CN104893378A - 一种低成本高效马来酸酐接枝聚乙烯改性沥青防水卷材及其制备方法 - Google Patents

一种低成本高效马来酸酐接枝聚乙烯改性沥青防水卷材及其制备方法 Download PDF

Info

Publication number
CN104893378A
CN104893378A CN201510234257.8A CN201510234257A CN104893378A CN 104893378 A CN104893378 A CN 104893378A CN 201510234257 A CN201510234257 A CN 201510234257A CN 104893378 A CN104893378 A CN 104893378A
Authority
CN
China
Prior art keywords
maleic anhydride
anhydride grafted
grafted polyethylene
asphalt
coiled material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510234257.8A
Other languages
English (en)
Inventor
蒋能
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Kuailai Waterproofing & Anti-Corrosion Co Ltd
Original Assignee
Anhui Kuailai Waterproofing & Anti-Corrosion Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Kuailai Waterproofing & Anti-Corrosion Co Ltd filed Critical Anhui Kuailai Waterproofing & Anti-Corrosion Co Ltd
Priority to CN201510234257.8A priority Critical patent/CN104893378A/zh
Publication of CN104893378A publication Critical patent/CN104893378A/zh
Pending legal-status Critical Current

Abstract

本发明涉及改性沥青防水卷材领域，具体涉及一种低成本高效马来酸酐接枝聚乙烯改性沥青防水卷材及其制备方法，该防水卷材以改性复合沥青作为基料，这种复合沥青材料利用马来酸酐接枝聚乙烯对基质沥青进行改性处理，其与基质沥青的相容性好，能有效的提高基质沥青的韧性，此外在其中掺混了价廉的改性高炉矿渣微粉和粉煤灰复合粉体，不仅达到了良好的增韧补强效果，还有效的降低了生产成本，以这种复合改性沥青基材制备得到的防水卷材不仅具有良好的防水效果，在实际使用过程中热稳定性好，粘接性好，生产过程环保高效，资源利用率高，市场竞争力强。

Description

一种低成本高效马来酸酐接枝聚乙烯改性沥青防水卷材及其制备方法
技术领域
本发明涉及改性沥青防水卷材领域，具体涉及一种低成本高效马来酸酐接枝聚乙烯改性沥青防水卷材及其制备方法。
背景技术
自粘聚合物改性沥青防水卷材是一种很有发展前景的新型防水材料，在国内外刚刚崛起，方兴未艾。它是由沥青与SBS、TP、浸水剂等助剂反应共混合成高聚物改性沥青基料，再配以活性助剂制成防水胶料，再以聚乙烯膜(铝箔或彩砂)作为表面材料，以自粘防水隔离层作为底层，制成了一种具有不透水性、低温柔度、抗变形性能及自愈性好等特点的防水卷材。随着自粘性沥青防水卷材使用范围的拓展，对材料的性能要求越来越高，急切需要研制一类生产成本低、资源利用率高、温差稳定性好、粘性持久、安全性高的改性沥青卷材。
发明内容
本发明的目的在于，提供一种低成本高效马来酸酐接枝聚乙烯改性沥青防水卷材及其制备方法，在降低生产成本的同时改善卷材的使用性能，为了实现上述目的，本发明采用的技术方案如下：
一种低成本高效马来酸酐接枝聚乙烯改性沥青防水卷材，其特征在于，该防水卷材以马来酸酐接枝聚乙烯改性沥青作为复合基料，该复合基料由以下重量份的原料制成：硅溶胶8-10、粉煤灰3-5、马来酸酐接枝聚乙烯18-24、硬脂酸1-2、基质沥青60-80、丙烯酸异辛酯2-3、有机硅流平剂0.8-1、N-羟甲基丙烯酰胺1-2、高炉矿渣微粉12-16、甲基硅油1-2、硅烷偶联剂1-2、环烷油12-18、十二烷基苯磺酸钠0.1-0.2、聚乙二醇2-3、水适量。
所述的一种低成本高效马来酸酐接枝聚乙烯改性沥青防水卷材及其制备方法，其特征在于，所述的制备方法包含以下步骤：
(1)先将高炉矿渣微粉送入恒温干燥箱中，在80-100℃条件下完全干燥除去水分，干燥结束后粉体自然冷却备用，接着将聚乙二醇溶于水中，配制成5-8wt％的溶液，随后将干燥后的高炉矿渣微粉与粉煤灰一起投入聚乙二醇溶液中，再加入十二烷基苯磺酸钠，在50-60℃条件下混合研磨60-80min，研磨结束后将物料烘干完全除去水分，得预处理高炉矿渣微粉和粉煤灰复合粉体，最后将预处理后的复合粉体与硅烷偶联剂、环烷油混合搅拌50-60min，所得浆料备用；
(2)将基质沥青投入搅拌容器中，加热至160-180℃，搅拌50-60min后投入步骤(1)所得浆料，升温至180-200℃，继续搅拌混合60-80min，接着降温至130-150℃，投入其它剩余物料，高速混合搅拌60-80min，得改性沥青混合基料，随后将其涂布于胎基两面，控制厚度，经冷却、覆膜、弯曲、包装后入库。
有益效果：本发明利用马来酸酐接枝聚乙烯对基质沥青进行改性处理，其与基质沥青的相容性好，能有效的提高基质沥青的韧性，此外在其中掺混了价廉的改性高炉矿渣微粉和粉煤灰复合粉体，不仅达到了良好的增韧补强效果，还有效的降低了生产成本，以这种复合改性沥青基材制备得到的防水卷材不仅具有良好的防水效果，在实际使用过程中热稳定性好，粘接性好，生产过程环保高效，资源利用率高，市场竞争力强。
具体实施方式
实施例
本实施例的防水卷材用改性沥青基料由以下重量份的原料制成：硅溶胶8、粉煤灰4、马来酸酐接枝聚乙烯20、硬脂酸1.2、基质沥青65、丙烯酸异辛酯2.5、有机硅流平剂0.8、N-羟甲基丙烯酰胺1.5、高炉矿渣微粉14、甲基硅油1.5、硅烷偶联剂1.5、环烷油16、十二烷基苯磺酸钠0.1、聚乙二醇2.5、水适量。
所述的一种低成本高效马来酸酐接枝聚乙烯改性沥青防水卷材的制备方法如下：
(1)先将高炉矿渣微粉送入恒温干燥箱中，在80-100℃条件下完全干燥除去水分，干燥结束后粉体自然冷却备用，接着将聚乙二醇溶于水中，配制成5wt％的溶液，随后将干燥后的高炉矿渣微粉与粉煤灰一起投入聚乙二醇溶液中，再加入十二烷基苯磺酸钠，在50-60℃条件下混合研磨70min，研磨结束后将物料烘干完全除去水分，得预处理高炉矿渣微粉和粉煤灰复合粉体，最后将预处理后的复合粉体与硅烷偶联剂、环烷油混合搅拌60min，所得浆料备用；
(2)将基质沥青投入搅拌容器中，加热至160-180℃，搅拌60min后投入步骤(1)所得浆料，升温至180-200℃，继续搅拌混合70min，接着降温至130-150℃，投入其它剩余物料，高速混合搅拌65min，得改性沥青混合基料，随后将其涂布于胎基两面，控制厚度，经冷却、覆膜、弯曲、包装后入库。
本实施例制得的防水卷材性能测试结果如下：
检测项目 检测值
耐热性/℃ 120℃无流淌、无滴落
低温柔性/℃ -20℃无裂痕
不透水性(0.3Mpa，120min) 不透水
拉伸强度(N/50mm) ≥840
最大拉力时延伸率/％ 45
剥离强度(N/mm，卷材与铝板) 2.1
热老化(尺寸变化率) 2.0％

Claims (2)

1.一种低成本高效马来酸酐接枝聚乙烯改性沥青防水卷材，其特征在于，该防水卷材以马来酸酐接枝聚乙烯改性沥青作为复合基料，该复合基料由以下重量份的原料制成：硅溶胶8-10、粉煤灰3-5、马来酸酐接枝聚乙烯18-24、硬脂酸1-2、基质沥青60-80、丙烯酸异辛酯2-3、有机硅流平剂0.8-1、N-羟甲基丙烯酰胺1-2、高炉矿渣微粉12-16、甲基硅油1-2、硅烷偶联剂1-2、环烷油12-18、十二烷基苯磺酸钠0.1-0.2、聚乙二醇2-3、水适量。
2.如权利要求1所述的一种低成本高效马来酸酐接枝聚乙烯改性沥青防水卷材及其制备方法，其特征在于，所述的制备方法包含以下步骤：
（1）先将高炉矿渣微粉送入恒温干燥箱中，在80-100℃条件下完全干燥除去水分，干燥结束后粉体自然冷却备用，接着将聚乙二醇溶于水中，配制成5-8wt%的溶液，随后将干燥后的高炉矿渣微粉与粉煤灰一起投入聚乙二醇溶液中，再加入十二烷基苯磺酸钠，在50-60℃条件下混合研磨60-80min，研磨结束后将物料烘干完全除去水分，得预处理高炉矿渣微粉和粉煤灰复合粉体，最后将预处理后的复合粉体与硅烷偶联剂、环烷油混合搅拌50-60min，所得浆料备用；
（2）将基质沥青投入搅拌容器中，加热至160-180℃，搅拌50-60min后投入步骤（1）所得浆料，升温至180-200℃，继续搅拌混合60-80min，接着降温至130-150℃，投入其它剩余物料，高速混合搅拌60-80min，得改性沥青混合基料，随后将其涂布于胎基两面，控制厚度，经冷却、覆膜、弯曲、包装后入库。
CN201510234257.8A 2015-05-09 2015-05-09 一种低成本高效马来酸酐接枝聚乙烯改性沥青防水卷材及其制备方法 Pending CN104893378A (zh)