CN104894736A - Aramid fiber coated continuous glass fiber cut-resistant fabric and preparation method thereof - Google Patents
Aramid fiber coated continuous glass fiber cut-resistant fabric and preparation method thereof Download PDFInfo
- Publication number
- CN104894736A CN104894736A CN201510362570.XA CN201510362570A CN104894736A CN 104894736 A CN104894736 A CN 104894736A CN 201510362570 A CN201510362570 A CN 201510362570A CN 104894736 A CN104894736 A CN 104894736A
- Authority
- CN
- China
- Prior art keywords
- continuous glass
- resistant fabric
- glass fibre
- fanglun
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to an aramid fiber coated continuous glass fiber cut-resistant fabric and a preparation method thereof. The cut-resistant fabric is manufactured by use of covering yarn, wherein the continuous glass fibers are taken as the core yarns, while the aramid 1414 is taken as the covering fibers. The preparation method comprises the steps of spinning the covering yarns on a ring spinning frame, putting the continuous glass fibers through a yarn guide rod and directly feeding into a front roller via a collector, and spinning. The cut-resistant fabric is high in strength, excellent in wear resistance, low in production cost and good in cut resistance, and can be applied to wider market.
Description
Technical field
The invention belongs to cut resistant fabric and preparation field thereof, particularly a kind of cut resistant fabric and preparation method thereof of Fanglun l414 bag continuous glass fibre.
Background technology
On market today, the fabric of cut resistant is of many uses, multiplex in cut resistant gloves, and for the work of some cutting classes, the safeguard function of gloves is vital.The general multiplex aramid fiber of traditional cut resistant fabric, the characteristic of aramid fiber is exactly high strength and high-modulus, and wherein the intensity of Fanglun l414 can reach more than 22CN/dtex, and comparing with hardness of steel is its 3 times, is 4 times of the polyester industrial yarn that intensity is higher.Thus, Fanglun l414 is the optimal selection of cut resistant fabric.From 2004, country was very fast to the demand growth of aramid fiber, but domestic market major part is occupied by external minority manufacturer, and the supply of goods is limited, and price is higher, more difficultly met domestic demand.More complicated production procedure and higher production cost make aramid fiber be limited in application on the market.
Summary of the invention
Technical problem to be solved by this invention is to provide cut resistant fabric of a kind of Fanglun l414 bag continuous glass fibre and preparation method thereof, the cut resistant fabric intensity of this invention is large, tool has good wearability, and the belt cutting-resisting property that production cost is low and good is applied to market widely.
The cut resistant fabric of a kind of Fanglun l414 bag continuous glass fibre of the present invention, the material of described cut resistant fabric is cladded yarn; Wherein, continuous glass fibre is as heart yarn, and Fanglun l414 is as outer wrapping fiber.
The specification of described continuous glass fibre is 50D-200D.
The preparation method of the cut resistant fabric of a kind of Fanglun l414 bag continuous glass fibre of the present invention, comprising: spun core-spun yarn on ring spinning frame, and continuous glass fibre, by after lever jack, directly feeds front roller through collector, spins and get final product.
The specification of gained yarn is 5s-50s.
On ring spinning frame during spun core-spun yarn, continuous glass fibre, by after lever jack, directly feeds front roller through collector, and feeds without the horn mouth of rear roller, otherwise there will be and lead inextensible phenomenon, cannot spin.
Coated Fanglun l414, by traditional spinning method, makes it the surface being coated on heart yarn, is namely completed the process of spinning by twisting, winding shaping.
Described continuous glass fibre, as heart yarn, strengthens wear-resisting, cut resistant intensity; Described Fanglun l414, as outer wrapping fiber, strengthens yarn strength widely, and anti-cutting performance is given prominence to.
The cladded yarn adopting RING SPINNING to produce can be used for production cut resistant fabric, is generally used for gloves.
Fanglun l414 is more expensive, can reduce production cost with the cored of continuous glass fibre, also improves intensity and the ABRASION RESISTANCE of cladded yarn simultaneously, thus the fabric of spinning has the function of cut resistant.
Cut resistant fabric of the present invention adopts cladded yarn technology, and continuous glass fibre, as heart yarn, provides high-strength belt cutting-resisting property, and the Fanglun l414 performance of outsourcing is given prominence to, and adds the bulk strength of cladded yarn.The cored of two kinds of high-intensity fibers, greatly strengthens ABRASION RESISTANCE and the intensity of yarn, more meets the performance requirement of cut resistant.Further, due to the more difficult production of Fanglun l414 and cost is higher, so the continuous glass fibre increased, also can replace the purposes of part Fanglun l414, thus reduce production cost, expand market application.
beneficial effect
(1) cut resistant fabric intensity of the present invention is large, and tool has good wearability, and the belt cutting-resisting property that production cost is low and good is applied to market widely;
(2) cut resistant fabric of the present invention, generally can be used on gloves, when wearing gloves, cuts class work for some danger, can play the effect that protection hand is not scratched.
Detailed description of the invention
Below in conjunction with specific embodiment, set forth the present invention further.Should be understood that these embodiments are only not used in for illustration of the present invention to limit the scope of the invention.In addition should be understood that those skilled in the art can make various changes or modifications the present invention, and these equivalent form of values fall within the application's appended claims limited range equally after the content of having read the present invention's instruction.
Embodiment 1
1) continuous glass fibre is heart yarn: glass fiber strength is higher, as inner core, can strengthen the bulk strength of cladded yarn after coated by outer wrapping fiber.
2) Fanglun l414 is as outer wrapping fiber: aramid fiber performance is given prominence to, high strength and modulus.
3) adopt RING SPINNING to prepare above-mentioned cladded yarn: by above-mentioned 1) and 2) in continuous glass fibre, Fanglun l414 twist together and spin resultant yarn.During coated yarn spinning, continuous glass fibre is without the drafting system of fine spining machine, and directly from front roller feeding, then acted on by twisting, Fanglun l414 looping forms cladded yarn on the surface of continuous glass fibre.Wherein, filament of glass fiber is 100D, and the fineness of cladded yarn is 30S; The skin of fabric is the rib stitch of cladded yarn, and internal layer rib stitch is the low elastic polyester filament composition of 100D; The grammes per square metre of fabric is 350 grams/m; Fabric cutting resistance, reaches 5 grades.
Claims (4)
1. a cut resistant fabric for Fanglun l414 bag continuous glass fibre, is characterized in that, the material of described cut resistant fabric is cladded yarn; Wherein, continuous glass fibre is as heart yarn, and Fanglun l414 is as outer wrapping fiber.
2. the cut resistant fabric of a kind of Fanglun l414 bag continuous glass fibre according to claim 1, is characterized in that, the specification of described continuous glass fibre is 50D-200D.
3. a preparation method for the cut resistant fabric of Fanglun l414 bag continuous glass fibre, comprising: spun core-spun yarn on ring spinning frame, and continuous glass fibre, by after lever jack, directly feeds front roller through collector, spins and get final product.
4. the preparation method of the cut resistant fabric of a kind of Fanglun l414 bag continuous glass fibre according to claim 3, is characterized in that, the specification of gained yarn is 5s-50s.