed technique scheme, the present invention compared with prior art has following beneficial effect:
1, calculate through manufacturing enterprise, the technical scheme recorded with the present invention produces Wood panel for decoration, although step is more, cost reduction 20 ~ 30%, greatly improves corporate profit margin, can promoting enterprise existence and developing in competition trend.
The Wood panel for decoration toughness of 2, making by the present invention is comparatively strong, can resistance to deformation, warpage, crack resistence, has again favorable moth-proof ant function, durable in use concurrently.
3, the Wood panel for decoration lines made by the present invention is beautiful, by force ornamental.
Detailed description of the invention
Below in conjunction with instantiation, the invention will be further described:
This method with eucalyptus clout making decorative panel includes following steps:
A, drying: eucalyptus rotary-cut clout is put into jet drier and carries out drying, being dried to moisture content is less than 10%;
B, both sides of plane part: after being cooled by steps A gained timber, carry out both sides of plane part process;
C, splicing: planing surface glue being coated in step B gained timber, and the described timber filling glue by planing surface and planing surface bonding;
D, compacting: the timber that step C gained has spliced is put and suppresses 12 hours to obtain blanket in a mold;
E, fracture comb: step D gained blanket is pressed different size sawed-off, and comb process is carried out to two ends obtain base bar;
F, toe joint: polylith step e gained base bar is pressed comb splicing by different size;
G, pasting: the mortar for filling cracks is smeared to the spliced base bar of step F gained;
H, horizontal band resaw: horizontal band resaw is carried out to step G gained base bar by different-thickness specification;
J, shaping: by the requirement of final products, through the base bar of horizontal band resaw, four side moulder to be carried out to step H gained, moulding, sanding, sawed-off process obtain decorative panel finished product.
The decorative panel toughness made is comparatively strong, can resistance to deformation, warpage, crack resistence, has again favorable moth-proof ant function, durable in use concurrently.
Claims (1)
1. make a method for decorative panel of eucalyptus clout, it is characterized in that including following steps:
A, drying: eucalyptus rotary-cut clout is carried out drying, being dried to moisture content is less than 10%;
B, both sides of plane part: after being cooled by steps A gained timber, carry out both sides of plane part process;
C, splicing: planing surface glue being coated in step B gained timber, and the described timber filling glue by planing surface and planing surface bonding;
D, compacting: the timber that step C gained has spliced is put and suppresses 12 hours to obtain blanket in a mold;
E, fracture comb: step D gained blanket is pressed different size sawed-off, and comb process is carried out to two ends obtain base bar;
F, toe joint: polylith step e gained base bar is pressed comb splicing by different size;
G, pasting: the mortar for filling cracks is smeared to the spliced base bar of step F gained;
H, horizontal band resaw: horizontal band resaw is carried out to step G gained base bar by different-thickness specification;
J, shaping: by the requirement of final products, through the base bar of horizontal band resaw, four side moulder to be carried out to step H gained, moulding, sanding, sawed-off process obtain decorative panel finished product.